- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.4
- 弯曲强度 [MPa]: 160.0
- 弯曲模量 [MPa]: 8.20
- 热变形温度 [℃]: 245.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO R1183 | ||
| Water Absorption | 0.40 % | 0.40 % | 23°C / 24 hrs; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 23°C / 50% RH; ISO 62 | ||
| 1.9 % | 1.9 % | in 23°C water; ISO 62 | |||
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 455 °F | after drying; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 83 | 83 | ISO 868 | ||
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | ISO R527 | ||
| Elongation at Break | 3.4 % | 3.4 % | ISO R527 | ||
| Modulus of Elasticity | 9.60 GPa | 1390 ksi | ISO R527 | ||
| Flexural Strength | 240 MPa | 34800 psi | After conditioning at 23°C and 50% RH; ISO 178 | ||
| Flexural Modulus | 8.20 GPa | 1190 ksi | After conditioning at 23°C and 50% RH; ISO 178 | ||
| Charpy Impact, Notched | 2.25 J/cm² | 10.7 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af | ||
| 20.0 J/cm² @Temperature -20.0 °C | 95.2 ft-lb/in² @Temperature -4.00 °F | After conditioning at 23°C/50%RH; ISO 179/Af | |||
| Tensile Creep Modulus, 1 hour | 9320 MPa | 1.35e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.90e+15 ohm-cm | 1.90e+15 ohm-cm | ASTM D257 | ||
| Surface Resistance | 4.80e+15 ohm | 4.80e+15 ohm | ASTM D257 | ||
| Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm | 864 kV/in @Thickness 0.0394 in | ASTM D149 | ||
| Dissipation Factor | 0.015 @Frequency 100000 Hz | 0.015 @Frequency 100000 Hz | NFC 26 230 | ||
| 0.030 @Frequency 100 Hz | 0.030 @Frequency 100 Hz | NFC 26 230 | |||
| 0.031 @Frequency 1000 Hz | 0.031 @Frequency 1000 Hz | NFC 26 230 | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 17.0 µm/m-°C @Temperature 20.0 - 60.0 °C | 9.44 µin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 - 60.0 °C | 55.6 µin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer | ||
| Melting Point | 255 °C | 491 °F | ISO R1218 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO R75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO R75 | ||
| Vicat Softening Point | 200 °C | 392 °F | 50 N - B method; ISO 306 | ||
| >= 230 °C | >= 446 °F | 10 N - A method; ISO 306 | |||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| Automotive classification | B-3 | FMVSS 302 | |||