- 吸水率 [%]: 1.4
- 缺口冲击强度: 0.98
- 拉伸强度 [MPa]: 157.0
- 弯曲模量 [MPa]: 7.60
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | Wet |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | Dry; ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | Dry; ASTM D785 |
| Tensile Strength, Yield | 157 MPa | 22800 psi | Wet; ASTM D638 |
| 194 MPa | 28100 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 4.0 % | 4.0 % | Wet; ASTM D638 | |
| Flexural Strength | 245 MPa | 35500 psi | Wet; ASTM D790 |
| 294 MPa | 42600 psi | Dry; ASTM D790 | |
| Flexural Modulus | 7.60 GPa | 1100 ksi | Wet; ASTM D790 |
| 9.60 GPa | 1390 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.980 J/cm | 1.84 ft-lb/in | Dry; ASTM D256 |
| 1.18 J/cm | 2.21 ft-lb/in | Wet; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Dry; ASTM D648 |