- 吸水率 [%]: 2.1
- 缺口冲击强度: 0.49
- 拉伸强度 [MPa]: 79.0
- 弯曲模量 [MPa]: 2.50
- 硬度: 120.0
- 热变形温度 [℃]: 258.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | Dry; ASTM D792 |
| Water Absorption | 2.1 % | 2.1 % | Wet |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 71 | 71 | Wet; ASTM D785 |
| 94 | 94 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 120 | 120 | Dry; ASTM D785 |
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | Wet; ASTM D638 |
| 108 MPa | 15700 psi | Dry; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | Dry; ASTM D638 |
| 8.0 % | 8.0 % | Wet; ASTM D638 | |
| Flexural Strength | 108 MPa | 15700 psi | Wet; ASTM D790 |
| 167 MPa | 24200 psi | Dry; ASTM D790 | |
| Flexural Modulus | 2.50 GPa | 363 ksi | Wet; ASTM D790 |
| 4.90 GPa | 711 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | Dry; ASTM D256 |
| 0.590 J/cm | 1.11 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 9.0 | 9.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |