- 吸水率 [%]: 2.3
- 缺口冲击强度: 0.29
- 拉伸强度 [MPa]: 58.0
- 弯曲模量 [MPa]: 1.30
- 硬度: 110.0
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | Dry; ASTM D792 |
| Water Absorption | 2.3 % | 2.3 % | Wet |
| Linear Mold Shrinkage | 0.0090 - 0.016 cm/cm | 0.0090 - 0.016 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55 | 55 | Wet; ASTM D785 |
| 85 | 85 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 110 | 110 | Wet; ASTM D785 |
| 120 | 120 | Dry; ASTM D785 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | Wet; ASTM D638 |
| 83.0 MPa | 12000 psi | Dry; ASTM D638 | |
| Elongation at Break | 7.0 % | 7.0 % | Dry; ASTM D638 |
| 70 % | 70 % | Wet; ASTM D638 | |
| Flexural Strength | 56.0 MPa | 8120 psi | Wet; ASTM D790 |
| 128 MPa | 18600 psi | Dry; ASTM D790 | |
| Flexural Modulus | 1.30 GPa | 189 ksi | Wet; ASTM D790 |
| 3.30 GPa | 479 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | Dry; ASTM D256 |
| 0.980 J/cm | 1.84 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 7.0 | 7.0 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Dry; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | Dry |
| Oxygen Index | 36 % | 36 % | Dry; ASTM D2863 |