- 吸水率 [%]: 1.3
- 缺口冲击强度: 0.3
- 拉伸强度 [MPa]: 98.0
- 弯曲模量 [MPa]: 5.60
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | Wet |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 89 | 89 | Dry; ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | Dry; ASTM D785 |
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | Wet; ASTM D638 |
| 127 MPa | 18400 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 3.5 % | 3.5 % | Wet; ASTM D638 | |
| Flexural Strength | 166 MPa | 24100 psi | Wet; ASTM D790 |
| 206 MPa | 29900 psi | Dry; ASTM D790 | |
| Flexural Modulus | 5.60 GPa | 812 ksi | Wet; ASTM D790 |
| 6.50 GPa | 943 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | Dry; ASTM D256 |
| 0.350 J/cm | 0.656 ft-lb/in | Wet; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | Dry; ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Dry; ASTM D648 |