- 密度 [g/cm3]: 1.07
- 缺口冲击强度: 8.59
- 弯曲强度 [MPa]: 48.0
- 弯曲模量 [MPa]: 1.80
- 硬度: 107.0
- 热变形温度 [℃]: 187.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.07 g/cc | 0.0387 lb/in³ | |
Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell R | 107 | 107 | ASTM D785 |
Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 |
Elongation at Break | 47 % | 47 % | ASTM D638 |
Flexural Strength | 72.0 MPa | 10400 psi | ASTM D790 |
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
Izod Impact, Notched | 8.59 J/cm | 16.1 ft-lb/in | ASTM D256 |
Izod Impact, Unnotched | NB | NB | ASTM D256 |
Thermal Properties | Metric | English | Comments |
Melting Point | 255 - 275 °C | 491 - 527 °F | |
Deflection Temperature at 0.46 MPa (66 psi) | 187 °C | 369 °F | ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
Processing Properties | Metric | English | Comments |
Processing Temperature | 285 - 302 °C | 545 - 576 °F | Approximate middle barrel temperature range |