- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 5.7
- 缺口冲击强度: 15.0
- 弯曲强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 6.30
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 5.7 % | 5.7 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 5.0 % | 5.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 7.40 GPa | 1070 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 6.30 GPa | 914 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179 | ||
| 7.50 J/cm² @Temperature -30.0 °C | 35.7 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 | ||
| 1.10 J/cm² @Temperature -30.0 °C | 5.24 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||