- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 4.8
- 缺口冲击强度: 17.0
- 弯曲强度 [MPa]: 167.0
- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 4.8 % | 4.8 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 167 MPa | 24200 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179 | ||
| 8.70 J/cm² @Temperature -30.0 °C | 41.4 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179 | ||
| 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||