- 吸水率 [%]: 1.2
- 缺口冲击强度: 1.59
- 拉伸强度 [MPa]: 59.0
- 弯曲模量 [MPa]: 1.897
- 硬度: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 3.17 mm | 0.015 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 35 - 50 % | 35 - 50 % | ASTM D638 |
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 1.897 GPa | 275.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.59 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 2.98 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ASTM D648 |