- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.7
- 成型收缩率 [%]: 0.01
- 缺口冲击强度: 0.48
- 弯曲模量 [MPa]: 0.620
- 硬度: 120.0
- 热变形温度 [℃]: 205.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.42 g/cc | 1.42 g/cc | DAM; ASTM D792 | ||
Density | 1.41 g/cc | 0.0509 lb/in³ | DAM; ISO 1183 | ||
Filler Content | 36 % | 36 % | DAM | ||
Water Absorption | 0.70 % @Temperature 23.0 °C | 0.70 % @Temperature 73.4 °F | Immersion 24h; DAM; ASTM D570 | ||
1.2 % @Temperature 23.0 °C | 1.2 % @Temperature 73.4 °F | Immersion 24h; DAM; ISO 62, Similar to | |||
1.7 % @Temperature 23.0 °C | 1.7 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | |||
4.7 % @Temperature 23.0 °C | 4.7 % @Temperature 73.4 °F | Saturation; DAM; ASTM D570 | |||
6.2 % @Temperature 23.0 °C | 6.2 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | Flow; DAM | ||
0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | Transverse; DAM | |||
0.011 cm/cm @Thickness 1.60 mm | 0.011 in/in @Thickness 0.0630 in | Flow; DAM | |||
0.011 cm/cm @Thickness 1.60 mm | 0.011 in/in @Thickness 0.0630 in | Transverse; DAM | |||
0.014 cm/cm @Thickness 6.40 mm | 0.014 in/in @Thickness 0.252 in | Flow; DAM | |||
0.014 cm/cm @Thickness 6.40 mm | 0.014 in/in @Thickness 0.252 in | Transverse; DAM | |||
Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Rockwell M | 85 | 85 | DAM; ASTM D785 | ||
Hardness, Rockwell R | 120 | 120 | DAM; ASTM D785 | ||
Tensile Strength at Break | 58.0 MPa @Temperature 23.0 °C | 8410 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
Tensile Strength | 32.0 MPa @Temperature 121 °C | 4640 psi @Temperature 250 °F | 50%RH; ASTM D638 | ||
39.0 MPa @Temperature 121 °C | 5660 psi @Temperature 250 °F | DAM; ASTM D638 | |||
41.0 MPa @Temperature 77.0 °C | 5950 psi @Temperature 171 °F | 50%RH; ASTM D638 | |||
52.0 MPa @Temperature 77.0 °C | 7540 psi @Temperature 171 °F | DAM; ASTM D638 | |||
61.0 MPa @Temperature 23.0 °C | 8850 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
79.0 MPa @Temperature 23.0 °C | 11500 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
121 MPa @Temperature -40.0 °C | 17500 psi @Temperature -40.0 °F | 50%RH; ASTM D638 | |||
124 MPa @Temperature -40.0 °C | 18000 psi @Temperature -40.0 °F | DAM; ASTM D638 | |||
Tensile Stress | 0.580 MPa @Strain 0.100 %, Temperature 150 °C | 84.1 psi @Strain 0.100 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | ||
0.700 MPa @Strain 0.100 %, Temperature 120 °C | 102 psi @Strain 0.100 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
0.800 MPa @Strain 0.100 %, Temperature 150 °C | 116 psi @Strain 0.100 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
0.900 MPa @Strain 0.100 %, Temperature 120 °C | 131 psi @Strain 0.100 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
0.900 MPa @Strain 0.100 %, Temperature 100 °C | 131 psi @Strain 0.100 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
1.00 MPa @Strain 0.100 %, Temperature 100 °C | 145 psi @Strain 0.100 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
1.00 MPa @Strain 0.100 %, Temperature 80.0 °C | 145 psi @Strain 0.100 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
1.16 MPa @Strain 0.200 %, Temperature 150 °C | 168 psi @Strain 0.200 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
1.20 MPa @Strain 0.100 %, Temperature 60.0 °C | 174 psi @Strain 0.100 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
1.30 MPa @Strain 0.100 %, Temperature 80.0 °C | 189 psi @Strain 0.100 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
1.50 MPa @Strain 0.200 %, Temperature 120 °C | 218 psi @Strain 0.200 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
1.59 MPa @Strain 0.200 %, Temperature 150 °C | 231 psi @Strain 0.200 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
1.75 MPa @Strain 0.300 %, Temperature 150 °C | 254 psi @Strain 0.300 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
1.80 MPa @Strain 0.200 %, Temperature 120 °C | 261 psi @Strain 0.200 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
1.80 MPa @Strain 0.200 %, Temperature 100 °C | 261 psi @Strain 0.200 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
2.00 MPa @Strain 0.200 %, Temperature 100 °C | 290 psi @Strain 0.200 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
2.00 MPa @Strain 0.200 %, Temperature 80.0 °C | 290 psi @Strain 0.200 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
2.10 MPa @Strain 0.100 %, Temperature 60.0 °C | 305 psi @Strain 0.100 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
2.13 MPa @Strain 0.400 %, Temperature 150 °C | 309 psi @Strain 0.400 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
2.20 MPa @Strain 0.300 %, Temperature 120 °C | 319 psi @Strain 0.300 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
2.20 MPa @Strain 0.100 %, Temperature 23.0 °C | 319 psi @Strain 0.100 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
2.24 MPa @Strain 0.300 %, Temperature 150 °C | 325 psi @Strain 0.300 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
2.30 MPa @Strain 0.200 %, Temperature 60.0 °C | 334 psi @Strain 0.200 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
2.60 MPa @Strain 0.400 %, Temperature 120 °C | 377 psi @Strain 0.400 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
2.68 MPa @Strain 0.200 %, Temperature 80.0 °C | 389 psi @Strain 0.200 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
2.70 MPa @Strain 0.300 %, Temperature 120 °C | 392 psi @Strain 0.300 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
2.70 MPa @Strain 0.300 %, Temperature 100 °C | 392 psi @Strain 0.300 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
2.90 MPa @Strain 0.300 %, Temperature 100 °C | 421 psi @Strain 0.300 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
2.90 MPa @Strain 0.300 %, Temperature 80.0 °C | 421 psi @Strain 0.300 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
3.10 MPa @Strain 0.500 %, Temperature 150 °C | 450 psi @Strain 0.500 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
3.20 MPa @Strain 0.400 %, Temperature 100 °C | 464 psi @Strain 0.400 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
3.20 MPa @Strain 0.400 %, Temperature 120 °C | 464 psi @Strain 0.400 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
3.30 MPa @Strain 0.400 %, Temperature 100 °C | 479 psi @Strain 0.400 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
3.30 MPa @Strain 0.300 %, Temperature 60.0 °C | 479 psi @Strain 0.300 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
3.34 MPa @Strain 0.400 %, Temperature 150 °C | 484 psi @Strain 0.400 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
3.59 MPa @Strain 0.600 %, Temperature 150 °C | 521 psi @Strain 0.600 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
3.60 MPa @Strain 0.500 %, Temperature 120 °C | 522 psi @Strain 0.500 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
3.92 MPa @Strain 0.300 %, Temperature 80.0 °C | 569 psi @Strain 0.300 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
3.98 MPa @Strain 0.500 %, Temperature 150 °C | 577 psi @Strain 0.500 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
4.07 MPa @Strain 0.700 %, Temperature 150 °C | 590 psi @Strain 0.700 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
4.10 MPa @Strain 0.400 %, Temperature 80.0 °C | 595 psi @Strain 0.400 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
4.10 MPa @Strain 0.200 %, Temperature 60.0 °C | 595 psi @Strain 0.200 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
4.30 MPa @Strain 0.200 %, Temperature 23.0 °C | 624 psi @Strain 0.200 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
4.30 MPa @Strain 0.500 %, Temperature 100 °C | 624 psi @Strain 0.500 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
4.30 MPa @Strain 0.500 %, Temperature 120 °C | 624 psi @Strain 0.500 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
4.40 MPa @Strain 0.600 %, Temperature 120 °C | 638 psi @Strain 0.600 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
4.50 MPa @Strain 0.500 %, Temperature 100 °C | 653 psi @Strain 0.500 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
4.60 MPa @Strain 0.400 %, Temperature 60.0 °C | 667 psi @Strain 0.400 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
4.66 MPa @Strain 0.800 %, Temperature 150 °C | 676 psi @Strain 0.800 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
4.69 MPa @Strain 0.600 %, Temperature 150 °C | 680 psi @Strain 0.600 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
4.71 MPa @Strain 0.400 %, Temperature 80.0 °C | 683 psi @Strain 0.400 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
4.80 MPa @Strain 0.700 %, Temperature 120 °C | 696 psi @Strain 0.700 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
4.90 MPa @Strain 0.500 %, Temperature 80.0 °C | 711 psi @Strain 0.500 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
5.00 MPa @Strain 0.100 %, Temperature 0.000 °C | 725 psi @Strain 0.100 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
5.04 MPa @Strain 0.900 %, Temperature 150 °C | 731 psi @Strain 0.900 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
5.10 MPa @Strain 0.600 %, Temperature 100 °C | 740 psi @Strain 0.600 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
5.10 MPa @Strain 0.100 %, Temperature 23.0 °C | 740 psi @Strain 0.100 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
5.20 MPa @Strain 0.600 %, Temperature 120 °C | 754 psi @Strain 0.600 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
5.30 MPa @Strain 0.100 %, Temperature 0.000 °C | 769 psi @Strain 0.100 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
5.33 MPa @Strain 0.800 %, Temperature 150 °C | 773 psi @Strain 0.800 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
5.40 MPa @Strain 0.800 %, Temperature 120 °C | 783 psi @Strain 0.800 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
5.40 MPa @Strain 0.600 %, Temperature 100 °C | 783 psi @Strain 0.600 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
5.63 MPa @Strain 1.00 %, Temperature 150 °C | 817 psi @Strain 1.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
5.70 MPa @Strain 0.500 %, Temperature 60.0 °C | 827 psi @Strain 0.500 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
5.80 MPa @Strain 0.600 %, Temperature 80.0 °C | 841 psi @Strain 0.600 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
5.90 MPa @Strain 0.700 %, Temperature 100 °C | 856 psi @Strain 0.700 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
5.98 MPa @Strain 0.900 %, Temperature 150 °C | 867 psi @Strain 0.900 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
6.00 MPa @Strain 0.900 %, Temperature 120 °C | 870 psi @Strain 0.900 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
6.00 MPa @Strain 0.300 %, Temperature 60.0 °C | 870 psi @Strain 0.300 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
6.08 MPa @Strain 0.700 %, Temperature 120 °C | 882 psi @Strain 0.700 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
6.10 MPa @Strain 0.300 %, Temperature 23.0 °C | 885 psi @Strain 0.300 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
6.20 MPa @Strain 0.700 %, Temperature 100 °C | 899 psi @Strain 0.700 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
6.30 MPa @Strain 0.100 %, Temperature -40.0 °C | 914 psi @Strain 0.100 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
6.31 MPa @Strain 1.10 %, Temperature 150 °C | 915 psi @Strain 1.10 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
6.37 MPa @Strain 0.500 %, Temperature 80.0 °C | 924 psi @Strain 0.500 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
6.60 MPa @Strain 0.600 %, Temperature 60.0 °C | 957 psi @Strain 0.600 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
6.60 MPa @Strain 1.00 %, Temperature 120 °C | 957 psi @Strain 1.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
6.60 MPa @Strain 0.800 %, Temperature 100 °C | 957 psi @Strain 0.800 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
6.60 MPa @Strain 0.700 %, Temperature 80.0 °C | 957 psi @Strain 0.700 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
6.62 MPa @Strain 1.00 %, Temperature 150 °C | 960 psi @Strain 1.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
6.70 MPa @Strain 0.100 %, Temperature -40.0 °C | 972 psi @Strain 0.100 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
6.78 MPa @Strain 0.800 %, Temperature 120 °C | 983 psi @Strain 0.800 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
6.79 MPa @Strain 1.20 %, Temperature 150 °C | 985 psi @Strain 1.20 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
6.90 MPa @Strain 0.800 %, Temperature 100 °C | 1000 psi @Strain 0.800 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
7.10 MPa @Strain 0.400 %, Temperature 60.0 °C | 1030 psi @Strain 0.400 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
7.13 MPa @Strain 1.10 %, Temperature 150 °C | 1030 psi @Strain 1.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
7.18 MPa @Strain 1.30 %, Temperature 150 °C | 1040 psi @Strain 1.30 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
7.20 MPa @Strain 1.10 %, Temperature 120 °C | 1040 psi @Strain 1.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
7.20 MPa @Strain 0.800 %, Temperature 80.0 °C | 1040 psi @Strain 0.800 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
7.30 MPa @Strain 0.700 %, Temperature 60.0 °C | 1060 psi @Strain 0.700 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
7.40 MPa @Strain 0.900 %, Temperature 100 °C | 1070 psi @Strain 0.900 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
7.42 MPa @Strain 0.900 %, Temperature 120 °C | 1080 psi @Strain 0.900 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
7.48 MPa @Strain 0.600 %, Temperature 80.0 °C | 1080 psi @Strain 0.600 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
7.50 MPa @Strain 0.400 %, Temperature 23.0 °C | 1090 psi @Strain 0.400 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
7.57 MPa @Strain 1.40 %, Temperature 150 °C | 1100 psi @Strain 1.40 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
7.65 MPa @Strain 0.900 %, Temperature 100 °C | 1110 psi @Strain 0.900 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
7.70 MPa @Strain 1.20 %, Temperature 120 °C | 1120 psi @Strain 1.20 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
7.71 MPa @Strain 1.20 %, Temperature 150 °C | 1120 psi @Strain 1.20 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
7.90 MPa @Strain 1.00 %, Temperature 100 °C | 1150 psi @Strain 1.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
7.95 MPa @Strain 1.50 %, Temperature 150 °C | 1150 psi @Strain 1.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
8.06 MPa @Strain 1.00 %, Temperature 120 °C | 1170 psi @Strain 1.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
8.10 MPa @Strain 1.30 %, Temperature 120 °C | 1170 psi @Strain 1.30 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
8.19 MPa @Strain 1.00 %, Temperature 100 °C | 1190 psi @Strain 1.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
8.20 MPa @Strain 0.900 %, Temperature 80.0 °C | 1190 psi @Strain 0.900 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
8.23 MPa @Strain 1.30 %, Temperature 150 °C | 1190 psi @Strain 1.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
8.40 MPa @Strain 1.40 %, Temperature 120 °C | 1220 psi @Strain 1.40 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
8.40 MPa @Strain 1.10 %, Temperature 100 °C | 1220 psi @Strain 1.10 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
8.44 MPa @Strain 1.60 %, Temperature 150 °C | 1220 psi @Strain 1.60 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
8.59 MPa @Strain 0.700 %, Temperature 80.0 °C | 1250 psi @Strain 0.700 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
8.60 MPa @Strain 0.800 %, Temperature 60.0 °C | 1250 psi @Strain 0.800 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
8.64 MPa @Strain 1.10 %, Temperature 120 °C | 1250 psi @Strain 1.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
8.73 MPa @Strain 1.70 %, Temperature 150 °C | 1270 psi @Strain 1.70 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
8.80 MPa @Strain 1.40 %, Temperature 150 °C | 1280 psi @Strain 1.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
8.80 MPa @Strain 1.10 %, Temperature 100 °C | 1280 psi @Strain 1.10 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
8.90 MPa @Strain 1.50 %, Temperature 120 °C | 1290 psi @Strain 1.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
9.10 MPa @Strain 1.20 %, Temperature 100 °C | 1320 psi @Strain 1.20 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
9.22 MPa @Strain 1.80 %, Temperature 150 °C | 1340 psi @Strain 1.80 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
9.25 MPa @Strain 1.50 %, Temperature 150 °C | 1340 psi @Strain 1.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
9.28 MPa @Strain 1.20 %, Temperature 120 °C | 1350 psi @Strain 1.20 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
9.30 MPa @Strain 1.00 %, Temperature 80.0 °C | 1350 psi @Strain 1.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
9.40 MPa @Strain 1.60 %, Temperature 120 °C | 1360 psi @Strain 1.60 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
9.50 MPa @Strain 1.20 %, Temperature 100 °C | 1380 psi @Strain 1.20 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
9.55 MPa @Strain 0.800 %, Temperature 80.0 °C | 1390 psi @Strain 0.800 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
9.70 MPa @Strain 0.900 %, Temperature 60.0 °C | 1410 psi @Strain 0.900 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
9.70 MPa @Strain 1.30 %, Temperature 100 °C | 1410 psi @Strain 1.30 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
9.70 MPa @Strain 1.90 %, Temperature 150 °C | 1410 psi @Strain 1.90 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
9.77 MPa @Strain 1.60 %, Temperature 150 °C | 1420 psi @Strain 1.60 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
9.80 MPa @Strain 1.70 %, Temperature 120 °C | 1420 psi @Strain 1.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
9.80 MPa @Strain 0.500 %, Temperature 23.0 °C | 1420 psi @Strain 0.500 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
9.86 MPa @Strain 1.30 %, Temperature 120 °C | 1430 psi @Strain 1.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
9.90 MPa @Strain 1.10 %, Temperature 80.0 °C | 1440 psi @Strain 1.10 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
9.90 MPa @Strain 0.500 %, Temperature 60.0 °C | 1440 psi @Strain 0.500 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
9.99 MPa @Strain 2.00 %, Temperature 150 °C | 1450 psi @Strain 2.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
10.0 MPa @Strain 0.200 %, Temperature 0.000 °C | 1450 psi @Strain 0.200 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
10.1 MPa @Strain 0.200 %, Temperature 23.0 °C | 1460 psi @Strain 0.200 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
10.2 MPa @Strain 1.80 %, Temperature 120 °C | 1480 psi @Strain 1.80 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
10.21 MPa @Strain 1.30 %, Temperature 100 °C | 1481 psi @Strain 1.30 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
10.28 MPa @Strain 1.70 %, Temperature 150 °C | 1491 psi @Strain 1.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
10.3 MPa @Strain 1.40 %, Temperature 100 °C | 1490 psi @Strain 1.40 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
10.37 MPa @Strain 1.40 %, Temperature 120 °C | 1504 psi @Strain 1.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
10.38 MPa @Strain 2.10 %, Temperature 150 °C | 1505 psi @Strain 2.10 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
10.4 MPa @Strain 1.20 %, Temperature 80.0 °C | 1510 psi @Strain 1.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
10.4 MPa @Strain 1.00 %, Temperature 60.0 °C | 1510 psi @Strain 1.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
10.42 MPa @Strain 0.900 %, Temperature 80.0 °C | 1511 psi @Strain 0.900 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
10.67 MPa @Strain 2.20 %, Temperature 150 °C | 1548 psi @Strain 2.20 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
10.67 MPa @Strain 1.80 %, Temperature 150 °C | 1548 psi @Strain 1.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
10.7 MPa @Strain 1.90 %, Temperature 120 °C | 1550 psi @Strain 1.90 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
10.73 MPa @Strain 0.200 %, Temperature 0.000 °C | 1556 psi @Strain 0.200 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
10.78 MPa @Strain 1.40 %, Temperature 100 °C | 1564 psi @Strain 1.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
10.88 MPa @Strain 1.60 %, Temperature 120 °C | 1578 psi @Strain 1.60 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
10.9 MPa @Strain 1.50 %, Temperature 100 °C | 1580 psi @Strain 1.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
11.0 MPa @Strain 1.30 %, Temperature 80.0 °C | 1600 psi @Strain 1.30 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
11.06 MPa @Strain 2.30 %, Temperature 150 °C | 1604 psi @Strain 2.30 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
11.1 MPa @Strain 2.00 %, Temperature 120 °C | 1610 psi @Strain 2.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
11.1 MPa @Strain 1.10 %, Temperature 60.0 °C | 1610 psi @Strain 1.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
11.25 MPa @Strain 1.90 %, Temperature 150 °C | 1632 psi @Strain 1.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
11.3 MPa @Strain 0.600 %, Temperature 23.0 °C | 1640 psi @Strain 0.600 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
11.32 MPa @Strain 1.00 %, Temperature 80.0 °C | 1642 psi @Strain 1.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
11.33 MPa @Strain 1.70 %, Temperature 120 °C | 1643 psi @Strain 1.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
11.35 MPa @Strain 2.40 %, Temperature 150 °C | 1646 psi @Strain 2.40 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
11.4 MPa @Strain 1.60 %, Temperature 100 °C | 1650 psi @Strain 1.60 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
11.46 MPa @Strain 1.50 %, Temperature 100 °C | 1662 psi @Strain 1.50 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
11.5 MPa @Strain 2.10 %, Temperature 120 °C | 1670 psi @Strain 2.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
11.57 MPa @Strain 2.00 %, Temperature 150 °C | 1678 psi @Strain 2.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
11.6 MPa @Strain 1.40 %, Temperature 80.0 °C | 1680 psi @Strain 1.40 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
11.64 MPa @Strain 2.50 %, Temperature 150 °C | 1688 psi @Strain 2.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
11.7 MPa @Strain 2.20 %, Temperature 120 °C | 1700 psi @Strain 2.20 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
11.8 MPa @Strain 1.70 %, Temperature 100 °C | 1710 psi @Strain 1.70 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
11.8 MPa @Strain 1.20 %, Temperature 60.0 °C | 1710 psi @Strain 1.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
11.9 MPa @Strain 1.80 %, Temperature 120 °C | 1730 psi @Strain 1.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
11.9 MPa @Strain 1.60 %, Temperature 100 °C | 1730 psi @Strain 1.60 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
11.93 MPa @Strain 2.60 %, Temperature 150 °C | 1730 psi @Strain 2.60 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
11.95 MPa @Strain 2.20 %, Temperature 150 °C | 1733 psi @Strain 2.20 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
12.0 MPa @Strain 2.30 %, Temperature 120 °C | 1740 psi @Strain 2.30 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
12.17 MPa @Strain 1.10 %, Temperature 80.0 °C | 1765 psi @Strain 1.10 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
12.2 MPa @Strain 0.600 %, Temperature 60.0 °C | 1770 psi @Strain 0.600 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
12.22 MPa @Strain 2.70 %, Temperature 150 °C | 1772 psi @Strain 2.70 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
12.3 MPa @Strain 1.50 %, Temperature 80.0 °C | 1780 psi @Strain 1.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
12.32 MPa @Strain 1.70 %, Temperature 100 °C | 1787 psi @Strain 1.70 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
12.35 MPa @Strain 1.90 %, Temperature 120 °C | 1791 psi @Strain 1.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
12.4 MPa @Strain 1.80 %, Temperature 100 °C | 1800 psi @Strain 1.80 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
12.4 MPa @Strain 2.40 %, Temperature 120 °C | 1800 psi @Strain 2.40 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
12.4 MPa @Strain 2.30 %, Temperature 150 °C | 1800 psi @Strain 2.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
12.42 MPa @Strain 2.80 %, Temperature 150 °C | 1801 psi @Strain 2.80 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
12.49 MPa @Strain 0.200 %, Temperature -40.0 °C | 1812 psi @Strain 0.200 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
12.5 MPa @Strain 1.30 %, Temperature 60.0 °C | 1810 psi @Strain 1.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
12.71 MPa @Strain 2.90 %, Temperature 150 °C | 1843 psi @Strain 2.90 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
12.79 MPa @Strain 2.40 %, Temperature 150 °C | 1855 psi @Strain 2.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
12.8 MPa @Strain 2.50 %, Temperature 120 °C | 1860 psi @Strain 2.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
12.8 MPa @Strain 1.90 %, Temperature 100 °C | 1860 psi @Strain 1.90 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
12.86 MPa @Strain 2.00 %, Temperature 120 °C | 1865 psi @Strain 2.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
12.9 MPa @Strain 0.700 %, Temperature 23.0 °C | 1870 psi @Strain 0.700 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
12.93 MPa @Strain 1.80 %, Temperature 100 °C | 1875 psi @Strain 1.80 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
13.01 MPa @Strain 1.20 %, Temperature 80.0 °C | 1887 psi @Strain 1.20 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
13.1 MPa @Strain 1.40 %, Temperature 60.0 °C | 1900 psi @Strain 1.40 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
13.1 MPa @Strain 1.60 %, Temperature 80.0 °C | 1900 psi @Strain 1.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
13.1 MPa @Strain 2.60 %, Temperature 120 °C | 1900 psi @Strain 2.60 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
13.1 MPa @Strain 3.00 %, Temperature 150 °C | 1900 psi @Strain 3.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
13.18 MPa @Strain 2.50 %, Temperature 150 °C | 1912 psi @Strain 2.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
13.25 MPa @Strain 2.10 %, Temperature 120 °C | 1922 psi @Strain 2.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
13.4 MPa @Strain 2.00 %, Temperature 100 °C | 1940 psi @Strain 2.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
13.4 MPa @Strain 2.70 %, Temperature 120 °C | 1940 psi @Strain 2.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
13.43 MPa @Strain 2.60 %, Temperature 150 °C | 1948 psi @Strain 2.60 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
13.48 MPa @Strain 3.10 %, Temperature 150 °C | 1955 psi @Strain 3.10 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
13.5 MPa @Strain 1.90 %, Temperature 100 °C | 1960 psi @Strain 1.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
13.5 MPa @Strain 0.200 %, Temperature -40.0 °C | 1960 psi @Strain 0.200 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
13.6 MPa @Strain 1.70 %, Temperature 80.0 °C | 1970 psi @Strain 1.70 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
13.68 MPa @Strain 3.20 %, Temperature 150 °C | 1984 psi @Strain 3.20 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
13.7 MPa @Strain 2.80 %, Temperature 120 °C | 1990 psi @Strain 2.80 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
13.7 MPa @Strain 2.20 %, Temperature 120 °C | 1990 psi @Strain 2.20 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
13.7 MPa @Strain 1.50 %, Temperature 60.0 °C | 1990 psi @Strain 1.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
13.75 MPa @Strain 2.70 %, Temperature 150 °C | 1994 psi @Strain 2.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
13.76 MPa @Strain 1.30 %, Temperature 80.0 °C | 1996 psi @Strain 1.30 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
13.9 MPa @Strain 0.700 %, Temperature 60.0 °C | 2020 psi @Strain 0.700 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
13.9 MPa @Strain 2.90 %, Temperature 120 °C | 2020 psi @Strain 2.90 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
13.9 MPa @Strain 2.10 %, Temperature 100 °C | 2020 psi @Strain 2.10 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
13.97 MPa @Strain 3.30 %, Temperature 150 °C | 2026 psi @Strain 3.30 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
14.05 MPa @Strain 2.00 %, Temperature 100 °C | 2038 psi @Strain 2.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
14.07 MPa @Strain 2.80 %, Temperature 150 °C | 2041 psi @Strain 2.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
14.08 MPa @Strain 2.30 %, Temperature 120 °C | 2042 psi @Strain 2.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
14.1 MPa @Strain 1.80 %, Temperature 80.0 °C | 2050 psi @Strain 1.80 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
14.1 MPa @Strain 0.800 %, Temperature 23.0 °C | 2050 psi @Strain 0.800 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
14.16 MPa @Strain 3.40 %, Temperature 150 °C | 2054 psi @Strain 3.40 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
14.2 MPa @Strain 3.00 %, Temperature 120 °C | 2060 psi @Strain 3.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
14.3 MPa @Strain 1.60 %, Temperature 60.0 °C | 2070 psi @Strain 1.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
14.4 MPa @Strain 2.10 %, Temperature 100 °C | 2090 psi @Strain 2.10 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
14.4 MPa @Strain 2.20 %, Temperature 100 °C | 2090 psi @Strain 2.20 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
14.45 MPa @Strain 3.50 %, Temperature 150 °C | 2096 psi @Strain 3.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
14.46 MPa @Strain 2.90 %, Temperature 150 °C | 2097 psi @Strain 2.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
14.5 MPa @Strain 3.10 %, Temperature 120 °C | 2100 psi @Strain 3.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
14.5 MPa @Strain 1.90 %, Temperature 80.0 °C | 2100 psi @Strain 1.90 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
14.51 MPa @Strain 1.40 %, Temperature 80.0 °C | 2105 psi @Strain 1.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
14.53 MPa @Strain 2.40 %, Temperature 120 °C | 2107 psi @Strain 2.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
14.55 MPa @Strain 3.60 %, Temperature 150 °C | 2110 psi @Strain 3.60 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
14.78 MPa @Strain 3.00 %, Temperature 150 °C | 2144 psi @Strain 3.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
14.78 MPa @Strain 2.20 %, Temperature 100 °C | 2144 psi @Strain 2.20 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
14.8 MPa @Strain 3.20 %, Temperature 120 °C | 2150 psi @Strain 3.20 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
14.84 MPa @Strain 3.70 %, Temperature 150 °C | 2152 psi @Strain 3.70 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
14.9 MPa @Strain 2.30 %, Temperature 100 °C | 2160 psi @Strain 2.30 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
14.91 MPa @Strain 2.50 %, Temperature 120 °C | 2163 psi @Strain 2.50 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
15.0 MPa @Strain 2.00 %, Temperature 80.0 °C | 2180 psi @Strain 2.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
15.0 MPa @Strain 3.30 %, Temperature 120 °C | 2180 psi @Strain 3.30 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
15.04 MPa @Strain 3.80 %, Temperature 150 °C | 2181 psi @Strain 3.80 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
15.1 MPa @Strain 3.10 %, Temperature 150 °C | 2190 psi @Strain 3.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
15.1 MPa @Strain 1.70 %, Temperature 60.0 °C | 2190 psi @Strain 1.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
15.1 MPa @Strain 0.900 %, Temperature 23.0 °C | 2190 psi @Strain 0.900 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
15.2 MPa @Strain 1.50 %, Temperature 80.0 °C | 2200 psi @Strain 1.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
15.2 MPa @Strain 0.800 %, Temperature 60.0 °C | 2200 psi @Strain 0.800 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
15.2 MPa @Strain 0.300 %, Temperature 23.0 °C | 2200 psi @Strain 0.300 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
15.2 MPa @Strain 3.40 %, Temperature 120 °C | 2200 psi @Strain 3.40 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
15.2 MPa @Strain 2.40 %, Temperature 100 °C | 2200 psi @Strain 2.40 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
15.23 MPa @Strain 3.90 %, Temperature 150 °C | 2209 psi @Strain 3.90 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
15.26 MPa @Strain 2.30 %, Temperature 100 °C | 2213 psi @Strain 2.30 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
15.3 MPa @Strain 0.300 %, Temperature 0.000 °C | 2220 psi @Strain 0.300 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
15.36 MPa @Strain 2.60 %, Temperature 120 °C | 2228 psi @Strain 2.60 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
15.36 MPa @Strain 3.20 %, Temperature 150 °C | 2228 psi @Strain 3.20 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
15.4 MPa @Strain 2.10 %, Temperature 80.0 °C | 2230 psi @Strain 2.10 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
15.5 MPa @Strain 2.50 %, Temperature 100 °C | 2250 psi @Strain 2.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
15.5 MPa @Strain 3.30 %, Temperature 150 °C | 2250 psi @Strain 3.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
15.5 MPa @Strain 3.50 %, Temperature 120 °C | 2250 psi @Strain 3.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
15.52 MPa @Strain 4.00 %, Temperature 150 °C | 2251 psi @Strain 4.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
15.62 MPa @Strain 4.10 %, Temperature 150 °C | 2265 psi @Strain 4.10 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
15.62 MPa @Strain 3.40 %, Temperature 150 °C | 2265 psi @Strain 3.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
15.68 MPa @Strain 2.40 %, Temperature 100 °C | 2274 psi @Strain 2.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
15.7 MPa @Strain 3.60 %, Temperature 120 °C | 2280 psi @Strain 3.60 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
15.8 MPa @Strain 2.20 %, Temperature 80.0 °C | 2290 psi @Strain 2.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
15.81 MPa @Strain 2.70 %, Temperature 120 °C | 2293 psi @Strain 2.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
15.9 MPa @Strain 1.80 %, Temperature 60.0 °C | 2310 psi @Strain 1.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
15.91 MPa @Strain 4.20 %, Temperature 150 °C | 2308 psi @Strain 4.20 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
15.92 MPa @Strain 1.60 %, Temperature 80.0 °C | 2309 psi @Strain 1.60 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
16.0 MPa @Strain 3.70 %, Temperature 120 °C | 2320 psi @Strain 3.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
16.0 MPa @Strain 3.50 %, Temperature 150 °C | 2320 psi @Strain 3.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
16.0 MPa @Strain 2.60 %, Temperature 100 °C | 2320 psi @Strain 2.60 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
16.01 MPa @Strain 4.30 %, Temperature 150 °C | 2322 psi @Strain 4.30 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
16.05 MPa @Strain 0.300 %, Temperature 0.000 °C | 2328 psi @Strain 0.300 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
16.13 MPa @Strain 2.80 %, Temperature 120 °C | 2339 psi @Strain 2.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
16.19 MPa @Strain 2.50 %, Temperature 100 °C | 2348 psi @Strain 2.50 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
16.2 MPa @Strain 2.30 %, Temperature 80.0 °C | 2350 psi @Strain 2.30 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
16.2 MPa @Strain 4.40 %, Temperature 150 °C | 2350 psi @Strain 4.40 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
16.2 MPa @Strain 3.60 %, Temperature 150 °C | 2350 psi @Strain 3.60 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
16.2 MPa @Strain 3.80 %, Temperature 120 °C | 2350 psi @Strain 3.80 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
16.3 MPa @Strain 3.90 %, Temperature 120 °C | 2360 psi @Strain 3.90 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
16.3 MPa @Strain 4.50 %, Temperature 150 °C | 2360 psi @Strain 4.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
16.4 MPa @Strain 2.70 %, Temperature 100 °C | 2380 psi @Strain 2.70 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
16.4 MPa @Strain 1.90 %, Temperature 60.0 °C | 2380 psi @Strain 1.90 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
16.45 MPa @Strain 3.70 %, Temperature 150 °C | 2386 psi @Strain 3.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
16.51 MPa @Strain 3.00 %, Temperature 120 °C | 2395 psi @Strain 3.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
16.55 MPa @Strain 1.70 %, Temperature 80.0 °C | 2400 psi @Strain 1.70 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
16.57 MPa @Strain 2.60 %, Temperature 100 °C | 2403 psi @Strain 2.60 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
16.59 MPa @Strain 4.60 %, Temperature 150 °C | 2406 psi @Strain 4.60 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
16.6 MPa @Strain 4.00 %, Temperature 120 °C | 2410 psi @Strain 4.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
16.6 MPa @Strain 2.40 %, Temperature 80.0 °C | 2410 psi @Strain 2.40 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
16.6 MPa @Strain 1.00 %, Temperature 23.0 °C | 2410 psi @Strain 1.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
16.7 MPa @Strain 0.900 %, Temperature 60.0 °C | 2420 psi @Strain 0.900 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
16.7 MPa @Strain 2.80 %, Temperature 100 °C | 2420 psi @Strain 2.80 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
16.71 MPa @Strain 3.80 %, Temperature 150 °C | 2424 psi @Strain 3.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
16.78 MPa @Strain 4.70 %, Temperature 150 °C | 2434 psi @Strain 4.70 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
16.83 MPa @Strain 3.10 %, Temperature 120 °C | 2441 psi @Strain 3.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
16.88 MPa @Strain 4.80 %, Temperature 150 °C | 2448 psi @Strain 4.80 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
16.9 MPa @Strain 3.90 %, Temperature 150 °C | 2450 psi @Strain 3.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
16.9 MPa @Strain 4.10 %, Temperature 120 °C | 2450 psi @Strain 4.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
16.9 MPa @Strain 2.00 %, Temperature 60.0 °C | 2450 psi @Strain 2.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
16.93 MPa @Strain 2.70 %, Temperature 100 °C | 2455 psi @Strain 2.70 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
16.98 MPa @Strain 4.90 %, Temperature 150 °C | 2463 psi @Strain 4.90 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
17.0 MPa @Strain 4.20 %, Temperature 120 °C | 2470 psi @Strain 4.20 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
17.0 MPa @Strain 2.50 %, Temperature 80.0 °C | 2470 psi @Strain 2.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
17.0 MPa @Strain 2.90 %, Temperature 100 °C | 2470 psi @Strain 2.90 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
17.1 MPa @Strain 4.30 %, Temperature 120 °C | 2480 psi @Strain 4.30 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
17.16 MPa @Strain 4.00 %, Temperature 150 °C | 2489 psi @Strain 4.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
17.17 MPa @Strain 5.00 %, Temperature 150 °C | 2490 psi @Strain 5.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
17.21 MPa @Strain 3.20 %, Temperature 120 °C | 2496 psi @Strain 3.20 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
17.21 MPa @Strain 1.80 %, Temperature 80.0 °C | 2496 psi @Strain 1.80 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
17.3 MPa @Strain 2.10 %, Temperature 60.0 °C | 2510 psi @Strain 2.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
17.3 MPa @Strain 2.60 %, Temperature 80.0 °C | 2510 psi @Strain 2.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
17.34 MPa @Strain 2.80 %, Temperature 100 °C | 2515 psi @Strain 2.80 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
17.35 MPa @Strain 4.10 %, Temperature 150 °C | 2516 psi @Strain 4.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
17.4 MPa @Strain 4.40 %, Temperature 120 °C | 2520 psi @Strain 4.40 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
17.4 MPa @Strain 3.00 %, Temperature 100 °C | 2520 psi @Strain 3.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
17.6 MPa @Strain 3.30 %, Temperature 120 °C | 2550 psi @Strain 3.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
17.6 MPa @Strain 4.50 %, Temperature 120 °C | 2550 psi @Strain 4.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
17.6 MPa @Strain 1.10 %, Temperature 23.0 °C | 2550 psi @Strain 1.10 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
17.61 MPa @Strain 4.30 %, Temperature 150 °C | 2554 psi @Strain 4.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
17.72 MPa @Strain 1.90 %, Temperature 80.0 °C | 2570 psi @Strain 1.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
17.8 MPa @Strain 2.20 %, Temperature 60.0 °C | 2580 psi @Strain 2.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
17.8 MPa @Strain 4.40 %, Temperature 150 °C | 2580 psi @Strain 4.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
17.8 MPa @Strain 4.60 %, Temperature 120 °C | 2580 psi @Strain 4.60 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
17.8 MPa @Strain 3.10 %, Temperature 100 °C | 2580 psi @Strain 3.10 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
17.82 MPa @Strain 2.90 %, Temperature 100 °C | 2585 psi @Strain 2.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
17.85 MPa @Strain 3.40 %, Temperature 120 °C | 2589 psi @Strain 3.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
17.85 MPa @Strain 5.50 %, Temperature 150 °C | 2589 psi @Strain 5.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
17.9 MPa @Strain 4.70 %, Temperature 120 °C | 2600 psi @Strain 4.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
17.9 MPa @Strain 2.70 %, Temperature 80.0 °C | 2600 psi @Strain 2.70 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
18.0 MPa @Strain 4.80 %, Temperature 120 °C | 2610 psi @Strain 4.80 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
18.05 MPa @Strain 3.50 %, Temperature 120 °C | 2618 psi @Strain 3.50 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
18.06 MPa @Strain 4.50 %, Temperature 150 °C | 2619 psi @Strain 4.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
18.08 MPa @Strain 2.00 %, Temperature 80.0 °C | 2622 psi @Strain 2.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
18.1 MPa @Strain 1.00 %, Temperature 60.0 °C | 2630 psi @Strain 1.00 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
18.2 MPa @Strain 3.20 %, Temperature 100 °C | 2640 psi @Strain 3.20 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
18.21 MPa @Strain 3.00 %, Temperature 100 °C | 2641 psi @Strain 3.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
18.3 MPa @Strain 2.80 %, Temperature 80.0 °C | 2650 psi @Strain 2.80 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
18.3 MPa @Strain 4.90 %, Temperature 120 °C | 2650 psi @Strain 4.90 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
18.3 MPa @Strain 2.30 %, Temperature 60.0 °C | 2650 psi @Strain 2.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
18.31 MPa @Strain 0.300 %, Temperature -40.0 °C | 2656 psi @Strain 0.300 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
18.32 MPa @Strain 4.60 %, Temperature 150 °C | 2657 psi @Strain 4.60 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
18.4 MPa @Strain 5.00 %, Temperature 120 °C | 2670 psi @Strain 5.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
18.4 MPa @Strain 3.30 %, Temperature 100 °C | 2670 psi @Strain 3.30 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
18.43 MPa @Strain 3.10 %, Temperature 100 °C | 2673 psi @Strain 3.10 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
18.45 MPa @Strain 4.70 %, Temperature 150 °C | 2676 psi @Strain 4.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
18.49 MPa @Strain 3.60 %, Temperature 120 °C | 2682 psi @Strain 3.60 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
18.53 MPa @Strain 6.00 %, Temperature 150 °C | 2688 psi @Strain 6.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
18.6 MPa @Strain 2.40 %, Temperature 60.0 °C | 2700 psi @Strain 2.40 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
18.64 MPa @Strain 4.80 %, Temperature 150 °C | 2704 psi @Strain 4.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
18.7 MPa @Strain 2.90 %, Temperature 80.0 °C | 2710 psi @Strain 2.90 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
18.7 MPa @Strain 1.20 %, Temperature 23.0 °C | 2710 psi @Strain 1.20 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
18.71 MPa @Strain 2.10 %, Temperature 80.0 °C | 2714 psi @Strain 2.10 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
18.75 MPa @Strain 3.70 %, Temperature 120 °C | 2719 psi @Strain 3.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
18.78 MPa @Strain 3.20 %, Temperature 100 °C | 2724 psi @Strain 3.20 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
18.8 MPa @Strain 3.40 %, Temperature 100 °C | 2730 psi @Strain 3.40 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
18.83 MPa @Strain 4.90 %, Temperature 150 °C | 2731 psi @Strain 4.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
18.9 MPa @Strain 3.00 %, Temperature 80.0 °C | 2740 psi @Strain 3.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
19.0 MPa @Strain 3.50 %, Temperature 100 °C | 2760 psi @Strain 3.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
19.01 MPa @Strain 3.80 %, Temperature 120 °C | 2757 psi @Strain 3.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
19.1 MPa @Strain 5.50 %, Temperature 120 °C | 2770 psi @Strain 5.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
19.1 MPa @Strain 2.50 %, Temperature 60.0 °C | 2770 psi @Strain 2.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
19.11 MPa @Strain 6.50 %, Temperature 150 °C | 2772 psi @Strain 6.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
19.17 MPa @Strain 3.30 %, Temperature 100 °C | 2780 psi @Strain 3.30 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
19.2 MPa @Strain 3.10 %, Temperature 80.0 °C | 2780 psi @Strain 3.10 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
19.2 MPa @Strain 1.10 %, Temperature 60.0 °C | 2780 psi @Strain 1.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
19.25 MPa @Strain 2.20 %, Temperature 80.0 °C | 2792 psi @Strain 2.20 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
19.3 MPa @Strain 0.400 %, Temperature 0.000 °C | 2800 psi @Strain 0.400 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
19.33 MPa @Strain 4.00 %, Temperature 120 °C | 2804 psi @Strain 4.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
19.38 MPa @Strain 5.40 %, Temperature 150 °C | 2811 psi @Strain 5.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
19.4 MPa @Strain 2.60 %, Temperature 60.0 °C | 2810 psi @Strain 2.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
19.5 MPa @Strain 3.60 %, Temperature 100 °C | 2830 psi @Strain 3.60 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
19.55 MPa @Strain 3.40 %, Temperature 100 °C | 2835 psi @Strain 3.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
19.6 MPa @Strain 3.20 %, Temperature 80.0 °C | 2840 psi @Strain 3.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
19.65 MPa @Strain 4.10 %, Temperature 120 °C | 2850 psi @Strain 4.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
19.69 MPa @Strain 7.00 %, Temperature 150 °C | 2856 psi @Strain 7.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
19.8 MPa @Strain 3.70 %, Temperature 100 °C | 2870 psi @Strain 3.70 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
19.8 MPa @Strain 3.30 %, Temperature 80.0 °C | 2870 psi @Strain 3.30 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
19.8 MPa @Strain 1.30 %, Temperature 23.0 °C | 2870 psi @Strain 1.30 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
19.83 MPa @Strain 2.30 %, Temperature 80.0 °C | 2876 psi @Strain 2.30 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
19.84 MPa @Strain 3.50 %, Temperature 100 °C | 2878 psi @Strain 3.50 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
19.9 MPa @Strain 4.20 %, Temperature 120 °C | 2890 psi @Strain 4.20 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
19.9 MPa @Strain 6.00 %, Temperature 120 °C | 2890 psi @Strain 6.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
20.0 MPa @Strain 3.80 %, Temperature 100 °C | 2900 psi @Strain 3.80 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
20.0 MPa @Strain 2.70 %, Temperature 60.0 °C | 2900 psi @Strain 2.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
20.08 MPa @Strain 7.50 %, Temperature 150 °C | 2912 psi @Strain 7.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
20.1 MPa @Strain 3.40 %, Temperature 80.0 °C | 2920 psi @Strain 3.40 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
20.13 MPa @Strain 3.60 %, Temperature 100 °C | 2920 psi @Strain 3.60 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
20.16 MPa @Strain 4.30 %, Temperature 120 °C | 2924 psi @Strain 4.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
20.2 MPa @Strain 3.90 %, Temperature 100 °C | 2930 psi @Strain 3.90 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
20.2 MPa @Strain 1.20 %, Temperature 60.0 °C | 2930 psi @Strain 1.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
20.21 MPa @Strain 5.90 %, Temperature 150 °C | 2931 psi @Strain 5.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
20.3 MPa @Strain 3.50 %, Temperature 80.0 °C | 2940 psi @Strain 3.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
20.3 MPa @Strain 0.300 %, Temperature -40.0 °C | 2940 psi @Strain 0.300 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
20.35 MPa @Strain 4.40 %, Temperature 120 °C | 2952 psi @Strain 4.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
20.37 MPa @Strain 2.40 %, Temperature 80.0 °C | 2954 psi @Strain 2.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
20.4 MPa @Strain 1.40 %, Temperature 23.0 °C | 2960 psi @Strain 1.40 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
20.45 MPa @Strain 3.70 %, Temperature 100 °C | 2966 psi @Strain 3.70 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
20.47 MPa @Strain 8.00 %, Temperature 150 °C | 2969 psi @Strain 8.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
20.5 MPa @Strain 6.50 %, Temperature 120 °C | 2970 psi @Strain 6.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
20.5 MPa @Strain 2.80 %, Temperature 60.0 °C | 2970 psi @Strain 2.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
20.6 MPa @Strain 3.60 %, Temperature 80.0 °C | 2990 psi @Strain 3.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
20.6 MPa @Strain 4.00 %, Temperature 100 °C | 2990 psi @Strain 4.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
20.67 MPa @Strain 4.50 %, Temperature 120 °C | 2998 psi @Strain 4.50 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
20.76 MPa @Strain 8.50 %, Temperature 150 °C | 3011 psi @Strain 8.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
20.8 MPa @Strain 4.10 %, Temperature 100 °C | 3020 psi @Strain 4.10 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
20.8 MPa @Strain 3.80 %, Temperature 100 °C | 3020 psi @Strain 3.80 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
20.84 MPa @Strain 6.40 %, Temperature 150 °C | 3023 psi @Strain 6.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
20.85 MPa @Strain 2.50 %, Temperature 80.0 °C | 3024 psi @Strain 2.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
20.86 MPa @Strain 4.60 %, Temperature 120 °C | 3025 psi @Strain 4.60 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
20.9 MPa @Strain 2.90 %, Temperature 60.0 °C | 3030 psi @Strain 2.90 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
20.99 MPa @Strain 3.90 %, Temperature 100 °C | 3044 psi @Strain 3.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
21.0 MPa @Strain 4.20 %, Temperature 100 °C | 3050 psi @Strain 4.20 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
21.0 MPa @Strain 7.00 %, Temperature 120 °C | 3050 psi @Strain 7.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
21.0 MPa @Strain 0.400 %, Temperature 23.0 °C | 3050 psi @Strain 0.400 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
21.05 MPa @Strain 9.00 %, Temperature 150 °C | 3053 psi @Strain 9.00 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
21.1 MPa @Strain 3.70 %, Temperature 80.0 °C | 3060 psi @Strain 3.70 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
21.12 MPa @Strain 4.80 %, Temperature 120 °C | 3063 psi @Strain 4.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
21.2 MPa @Strain 4.30 %, Temperature 100 °C | 3070 psi @Strain 4.30 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
21.2 MPa @Strain 3.00 %, Temperature 60.0 °C | 3070 psi @Strain 3.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
21.2 MPa @Strain 1.30 %, Temperature 60.0 °C | 3070 psi @Strain 1.30 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
21.25 MPa @Strain 4.00 %, Temperature 100 °C | 3082 psi @Strain 4.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
21.3 MPa @Strain 3.80 %, Temperature 80.0 °C | 3090 psi @Strain 3.80 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
21.32 MPa @Strain 6.90 %, Temperature 150 °C | 3092 psi @Strain 6.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
21.33 MPa @Strain 0.400 %, Temperature 0.000 °C | 3094 psi @Strain 0.400 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
21.34 MPa @Strain 9.50 %, Temperature 150 °C | 3095 psi @Strain 9.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
21.39 MPa @Strain 2.60 %, Temperature 80.0 °C | 3102 psi @Strain 2.60 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
21.4 MPa @Strain 1.50 %, Temperature 23.0 °C | 3100 psi @Strain 1.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
21.44 MPa @Strain 4.90 %, Temperature 120 °C | 3110 psi @Strain 4.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
21.5 MPa @Strain 4.40 %, Temperature 100 °C | 3120 psi @Strain 4.40 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
21.5 MPa @Strain 7.50 %, Temperature 120 °C | 3120 psi @Strain 7.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
21.5 MPa @Strain 3.10 %, Temperature 60.0 °C | 3120 psi @Strain 3.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
21.57 MPa @Strain 5.40 %, Temperature 120 °C | 3128 psi @Strain 5.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
21.57 MPa @Strain 4.10 %, Temperature 100 °C | 3128 psi @Strain 4.10 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
21.6 MPa @Strain 3.90 %, Temperature 80.0 °C | 3130 psi @Strain 3.90 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
21.63 MPa @Strain 10.0 %, Temperature 150 °C | 3137 psi @Strain 10.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
21.75 MPa @Strain 2.70 %, Temperature 80.0 °C | 3155 psi @Strain 2.70 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
21.79 MPa @Strain 7.40 %, Temperature 150 °C | 3160 psi @Strain 7.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
21.8 MPa @Strain 4.50 %, Temperature 100 °C | 3160 psi @Strain 4.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
21.89 MPa @Strain 4.20 %, Temperature 100 °C | 3175 psi @Strain 4.20 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
21.9 MPa @Strain 4.00 %, Temperature 80.0 °C | 3180 psi @Strain 4.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
21.9 MPa @Strain 8.00 %, Temperature 120 °C | 3180 psi @Strain 8.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
21.9 MPa @Strain 3.20 %, Temperature 60.0 °C | 3180 psi @Strain 3.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
22.0 MPa @Strain 4.60 %, Temperature 100 °C | 3190 psi @Strain 4.60 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
22.08 MPa @Strain 2.80 %, Temperature 80.0 °C | 3202 psi @Strain 2.80 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
22.1 MPa @Strain 1.40 %, Temperature 60.0 °C | 3210 psi @Strain 1.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
22.1 MPa @Strain 4.10 %, Temperature 80.0 °C | 3210 psi @Strain 4.10 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
22.12 MPa @Strain 11.0 %, Temperature 150 °C | 3208 psi @Strain 11.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
22.14 MPa @Strain 4.30 %, Temperature 100 °C | 3211 psi @Strain 4.30 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
22.2 MPa @Strain 4.70 %, Temperature 100 °C | 3220 psi @Strain 4.70 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
22.2 MPa @Strain 3.30 %, Temperature 60.0 °C | 3220 psi @Strain 3.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
22.28 MPa @Strain 7.90 %, Temperature 150 °C | 3231 psi @Strain 7.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
22.3 MPa @Strain 4.20 %, Temperature 80.0 °C | 3230 psi @Strain 4.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
22.3 MPa @Strain 1.60 %, Temperature 23.0 °C | 3230 psi @Strain 1.60 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
22.31 MPa @Strain 5.90 %, Temperature 120 °C | 3236 psi @Strain 5.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
22.37 MPa @Strain 4.40 %, Temperature 100 °C | 3245 psi @Strain 4.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
22.4 MPa @Strain 4.80 %, Temperature 100 °C | 3250 psi @Strain 4.80 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
22.4 MPa @Strain 8.50 %, Temperature 120 °C | 3250 psi @Strain 8.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
22.5 MPa @Strain 12.0 %, Temperature 150 °C | 3260 psi @Strain 12.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
22.5 MPa @Strain 4.30 %, Temperature 80.0 °C | 3260 psi @Strain 4.30 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
22.5 MPa @Strain 3.40 %, Temperature 60.0 °C | 3260 psi @Strain 3.40 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
22.56 MPa @Strain 2.90 %, Temperature 80.0 °C | 3272 psi @Strain 2.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
22.6 MPa @Strain 4.90 %, Temperature 100 °C | 3280 psi @Strain 4.90 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
22.62 MPa @Strain 4.50 %, Temperature 100 °C | 3281 psi @Strain 4.50 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
22.67 MPa @Strain 8.40 %, Temperature 150 °C | 3288 psi @Strain 8.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
22.7 MPa @Strain 9.00 %, Temperature 120 °C | 3290 psi @Strain 9.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
22.7 MPa @Strain 4.40 %, Temperature 80.0 °C | 3290 psi @Strain 4.40 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
22.76 MPa @Strain 0.400 %, Temperature -40.0 °C | 3301 psi @Strain 0.400 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
22.78 MPa @Strain 4.60 %, Temperature 100 °C | 3304 psi @Strain 4.60 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
22.8 MPa @Strain 5.00 %, Temperature 100 °C | 3310 psi @Strain 5.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
22.8 MPa @Strain 3.50 %, Temperature 60.0 °C | 3310 psi @Strain 3.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
22.8 MPa @Strain 1.70 %, Temperature 23.0 °C | 3310 psi @Strain 1.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
22.89 MPa @Strain 13.0 %, Temperature 150 °C | 3320 psi @Strain 13.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
23.0 MPa @Strain 4.50 %, Temperature 80.0 °C | 3340 psi @Strain 4.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
23.0 MPa @Strain 3.60 %, Temperature 60.0 °C | 3340 psi @Strain 3.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
23.01 MPa @Strain 3.00 %, Temperature 80.0 °C | 3337 psi @Strain 3.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
23.04 MPa @Strain 4.70 %, Temperature 100 °C | 3342 psi @Strain 4.70 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
23.09 MPa @Strain 8.90 %, Temperature 150 °C | 3349 psi @Strain 8.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
23.1 MPa @Strain 9.50 %, Temperature 120 °C | 3350 psi @Strain 9.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
23.1 MPa @Strain 1.50 %, Temperature 60.0 °C | 3350 psi @Strain 1.50 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
23.18 MPa @Strain 14.0 %, Temperature 150 °C | 3362 psi @Strain 14.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
23.2 MPa @Strain 4.60 %, Temperature 80.0 °C | 3360 psi @Strain 4.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
23.26 MPa @Strain 4.80 %, Temperature 100 °C | 3374 psi @Strain 4.80 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
23.26 MPa @Strain 6.40 %, Temperature 120 °C | 3374 psi @Strain 6.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
23.39 MPa @Strain 9.40 %, Temperature 150 °C | 3392 psi @Strain 9.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
23.4 MPa @Strain 10.0 %, Temperature 120 °C | 3390 psi @Strain 10.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
23.4 MPa @Strain 4.70 %, Temperature 80.0 °C | 3390 psi @Strain 4.70 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
23.4 MPa @Strain 3.70 %, Temperature 60.0 °C | 3390 psi @Strain 3.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
23.4 MPa @Strain 1.80 %, Temperature 23.0 °C | 3390 psi @Strain 1.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
23.46 MPa @Strain 3.10 %, Temperature 80.0 °C | 3403 psi @Strain 3.10 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
23.47 MPa @Strain 15.0 %, Temperature 150 °C | 3404 psi @Strain 15.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
23.49 MPa @Strain 4.90 %, Temperature 100 °C | 3407 psi @Strain 4.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
23.5 MPa @Strain 4.80 %, Temperature 80.0 °C | 3410 psi @Strain 4.80 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
23.6 MPa @Strain 5.50 %, Temperature 100 °C | 3420 psi @Strain 5.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
23.7 MPa @Strain 4.90 %, Temperature 80.0 °C | 3440 psi @Strain 4.90 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
23.7 MPa @Strain 3.80 %, Temperature 60.0 °C | 3440 psi @Strain 3.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
23.72 MPa @Strain 9.90 %, Temperature 150 °C | 3440 psi @Strain 9.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
23.77 MPa @Strain 16.0 %, Temperature 150 °C | 3448 psi @Strain 16.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
23.8 MPa @Strain 1.60 %, Temperature 60.0 °C | 3450 psi @Strain 1.60 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
23.81 MPa @Strain 5.40 %, Temperature 100 °C | 3453 psi @Strain 5.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
23.9 MPa @Strain 11.0 %, Temperature 120 °C | 3470 psi @Strain 11.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
23.9 MPa @Strain 3.90 %, Temperature 60.0 °C | 3470 psi @Strain 3.90 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
23.91 MPa @Strain 3.20 %, Temperature 80.0 °C | 3468 psi @Strain 3.20 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
23.96 MPa @Strain 17.0 %, Temperature 150 °C | 3475 psi @Strain 17.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
24.0 MPa @Strain 5.00 %, Temperature 80.0 °C | 3480 psi @Strain 5.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
24.09 MPa @Strain 6.90 %, Temperature 120 °C | 3494 psi @Strain 6.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
24.18 MPa @Strain 10.9 %, Temperature 150 °C | 3507 psi @Strain 10.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
24.25 MPa @Strain 18.0 %, Temperature 150 °C | 3517 psi @Strain 18.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
24.3 MPa @Strain 3.30 %, Temperature 80.0 °C | 3520 psi @Strain 3.30 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
24.3 MPa @Strain 4.00 %, Temperature 60.0 °C | 3520 psi @Strain 4.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
24.3 MPa @Strain 1.90 %, Temperature 23.0 °C | 3520 psi @Strain 1.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
24.35 MPa @Strain 19.0 %, Temperature 150 °C | 3532 psi @Strain 19.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
24.5 MPa @Strain 12.0 %, Temperature 120 °C | 3550 psi @Strain 12.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
24.5 MPa @Strain 1.70 %, Temperature 60.0 °C | 3550 psi @Strain 1.70 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
24.6 MPa @Strain 4.10 %, Temperature 60.0 °C | 3570 psi @Strain 4.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
24.6 MPa @Strain 5.50 %, Temperature 80.0 °C | 3570 psi @Strain 5.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
24.6 MPa @Strain 5.90 %, Temperature 100 °C | 3570 psi @Strain 5.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
24.64 MPa @Strain 20.0 %, Temperature 150 °C | 3574 psi @Strain 20.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
24.66 MPa @Strain 3.40 %, Temperature 80.0 °C | 3577 psi @Strain 3.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
24.7 MPa @Strain 6.00 %, Temperature 100 °C | 3580 psi @Strain 6.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
24.74 MPa @Strain 21.0 %, Temperature 150 °C | 3588 psi @Strain 21.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
24.77 MPa @Strain 11.9 %, Temperature 150 °C | 3593 psi @Strain 11.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
24.81 MPa @Strain 7.40 %, Temperature 120 °C | 3598 psi @Strain 7.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
24.9 MPa @Strain 13.0 %, Temperature 120 °C | 3610 psi @Strain 13.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
24.93 MPa @Strain 22.0 %, Temperature 150 °C | 3616 psi @Strain 22.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
24.99 MPa @Strain 3.50 %, Temperature 80.0 °C | 3624 psi @Strain 3.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
25.0 MPa @Strain 4.20 %, Temperature 60.0 °C | 3630 psi @Strain 4.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
25.03 MPa @Strain 23.0 %, Temperature 150 °C | 3630 psi @Strain 23.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
25.1 MPa @Strain 2.00 %, Temperature 23.0 °C | 3640 psi @Strain 2.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
25.2 MPa @Strain 4.30 %, Temperature 60.0 °C | 3650 psi @Strain 4.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
25.22 MPa @Strain 24.0 %, Temperature 150 °C | 3658 psi @Strain 24.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
25.24 MPa @Strain 12.9 %, Temperature 150 °C | 3661 psi @Strain 12.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
25.29 MPa @Strain 3.60 %, Temperature 80.0 °C | 3668 psi @Strain 3.60 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
25.3 MPa @Strain 1.80 %, Temperature 60.0 °C | 3670 psi @Strain 1.80 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
25.3 MPa @Strain 0.500 %, Temperature 0.000 °C | 3670 psi @Strain 0.500 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
25.3 MPa @Strain 14.0 %, Temperature 120 °C | 3670 psi @Strain 14.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
25.32 MPa @Strain 25.0 %, Temperature 150 °C | 3672 psi @Strain 25.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
25.37 MPa @Strain 7.90 %, Temperature 120 °C | 3680 psi @Strain 7.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
25.4 MPa @Strain 6.50 %, Temperature 100 °C | 3680 psi @Strain 6.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
25.4 MPa @Strain 4.40 %, Temperature 60.0 °C | 3680 psi @Strain 4.40 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
25.51 MPa @Strain 26.0 %, Temperature 150 °C | 3700 psi @Strain 26.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
25.61 MPa @Strain 27.0 %, Temperature 150 °C | 3714 psi @Strain 27.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
25.62 MPa @Strain 13.9 %, Temperature 150 °C | 3716 psi @Strain 13.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
25.62 MPa @Strain 3.70 %, Temperature 80.0 °C | 3716 psi @Strain 3.70 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
25.7 MPa @Strain 4.50 %, Temperature 60.0 °C | 3730 psi @Strain 4.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
25.7 MPa @Strain 2.10 %, Temperature 23.0 °C | 3730 psi @Strain 2.10 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
25.7 MPa @Strain 15.0 %, Temperature 120 °C | 3730 psi @Strain 15.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
25.7 MPa @Strain 6.00 %, Temperature 80.0 °C | 3730 psi @Strain 6.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
25.71 MPa @Strain 28.0 %, Temperature 150 °C | 3729 psi @Strain 28.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
25.74 MPa @Strain 6.40 %, Temperature 100 °C | 3733 psi @Strain 6.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
25.8 MPa @Strain 29.0 %, Temperature 150 °C | 3740 psi @Strain 29.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
25.8 MPa @Strain 0.500 %, Temperature 23.0 °C | 3740 psi @Strain 0.500 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
25.9 MPa @Strain 4.60 %, Temperature 60.0 °C | 3760 psi @Strain 4.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
25.9 MPa @Strain 1.90 %, Temperature 60.0 °C | 3760 psi @Strain 1.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
25.9 MPa @Strain 30.0 %, Temperature 150 °C | 3760 psi @Strain 30.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
25.9 MPa @Strain 8.40 %, Temperature 120 °C | 3760 psi @Strain 8.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
25.93 MPa @Strain 14.9 %, Temperature 150 °C | 3761 psi @Strain 14.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
26.0 MPa @Strain 16.0 %, Temperature 120 °C | 3770 psi @Strain 16.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
26.01 MPa @Strain 3.80 %, Temperature 80.0 °C | 3772 psi @Strain 3.80 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
26.09 MPa @Strain 31.0 %, Temperature 150 °C | 3784 psi @Strain 31.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.1 MPa @Strain 7.00 %, Temperature 100 °C | 3790 psi @Strain 7.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
26.19 MPa @Strain 32.0 %, Temperature 150 °C | 3799 psi @Strain 32.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.2 MPa @Strain 4.70 %, Temperature 60.0 °C | 3800 psi @Strain 4.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
26.2 MPa @Strain 2.20 %, Temperature 23.0 °C | 3800 psi @Strain 2.20 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
26.28 MPa @Strain 15.9 %, Temperature 150 °C | 3812 psi @Strain 15.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
26.29 MPa @Strain 33.0 %, Temperature 150 °C | 3813 psi @Strain 33.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.3 MPa @Strain 17.0 %, Temperature 120 °C | 3810 psi @Strain 17.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
26.3 MPa @Strain 4.80 %, Temperature 60.0 °C | 3810 psi @Strain 4.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
26.3 MPa @Strain 0.400 %, Temperature -40.0 °C | 3810 psi @Strain 0.400 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
26.37 MPa @Strain 3.90 %, Temperature 80.0 °C | 3825 psi @Strain 3.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
26.38 MPa @Strain 34.0 %, Temperature 150 °C | 3826 psi @Strain 34.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.38 MPa @Strain 35.0 %, Temperature 150 °C | 3826 psi @Strain 35.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.41 MPa @Strain 8.90 %, Temperature 120 °C | 3830 psi @Strain 8.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
26.42 MPa @Strain 0.500 %, Temperature 0.000 °C | 3832 psi @Strain 0.500 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
26.48 MPa @Strain 36.0 %, Temperature 150 °C | 3841 psi @Strain 36.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.5 MPa @Strain 18.0 %, Temperature 120 °C | 3840 psi @Strain 18.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
26.5 MPa @Strain 6.50 %, Temperature 80.0 °C | 3840 psi @Strain 6.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
26.5 MPa @Strain 2.00 %, Temperature 60.0 °C | 3840 psi @Strain 2.00 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
26.58 MPa @Strain 6.90 %, Temperature 100 °C | 3855 psi @Strain 6.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
26.58 MPa @Strain 37.0 %, Temperature 150 °C | 3855 psi @Strain 37.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.59 MPa @Strain 16.9 %, Temperature 150 °C | 3857 psi @Strain 16.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
26.6 MPa @Strain 4.90 %, Temperature 60.0 °C | 3860 psi @Strain 4.90 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
26.68 MPa @Strain 38.0 %, Temperature 150 °C | 3870 psi @Strain 38.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.7 MPa @Strain 7.50 %, Temperature 100 °C | 3870 psi @Strain 7.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
26.73 MPa @Strain 4.00 %, Temperature 80.0 °C | 3877 psi @Strain 4.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
26.77 MPa @Strain 39.0 %, Temperature 150 °C | 3883 psi @Strain 39.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.77 MPa @Strain 40.0 %, Temperature 150 °C | 3883 psi @Strain 40.0 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
26.8 MPa @Strain 19.0 %, Temperature 120 °C | 3890 psi @Strain 19.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
26.88 MPa @Strain 9.40 %, Temperature 120 °C | 3899 psi @Strain 9.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
26.89 MPa @Strain 17.9 %, Temperature 150 °C | 3900 psi @Strain 17.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
26.97 MPa @Strain 4.10 %, Temperature 80.0 °C | 3912 psi @Strain 4.10 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
27.0 MPa @Strain 2.30 %, Temperature 23.0 °C | 3920 psi @Strain 2.30 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
27.0 MPa @Strain 20.0 %, Temperature 120 °C | 3920 psi @Strain 20.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
27.1 MPa @Strain 7.00 %, Temperature 80.0 °C | 3930 psi @Strain 7.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
27.1 MPa @Strain 2.10 %, Temperature 60.0 °C | 3930 psi @Strain 2.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
27.15 MPa @Strain 18.9 %, Temperature 150 °C | 3938 psi @Strain 18.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
27.2 MPa @Strain 21.0 %, Temperature 120 °C | 3950 psi @Strain 21.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
27.2 MPa @Strain 8.00 %, Temperature 100 °C | 3950 psi @Strain 8.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
27.22 MPa @Strain 4.20 %, Temperature 80.0 °C | 3948 psi @Strain 4.20 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
27.29 MPa @Strain 9.90 %, Temperature 120 °C | 3958 psi @Strain 9.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
27.35 MPa @Strain 19.9 %, Temperature 150 °C | 3967 psi @Strain 19.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
27.36 MPa @Strain 7.40 %, Temperature 100 °C | 3968 psi @Strain 7.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
27.4 MPa @Strain 5.00 %, Temperature 60.0 °C | 3970 psi @Strain 5.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
27.5 MPa @Strain 22.0 %, Temperature 120 °C | 3990 psi @Strain 22.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
27.58 MPa @Strain 4.30 %, Temperature 80.0 °C | 4000 psi @Strain 4.30 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
27.6 MPa @Strain 2.20 %, Temperature 60.0 °C | 4000 psi @Strain 2.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
27.6 MPa @Strain 2.40 %, Temperature 23.0 °C | 4000 psi @Strain 2.40 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
27.6 MPa @Strain 20.9 %, Temperature 150 °C | 4000 psi @Strain 20.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
27.7 MPa @Strain 23.0 %, Temperature 120 °C | 4020 psi @Strain 23.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
27.7 MPa @Strain 7.50 %, Temperature 80.0 °C | 4020 psi @Strain 7.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
27.7 MPa @Strain 8.50 %, Temperature 100 °C | 4020 psi @Strain 8.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
27.77 MPa @Strain 10.9 %, Temperature 120 °C | 4028 psi @Strain 10.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
27.8 MPa @Strain 24.0 %, Temperature 120 °C | 4030 psi @Strain 24.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
27.82 MPa @Strain 21.9 %, Temperature 150 °C | 4035 psi @Strain 21.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
27.85 MPa @Strain 4.40 %, Temperature 80.0 °C | 4039 psi @Strain 4.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
28.0 MPa @Strain 25.0 %, Temperature 120 °C | 4060 psi @Strain 25.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
28.02 MPa @Strain 22.9 %, Temperature 150 °C | 4064 psi @Strain 22.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
28.09 MPa @Strain 7.90 %, Temperature 100 °C | 4074 psi @Strain 7.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
28.1 MPa @Strain 9.00 %, Temperature 100 °C | 4080 psi @Strain 9.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
28.1 MPa @Strain 2.50 %, Temperature 23.0 °C | 4080 psi @Strain 2.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
28.2 MPa @Strain 2.30 %, Temperature 60.0 °C | 4090 psi @Strain 2.30 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
28.2 MPa @Strain 8.00 %, Temperature 80.0 °C | 4090 psi @Strain 8.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
28.2 MPa @Strain 26.0 %, Temperature 120 °C | 4090 psi @Strain 26.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
28.21 MPa @Strain 4.50 %, Temperature 80.0 °C | 4092 psi @Strain 4.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
28.23 MPa @Strain 23.9 %, Temperature 150 °C | 4094 psi @Strain 23.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
28.3 MPa @Strain 27.0 %, Temperature 120 °C | 4100 psi @Strain 27.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
28.36 MPa @Strain 24.9 %, Temperature 150 °C | 4113 psi @Strain 24.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
28.4 MPa @Strain 28.0 %, Temperature 120 °C | 4120 psi @Strain 28.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
28.42 MPa @Strain 4.60 %, Temperature 80.0 °C | 4122 psi @Strain 4.60 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
28.44 MPa @Strain 11.9 %, Temperature 120 °C | 4125 psi @Strain 11.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
28.5 MPa @Strain 9.50 %, Temperature 100 °C | 4130 psi @Strain 9.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
28.57 MPa @Strain 25.9 %, Temperature 150 °C | 4144 psi @Strain 25.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
28.6 MPa @Strain 29.0 %, Temperature 120 °C | 4150 psi @Strain 29.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
28.6 MPa @Strain 2.40 %, Temperature 60.0 °C | 4150 psi @Strain 2.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
28.6 MPa @Strain 2.60 %, Temperature 23.0 °C | 4150 psi @Strain 2.60 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
28.6 MPa @Strain 5.50 %, Temperature 60.0 °C | 4150 psi @Strain 5.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
28.69 MPa @Strain 4.70 %, Temperature 80.0 °C | 4161 psi @Strain 4.70 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
28.7 MPa @Strain 30.0 %, Temperature 120 °C | 4160 psi @Strain 30.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
28.7 MPa @Strain 8.50 %, Temperature 80.0 °C | 4160 psi @Strain 8.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
28.71 MPa @Strain 8.40 %, Temperature 100 °C | 4164 psi @Strain 8.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
28.76 MPa @Strain 26.9 %, Temperature 150 °C | 4171 psi @Strain 26.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
28.8 MPa @Strain 31.0 %, Temperature 120 °C | 4180 psi @Strain 31.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
28.9 MPa @Strain 32.0 %, Temperature 120 °C | 4190 psi @Strain 32.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
28.9 MPa @Strain 10.0 %, Temperature 100 °C | 4190 psi @Strain 10.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
28.96 MPa @Strain 27.9 %, Temperature 150 °C | 4200 psi @Strain 27.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
28.99 MPa @Strain 4.80 %, Temperature 80.0 °C | 4205 psi @Strain 4.80 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
29.0 MPa @Strain 2.70 %, Temperature 23.0 °C | 4210 psi @Strain 2.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
29.1 MPa @Strain 2.50 %, Temperature 60.0 °C | 4220 psi @Strain 2.50 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
29.1 MPa @Strain 28.9 %, Temperature 150 °C | 4220 psi @Strain 28.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
29.1 MPa @Strain 33.0 %, Temperature 120 °C | 4220 psi @Strain 33.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
29.12 MPa @Strain 12.9 %, Temperature 120 °C | 4224 psi @Strain 12.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
29.2 MPa @Strain 34.0 %, Temperature 120 °C | 4240 psi @Strain 34.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
29.23 MPa @Strain 29.9 %, Temperature 150 °C | 4239 psi @Strain 29.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
29.26 MPa @Strain 4.90 %, Temperature 80.0 °C | 4244 psi @Strain 4.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
29.27 MPa @Strain 8.90 %, Temperature 100 °C | 4245 psi @Strain 8.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
29.3 MPa @Strain 9.00 %, Temperature 80.0 °C | 4250 psi @Strain 9.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
29.3 MPa @Strain 35.0 %, Temperature 120 °C | 4250 psi @Strain 35.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
29.4 MPa @Strain 36.0 %, Temperature 120 °C | 4260 psi @Strain 36.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
29.4 MPa @Strain 2.60 %, Temperature 60.0 °C | 4260 psi @Strain 2.60 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
29.4 MPa @Strain 6.00 %, Temperature 60.0 °C | 4260 psi @Strain 6.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
29.43 MPa @Strain 30.9 %, Temperature 150 °C | 4268 psi @Strain 30.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
29.5 MPa @Strain 37.0 %, Temperature 120 °C | 4280 psi @Strain 37.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
29.5 MPa @Strain 11.0 %, Temperature 100 °C | 4280 psi @Strain 11.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
29.53 MPa @Strain 5.40 %, Temperature 80.0 °C | 4283 psi @Strain 5.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
29.55 MPa @Strain 31.9 %, Temperature 150 °C | 4286 psi @Strain 31.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
29.55 MPa @Strain 0.500 %, Temperature -40.0 °C | 4286 psi @Strain 0.500 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
29.6 MPa @Strain 38.0 %, Temperature 120 °C | 4290 psi @Strain 38.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
29.7 MPa @Strain 39.0 %, Temperature 120 °C | 4310 psi @Strain 39.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
29.7 MPa @Strain 13.9 %, Temperature 120 °C | 4310 psi @Strain 13.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
29.7 MPa @Strain 9.50 %, Temperature 80.0 °C | 4310 psi @Strain 9.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
29.7 MPa @Strain 2.80 %, Temperature 23.0 °C | 4310 psi @Strain 2.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
29.71 MPa @Strain 32.9 %, Temperature 150 °C | 4309 psi @Strain 32.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
29.8 MPa @Strain 40.0 %, Temperature 120 °C | 4320 psi @Strain 40.0 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
29.82 MPa @Strain 33.9 %, Temperature 150 °C | 4325 psi @Strain 33.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
29.86 MPa @Strain 9.40 %, Temperature 100 °C | 4331 psi @Strain 9.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
29.9 MPa @Strain 2.70 %, Temperature 60.0 °C | 4340 psi @Strain 2.70 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
29.9 MPa @Strain 0.600 %, Temperature 0.000 °C | 4340 psi @Strain 0.600 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
29.94 MPa @Strain 34.9 %, Temperature 150 °C | 4342 psi @Strain 34.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.1 MPa @Strain 35.9 %, Temperature 150 °C | 4370 psi @Strain 35.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.1 MPa @Strain 10.0 %, Temperature 80.0 °C | 4370 psi @Strain 10.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
30.1 MPa @Strain 12.0 %, Temperature 100 °C | 4370 psi @Strain 12.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
30.1 MPa @Strain 6.50 %, Temperature 60.0 °C | 4370 psi @Strain 6.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
30.22 MPa @Strain 14.9 %, Temperature 120 °C | 4383 psi @Strain 14.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
30.22 MPa @Strain 36.9 %, Temperature 150 °C | 4383 psi @Strain 36.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.3 MPa @Strain 2.90 %, Temperature 23.0 °C | 4390 psi @Strain 2.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
30.3 MPa @Strain 2.80 %, Temperature 60.0 °C | 4390 psi @Strain 2.80 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
30.32 MPa @Strain 37.9 %, Temperature 150 °C | 4398 psi @Strain 37.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.35 MPa @Strain 9.90 %, Temperature 100 °C | 4402 psi @Strain 9.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
30.47 MPa @Strain 38.9 %, Temperature 150 °C | 4419 psi @Strain 38.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.51 MPa @Strain 5.90 %, Temperature 80.0 °C | 4425 psi @Strain 5.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
30.56 MPa @Strain 39.9 %, Temperature 150 °C | 4432 psi @Strain 39.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.6 MPa @Strain 13.0 %, Temperature 100 °C | 4440 psi @Strain 13.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
30.6 MPa @Strain 0.600 %, Temperature 23.0 °C | 4440 psi @Strain 0.600 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
30.68 MPa @Strain 40.9 %, Temperature 150 °C | 4450 psi @Strain 40.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.69 MPa @Strain 15.9 %, Temperature 120 °C | 4451 psi @Strain 15.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
30.7 MPa @Strain 11.0 %, Temperature 80.0 °C | 4450 psi @Strain 11.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
30.7 MPa @Strain 3.00 %, Temperature 23.0 °C | 4450 psi @Strain 3.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
30.8 MPa @Strain 7.00 %, Temperature 60.0 °C | 4470 psi @Strain 7.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
30.8 MPa @Strain 2.90 %, Temperature 60.0 °C | 4470 psi @Strain 2.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
30.81 MPa @Strain 41.9 %, Temperature 150 °C | 4469 psi @Strain 41.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.83 MPa @Strain 10.9 %, Temperature 100 °C | 4472 psi @Strain 10.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
30.93 MPa @Strain 42.9 %, Temperature 150 °C | 4486 psi @Strain 42.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
31.0 MPa @Strain 14.0 %, Temperature 100 °C | 4500 psi @Strain 14.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
31.03 MPa @Strain 43.9 %, Temperature 150 °C | 4501 psi @Strain 43.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
31.14 MPa @Strain 44.9 %, Temperature 150 °C | 4516 psi @Strain 44.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
31.15 MPa @Strain 16.9 %, Temperature 120 °C | 4518 psi @Strain 16.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
31.2 MPa @Strain 3.00 %, Temperature 60.0 °C | 4530 psi @Strain 3.00 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
31.2 MPa @Strain 3.10 %, Temperature 23.0 °C | 4530 psi @Strain 3.10 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
31.26 MPa @Strain 45.9 %, Temperature 150 °C | 4534 psi @Strain 45.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
31.3 MPa @Strain 7.50 %, Temperature 60.0 °C | 4540 psi @Strain 7.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
31.31 MPa @Strain 0.600 %, Temperature 0.000 °C | 4541 psi @Strain 0.600 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
31.36 MPa @Strain 46.9 %, Temperature 150 °C | 4548 psi @Strain 46.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
31.4 MPa @Strain 15.0 %, Temperature 100 °C | 4550 psi @Strain 15.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
31.4 MPa @Strain 12.0 %, Temperature 80.0 °C | 4550 psi @Strain 12.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
31.47 MPa @Strain 47.9 %, Temperature 150 °C | 4564 psi @Strain 47.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
31.5 MPa @Strain 3.20 %, Temperature 23.0 °C | 4570 psi @Strain 3.20 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
31.5 MPa @Strain 3.10 %, Temperature 60.0 °C | 4570 psi @Strain 3.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
31.55 MPa @Strain 48.9 %, Temperature 150 °C | 4576 psi @Strain 48.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
31.58 MPa @Strain 11.9 %, Temperature 100 °C | 4580 psi @Strain 11.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
31.58 MPa @Strain 17.9 %, Temperature 120 °C | 4580 psi @Strain 17.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
31.64 MPa @Strain 49.9 %, Temperature 150 °C | 4589 psi @Strain 49.9 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
31.7 MPa @Strain 16.0 %, Temperature 100 °C | 4600 psi @Strain 16.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
31.76 MPa @Strain 6.40 %, Temperature 80.0 °C | 4606 psi @Strain 6.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
31.8 MPa @Strain 3.20 %, Temperature 60.0 °C | 4610 psi @Strain 3.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
31.9 MPa @Strain 3.30 %, Temperature 23.0 °C | 4630 psi @Strain 3.30 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
31.97 MPa @Strain 18.9 %, Temperature 120 °C | 4637 psi @Strain 18.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
32.0 MPa @Strain 17.0 %, Temperature 100 °C | 4640 psi @Strain 17.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
32.0 MPa @Strain 13.0 %, Temperature 80.0 °C | 4640 psi @Strain 13.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
32.0 MPa @Strain 8.00 %, Temperature 60.0 °C | 4640 psi @Strain 8.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
32.01 MPa @Strain 51.0 %, Temperature 150 °C | 4643 psi @Strain 51.0 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
32.2 MPa @Strain 3.30 %, Temperature 60.0 °C | 4670 psi @Strain 3.30 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
32.3 MPa @Strain 3.40 %, Temperature 23.0 °C | 4680 psi @Strain 3.40 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
32.3 MPa @Strain 18.0 %, Temperature 100 °C | 4680 psi @Strain 18.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
32.31 MPa @Strain 19.9 %, Temperature 120 °C | 4686 psi @Strain 19.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
32.35 MPa @Strain 52.0 %, Temperature 150 °C | 4692 psi @Strain 52.0 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
32.4 MPa @Strain 8.50 %, Temperature 60.0 °C | 4700 psi @Strain 8.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
32.45 MPa @Strain 12.9 %, Temperature 100 °C | 4706 psi @Strain 12.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
32.5 MPa @Strain 3.40 %, Temperature 60.0 °C | 4710 psi @Strain 3.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
32.6 MPa @Strain 14.0 %, Temperature 80.0 °C | 4730 psi @Strain 14.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
32.6 MPa @Strain 19.0 %, Temperature 100 °C | 4730 psi @Strain 19.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
32.62 MPa @Strain 20.9 %, Temperature 120 °C | 4731 psi @Strain 20.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
32.7 MPa @Strain 3.50 %, Temperature 23.0 °C | 4740 psi @Strain 3.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
32.71 MPa @Strain 6.90 %, Temperature 80.0 °C | 4744 psi @Strain 6.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
32.8 MPa @Strain 20.0 %, Temperature 100 °C | 4760 psi @Strain 20.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
32.89 MPa @Strain 21.9 %, Temperature 120 °C | 4770 psi @Strain 21.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
32.9 MPa @Strain 3.50 %, Temperature 60.0 °C | 4770 psi @Strain 3.50 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
32.9 MPa @Strain 9.00 %, Temperature 60.0 °C | 4770 psi @Strain 9.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
33.0 MPa @Strain 21.0 %, Temperature 100 °C | 4790 psi @Strain 21.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
33.0 MPa @Strain 15.0 %, Temperature 80.0 °C | 4790 psi @Strain 15.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
33.1 MPa @Strain 3.60 %, Temperature 23.0 °C | 4800 psi @Strain 3.60 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
33.1 MPa @Strain 3.60 %, Temperature 60.0 °C | 4800 psi @Strain 3.60 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
33.13 MPa @Strain 13.9 %, Temperature 100 °C | 4805 psi @Strain 13.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
33.19 MPa @Strain 22.9 %, Temperature 120 °C | 4814 psi @Strain 22.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
33.2 MPa @Strain 22.0 %, Temperature 100 °C | 4820 psi @Strain 22.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
33.2 MPa @Strain 0.500 %, Temperature -40.0 °C | 4820 psi @Strain 0.500 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
33.4 MPa @Strain 3.70 %, Temperature 60.0 °C | 4840 psi @Strain 3.70 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
33.4 MPa @Strain 3.70 %, Temperature 23.0 °C | 4840 psi @Strain 3.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
33.4 MPa @Strain 9.50 %, Temperature 60.0 °C | 4840 psi @Strain 9.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
33.4 MPa @Strain 23.0 %, Temperature 100 °C | 4840 psi @Strain 23.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
33.48 MPa @Strain 23.9 %, Temperature 120 °C | 4856 psi @Strain 23.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
33.5 MPa @Strain 16.0 %, Temperature 80.0 °C | 4860 psi @Strain 16.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
33.58 MPa @Strain 7.40 %, Temperature 80.0 °C | 4870 psi @Strain 7.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
33.6 MPa @Strain 24.0 %, Temperature 100 °C | 4870 psi @Strain 24.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
33.7 MPa @Strain 25.0 %, Temperature 100 °C | 4890 psi @Strain 25.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
33.73 MPa @Strain 24.9 %, Temperature 120 °C | 4892 psi @Strain 24.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
33.74 MPa @Strain 14.9 %, Temperature 100 °C | 4894 psi @Strain 14.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
33.8 MPa @Strain 17.0 %, Temperature 80.0 °C | 4900 psi @Strain 17.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
33.8 MPa @Strain 3.80 %, Temperature 60.0 °C | 4900 psi @Strain 3.80 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
33.8 MPa @Strain 3.80 %, Temperature 23.0 °C | 4900 psi @Strain 3.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
33.9 MPa @Strain 26.0 %, Temperature 100 °C | 4920 psi @Strain 26.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
33.96 MPa @Strain 25.9 %, Temperature 120 °C | 4925 psi @Strain 25.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
34.0 MPa @Strain 27.0 %, Temperature 100 °C | 4930 psi @Strain 27.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.0 MPa @Strain 3.90 %, Temperature 23.0 °C | 4930 psi @Strain 3.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
34.0 MPa @Strain 3.90 %, Temperature 60.0 °C | 4930 psi @Strain 3.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
34.1 MPa @Strain 10.0 %, Temperature 60.0 °C | 4950 psi @Strain 10.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
34.1 MPa @Strain 28.0 %, Temperature 100 °C | 4950 psi @Strain 28.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.2 MPa @Strain 29.0 %, Temperature 100 °C | 4960 psi @Strain 29.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.2 MPa @Strain 18.0 %, Temperature 80.0 °C | 4960 psi @Strain 18.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
34.21 MPa @Strain 26.9 %, Temperature 120 °C | 4962 psi @Strain 26.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
34.29 MPa @Strain 15.9 %, Temperature 100 °C | 4973 psi @Strain 15.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
34.3 MPa @Strain 30.0 %, Temperature 100 °C | 4970 psi @Strain 30.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.3 MPa @Strain 0.700 %, Temperature 0.000 °C | 4970 psi @Strain 0.700 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
34.38 MPa @Strain 7.90 %, Temperature 80.0 °C | 4986 psi @Strain 7.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
34.4 MPa @Strain 4.00 %, Temperature 60.0 °C | 4990 psi @Strain 4.00 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
34.4 MPa @Strain 31.0 %, Temperature 100 °C | 4990 psi @Strain 31.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.45 MPa @Strain 27.9 %, Temperature 120 °C | 4997 psi @Strain 27.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
34.5 MPa @Strain 32.0 %, Temperature 100 °C | 5000 psi @Strain 32.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.5 MPa @Strain 19.0 %, Temperature 80.0 °C | 5000 psi @Strain 19.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
34.5 MPa @Strain 4.00 %, Temperature 23.0 °C | 5000 psi @Strain 4.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
34.6 MPa @Strain 4.10 %, Temperature 60.0 °C | 5020 psi @Strain 4.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
34.6 MPa @Strain 33.0 %, Temperature 100 °C | 5020 psi @Strain 33.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.65 MPa @Strain 28.9 %, Temperature 120 °C | 5026 psi @Strain 28.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
34.7 MPa @Strain 34.0 %, Temperature 100 °C | 5030 psi @Strain 34.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.72 MPa @Strain 0.600 %, Temperature -40.0 °C | 5036 psi @Strain 0.600 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
34.8 MPa @Strain 35.0 %, Temperature 100 °C | 5050 psi @Strain 35.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.8 MPa @Strain 20.0 %, Temperature 80.0 °C | 5050 psi @Strain 20.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
34.8 MPa @Strain 4.20 %, Temperature 60.0 °C | 5050 psi @Strain 4.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
34.81 MPa @Strain 16.9 %, Temperature 100 °C | 5049 psi @Strain 16.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
34.81 MPa @Strain 29.9 %, Temperature 120 °C | 5049 psi @Strain 29.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
34.9 MPa @Strain 36.0 %, Temperature 100 °C | 5060 psi @Strain 36.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
34.9 MPa @Strain 11.0 %, Temperature 60.0 °C | 5060 psi @Strain 11.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
35.0 MPa @Strain 4.10 %, Temperature 23.0 °C | 5080 psi @Strain 4.10 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
35.0 MPa @Strain 37.0 %, Temperature 100 °C | 5080 psi @Strain 37.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
35.0 MPa @Strain 21.0 %, Temperature 80.0 °C | 5080 psi @Strain 21.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
35.05 MPa @Strain 30.9 %, Temperature 120 °C | 5084 psi @Strain 30.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
35.1 MPa @Strain 38.0 %, Temperature 100 °C | 5090 psi @Strain 38.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
35.1 MPa @Strain 4.30 %, Temperature 60.0 °C | 5090 psi @Strain 4.30 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
35.12 MPa @Strain 8.40 %, Temperature 80.0 °C | 5094 psi @Strain 8.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
35.2 MPa @Strain 0.700 %, Temperature 23.0 °C | 5110 psi @Strain 0.700 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
35.2 MPa @Strain 39.0 %, Temperature 100 °C | 5110 psi @Strain 39.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
35.26 MPa @Strain 31.9 %, Temperature 120 °C | 5114 psi @Strain 31.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
35.26 MPa @Strain 17.9 %, Temperature 100 °C | 5114 psi @Strain 17.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
35.3 MPa @Strain 40.0 %, Temperature 100 °C | 5120 psi @Strain 40.0 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
35.4 MPa @Strain 22.0 %, Temperature 80.0 °C | 5130 psi @Strain 22.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
35.4 MPa @Strain 4.40 %, Temperature 60.0 °C | 5130 psi @Strain 4.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
35.4 MPa @Strain 4.20 %, Temperature 23.0 °C | 5130 psi @Strain 4.20 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
35.41 MPa @Strain 32.9 %, Temperature 120 °C | 5136 psi @Strain 32.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
35.5 MPa @Strain 23.0 %, Temperature 80.0 °C | 5150 psi @Strain 23.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
35.5 MPa @Strain 12.0 %, Temperature 60.0 °C | 5150 psi @Strain 12.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
35.5 MPa @Strain 4.50 %, Temperature 60.0 °C | 5150 psi @Strain 4.50 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
35.59 MPa @Strain 33.9 %, Temperature 120 °C | 5162 psi @Strain 33.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
35.7 MPa @Strain 4.30 %, Temperature 23.0 °C | 5180 psi @Strain 4.30 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
35.73 MPa @Strain 18.9 %, Temperature 100 °C | 5182 psi @Strain 18.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
35.75 MPa @Strain 34.9 %, Temperature 120 °C | 5185 psi @Strain 34.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
35.79 MPa @Strain 8.90 %, Temperature 80.0 °C | 5191 psi @Strain 8.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
35.8 MPa @Strain 24.0 %, Temperature 80.0 °C | 5190 psi @Strain 24.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
35.9 MPa @Strain 4.60 %, Temperature 60.0 °C | 5210 psi @Strain 4.60 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
35.93 MPa @Strain 35.9 %, Temperature 120 °C | 5211 psi @Strain 35.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
36.0 MPa @Strain 25.0 %, Temperature 80.0 °C | 5220 psi @Strain 25.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
36.0 MPa @Strain 4.40 %, Temperature 23.0 °C | 5220 psi @Strain 4.40 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
36.0 MPa @Strain 13.0 %, Temperature 60.0 °C | 5220 psi @Strain 13.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
36.03 MPa @Strain 0.700 %, Temperature 0.000 °C | 5226 psi @Strain 0.700 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
36.08 MPa @Strain 36.9 %, Temperature 120 °C | 5233 psi @Strain 36.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
36.1 MPa @Strain 26.0 %, Temperature 80.0 °C | 5240 psi @Strain 26.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
36.1 MPa @Strain 4.70 %, Temperature 60.0 °C | 5240 psi @Strain 4.70 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
36.15 MPa @Strain 19.9 %, Temperature 100 °C | 5243 psi @Strain 19.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
36.24 MPa @Strain 37.9 %, Temperature 120 °C | 5256 psi @Strain 37.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
36.3 MPa @Strain 4.80 %, Temperature 60.0 °C | 5260 psi @Strain 4.80 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
36.3 MPa @Strain 4.50 %, Temperature 23.0 °C | 5260 psi @Strain 4.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
36.33 MPa @Strain 38.9 %, Temperature 120 °C | 5269 psi @Strain 38.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
36.4 MPa @Strain 27.0 %, Temperature 80.0 °C | 5280 psi @Strain 27.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
36.45 MPa @Strain 9.40 %, Temperature 80.0 °C | 5287 psi @Strain 9.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
36.5 MPa @Strain 4.90 %, Temperature 60.0 °C | 5290 psi @Strain 4.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
36.5 MPa @Strain 4.60 %, Temperature 23.0 °C | 5290 psi @Strain 4.60 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
36.5 MPa @Strain 14.0 %, Temperature 60.0 °C | 5290 psi @Strain 14.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
36.5 MPa @Strain 28.0 %, Temperature 80.0 °C | 5290 psi @Strain 28.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
36.5 MPa @Strain 20.9 %, Temperature 100 °C | 5290 psi @Strain 20.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
36.51 MPa @Strain 39.9 %, Temperature 120 °C | 5295 psi @Strain 39.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
36.67 MPa @Strain 40.9 %, Temperature 120 °C | 5319 psi @Strain 40.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
36.7 MPa @Strain 29.0 %, Temperature 80.0 °C | 5320 psi @Strain 29.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
36.8 MPa @Strain 30.0 %, Temperature 80.0 °C | 5340 psi @Strain 30.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
36.8 MPa @Strain 4.70 %, Temperature 23.0 °C | 5340 psi @Strain 4.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
36.8 MPa @Strain 5.40 %, Temperature 60.0 °C | 5340 psi @Strain 5.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
36.83 MPa @Strain 41.9 %, Temperature 120 °C | 5342 psi @Strain 41.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
36.86 MPa @Strain 21.9 %, Temperature 100 °C | 5346 psi @Strain 21.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
36.9 MPa @Strain 15.0 %, Temperature 60.0 °C | 5350 psi @Strain 15.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
36.93 MPa @Strain 42.9 %, Temperature 120 °C | 5356 psi @Strain 42.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.0 MPa @Strain 31.0 %, Temperature 80.0 °C | 5370 psi @Strain 31.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
37.02 MPa @Strain 9.90 %, Temperature 80.0 °C | 5369 psi @Strain 9.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
37.08 MPa @Strain 43.9 %, Temperature 120 °C | 5378 psi @Strain 43.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.1 MPa @Strain 32.0 %, Temperature 80.0 °C | 5380 psi @Strain 32.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
37.1 MPa @Strain 4.80 %, Temperature 23.0 °C | 5380 psi @Strain 4.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
37.22 MPa @Strain 22.9 %, Temperature 100 °C | 5398 psi @Strain 22.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
37.25 MPa @Strain 44.9 %, Temperature 120 °C | 5403 psi @Strain 44.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.3 MPa @Strain 33.0 %, Temperature 80.0 °C | 5410 psi @Strain 33.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
37.3 MPa @Strain 16.0 %, Temperature 60.0 °C | 5410 psi @Strain 16.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
37.33 MPa @Strain 45.9 %, Temperature 120 °C | 5414 psi @Strain 45.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.4 MPa @Strain 34.0 %, Temperature 80.0 °C | 5420 psi @Strain 34.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
37.4 MPa @Strain 4.90 %, Temperature 23.0 °C | 5420 psi @Strain 4.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
37.44 MPa @Strain 46.9 %, Temperature 120 °C | 5430 psi @Strain 46.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.5 MPa @Strain 35.0 %, Temperature 80.0 °C | 5440 psi @Strain 35.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
37.54 MPa @Strain 23.9 %, Temperature 100 °C | 5445 psi @Strain 23.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
37.57 MPa @Strain 10.9 %, Temperature 80.0 °C | 5449 psi @Strain 10.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
37.6 MPa @Strain 5.90 %, Temperature 60.0 °C | 5450 psi @Strain 5.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
37.6 MPa @Strain 36.0 %, Temperature 80.0 °C | 5450 psi @Strain 36.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
37.6 MPa @Strain 47.9 %, Temperature 120 °C | 5450 psi @Strain 47.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.7 MPa @Strain 48.9 %, Temperature 120 °C | 5470 psi @Strain 48.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.7 MPa @Strain 37.0 %, Temperature 80.0 °C | 5470 psi @Strain 37.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
37.7 MPa @Strain 17.0 %, Temperature 60.0 °C | 5470 psi @Strain 17.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
37.79 MPa @Strain 49.9 %, Temperature 120 °C | 5481 psi @Strain 49.9 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.82 MPa @Strain 24.9 %, Temperature 100 °C | 5485 psi @Strain 24.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
37.89 MPa @Strain 51.0 %, Temperature 120 °C | 5495 psi @Strain 51.0 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
37.9 MPa @Strain 38.0 %, Temperature 80.0 °C | 5500 psi @Strain 38.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
37.9 MPa @Strain 0.800 %, Temperature 0.000 °C | 5500 psi @Strain 0.800 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
37.98 MPa @Strain 52.0 %, Temperature 120 °C | 5509 psi @Strain 52.0 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
38.0 MPa @Strain 39.0 %, Temperature 80.0 °C | 5510 psi @Strain 39.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
38.0 MPa @Strain 18.0 %, Temperature 60.0 °C | 5510 psi @Strain 18.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
38.1 MPa @Strain 40.0 %, Temperature 80.0 °C | 5530 psi @Strain 40.0 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
38.12 MPa @Strain 25.9 %, Temperature 100 °C | 5529 psi @Strain 25.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
38.3 MPa @Strain 19.0 %, Temperature 60.0 °C | 5550 psi @Strain 19.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
38.4 MPa @Strain 5.00 %, Temperature 23.0 °C | 5570 psi @Strain 5.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
38.42 MPa @Strain 26.9 %, Temperature 100 °C | 5572 psi @Strain 26.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
38.44 MPa @Strain 11.9 %, Temperature 80.0 °C | 5575 psi @Strain 11.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
38.6 MPa @Strain 20.0 %, Temperature 60.0 °C | 5600 psi @Strain 20.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
38.66 MPa @Strain 27.9 %, Temperature 100 °C | 5607 psi @Strain 27.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
38.88 MPa @Strain 28.9 %, Temperature 100 °C | 5639 psi @Strain 28.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
38.9 MPa @Strain 21.0 %, Temperature 60.0 °C | 5640 psi @Strain 21.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
38.9 MPa @Strain 6.40 %, Temperature 60.0 °C | 5640 psi @Strain 6.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
39.1 MPa @Strain 22.0 %, Temperature 60.0 °C | 5670 psi @Strain 22.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
39.11 MPa @Strain 29.9 %, Temperature 100 °C | 5672 psi @Strain 29.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
39.2 MPa @Strain 0.600 %, Temperature -40.0 °C | 5690 psi @Strain 0.600 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
39.37 MPa @Strain 30.9 %, Temperature 100 °C | 5710 psi @Strain 30.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
39.4 MPa @Strain 23.0 %, Temperature 60.0 °C | 5710 psi @Strain 23.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
39.45 MPa @Strain 12.9 %, Temperature 80.0 °C | 5722 psi @Strain 12.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
39.5 MPa @Strain 24.0 %, Temperature 60.0 °C | 5730 psi @Strain 24.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
39.55 MPa @Strain 31.9 %, Temperature 100 °C | 5736 psi @Strain 31.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
39.7 MPa @Strain 0.800 %, Temperature 23.0 °C | 5760 psi @Strain 0.800 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
39.78 MPa @Strain 0.700 %, Temperature -40.0 °C | 5770 psi @Strain 0.700 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
39.79 MPa @Strain 32.9 %, Temperature 100 °C | 5771 psi @Strain 32.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
39.8 MPa @Strain 25.0 %, Temperature 60.0 °C | 5770 psi @Strain 25.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
39.8 MPa @Strain 5.50 %, Temperature 23.0 °C | 5770 psi @Strain 5.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
39.8 MPa @Strain 6.90 %, Temperature 60.0 °C | 5770 psi @Strain 6.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
39.98 MPa @Strain 33.9 %, Temperature 100 °C | 5799 psi @Strain 33.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
40.0 MPa @Strain 26.0 %, Temperature 60.0 °C | 5800 psi @Strain 26.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
40.13 MPa @Strain 34.9 %, Temperature 100 °C | 5820 psi @Strain 34.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
40.13 MPa @Strain 35.9 %, Temperature 100 °C | 5820 psi @Strain 35.9 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
40.2 MPa @Strain 27.0 %, Temperature 60.0 °C | 5830 psi @Strain 27.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
40.25 MPa @Strain 13.9 %, Temperature 80.0 °C | 5838 psi @Strain 13.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
40.3 MPa @Strain 28.0 %, Temperature 60.0 °C | 5850 psi @Strain 28.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
40.5 MPa @Strain 29.0 %, Temperature 60.0 °C | 5870 psi @Strain 29.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
40.6 MPa @Strain 7.40 %, Temperature 60.0 °C | 5890 psi @Strain 7.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
40.7 MPa @Strain 30.0 %, Temperature 60.0 °C | 5900 psi @Strain 30.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
40.9 MPa @Strain 31.0 %, Temperature 60.0 °C | 5930 psi @Strain 31.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
40.9 MPa @Strain 6.00 %, Temperature 23.0 °C | 5930 psi @Strain 6.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
40.9 MPa @Strain 0.900 %, Temperature 0.000 °C | 5930 psi @Strain 0.900 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
40.91 MPa @Strain 0.800 %, Temperature 0.000 °C | 5934 psi @Strain 0.800 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
40.99 MPa @Strain 14.9 %, Temperature 80.0 °C | 5945 psi @Strain 14.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
41.0 MPa @Strain 32.0 %, Temperature 60.0 °C | 5950 psi @Strain 32.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
41.1 MPa @Strain 33.0 %, Temperature 60.0 °C | 5960 psi @Strain 33.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
41.2 MPa @Strain 34.0 %, Temperature 60.0 °C | 5980 psi @Strain 34.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
41.4 MPa @Strain 35.0 %, Temperature 60.0 °C | 6000 psi @Strain 35.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
41.4 MPa @Strain 7.90 %, Temperature 60.0 °C | 6000 psi @Strain 7.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
41.5 MPa @Strain 36.0 %, Temperature 60.0 °C | 6020 psi @Strain 36.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
41.6 MPa @Strain 37.0 %, Temperature 60.0 °C | 6030 psi @Strain 37.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
41.66 MPa @Strain 15.9 %, Temperature 80.0 °C | 6042 psi @Strain 15.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
41.8 MPa @Strain 38.0 %, Temperature 60.0 °C | 6060 psi @Strain 38.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
41.9 MPa @Strain 39.0 %, Temperature 60.0 °C | 6080 psi @Strain 39.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
41.9 MPa @Strain 6.50 %, Temperature 23.0 °C | 6080 psi @Strain 6.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
42.0 MPa @Strain 40.0 %, Temperature 60.0 °C | 6090 psi @Strain 40.0 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
42.2 MPa @Strain 8.40 %, Temperature 60.0 °C | 6120 psi @Strain 8.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
42.29 MPa @Strain 16.9 %, Temperature 80.0 °C | 6134 psi @Strain 16.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
42.7 MPa @Strain 7.00 %, Temperature 23.0 °C | 6190 psi @Strain 7.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
42.84 MPa @Strain 17.9 %, Temperature 80.0 °C | 6213 psi @Strain 17.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
42.9 MPa @Strain 8.90 %, Temperature 60.0 °C | 6220 psi @Strain 8.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
43.39 MPa @Strain 18.9 %, Temperature 80.0 °C | 6293 psi @Strain 18.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
43.4 MPa @Strain 7.50 %, Temperature 23.0 °C | 6290 psi @Strain 7.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
43.5 MPa @Strain 9.40 %, Temperature 60.0 °C | 6310 psi @Strain 9.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
43.89 MPa @Strain 19.9 %, Temperature 80.0 °C | 6366 psi @Strain 19.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
44.0 MPa @Strain 1.00 %, Temperature 0.000 °C | 6380 psi @Strain 1.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
44.1 MPa @Strain 8.00 %, Temperature 23.0 °C | 6400 psi @Strain 8.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
44.2 MPa @Strain 9.90 %, Temperature 60.0 °C | 6410 psi @Strain 9.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
44.2 MPa @Strain 0.900 %, Temperature 23.0 °C | 6410 psi @Strain 0.900 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
44.37 MPa @Strain 20.9 %, Temperature 80.0 °C | 6435 psi @Strain 20.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
44.7 MPa @Strain 10.9 %, Temperature 60.0 °C | 6480 psi @Strain 10.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
44.7 MPa @Strain 8.50 %, Temperature 23.0 °C | 6480 psi @Strain 8.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
44.7 MPa @Strain 0.700 %, Temperature -40.0 °C | 6480 psi @Strain 0.700 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
44.84 MPa @Strain 21.9 %, Temperature 80.0 °C | 6504 psi @Strain 21.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
44.93 MPa @Strain 0.800 %, Temperature -40.0 °C | 6517 psi @Strain 0.800 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
44.97 MPa @Strain 0.900 %, Temperature 0.000 °C | 6522 psi @Strain 0.900 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
45.2 MPa @Strain 22.9 %, Temperature 80.0 °C | 6560 psi @Strain 22.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
45.4 MPa @Strain 9.00 %, Temperature 23.0 °C | 6580 psi @Strain 9.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
45.64 MPa @Strain 23.9 %, Temperature 80.0 °C | 6620 psi @Strain 23.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
45.7 MPa @Strain 11.9 %, Temperature 60.0 °C | 6630 psi @Strain 11.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
45.9 MPa @Strain 9.50 %, Temperature 23.0 °C | 6660 psi @Strain 9.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
46.03 MPa @Strain 24.9 %, Temperature 80.0 °C | 6676 psi @Strain 24.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
46.38 MPa @Strain 25.9 %, Temperature 80.0 °C | 6727 psi @Strain 25.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
46.4 MPa @Strain 1.10 %, Temperature 0.000 °C | 6730 psi @Strain 1.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
46.69 MPa @Strain 26.9 %, Temperature 80.0 °C | 6772 psi @Strain 26.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
46.7 MPa @Strain 10.0 %, Temperature 23.0 °C | 6770 psi @Strain 10.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
46.8 MPa @Strain 12.9 %, Temperature 60.0 °C | 6790 psi @Strain 12.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
46.9 MPa @Strain 27.9 %, Temperature 80.0 °C | 6800 psi @Strain 27.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
47.2 MPa @Strain 28.9 %, Temperature 80.0 °C | 6850 psi @Strain 28.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
47.4 MPa @Strain 29.9 %, Temperature 80.0 °C | 6870 psi @Strain 29.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
47.6 MPa @Strain 30.9 %, Temperature 80.0 °C | 6900 psi @Strain 30.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
47.6 MPa @Strain 13.9 %, Temperature 60.0 °C | 6900 psi @Strain 13.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
47.6 MPa @Strain 11.0 %, Temperature 23.0 °C | 6900 psi @Strain 11.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
47.7 MPa @Strain 31.9 %, Temperature 80.0 °C | 6920 psi @Strain 31.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
47.8 MPa @Strain 32.9 %, Temperature 80.0 °C | 6930 psi @Strain 32.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
47.9 MPa @Strain 33.9 %, Temperature 80.0 °C | 6950 psi @Strain 33.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
48.0 MPa @Strain 34.9 %, Temperature 80.0 °C | 6960 psi @Strain 34.9 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
48.3 MPa @Strain 12.0 %, Temperature 23.0 °C | 7010 psi @Strain 12.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
48.4 MPa @Strain 14.9 %, Temperature 60.0 °C | 7020 psi @Strain 14.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
48.4 MPa @Strain 1.00 %, Temperature 23.0 °C | 7020 psi @Strain 1.00 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
48.6 MPa @Strain 1.20 %, Temperature 0.000 °C | 7050 psi @Strain 1.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
48.9 MPa @Strain 13.0 %, Temperature 23.0 °C | 7090 psi @Strain 13.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
49.2 MPa @Strain 15.9 %, Temperature 60.0 °C | 7140 psi @Strain 15.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
49.5 MPa @Strain 14.0 %, Temperature 23.0 °C | 7180 psi @Strain 14.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
49.73 MPa @Strain 1.00 %, Temperature 0.000 °C | 7213 psi @Strain 1.00 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
49.8 MPa @Strain 16.9 %, Temperature 60.0 °C | 7220 psi @Strain 16.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
49.92 MPa @Strain 0.900 %, Temperature -40.0 °C | 7240 psi @Strain 0.900 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
50.0 MPa @Strain 15.0 %, Temperature 23.0 °C | 7250 psi @Strain 15.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
50.4 MPa @Strain 16.0 %, Temperature 23.0 °C | 7310 psi @Strain 16.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
50.4 MPa @Strain 0.800 %, Temperature -40.0 °C | 7310 psi @Strain 0.800 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
50.5 MPa @Strain 17.9 %, Temperature 60.0 °C | 7320 psi @Strain 17.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
50.8 MPa @Strain 17.0 %, Temperature 23.0 °C | 7370 psi @Strain 17.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
50.8 MPa @Strain 1.30 %, Temperature 0.000 °C | 7370 psi @Strain 1.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
51.1 MPa @Strain 18.0 %, Temperature 23.0 °C | 7410 psi @Strain 18.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
51.1 MPa @Strain 18.9 %, Temperature 60.0 °C | 7410 psi @Strain 18.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
51.5 MPa @Strain 19.0 %, Temperature 23.0 °C | 7470 psi @Strain 19.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
51.7 MPa @Strain 19.9 %, Temperature 60.0 °C | 7500 psi @Strain 19.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
51.8 MPa @Strain 20.0 %, Temperature 23.0 °C | 7510 psi @Strain 20.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
52.0 MPa @Strain 21.0 %, Temperature 23.0 °C | 7540 psi @Strain 21.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
52.0 MPa @Strain 1.10 %, Temperature 23.0 °C | 7540 psi @Strain 1.10 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
52.1 MPa @Strain 20.9 %, Temperature 60.0 °C | 7560 psi @Strain 20.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
52.3 MPa @Strain 22.0 %, Temperature 23.0 °C | 7590 psi @Strain 22.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
52.5 MPa @Strain 23.0 %, Temperature 23.0 °C | 7610 psi @Strain 23.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
52.7 MPa @Strain 24.0 %, Temperature 23.0 °C | 7640 psi @Strain 24.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
52.7 MPa @Strain 21.9 %, Temperature 60.0 °C | 7640 psi @Strain 21.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
52.7 MPa @Strain 1.40 %, Temperature 0.000 °C | 7640 psi @Strain 1.40 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
52.9 MPa @Strain 25.0 %, Temperature 23.0 °C | 7670 psi @Strain 25.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
53.1 MPa @Strain 26.0 %, Temperature 23.0 °C | 7700 psi @Strain 26.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
53.1 MPa @Strain 22.9 %, Temperature 60.0 °C | 7700 psi @Strain 22.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
53.3 MPa @Strain 27.0 %, Temperature 23.0 °C | 7730 psi @Strain 27.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
53.5 MPa @Strain 28.0 %, Temperature 23.0 °C | 7760 psi @Strain 28.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
53.6 MPa @Strain 23.9 %, Temperature 60.0 °C | 7770 psi @Strain 23.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
53.66 MPa @Strain 1.10 %, Temperature 0.000 °C | 7783 psi @Strain 1.10 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
53.7 MPa @Strain 29.0 %, Temperature 23.0 °C | 7790 psi @Strain 29.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
53.9 MPa @Strain 30.0 %, Temperature 23.0 °C | 7820 psi @Strain 30.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
54.0 MPa @Strain 31.0 %, Temperature 23.0 °C | 7830 psi @Strain 31.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
54.0 MPa @Strain 24.9 %, Temperature 60.0 °C | 7830 psi @Strain 24.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
54.2 MPa @Strain 32.0 %, Temperature 23.0 °C | 7860 psi @Strain 32.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
54.3 MPa @Strain 1.50 %, Temperature 0.000 °C | 7880 psi @Strain 1.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
54.4 MPa @Strain 33.0 %, Temperature 23.0 °C | 7890 psi @Strain 33.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
54.4 MPa @Strain 25.9 %, Temperature 60.0 °C | 7890 psi @Strain 25.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
54.6 MPa @Strain 34.0 %, Temperature 23.0 °C | 7920 psi @Strain 34.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
54.7 MPa @Strain 35.0 %, Temperature 23.0 °C | 7930 psi @Strain 35.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
54.7 MPa @Strain 26.9 %, Temperature 60.0 °C | 7930 psi @Strain 26.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
54.8 MPa @Strain 36.0 %, Temperature 23.0 °C | 7950 psi @Strain 36.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
54.86 MPa @Strain 1.00 %, Temperature -40.0 °C | 7957 psi @Strain 1.00 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
55.0 MPa @Strain 37.0 %, Temperature 23.0 °C | 7980 psi @Strain 37.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
55.1 MPa @Strain 27.9 %, Temperature 60.0 °C | 7990 psi @Strain 27.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
55.2 MPa @Strain 38.0 %, Temperature 23.0 °C | 8010 psi @Strain 38.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
55.3 MPa @Strain 39.0 %, Temperature 23.0 °C | 8020 psi @Strain 39.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
55.3 MPa @Strain 1.20 %, Temperature 23.0 °C | 8020 psi @Strain 1.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
55.4 MPa @Strain 40.0 %, Temperature 23.0 °C | 8040 psi @Strain 40.0 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
55.4 MPa @Strain 28.9 %, Temperature 60.0 °C | 8040 psi @Strain 28.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
55.7 MPa @Strain 29.9 %, Temperature 60.0 °C | 8080 psi @Strain 29.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
55.7 MPa @Strain 1.60 %, Temperature 0.000 °C | 8080 psi @Strain 1.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
55.7 MPa @Strain 0.900 %, Temperature -40.0 °C | 8080 psi @Strain 0.900 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
56.0 MPa @Strain 30.9 %, Temperature 60.0 °C | 8120 psi @Strain 30.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
56.3 MPa @Strain 31.9 %, Temperature 60.0 °C | 8170 psi @Strain 31.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
56.6 MPa @Strain 32.9 %, Temperature 60.0 °C | 8210 psi @Strain 32.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
56.8 MPa @Strain 33.9 %, Temperature 60.0 °C | 8240 psi @Strain 33.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
56.8 MPa @Strain 1.70 %, Temperature 0.000 °C | 8240 psi @Strain 1.70 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
57.1 MPa @Strain 34.9 %, Temperature 60.0 °C | 8280 psi @Strain 34.9 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
57.45 MPa @Strain 1.20 %, Temperature 0.000 °C | 8332 psi @Strain 1.20 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
57.9 MPa @Strain 1.80 %, Temperature 0.000 °C | 8400 psi @Strain 1.80 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
58.3 MPa @Strain 1.30 %, Temperature 23.0 °C | 8460 psi @Strain 1.30 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
58.9 MPa @Strain 1.90 %, Temperature 0.000 °C | 8540 psi @Strain 1.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
59.6 MPa @Strain 2.00 %, Temperature 0.000 °C | 8640 psi @Strain 2.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
59.72 MPa @Strain 1.10 %, Temperature -40.0 °C | 8662 psi @Strain 1.10 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
60.4 MPa @Strain 2.10 %, Temperature 0.000 °C | 8760 psi @Strain 2.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
60.6 MPa @Strain 1.00 %, Temperature -40.0 °C | 8790 psi @Strain 1.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
60.95 MPa @Strain 1.30 %, Temperature 0.000 °C | 8840 psi @Strain 1.30 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
61.1 MPa @Strain 1.40 %, Temperature 23.0 °C | 8860 psi @Strain 1.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
61.3 MPa @Strain 2.20 %, Temperature 0.000 °C | 8890 psi @Strain 2.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
62.1 MPa @Strain 2.30 %, Temperature 0.000 °C | 9010 psi @Strain 2.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
62.8 MPa @Strain 2.40 %, Temperature 0.000 °C | 9110 psi @Strain 2.40 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
63.5 MPa @Strain 2.50 %, Temperature 0.000 °C | 9210 psi @Strain 2.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
63.8 MPa @Strain 1.50 %, Temperature 23.0 °C | 9250 psi @Strain 1.50 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
63.89 MPa @Strain 1.20 %, Temperature -40.0 °C | 9266 psi @Strain 1.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
64.0 MPa @Strain 2.60 %, Temperature 0.000 °C | 9280 psi @Strain 2.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
64.4 MPa @Strain 2.70 %, Temperature 0.000 °C | 9340 psi @Strain 2.70 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
64.51 MPa @Strain 1.40 %, Temperature 0.000 °C | 9356 psi @Strain 1.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
64.8 MPa @Strain 2.80 %, Temperature 0.000 °C | 9400 psi @Strain 2.80 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
65.1 MPa @Strain 2.90 %, Temperature 0.000 °C | 9440 psi @Strain 2.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
65.3 MPa @Strain 1.10 %, Temperature -40.0 °C | 9470 psi @Strain 1.10 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
65.5 MPa @Strain 3.00 %, Temperature 0.000 °C | 9500 psi @Strain 3.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
65.7 MPa @Strain 3.10 %, Temperature 0.000 °C | 9530 psi @Strain 3.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
65.9 MPa @Strain 1.60 %, Temperature 23.0 °C | 9560 psi @Strain 1.60 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
66.1 MPa @Strain 3.20 %, Temperature 0.000 °C | 9590 psi @Strain 3.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
66.4 MPa @Strain 3.30 %, Temperature 0.000 °C | 9630 psi @Strain 3.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
66.5 MPa @Strain 3.40 %, Temperature 0.000 °C | 9650 psi @Strain 3.40 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
66.8 MPa @Strain 3.50 %, Temperature 0.000 °C | 9690 psi @Strain 3.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
67.0 MPa @Strain 3.60 %, Temperature 0.000 °C | 9720 psi @Strain 3.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
67.4 MPa @Strain 3.70 %, Temperature 0.000 °C | 9780 psi @Strain 3.70 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
67.6 MPa @Strain 3.80 %, Temperature 0.000 °C | 9800 psi @Strain 3.80 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
67.7 MPa @Strain 1.70 %, Temperature 23.0 °C | 9820 psi @Strain 1.70 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
67.77 MPa @Strain 1.50 %, Temperature 0.000 °C | 9829 psi @Strain 1.50 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
67.9 MPa @Strain 3.90 %, Temperature 0.000 °C | 9850 psi @Strain 3.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
68.3 MPa @Strain 4.00 %, Temperature 0.000 °C | 9910 psi @Strain 4.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
68.34 MPa @Strain 1.30 %, Temperature -40.0 °C | 9912 psi @Strain 1.30 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
68.6 MPa @Strain 4.10 %, Temperature 0.000 °C | 9950 psi @Strain 4.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
68.8 MPa @Strain 4.20 %, Temperature 0.000 °C | 9980 psi @Strain 4.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
69.0 MPa @Strain 4.30 %, Temperature 0.000 °C | 10000 psi @Strain 4.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
69.3 MPa @Strain 4.40 %, Temperature 0.000 °C | 10100 psi @Strain 4.40 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
69.4 MPa @Strain 4.50 %, Temperature 0.000 °C | 10100 psi @Strain 4.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
69.5 MPa @Strain 1.80 %, Temperature 23.0 °C | 10100 psi @Strain 1.80 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
69.6 MPa @Strain 4.60 %, Temperature 0.000 °C | 10100 psi @Strain 4.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
69.6 MPa @Strain 1.20 %, Temperature -40.0 °C | 10100 psi @Strain 1.20 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
69.7 MPa @Strain 4.70 %, Temperature 0.000 °C | 10100 psi @Strain 4.70 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
69.9 MPa @Strain 4.80 %, Temperature 0.000 °C | 10100 psi @Strain 4.80 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
70.0 MPa @Strain 4.90 %, Temperature 0.000 °C | 10200 psi @Strain 4.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
70.49 MPa @Strain 1.60 %, Temperature 0.000 °C | 10220 psi @Strain 1.60 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
70.5 MPa @Strain 5.00 %, Temperature 0.000 °C | 10200 psi @Strain 5.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
70.9 MPa @Strain 1.90 %, Temperature 23.0 °C | 10300 psi @Strain 1.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
71.7 MPa @Strain 5.50 %, Temperature 0.000 °C | 10400 psi @Strain 5.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
72.2 MPa @Strain 6.00 %, Temperature 0.000 °C | 10500 psi @Strain 6.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
72.2 MPa @Strain 2.00 %, Temperature 23.0 °C | 10500 psi @Strain 2.00 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
72.6 MPa @Strain 6.50 %, Temperature 0.000 °C | 10500 psi @Strain 6.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
72.67 MPa @Strain 1.40 %, Temperature -40.0 °C | 10540 psi @Strain 1.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
73.15 MPa @Strain 1.70 %, Temperature 0.000 °C | 10610 psi @Strain 1.70 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
73.2 MPa @Strain 2.10 %, Temperature 23.0 °C | 10600 psi @Strain 2.10 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
73.3 MPa @Strain 7.00 %, Temperature 0.000 °C | 10600 psi @Strain 7.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
73.7 MPa @Strain 1.30 %, Temperature -40.0 °C | 10700 psi @Strain 1.30 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
73.9 MPa @Strain 7.50 %, Temperature 0.000 °C | 10700 psi @Strain 7.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
74.2 MPa @Strain 8.00 %, Temperature 0.000 °C | 10800 psi @Strain 8.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
74.2 MPa @Strain 2.20 %, Temperature 23.0 °C | 10800 psi @Strain 2.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
74.4 MPa @Strain 8.50 %, Temperature 0.000 °C | 10800 psi @Strain 8.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
74.9 MPa @Strain 9.00 %, Temperature 0.000 °C | 10900 psi @Strain 9.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
75.0 MPa @Strain 2.30 %, Temperature 23.0 °C | 10900 psi @Strain 2.30 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
75.2 MPa @Strain 9.50 %, Temperature 0.000 °C | 10900 psi @Strain 9.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
75.4 MPa @Strain 2.40 %, Temperature 23.0 °C | 10900 psi @Strain 2.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
75.49 MPa @Strain 1.80 %, Temperature 0.000 °C | 10950 psi @Strain 1.80 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
75.6 MPa @Strain 10.0 %, Temperature 0.000 °C | 11000 psi @Strain 10.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
76.0 MPa @Strain 2.50 %, Temperature 23.0 °C | 11000 psi @Strain 2.50 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
76.2 MPa @Strain 11.0 %, Temperature 0.000 °C | 11100 psi @Strain 11.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
76.5 MPa @Strain 12.0 %, Temperature 0.000 °C | 11100 psi @Strain 12.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
76.5 MPa @Strain 2.60 %, Temperature 23.0 °C | 11100 psi @Strain 2.60 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
76.62 MPa @Strain 1.50 %, Temperature -40.0 °C | 11110 psi @Strain 1.50 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
76.8 MPa @Strain 2.70 %, Temperature 23.0 °C | 11100 psi @Strain 2.70 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.0 MPa @Strain 13.0 %, Temperature 0.000 °C | 11200 psi @Strain 13.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
77.1 MPa @Strain 2.80 %, Temperature 23.0 °C | 11200 psi @Strain 2.80 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.2 MPa @Strain 2.90 %, Temperature 23.0 °C | 11200 psi @Strain 2.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.2 MPa @Strain 14.0 %, Temperature 0.000 °C | 11200 psi @Strain 14.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
77.5 MPa @Strain 3.00 %, Temperature 23.0 °C | 11200 psi @Strain 3.00 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.6 MPa @Strain 3.10 %, Temperature 23.0 °C | 11300 psi @Strain 3.10 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.6 MPa @Strain 15.0 %, Temperature 0.000 °C | 11300 psi @Strain 15.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
77.6 MPa @Strain 1.40 %, Temperature -40.0 °C | 11300 psi @Strain 1.40 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
77.66 MPa @Strain 1.90 %, Temperature 0.000 °C | 11260 psi @Strain 1.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
77.7 MPa @Strain 16.0 %, Temperature 0.000 °C | 11300 psi @Strain 16.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
77.7 MPa @Strain 3.20 %, Temperature 23.0 °C | 11300 psi @Strain 3.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.8 MPa @Strain 3.30 %, Temperature 23.0 °C | 11300 psi @Strain 3.30 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.8 MPa @Strain 4.90 %, Temperature 23.0 °C | 11300 psi @Strain 4.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.8 MPa @Strain 5.90 %, Temperature 23.0 °C | 11300 psi @Strain 5.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.8 MPa @Strain 6.40 %, Temperature 23.0 °C | 11300 psi @Strain 6.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.8 MPa @Strain 6.90 %, Temperature 23.0 °C | 11300 psi @Strain 6.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.8 MPa @Strain 7.40 %, Temperature 23.0 °C | 11300 psi @Strain 7.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.8 MPa @Strain 7.90 %, Temperature 23.0 °C | 11300 psi @Strain 7.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 8.40 %, Temperature 23.0 °C | 11300 psi @Strain 8.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 8.90 %, Temperature 23.0 °C | 11300 psi @Strain 8.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 9.40 %, Temperature 23.0 °C | 11300 psi @Strain 9.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 4.30 %, Temperature 23.0 °C | 11300 psi @Strain 4.30 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 4.50 %, Temperature 23.0 °C | 11300 psi @Strain 4.50 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 4.60 %, Temperature 23.0 °C | 11300 psi @Strain 4.60 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 3.40 %, Temperature 23.0 °C | 11300 psi @Strain 3.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 3.50 %, Temperature 23.0 °C | 11300 psi @Strain 3.50 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 3.60 %, Temperature 23.0 °C | 11300 psi @Strain 3.60 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 5.40 %, Temperature 23.0 °C | 11300 psi @Strain 5.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 17.0 %, Temperature 0.000 °C | 11300 psi @Strain 17.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
77.9 MPa @Strain 4.10 %, Temperature 23.0 °C | 11300 psi @Strain 4.10 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
77.9 MPa @Strain 4.80 %, Temperature 23.0 °C | 11300 psi @Strain 4.80 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 4.20 %, Temperature 23.0 °C | 11300 psi @Strain 4.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 4.00 %, Temperature 23.0 °C | 11300 psi @Strain 4.00 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 3.70 %, Temperature 23.0 °C | 11300 psi @Strain 3.70 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 3.80 %, Temperature 23.0 °C | 11300 psi @Strain 3.80 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 3.90 %, Temperature 23.0 °C | 11300 psi @Strain 3.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 4.70 %, Temperature 23.0 °C | 11300 psi @Strain 4.70 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 9.90 %, Temperature 23.0 °C | 11300 psi @Strain 9.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 10.9 %, Temperature 23.0 °C | 11300 psi @Strain 10.9 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.0 MPa @Strain 11.9 %, Temperature 23.0 °C | 11300 psi @Strain 11.9 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.1 MPa @Strain 18.0 %, Temperature 0.000 °C | 11300 psi @Strain 18.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
78.2 MPa @Strain 12.9 %, Temperature 23.0 °C | 11300 psi @Strain 12.9 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.3 MPa @Strain 13.9 %, Temperature 23.0 °C | 11400 psi @Strain 13.9 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.4 MPa @Strain 14.9 %, Temperature 23.0 °C | 11400 psi @Strain 14.9 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.4 MPa @Strain 15.9 %, Temperature 23.0 °C | 11400 psi @Strain 15.9 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.5 MPa @Strain 16.9 %, Temperature 23.0 °C | 11400 psi @Strain 16.9 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.5 MPa @Strain 17.9 %, Temperature 23.0 °C | 11400 psi @Strain 17.9 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
78.5 MPa @Strain 19.0 %, Temperature 0.000 °C | 11400 psi @Strain 19.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
78.9 MPa @Strain 20.0 %, Temperature 0.000 °C | 11400 psi @Strain 20.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
79.2 MPa @Strain 21.0 %, Temperature 0.000 °C | 11500 psi @Strain 21.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
79.5 MPa @Strain 22.0 %, Temperature 0.000 °C | 11500 psi @Strain 22.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
79.65 MPa @Strain 2.00 %, Temperature 0.000 °C | 11550 psi @Strain 2.00 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
79.7 MPa @Strain 23.0 %, Temperature 0.000 °C | 11600 psi @Strain 23.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
79.9 MPa @Strain 24.0 %, Temperature 0.000 °C | 11600 psi @Strain 24.0 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
80.05 MPa @Strain 1.60 %, Temperature -40.0 °C | 11610 psi @Strain 1.60 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
81.0 MPa @Strain 1.50 %, Temperature -40.0 °C | 11700 psi @Strain 1.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
81.46 MPa @Strain 2.10 %, Temperature 0.000 °C | 11810 psi @Strain 2.10 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
82.89 MPa @Strain 2.20 %, Temperature 0.000 °C | 12020 psi @Strain 2.20 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
83.33 MPa @Strain 1.70 %, Temperature -40.0 °C | 12090 psi @Strain 1.70 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
84.15 MPa @Strain 2.30 %, Temperature 0.000 °C | 12200 psi @Strain 2.30 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
84.2 MPa @Strain 1.60 %, Temperature -40.0 °C | 12200 psi @Strain 1.60 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
85.51 MPa @Strain 2.40 %, Temperature 0.000 °C | 12400 psi @Strain 2.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
86.59 MPa @Strain 2.50 %, Temperature 0.000 °C | 12560 psi @Strain 2.50 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
86.77 MPa @Strain 1.80 %, Temperature -40.0 °C | 12580 psi @Strain 1.80 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
87.2 MPa @Strain 1.70 %, Temperature -40.0 °C | 12600 psi @Strain 1.70 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
87.56 MPa @Strain 2.60 %, Temperature 0.000 °C | 12700 psi @Strain 2.60 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
88.31 MPa @Strain 2.70 %, Temperature 0.000 °C | 12810 psi @Strain 2.70 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
88.96 MPa @Strain 2.80 %, Temperature 0.000 °C | 12900 psi @Strain 2.80 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
89.56 MPa @Strain 2.90 %, Temperature 0.000 °C | 12990 psi @Strain 2.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
89.79 MPa @Strain 1.90 %, Temperature -40.0 °C | 13020 psi @Strain 1.90 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
89.8 MPa @Strain 1.80 %, Temperature -40.0 °C | 13000 psi @Strain 1.80 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
90.04 MPa @Strain 3.00 %, Temperature 0.000 °C | 13060 psi @Strain 3.00 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
90.61 MPa @Strain 3.10 %, Temperature 0.000 °C | 13140 psi @Strain 3.10 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
90.9 MPa @Strain 3.20 %, Temperature 0.000 °C | 13200 psi @Strain 3.20 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
91.37 MPa @Strain 3.30 %, Temperature 0.000 °C | 13250 psi @Strain 3.30 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
91.62 MPa @Strain 3.40 %, Temperature 0.000 °C | 13290 psi @Strain 3.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
91.85 MPa @Strain 3.50 %, Temperature 0.000 °C | 13320 psi @Strain 3.50 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
91.9 MPa @Strain 3.60 %, Temperature 0.000 °C | 13300 psi @Strain 3.60 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.0 MPa @Strain 1.90 %, Temperature -40.0 °C | 13300 psi @Strain 1.90 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
92.05 MPa @Strain 3.70 %, Temperature 0.000 °C | 13350 psi @Strain 3.70 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.17 MPa @Strain 3.80 %, Temperature 0.000 °C | 13370 psi @Strain 3.80 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.44 MPa @Strain 3.90 %, Temperature 0.000 °C | 13410 psi @Strain 3.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.44 MPa @Strain 4.00 %, Temperature 0.000 °C | 13410 psi @Strain 4.00 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.47 MPa @Strain 2.00 %, Temperature -40.0 °C | 13410 psi @Strain 2.00 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
92.56 MPa @Strain 4.10 %, Temperature 0.000 °C | 13420 psi @Strain 4.10 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.71 MPa @Strain 4.30 %, Temperature 0.000 °C | 13450 psi @Strain 4.30 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.72 MPa @Strain 4.20 %, Temperature 0.000 °C | 13450 psi @Strain 4.20 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.86 MPa @Strain 4.40 %, Temperature 0.000 °C | 13470 psi @Strain 4.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.86 MPa @Strain 4.50 %, Temperature 0.000 °C | 13470 psi @Strain 4.50 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.86 MPa @Strain 4.90 %, Temperature 0.000 °C | 13470 psi @Strain 4.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.86 MPa @Strain 5.40 %, Temperature 0.000 °C | 13470 psi @Strain 5.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.97 MPa @Strain 4.60 %, Temperature 0.000 °C | 13480 psi @Strain 4.60 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.98 MPa @Strain 6.40 %, Temperature 0.000 °C | 13490 psi @Strain 6.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.98 MPa @Strain 4.80 %, Temperature 0.000 °C | 13490 psi @Strain 4.80 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
92.99 MPa @Strain 5.90 %, Temperature 0.000 °C | 13490 psi @Strain 5.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.02 MPa @Strain 4.70 %, Temperature 0.000 °C | 13490 psi @Strain 4.70 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.04 MPa @Strain 6.90 %, Temperature 0.000 °C | 13490 psi @Strain 6.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.05 MPa @Strain 7.40 %, Temperature 0.000 °C | 13500 psi @Strain 7.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.11 MPa @Strain 8.40 %, Temperature 0.000 °C | 13500 psi @Strain 8.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.13 MPa @Strain 7.90 %, Temperature 0.000 °C | 13510 psi @Strain 7.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.2 MPa @Strain 8.90 %, Temperature 0.000 °C | 13500 psi @Strain 8.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.27 MPa @Strain 9.40 %, Temperature 0.000 °C | 13530 psi @Strain 9.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.33 MPa @Strain 9.90 %, Temperature 0.000 °C | 13540 psi @Strain 9.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
93.42 MPa @Strain 10.9 %, Temperature 0.000 °C | 13550 psi @Strain 10.9 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
94.2 MPa @Strain 2.00 %, Temperature -40.0 °C | 13700 psi @Strain 2.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
95.16 MPa @Strain 2.10 %, Temperature -40.0 °C | 13800 psi @Strain 2.10 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
96.4 MPa @Strain 2.10 %, Temperature -40.0 °C | 14000 psi @Strain 2.10 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
97.62 MPa @Strain 2.20 %, Temperature -40.0 °C | 14160 psi @Strain 2.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
98.2 MPa @Strain 2.20 %, Temperature -40.0 °C | 14200 psi @Strain 2.20 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
99.6 MPa @Strain 2.30 %, Temperature -40.0 °C | 14400 psi @Strain 2.30 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
99.9 MPa @Strain 2.30 %, Temperature -40.0 °C | 14500 psi @Strain 2.30 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
101.1 MPa @Strain 2.40 %, Temperature -40.0 °C | 14660 psi @Strain 2.40 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
101.96 MPa @Strain 2.40 %, Temperature -40.0 °C | 14788 psi @Strain 2.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
102.3 MPa @Strain 2.50 %, Temperature -40.0 °C | 14840 psi @Strain 2.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
103.3 MPa @Strain 2.60 %, Temperature -40.0 °C | 14980 psi @Strain 2.60 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
103.78 MPa @Strain 2.50 %, Temperature -40.0 °C | 15052 psi @Strain 2.50 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
104.1 MPa @Strain 2.70 %, Temperature -40.0 °C | 15100 psi @Strain 2.70 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
105.2 MPa @Strain 2.80 %, Temperature -40.0 °C | 15260 psi @Strain 2.80 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
105.26 MPa @Strain 2.60 %, Temperature -40.0 °C | 15267 psi @Strain 2.60 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
106.3 MPa @Strain 2.90 %, Temperature -40.0 °C | 15420 psi @Strain 2.90 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
106.69 MPa @Strain 2.70 %, Temperature -40.0 °C | 15474 psi @Strain 2.70 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
107.3 MPa @Strain 3.00 %, Temperature -40.0 °C | 15560 psi @Strain 3.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
108.21 MPa @Strain 2.80 %, Temperature -40.0 °C | 15695 psi @Strain 2.80 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
108.3 MPa @Strain 3.10 %, Temperature -40.0 °C | 15710 psi @Strain 3.10 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
109 MPa @Strain 3.20 %, Temperature -40.0 °C | 15800 psi @Strain 3.20 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
109.46 MPa @Strain 2.90 %, Temperature -40.0 °C | 15876 psi @Strain 2.90 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
109.6 MPa @Strain 3.30 %, Temperature -40.0 °C | 15900 psi @Strain 3.30 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
110.1 MPa @Strain 3.40 %, Temperature -40.0 °C | 15970 psi @Strain 3.40 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
110.51 MPa @Strain 3.00 %, Temperature -40.0 °C | 16028 psi @Strain 3.00 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
110.6 MPa @Strain 3.50 %, Temperature -40.0 °C | 16040 psi @Strain 3.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
111 MPa @Strain 3.60 %, Temperature -40.0 °C | 16100 psi @Strain 3.60 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
111.33 MPa @Strain 3.10 %, Temperature -40.0 °C | 16147 psi @Strain 3.10 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
111.4 MPa @Strain 3.70 %, Temperature -40.0 °C | 16160 psi @Strain 3.70 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
111.7 MPa @Strain 3.80 %, Temperature -40.0 °C | 16200 psi @Strain 3.80 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
111.9 MPa @Strain 3.90 %, Temperature -40.0 °C | 16230 psi @Strain 3.90 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
112.11 MPa @Strain 3.20 %, Temperature -40.0 °C | 16260 psi @Strain 3.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
112.4 MPa @Strain 4.00 %, Temperature -40.0 °C | 16300 psi @Strain 4.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
112.8 MPa @Strain 4.10 %, Temperature -40.0 °C | 16360 psi @Strain 4.10 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
112.82 MPa @Strain 3.30 %, Temperature -40.0 °C | 16363 psi @Strain 3.30 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
113.2 MPa @Strain 4.20 %, Temperature -40.0 °C | 16420 psi @Strain 4.20 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
113.6 MPa @Strain 4.30 %, Temperature -40.0 °C | 16480 psi @Strain 4.30 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
113.64 MPa @Strain 3.40 %, Temperature -40.0 °C | 16482 psi @Strain 3.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
113.7 MPa @Strain 4.40 %, Temperature -40.0 °C | 16490 psi @Strain 4.40 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
113.9 MPa @Strain 4.50 %, Temperature -40.0 °C | 16520 psi @Strain 4.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
114.1 MPa @Strain 4.60 %, Temperature -40.0 °C | 16550 psi @Strain 4.60 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
114.24 MPa @Strain 3.50 %, Temperature -40.0 °C | 16569 psi @Strain 3.50 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
114.4 MPa @Strain 4.70 %, Temperature -40.0 °C | 16590 psi @Strain 4.70 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
114.8 MPa @Strain 4.80 %, Temperature -40.0 °C | 16650 psi @Strain 4.80 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
114.83 MPa @Strain 3.60 %, Temperature -40.0 °C | 16655 psi @Strain 3.60 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
115 MPa @Strain 4.90 %, Temperature -40.0 °C | 16700 psi @Strain 4.90 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
115.1 MPa @Strain 5.00 %, Temperature -40.0 °C | 16690 psi @Strain 5.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
115.3 MPa @Strain 5.50 %, Temperature -40.0 °C | 16720 psi @Strain 5.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
115.33 MPa @Strain 3.70 %, Temperature -40.0 °C | 16727 psi @Strain 3.70 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
115.5 MPa @Strain 6.00 %, Temperature -40.0 °C | 16750 psi @Strain 6.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
115.7 MPa @Strain 6.50 %, Temperature -40.0 °C | 16780 psi @Strain 6.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
115.88 MPa @Strain 3.80 %, Temperature -40.0 °C | 16807 psi @Strain 3.80 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
115.9 MPa @Strain 7.00 %, Temperature -40.0 °C | 16810 psi @Strain 7.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
116.1 MPa @Strain 7.50 %, Temperature -40.0 °C | 16840 psi @Strain 7.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
116.2 MPa @Strain 8.00 %, Temperature -40.0 °C | 16850 psi @Strain 8.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
116.21 MPa @Strain 3.90 %, Temperature -40.0 °C | 16855 psi @Strain 3.90 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
116.55 MPa @Strain 4.00 %, Temperature -40.0 °C | 16904 psi @Strain 4.00 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
116.81 MPa @Strain 4.10 %, Temperature -40.0 °C | 16942 psi @Strain 4.10 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
117.07 MPa @Strain 4.20 %, Temperature -40.0 °C | 16980 psi @Strain 4.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
117.2 MPa @Strain 4.30 %, Temperature -40.0 °C | 17000 psi @Strain 4.30 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
117.37 MPa @Strain 4.40 %, Temperature -40.0 °C | 17023 psi @Strain 4.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
117.52 MPa @Strain 4.50 %, Temperature -40.0 °C | 17045 psi @Strain 4.50 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
117.73 MPa @Strain 4.60 %, Temperature -40.0 °C | 17075 psi @Strain 4.60 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
117.86 MPa @Strain 4.70 %, Temperature -40.0 °C | 17094 psi @Strain 4.70 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
118.01 MPa @Strain 4.80 %, Temperature -40.0 °C | 17116 psi @Strain 4.80 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
118.09 MPa @Strain 4.90 %, Temperature -40.0 °C | 17128 psi @Strain 4.90 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
118.22 MPa @Strain 5.40 %, Temperature -40.0 °C | 17146 psi @Strain 5.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
118.41 MPa @Strain 6.90 %, Temperature -40.0 °C | 17174 psi @Strain 6.90 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
118.47 MPa @Strain 5.90 %, Temperature -40.0 °C | 17183 psi @Strain 5.90 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
118.53 MPa @Strain 6.40 %, Temperature -40.0 °C | 17191 psi @Strain 6.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
Elongation at Break | 6.0 % @Temperature -40.0 °C | 6.0 % @Temperature -40.0 °F | DAM; ASTM D638 | ||
11 % @Temperature -40.0 °C | 11 % @Temperature -40.0 °F | 50%RH; ASTM D638 | |||
18 % @Temperature 23.0 °C | 18 % @Temperature 73.4 °F | DAM; ISO 527 | |||
20 % @Temperature 23.0 °C | 20 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
40 % @Temperature 23.0 °C | 40 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
45 % @Temperature 23.0 °C | 45 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
55 % @Temperature 77.0 °C | 55 % @Temperature 171 °F | DAM; ASTM D638 | |||
59 % @Temperature 77.0 °C | 59 % @Temperature 171 °F | 50%RH; ASTM D638 | |||
77 % @Temperature 121 °C | 77 % @Temperature 250 °F | DAM; ASTM D638 | |||
79 % @Temperature 121 °C | 79 % @Temperature 250 °F | 50%RH; ASTM D638 | |||
Tensile Modulus | 2.00 GPa @Temperature 23.0 °C | 290 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
4.90 GPa @Temperature 23.0 °C | 711 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
Flexural Modulus | 0.620 GPa @Temperature 121 °C | 89.9 ksi @Temperature 250 °F | 50%RH; ASTM D790 | ||
0.638 GPa @Temperature -40.0 °C | 92.5 ksi @Temperature -40.0 °F | 50%RH; ASTM D790 | |||
0.690 GPa @Temperature 121 °C | 100 ksi @Temperature 250 °F | DAM; ASTM D790 | |||
1.00 GPa @Temperature 77.0 °C | 145 ksi @Temperature 171 °F | 50%RH; ASTM D790 | |||
1.24 GPa @Temperature 77.0 °C | 180 ksi @Temperature 171 °F | DAM; ASTM D790 | |||
1.76 GPa @Temperature 23.0 °C | 255 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | |||
1.80 GPa @Temperature 23.0 °C | 261 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | |||
4.50 GPa @Temperature 23.0 °C | 653 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
4.585 GPa @Temperature 23.0 °C | 665.0 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
6.445 GPa @Temperature -40.0 °C | 934.8 ksi @Temperature -40.0 °F | DAM; ASTM D790 | |||
Shear Strength | 83.0 MPa @Temperature 23.0 °C | 12000 psi @Temperature 73.4 °F | DAM; ASTM D732 | ||
Izod Impact, Notched | 0.480 J/cm @Temperature -40.0 °C | 0.899 ft-lb/in @Temperature -40.0 °F | DAM; ASTM D256 | ||
0.800 J/cm @Temperature -40.0 °C | 1.50 ft-lb/in @Temperature -40.0 °F | 50%RH; ASTM D256 | |||
1.07 J/cm @Temperature 23.0 °C | 2.00 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | |||
1.88 J/cm @Temperature 23.0 °C | 3.52 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 180/1A | ||
5.00 kJ/m² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | |||
6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
13.0 kJ/m² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
Izod Impact, Unnotched (ISO) | 90.0 kJ/m² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1U | ||
100 kJ/m² @Temperature -30.0 °C | 47.6 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1U | |||
190 kJ/m² @Temperature 23.0 °C | 90.4 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1U | |||
330 kJ/m² @Temperature 23.0 °C | 157 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1U | |||
Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
12.0 J/cm² @Temperature -30.0 °C | 57.1 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
21.0 J/cm² @Temperature 23.0 °C | 99.9 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
33.0 J/cm² @Temperature 23.0 °C | 157 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
Charpy Impact, Notched | 0.300 J/cm² @Temperature -40.0 °C | 1.43 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 179/1eA | ||
0.400 J/cm² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | |||
0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+10 ohm-cm @Temperature 23.0 °C | 1.00e+10 ohm-cm @Temperature 73.4 °F | 50%RH; ASTM D257 | ||
1.00e+13 ohm-cm @Temperature 23.0 °C | 1.00e+13 ohm-cm @Temperature 73.4 °F | DAM; ASTM D257 | |||
1.00e+13 ohm-cm @Temperature 23.0 °C | 1.00e+13 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.5 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | ||
3.8 @Frequency 1000 Hz, Temperature 23.0 °C | 3.8 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
3.8 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.8 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
4.0 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.0 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
4.0 @Frequency 100 Hz, Temperature 23.0 °C | 4.0 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
7.3 @Frequency 1000 Hz, Temperature 23.0 °C | 7.3 @Frequency 1000 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
Dielectric Strength | 16.5 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 419 kV/in @Thickness 0.126 in, Temperature 73.4 °F | DAM; Short Time; ASTM D149 | ||
24.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C | 610 kV/in @Thickness 0.0787 in, Temperature 73.4 °F | DAM; IEC 60243-1 | |||
158 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 4010 kV/in @Thickness 0.126 in, Temperature 73.4 °F | 50%RH; Short Time; ASTM D149 | |||
Dissipation Factor | 0.010 @Frequency 1000 Hz, Temperature 23.0 °C | 0.010 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | ||
0.010 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.010 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
0.010 @Frequency 100 Hz, Temperature 23.0 °C | 0.010 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
0.010 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.010 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
0.070 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.070 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
0.10 @Frequency 1000 Hz, Temperature 23.0 °C | 0.10 @Frequency 1000 Hz, Temperature 73.4 °F | 50%RH; ASTM D150 | |||
Comparative Tracking Index | 400 V @Temperature 23.0 °C | 400 V @Temperature 73.4 °F | DAM; UL 746A | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 29.4 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
53.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 29.4 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
65.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 36.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
65.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 36.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
98.0 µm/m-°C @Temperature 55.0 - 160 °C | 54.4 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
98.0 µm/m-°C @Temperature 55.0 - 160 °C | 54.4 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
Melting Point | 258 °C | 496 °F | DAM; ASTM D3418 | ||
Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 | ||
215 °C | 419 °F | DAM; ASTM D648 | |||
Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DAM; ASTM D648 | ||
80.0 °C | 176 °F | DAM; ISO 75-1/-2 | |||
UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
65.0 °C @Thickness 0.810 mm | 149 °F @Thickness 0.0319 in | DAM; UL 746B | |||
65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
UL RTI, Mechanical with Impact | 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | ||
65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
65.0 °C @Thickness 0.810 mm | 149 °F @Thickness 0.0319 in | DAM; UL 746B | |||
UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.810 mm | 149 °F @Thickness 0.0319 in | DAM; UL 746B | ||
65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | ||
HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | DAM; IEC 60695-11-10 | |||
HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | DAM; UL94 | |||
HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
Oxygen Index | 22 % | 22 % | DAM; ASTM D2863 | ||
25 % | 25 % | DAM; ISO 4589-1/-2 | |||
Processing Properties | Metric | English | Comments | ||
Melt Temperature | 256 °C | 493 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
295 °C | 563 °F | DAM; Optimum | |||
285 - 305 °C | 545 - 581 °F | DAM | |||
Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
100 °C | 212 °F | DAM; optimum | |||
Drying Temperature | 80.0 °C | 176 °F | DAM | ||
Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
Descriptive Properties | |||||
Additive | Impact Modifier | DAM | |||
Appearance | Natural Color | DAM | |||
Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
Features | Impact Resistance, Good | DAM | |||
Warpage, Low | DAM | ||||
Filler | Mineral filler | DAM | |||
Forms | Pellets | DAM | |||
Generic | Nylon 66 | DAM | |||
Heat Stabilized | Yes | DAM | |||
Material Status | Current | DAM | |||
Part Marking Code | >PA66-IMD36< | ISO 11469; DAM | |||
Polymer Family | Polyamide | DAM | |||
Polymer Type | PA66 | DAM | |||
Processing Method | Injection Molding | DAM | |||
Product Category | Low Warp Resins | DAM | |||
Mineral Reinforced Resins | DAM | ||||
Toughened Resins | DAM | ||||
Resin Identification | PA66-IMD36 | ISO 1043; DAM | |||
RoHS Compliance | Contact Manufacturer | DAM | |||
Uses | Appliance Components | DAM | |||
Automotive Applications | DAM | ||||
Gears | DAM | ||||
Housings | DAM | ||||
Parts, Engineering | DAM | ||||
Tool, Power & Others | DAM |