  4. DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66

DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66

DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.23
  • 吸水率 [%]: 1.7
  • 成型收缩率 [%]: 0.006
  • 缺口冲击强度: 0.48
  • 弯曲模量 [MPa]: 2.76
  • 硬度: 113.0
  • 热变形温度 [℃]: 258.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.22 g/cc1.22 g/ccDAM; ASTM D792
Density 1.23 g/cc0.0444 lb/in³DAM; ISO 1183
Filler Content 13 %13 %DAM
Water Absorption  1.7 %
@Temperature 23.0 °C		1.7 %
@Temperature 73.4 °F		Immersion 24h; DAM; ISO 62, Similar to
 2.2 %
@Temperature 23.0 °C		2.2 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 7.1 %
@Temperature 23.0 °C		7.1 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 7.6 %
@Temperature 23.0 °C		7.6 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.0060 cm/cm
@Thickness 1.60 mm		0.0060 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0070 cm/cm
@Thickness 3.20 mm		0.0070 in/in
@Thickness 0.126 in		Flow; DAM
 0.0090 cm/cm
@Thickness 6.40 mm		0.0090 in/in
@Thickness 0.252 in		Flow; DAM
 0.012 cm/cm
@Thickness 1.60 mm		0.012 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.014 cm/cm
@Thickness 3.20 mm		0.014 in/in
@Thickness 0.126 in		Transverse; DAM
 0.017 cm/cm
@Thickness 6.40 mm		0.017 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.012 cm/cm
@Thickness 2.00 mm		0.012 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 848450%RH; ASTM D785
 9595DAM; ASTM D785
Hardness, Rockwell R 11311350%RH; ASTM D785
 122122DAM; ASTM D785
Tensile Strength at Break  75.0 MPa
@Temperature 23.0 °C		10900 psi
@Temperature 73.4 °F		50%RH; ISO 527
 120 MPa
@Temperature 23.0 °C		17400 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 121 MPa
@Temperature 23.0 °C		17500 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  1.60 MPa
@Strain 0.100 %,
Temperature 120 °C		232 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.00 MPa
@Strain 0.100 %,
Temperature 80.0 °C		290 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.05 MPa
@Strain 0.100 %,
Temperature 120 °C		297 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.50 MPa
@Strain 0.100 %,
Temperature 80.0 °C		363 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.50 MPa
@Strain 0.100 %,
Temperature 60.0 °C		363 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.432 MPa
@Strain 0.200 %,
Temperature 120 °C		497.8 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.50 MPa
@Strain 0.100 %,
Temperature 23.0 °C		508 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.70 MPa
@Strain 0.100 %,
Temperature 60.0 °C		537 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 3.998 MPa
@Strain 0.200 %,
Temperature 120 °C		579.9 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.00 MPa
@Strain 0.200 %,
Temperature 80.0 °C		580 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.80 MPa
@Strain 0.200 %,
Temperature 60.0 °C		696 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.104 MPa
@Strain 0.300 %,
Temperature 120 °C		740.3 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.20 MPa
@Strain 0.200 %,
Temperature 80.0 °C		754 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.50 MPa
@Strain 0.100 %,
Temperature 23.0 °C		798 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.50 MPa
@Strain 0.100 %,
Temperature 0.000 °C		798 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 5.60 MPa
@Strain 0.100 %,
Temperature 0.000 °C		812 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 5.807 MPa
@Strain 0.300 %,
Temperature 120 °C		842.2 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.92 MPa
@Strain 0.300 %,
Temperature 80.0 °C		859 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.10 MPa
@Strain 0.100 %,
Temperature -40.0 °C		885 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 6.486 MPa
@Strain 0.200 %,
Temperature 23.0 °C		940.7 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 6.50 MPa
@Strain 0.100 %,
Temperature -40.0 °C		943 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.60 MPa
@Strain 0.400 %,
Temperature 120 °C		957 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.10 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1030 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.40 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1070 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.50 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1090 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.50 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1090 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 8.092 MPa
@Strain 0.400 %,
Temperature 120 °C		1174 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.448 MPa
@Strain 0.500 %,
Temperature 120 °C		1225 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.70 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1260 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.90 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1290 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.70 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1410 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.776 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1418 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.901 MPa
@Strain 0.500 %,
Temperature 120 °C		1436 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.12 MPa
@Strain 0.600 %,
Temperature 120 °C		1468 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.15 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1472 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.2 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1620 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 11.2 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1620 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 11.413 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1655.3 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 11.64 MPa
@Strain 0.600 %,
Temperature 80.0 °C		1688 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.704 MPa
@Strain 0.700 %,
Temperature 120 °C		1697.5 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.8 MPa
@Strain 0.500 %,
Temperature 60.0 °C		1710 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.805 MPa
@Strain 0.600 %,
Temperature 120 °C		1712.2 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.1 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1750 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.4 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1800 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 12.69 MPa
@Strain 0.400 %,
Temperature 23.0 °C		1841 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 13.112 MPa
@Strain 0.800 %,
Temperature 120 °C		1901.7 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.386 MPa
@Strain 0.700 %,
Temperature 80.0 °C		1941.5 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.464 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1952.8 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 13.709 MPa
@Strain 0.700 %,
Temperature 120 °C		1988.3 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.9 MPa
@Strain 0.600 %,
Temperature 60.0 °C		2020 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.0 MPa
@Strain 0.400 %,
Temperature 60.0 °C		2030 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 14.4 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2090 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.52 MPa
@Strain 0.900 %,
Temperature 120 °C		2106 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.07 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2186 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 15.132 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2194.7 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.518 MPa
@Strain 0.800 %,
Temperature 120 °C		2250.7 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.928 MPa
@Strain 1.00 %,
Temperature 120 °C		2310.2 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.074 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2331.3 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 16.1 MPa
@Strain 0.700 %,
Temperature 60.0 °C		2340 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.6 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2410 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.8 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2440 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 16.878 MPa
@Strain 0.900 %,
Temperature 80.0 °C		2448.0 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.069 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2475.7 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 17.136 MPa
@Strain 0.900 %,
Temperature 120 °C		2485.4 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.248 MPa
@Strain 1.10 %,
Temperature 120 °C		2501.6 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.3 MPa
@Strain 0.800 %,
Temperature 60.0 °C		2650 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.392 MPa
@Strain 1.20 %,
Temperature 120 °C		2667.5 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.43 MPa
@Strain 1.00 %,
Temperature 80.0 °C		2673 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.659 MPa
@Strain 1.00 %,
Temperature 120 °C		2706.3 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.7 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2710 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.7 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2710 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2760 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.176 MPa
@Strain 0.600 %,
Temperature 23.0 °C		2781.2 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 19.62 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2846 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 19.624 MPa
@Strain 1.30 %,
Temperature 120 °C		2846.2 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.982 MPa
@Strain 1.10 %,
Temperature 80.0 °C		2898.1 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.094 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2914.4 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 20.278 MPa
@Strain 1.10 %,
Temperature 120 °C		2941.1 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.3 MPa
@Strain 0.900 %,
Temperature 60.0 °C		2940 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.8 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3020 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.856 MPa
@Strain 1.40 %,
Temperature 120 °C		3024.9 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.534 MPa
@Strain 1.20 %,
Temperature 80.0 °C		3123.2 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.6 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3130 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 21.706 MPa
@Strain 1.20 %,
Temperature 120 °C		3148.2 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.912 MPa
@Strain 1.50 %,
Temperature 120 °C		3178.1 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.0 MPa
@Strain 1.00 %,
Temperature 60.0 °C		3190 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.09 MPa
@Strain 0.700 %,
Temperature 23.0 °C		3204 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.422 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3252.0 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 22.5 MPa
@Strain 0.600 %,
Temperature 60.0 °C		3260 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.7 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3290 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.88 MPa
@Strain 1.60 %,
Temperature 120 °C		3318 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.086 MPa
@Strain 1.30 %,
Temperature 80.0 °C		3348.3 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.134 MPa
@Strain 1.30 %,
Temperature 120 °C		3355.3 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.8 MPa
@Strain 1.10 %,
Temperature 60.0 °C		3450 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.024 MPa
@Strain 1.70 %,
Temperature 120 °C		3484.4 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.347 MPa
@Strain 1.40 %,
Temperature 80.0 °C		3531.2 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.4 MPa
@Strain 1.10 %,
Temperature 80.0 °C		3540 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.4 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3540 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 24.466 MPa
@Strain 1.40 %,
Temperature 120 °C		3548.5 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.91 MPa
@Strain 0.800 %,
Temperature 23.0 °C		3613 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.09 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3639 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 25.168 MPa
@Strain 1.80 %,
Temperature 120 °C		3650.3 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.6 MPa
@Strain 1.20 %,
Temperature 60.0 °C		3710 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.705 MPa
@Strain 1.50 %,
Temperature 80.0 °C		3728.2 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.799 MPa
@Strain 1.50 %,
Temperature 120 °C		3741.8 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.8 MPa
@Strain 0.700 %,
Temperature 60.0 °C		3740 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.136 MPa
@Strain 1.90 %,
Temperature 120 °C		3790.7 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.2 MPa
@Strain 1.20 %,
Temperature 80.0 °C		3800 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.214 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3802.0 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 27.063 MPa
@Strain 1.60 %,
Temperature 80.0 °C		3925.2 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.104 MPa
@Strain 2.00 %,
Temperature 120 °C		3931.1 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.132 MPa
@Strain 1.60 %,
Temperature 120 °C		3935.2 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.2 MPa
@Strain 1.30 %,
Temperature 60.0 °C		3950 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.636 MPa
@Strain 0.900 %,
Temperature 23.0 °C		4008.3 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.984 MPa
@Strain 2.10 %,
Temperature 120 °C		4058.7 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.0 MPa
@Strain 1.30 %,
Temperature 80.0 °C		4060 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.078 MPa
@Strain 0.500 %,
Temperature 0.000 °C		4072.4 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 28.1 MPa
@Strain 0.500 %,
Temperature 0.000 °C		4080 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 28.227 MPa
@Strain 1.70 %,
Temperature 80.0 °C		4094.0 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.274 MPa
@Strain 1.70 %,
Temperature 120 °C		4100.8 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.9 MPa
@Strain 1.40 %,
Temperature 60.0 °C		4190 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.952 MPa
@Strain 2.20 %,
Temperature 120 °C		4199.1 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.2 MPa
@Strain 0.800 %,
Temperature 60.0 °C		4240 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.585 MPa
@Strain 1.80 %,
Temperature 80.0 °C		4290.9 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.607 MPa
@Strain 1.80 %,
Temperature 120 °C		4294.1 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.7 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4310 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.744 MPa
@Strain 2.30 %,
Temperature 120 °C		4314.0 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.0 MPa
@Strain 0.600 %,
Temperature 23.0 °C		4350 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.174 MPa
@Strain 1.00 %,
Temperature 23.0 °C		4376.4 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.5 MPa
@Strain 1.50 %,
Temperature 60.0 °C		4420 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.536 MPa
@Strain 2.40 %,
Temperature 120 °C		4428.9 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.749 MPa
@Strain 1.90 %,
Temperature 80.0 °C		4459.8 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.75 MPa
@Strain 1.90 %,
Temperature 120 °C		4460 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.3 MPa
@Strain 1.50 %,
Temperature 80.0 °C		4540 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.328 MPa
@Strain 2.50 %,
Temperature 120 °C		4543.8 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 31.4 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4550 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 31.892 MPa
@Strain 2.00 %,
Temperature 120 °C		4625.6 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.913 MPa
@Strain 2.00 %,
Temperature 80.0 °C		4628.6 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.1 MPa
@Strain 1.60 %,
Temperature 60.0 °C		4660 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.208 MPa
@Strain 2.60 %,
Temperature 120 °C		4671.4 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.4 MPa
@Strain 0.900 %,
Temperature 60.0 °C		4700 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.43 MPa
@Strain 1.10 %,
Temperature 23.0 °C		4704 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.8 MPa
@Strain 1.60 %,
Temperature 80.0 °C		4760 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.844 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4763.6 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.912 MPa
@Strain 2.70 %,
Temperature 120 °C		4773.5 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.939 MPa
@Strain 2.10 %,
Temperature 120 °C		4777.4 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.077 MPa
@Strain 2.10 %,
Temperature 80.0 °C		4797.4 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.1 MPa
@Strain 0.600 %,
Temperature 0.000 °C		4800 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.6 MPa
@Strain 1.70 %,
Temperature 60.0 °C		4870 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.616 MPa
@Strain 2.80 %,
Temperature 120 °C		4875.6 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.835 MPa
@Strain 0.600 %,
Temperature 0.000 °C		4907.4 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.082 MPa
@Strain 2.20 %,
Temperature 120 °C		4943.2 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.144 MPa
@Strain 2.20 %,
Temperature 80.0 °C		4952.2 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.2 MPa
@Strain 1.70 %,
Temperature 80.0 °C		4960 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.232 MPa
@Strain 2.90 %,
Temperature 120 °C		4964.9 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.686 MPa
@Strain 1.20 %,
Temperature 23.0 °C		5030.8 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 34.848 MPa
@Strain 3.00 %,
Temperature 120 °C		5054.3 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.87 MPa
@Strain 0.700 %,
Temperature 23.0 °C		5057 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 35.0 MPa
@Strain 1.80 %,
Temperature 60.0 °C		5080 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.211 MPa
@Strain 2.30 %,
Temperature 80.0 °C		5106.9 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.224 MPa
@Strain 2.30 %,
Temperature 120 °C		5108.8 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.4 MPa
@Strain 1.00 %,
Temperature 60.0 °C		5130 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.464 MPa
@Strain 3.10 %,
Temperature 120 °C		5143.6 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.8 MPa
@Strain 1.80 %,
Temperature 80.0 °C		5190 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.904 MPa
@Strain 3.20 %,
Temperature 120 °C		5207.4 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.084 MPa
@Strain 2.40 %,
Temperature 80.0 °C		5233.6 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.176 MPa
@Strain 2.40 %,
Temperature 120 °C		5246.9 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.3 MPa
@Strain 1.90 %,
Temperature 60.0 °C		5260 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.432 MPa
@Strain 3.30 %,
Temperature 120 °C		5284.0 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.872 MPa
@Strain 3.40 %,
Temperature 120 °C		5347.8 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.942 MPa
@Strain 1.30 %,
Temperature 23.0 °C		5358.0 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.054 MPa
@Strain 2.50 %,
Temperature 80.0 °C		5374.2 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.128 MPa
@Strain 2.50 %,
Temperature 120 °C		5385.0 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.2 MPa
@Strain 1.90 %,
Temperature 80.0 °C		5400 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.312 MPa
@Strain 3.50 %,
Temperature 120 °C		5411.7 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.6 MPa
@Strain 0.600 %,
Temperature -40.0 °C		5450 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 37.664 MPa
@Strain 3.60 %,
Temperature 120 °C		5462.7 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.8 MPa
@Strain 2.00 %,
Temperature 60.0 °C		5480 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.024 MPa
@Strain 2.60 %,
Temperature 80.0 °C		5514.9 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.08 MPa
@Strain 2.60 %,
Temperature 120 °C		5523 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.104 MPa
@Strain 3.70 %,
Temperature 120 °C		5526.5 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.2 MPa
@Strain 0.700 %,
Temperature 0.000 °C		5540 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 38.3 MPa
@Strain 1.10 %,
Temperature 60.0 °C		5550 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.456 MPa
@Strain 3.80 %,
Temperature 120 °C		5577.6 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.6 MPa
@Strain 2.00 %,
Temperature 80.0 °C		5600 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.632 MPa
@Strain 3.90 %,
Temperature 120 °C		5603.1 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.897 MPa
@Strain 2.70 %,
Temperature 80.0 °C		5641.5 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.984 MPa
@Strain 4.00 %,
Temperature 120 °C		5654.2 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.01 MPa
@Strain 1.40 %,
Temperature 23.0 °C		5658 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.032 MPa
@Strain 2.70 %,
Temperature 120 °C		5661.1 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.1 MPa
@Strain 2.10 %,
Temperature 60.0 °C		5670 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.168 MPa
@Strain 0.600 %,
Temperature -40.0 °C		5680.8 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 39.248 MPa
@Strain 4.10 %,
Temperature 120 °C		5692.5 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.491 MPa
@Strain 0.700 %,
Temperature 0.000 °C		5727.7 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 39.512 MPa
@Strain 4.20 %,
Temperature 120 °C		5730.7 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.58 MPa
@Strain 0.800 %,
Temperature 23.0 °C		5741 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 39.77 MPa
@Strain 2.80 %,
Temperature 80.0 °C		5768 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 39.776 MPa
@Strain 4.30 %,
Temperature 120 °C		5769.0 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.952 MPa
@Strain 4.40 %,
Temperature 120 °C		5794.6 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.984 MPa
@Strain 2.80 %,
Temperature 120 °C		5799.2 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.0 MPa
@Strain 2.10 %,
Temperature 80.0 °C		5800 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.128 MPa
@Strain 4.50 %,
Temperature 120 °C		5820.1 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 2.20 %,
Temperature 60.0 °C		5850 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.304 MPa
@Strain 4.60 %,
Temperature 120 °C		5845.6 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.48 MPa
@Strain 4.70 %,
Temperature 120 °C		5871 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.546 MPa
@Strain 2.90 %,
Temperature 80.0 °C		5880.7 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 40.656 MPa
@Strain 4.80 %,
Temperature 120 °C		5896.7 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.746 MPa
@Strain 2.90 %,
Temperature 120 °C		5909.7 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.832 MPa
@Strain 4.90 %,
Temperature 120 °C		5922.2 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.92 MPa
@Strain 5.00 %,
Temperature 120 °C		5935 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.1 MPa
@Strain 1.20 %,
Temperature 60.0 °C		5960 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.172 MPa
@Strain 1.50 %,
Temperature 23.0 °C		5971.5 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.225 MPa
@Strain 3.00 %,
Temperature 80.0 °C		5979.2 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 41.3 MPa
@Strain 2.20 %,
Temperature 80.0 °C		5990 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.36 MPa
@Strain 5.50 %,
Temperature 120 °C		5999 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.5 MPa
@Strain 2.30 %,
Temperature 60.0 °C		6020 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.602 MPa
@Strain 3.00 %,
Temperature 120 °C		6033.9 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.8 MPa
@Strain 10.0 %,
Temperature 120 °C		6060 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.8 MPa
@Strain 6.00 %,
Temperature 120 °C		6060 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.904 MPa
@Strain 3.10 %,
Temperature 80.0 °C		6077.7 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.064 MPa
@Strain 6.50 %,
Temperature 120 °C		6100.9 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.064 MPa
@Strain 9.50 %,
Temperature 120 °C		6100.9 psi
@Strain 9.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.152 MPa
@Strain 9.00 %,
Temperature 120 °C		6113.6 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.24 MPa
@Strain 8.50 %,
Temperature 120 °C		6126 psi
@Strain 8.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.24 MPa
@Strain 7.00 %,
Temperature 120 °C		6126 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.328 MPa
@Strain 7.50 %,
Temperature 120 °C		6139.2 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.328 MPa
@Strain 8.00 %,
Temperature 120 °C		6139.2 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.459 MPa
@Strain 3.10 %,
Temperature 120 °C		6158.2 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.583 MPa
@Strain 3.20 %,
Temperature 80.0 °C		6176.2 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.6 MPa
@Strain 2.40 %,
Temperature 60.0 °C		6180 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 42.7 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6190 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.126 MPa
@Strain 3.20 %,
Temperature 120 °C		6254.9 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.146 MPa
@Strain 1.60 %,
Temperature 23.0 °C		6257.8 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.262 MPa
@Strain 3.30 %,
Temperature 80.0 °C		6274.6 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.3 MPa
@Strain 0.800 %,
Temperature 0.000 °C		6280 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 43.7 MPa
@Strain 2.50 %,
Temperature 60.0 °C		6340 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 43.747 MPa
@Strain 3.40 %,
Temperature 80.0 °C		6345.0 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.8 MPa
@Strain 0.700 %,
Temperature -40.0 °C		6350 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.8 MPa
@Strain 1.30 %,
Temperature 60.0 °C		6350 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.887 MPa
@Strain 3.30 %,
Temperature 120 °C		6365.3 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.9 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6370 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.232 MPa
@Strain 3.50 %,
Temperature 80.0 °C		6415.3 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 0.900 %,
Temperature 23.0 °C		6430 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.554 MPa
@Strain 3.40 %,
Temperature 120 °C		6462.0 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.717 MPa
@Strain 3.60 %,
Temperature 80.0 °C		6485.7 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.8 MPa
@Strain 2.60 %,
Temperature 60.0 °C		6500 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 44.945 MPa
@Strain 0.800 %,
Temperature 0.000 °C		6518.7 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 45.026 MPa
@Strain 1.70 %,
Temperature 23.0 °C		6530.5 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.1 MPa
@Strain 2.50 %,
Temperature 80.0 °C		6540 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.186 MPa
@Strain 0.700 %,
Temperature -40.0 °C		6553.7 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 45.202 MPa
@Strain 3.70 %,
Temperature 80.0 °C		6556.0 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.22 MPa
@Strain 3.50 %,
Temperature 120 °C		6559 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.59 MPa
@Strain 3.80 %,
Temperature 80.0 °C		6612 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.8 MPa
@Strain 2.70 %,
Temperature 60.0 °C		6640 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 45.886 MPa
@Strain 3.60 %,
Temperature 120 °C		6655.2 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.978 MPa
@Strain 3.90 %,
Temperature 80.0 °C		6668.6 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.2 MPa
@Strain 1.40 %,
Temperature 60.0 °C		6700 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.3 MPa
@Strain 2.60 %,
Temperature 80.0 °C		6720 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.362 MPa
@Strain 3.70 %,
Temperature 120 °C		6724.3 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.366 MPa
@Strain 4.00 %,
Temperature 80.0 °C		6724.8 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.657 MPa
@Strain 4.10 %,
Temperature 80.0 °C		6767.0 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.718 MPa
@Strain 1.80 %,
Temperature 23.0 °C		6775.9 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.8 MPa
@Strain 2.80 %,
Temperature 60.0 °C		6790 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 46.934 MPa
@Strain 3.80 %,
Temperature 120 °C		6807.2 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.948 MPa
@Strain 4.20 %,
Temperature 80.0 °C		6809.2 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.239 MPa
@Strain 4.30 %,
Temperature 80.0 °C		6851.4 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.41 MPa
@Strain 3.90 %,
Temperature 120 °C		6876 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.5 MPa
@Strain 2.70 %,
Temperature 80.0 °C		6890 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 47.53 MPa
@Strain 4.40 %,
Temperature 80.0 °C		6894 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.8 MPa
@Strain 2.90 %,
Temperature 60.0 °C		6930 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.821 MPa
@Strain 4.50 %,
Temperature 80.0 °C		6935.9 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.886 MPa
@Strain 4.00 %,
Temperature 120 °C		6945.3 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.918 MPa
@Strain 4.60 %,
Temperature 80.0 °C		6949.9 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.209 MPa
@Strain 4.70 %,
Temperature 80.0 °C		6992.1 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.3 MPa
@Strain 0.900 %,
Temperature 0.000 °C		7010 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.362 MPa
@Strain 4.10 %,
Temperature 120 °C		7014.3 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.403 MPa
@Strain 4.80 %,
Temperature 80.0 °C		7020.3 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 4.90 %,
Temperature 80.0 °C		7030 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 1.50 %,
Temperature 60.0 °C		7030 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.504 MPa
@Strain 1.90 %,
Temperature 23.0 °C		7034.9 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.6 MPa
@Strain 3.00 %,
Temperature 60.0 °C		7050 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.694 MPa
@Strain 5.00 %,
Temperature 80.0 °C		7062.5 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.8 MPa
@Strain 2.80 %,
Temperature 80.0 °C		7080 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 48.838 MPa
@Strain 4.20 %,
Temperature 120 °C		7083.4 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.01 MPa
@Strain 1.00 %,
Temperature 23.0 °C		7108 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.218 MPa
@Strain 4.30 %,
Temperature 120 °C		7138.5 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.28 MPa
@Strain 5.50 %,
Temperature 80.0 °C		7147 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 3.10 %,
Temperature 60.0 °C		7180 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.504 MPa
@Strain 4.40 %,
Temperature 120 °C		7180.0 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.79 MPa
@Strain 4.50 %,
Temperature 120 °C		7221 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.9 MPa
@Strain 2.90 %,
Temperature 80.0 °C		7240 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 49.9 MPa
@Strain 0.800 %,
Temperature -40.0 °C		7240 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 50.0 MPa
@Strain 6.00 %,
Temperature 80.0 °C		7250 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.17 MPa
@Strain 4.60 %,
Temperature 120 °C		7277 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.29 MPa
@Strain 2.00 %,
Temperature 23.0 °C		7294 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.3 MPa
@Strain 6.50 %,
Temperature 80.0 °C		7300 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.3 MPa
@Strain 3.20 %,
Temperature 60.0 °C		7300 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.456 MPa
@Strain 4.70 %,
Temperature 120 °C		7318.0 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.5 MPa
@Strain 12.0 %,
Temperature 80.0 °C		7320 psi
@Strain 12.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.601 MPa
@Strain 0.900 %,
Temperature 0.000 °C		7339.1 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.7 MPa
@Strain 7.00 %,
Temperature 80.0 °C		7350 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.742 MPa
@Strain 4.80 %,
Temperature 120 °C		7359.5 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.8 MPa
@Strain 11.0 %,
Temperature 80.0 °C		7370 psi
@Strain 11.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.9 MPa
@Strain 7.50 %,
Temperature 80.0 °C		7380 psi
@Strain 7.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.932 MPa
@Strain 4.90 %,
Temperature 120 °C		7387.1 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.0 MPa
@Strain 8.00 %,
Temperature 80.0 °C		7400 psi
@Strain 8.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.0 MPa
@Strain 10.0 %,
Temperature 80.0 °C		7400 psi
@Strain 10.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.0 MPa
@Strain 1.60 %,
Temperature 60.0 °C		7400 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.1 MPa
@Strain 8.50 %,
Temperature 80.0 °C		7410 psi
@Strain 8.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 9.00 %,
Temperature 80.0 °C		7410 psi
@Strain 9.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 9.50 %,
Temperature 80.0 °C		7410 psi
@Strain 9.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 3.30 %,
Temperature 60.0 °C		7410 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 3.00 %,
Temperature 80.0 °C		7410 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 51.218 MPa
@Strain 5.00 %,
Temperature 120 °C		7428.6 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.306 MPa
@Strain 0.800 %,
Temperature -40.0 °C		7441.3 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 51.8 MPa
@Strain 3.40 %,
Temperature 60.0 °C		7510 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.979 MPa
@Strain 5.50 %,
Temperature 120 °C		7538.9 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.982 MPa
@Strain 2.10 %,
Temperature 23.0 °C		7539.4 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.1 MPa
@Strain 3.10 %,
Temperature 80.0 °C		7560 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.5 MPa
@Strain 3.50 %,
Temperature 60.0 °C		7610 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.931 MPa
@Strain 6.00 %,
Temperature 120 °C		7677.0 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.0 MPa
@Strain 3.60 %,
Temperature 60.0 °C		7690 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.1 MPa
@Strain 3.20 %,
Temperature 80.0 °C		7700 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.2 MPa
@Strain 1.70 %,
Temperature 60.0 °C		7720 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.2 MPa
@Strain 1.00 %,
Temperature 0.000 °C		7720 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 53.47 MPa
@Strain 1.10 %,
Temperature 23.0 °C		7755 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 53.486 MPa
@Strain 2.20 %,
Temperature 23.0 °C		7757.5 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.5 MPa
@Strain 3.70 %,
Temperature 60.0 °C		7760 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.598 MPa
@Strain 6.50 %,
Temperature 120 °C		7773.7 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.978 MPa
@Strain 7.00 %,
Temperature 120 °C		7828.9 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.0 MPa
@Strain 3.80 %,
Temperature 60.0 °C		7830 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 3.30 %,
Temperature 80.0 °C		7860 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.359 MPa
@Strain 7.50 %,
Temperature 120 °C		7884.1 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.4 MPa
@Strain 3.90 %,
Temperature 60.0 °C		7890 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.645 MPa
@Strain 8.00 %,
Temperature 120 °C		7925.6 psi
@Strain 8.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.8 MPa
@Strain 4.00 %,
Temperature 60.0 °C		7950 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.835 MPa
@Strain 12.0 %,
Temperature 120 °C		7953.2 psi
@Strain 12.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.835 MPa
@Strain 8.50 %,
Temperature 120 °C		7953.2 psi
@Strain 8.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.93 MPa
@Strain 9.00 %,
Temperature 120 °C		7967 psi
@Strain 9.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.99 MPa
@Strain 2.30 %,
Temperature 23.0 °C		7976 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.026 MPa
@Strain 9.50 %,
Temperature 120 °C		7980.9 psi
@Strain 9.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.026 MPa
@Strain 10.0 %,
Temperature 120 °C		7980.9 psi
@Strain 10.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.026 MPa
@Strain 11.0 %,
Temperature 120 °C		7980.9 psi
@Strain 11.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.1 MPa
@Strain 1.80 %,
Temperature 60.0 °C		7990 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 55.2 MPa
@Strain 4.10 %,
Temperature 60.0 °C		8010 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.2 MPa
@Strain 3.40 %,
Temperature 80.0 °C		8010 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.5 MPa
@Strain 4.20 %,
Temperature 60.0 °C		8050 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.8 MPa
@Strain 4.30 %,
Temperature 60.0 °C		8090 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.8 MPa
@Strain 0.900 %,
Temperature -40.0 °C		8090 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 56.0 MPa
@Strain 4.40 %,
Temperature 60.0 °C		8120 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.156 MPa
@Strain 1.00 %,
Temperature 0.000 °C		8144.8 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 56.2 MPa
@Strain 3.50 %,
Temperature 80.0 °C		8150 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.3 MPa
@Strain 4.50 %,
Temperature 60.0 °C		8170 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.494 MPa
@Strain 2.40 %,
Temperature 23.0 °C		8193.8 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 56.5 MPa
@Strain 4.60 %,
Temperature 60.0 °C		8190 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.8 MPa
@Strain 4.70 %,
Temperature 60.0 °C		8240 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.0 MPa
@Strain 4.80 %,
Temperature 60.0 °C		8270 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.1 MPa
@Strain 4.90 %,
Temperature 60.0 °C		8280 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.1 MPa
@Strain 1.90 %,
Temperature 60.0 °C		8280 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 57.2 MPa
@Strain 3.60 %,
Temperature 80.0 °C		8300 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.4 MPa
@Strain 5.00 %,
Temperature 60.0 °C		8330 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.426 MPa
@Strain 0.900 %,
Temperature -40.0 °C		8329.0 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 57.7 MPa
@Strain 1.10 %,
Temperature 0.000 °C		8370 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.7 MPa
@Strain 14.0 %,
Temperature 60.0 °C		8370 psi
@Strain 14.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.9 MPa
@Strain 5.50 %,
Temperature 60.0 °C		8400 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.904 MPa
@Strain 2.50 %,
Temperature 23.0 °C		8398.3 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.02 MPa
@Strain 1.20 %,
Temperature 23.0 °C		8415 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.1 MPa
@Strain 3.70 %,
Temperature 80.0 °C		8430 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 58.5 MPa
@Strain 6.00 %,
Temperature 60.0 °C		8480 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 58.5 MPa
@Strain 13.0 %,
Temperature 60.0 °C		8480 psi
@Strain 13.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 58.9 MPa
@Strain 2.00 %,
Temperature 60.0 °C		8540 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 58.9 MPa
@Strain 3.80 %,
Temperature 80.0 °C		8540 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.0 MPa
@Strain 6.50 %,
Temperature 60.0 °C		8560 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.0 MPa
@Strain 12.0 %,
Temperature 60.0 °C		8560 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.3 MPa
@Strain 7.00 %,
Temperature 60.0 °C		8600 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.3 MPa
@Strain 11.0 %,
Temperature 60.0 °C		8600 psi
@Strain 11.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.314 MPa
@Strain 2.60 %,
Temperature 23.0 °C		8602.8 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.4 MPa
@Strain 7.50 %,
Temperature 60.0 °C		8620 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.5 MPa
@Strain 8.00 %,
Temperature 60.0 °C		8630 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.5 MPa
@Strain 10.0 %,
Temperature 60.0 °C		8630 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.6 MPa
@Strain 9.50 %,
Temperature 60.0 °C		8640 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.6 MPa
@Strain 8.50 %,
Temperature 60.0 °C		8640 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.7 MPa
@Strain 9.00 %,
Temperature 60.0 °C		8660 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.7 MPa
@Strain 3.90 %,
Temperature 80.0 °C		8660 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.5 MPa
@Strain 4.00 %,
Temperature 80.0 °C		8770 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.536 MPa
@Strain 2.70 %,
Temperature 23.0 °C		8780.0 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 60.6 MPa
@Strain 2.10 %,
Temperature 60.0 °C		8790 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 61.0 MPa
@Strain 4.10 %,
Temperature 80.0 °C		8850 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.61 MPa
@Strain 1.10 %,
Temperature 0.000 °C		8936 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 61.7 MPa
@Strain 4.20 %,
Temperature 80.0 °C		8950 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.9 MPa
@Strain 1.00 %,
Temperature -40.0 °C		8980 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 61.946 MPa
@Strain 2.80 %,
Temperature 23.0 °C		8984.5 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.0 MPa
@Strain 1.20 %,
Temperature 0.000 °C		8990 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.3 MPa
@Strain 4.30 %,
Temperature 80.0 °C		9040 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.34 MPa
@Strain 1.30 %,
Temperature 23.0 °C		9042 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.5 MPa
@Strain 2.20 %,
Temperature 60.0 °C		9060 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 62.9 MPa
@Strain 4.40 %,
Temperature 80.0 °C		9120 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.24 MPa
@Strain 1.00 %,
Temperature -40.0 °C		9172 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 63.262 MPa
@Strain 2.90 %,
Temperature 23.0 °C		9175.4 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.4 MPa
@Strain 4.50 %,
Temperature 80.0 °C		9200 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.9 MPa
@Strain 4.60 %,
Temperature 80.0 °C		9270 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.2 MPa
@Strain 2.30 %,
Temperature 60.0 °C		9310 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.39 MPa
@Strain 3.00 %,
Temperature 23.0 °C		9339 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 64.4 MPa
@Strain 4.70 %,
Temperature 80.0 °C		9340 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.7 MPa
@Strain 4.80 %,
Temperature 80.0 °C		9380 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.0 MPa
@Strain 4.90 %,
Temperature 80.0 °C		9430 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.5 MPa
@Strain 5.00 %,
Temperature 80.0 °C		9500 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.612 MPa
@Strain 3.10 %,
Temperature 23.0 °C		9516.2 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 65.8 MPa
@Strain 2.40 %,
Temperature 60.0 °C		9540 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.2 MPa
@Strain 1.30 %,
Temperature 0.000 °C		9600 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.7 MPa
@Strain 5.50 %,
Temperature 80.0 °C		9670 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.74 MPa
@Strain 3.20 %,
Temperature 23.0 °C		9680 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 66.76 MPa
@Strain 1.40 %,
Temperature 23.0 °C		9683 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.761 MPa
@Strain 1.20 %,
Temperature 0.000 °C		9682.9 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 67.1 MPa
@Strain 2.50 %,
Temperature 60.0 °C		9730 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.68 MPa
@Strain 3.30 %,
Temperature 23.0 °C		9816 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 67.8 MPa
@Strain 1.10 %,
Temperature -40.0 °C		9830 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 67.8 MPa
@Strain 6.00 %,
Temperature 80.0 °C		9830 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 68.4 MPa
@Strain 6.50 %,
Temperature 80.0 °C		9920 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 68.5 MPa
@Strain 2.60 %,
Temperature 60.0 °C		9940 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 68.62 MPa
@Strain 3.40 %,
Temperature 23.0 °C		9953 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.952 MPa
@Strain 1.10 %,
Temperature -40.0 °C		10001 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 69.0 MPa
@Strain 7.00 %,
Temperature 80.0 °C		10000 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.5 MPa
@Strain 7.50 %,
Temperature 80.0 °C		10100 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.56 MPa
@Strain 3.50 %,
Temperature 23.0 °C		10090 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 69.8 MPa
@Strain 8.00 %,
Temperature 80.0 °C		10100 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.0 MPa
@Strain 2.70 %,
Temperature 60.0 °C		10200 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 70.1 MPa
@Strain 8.50 %,
Temperature 80.0 °C		10200 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.2 MPa
@Strain 1.40 %,
Temperature 0.000 °C		10200 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.4 MPa
@Strain 9.00 %,
Temperature 80.0 °C		10200 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.4 MPa
@Strain 15.0 %,
Temperature 80.0 °C		10200 psi
@Strain 15.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.5 MPa
@Strain 14.0 %,
Temperature 80.0 °C		10200 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.5 MPa
@Strain 9.50 %,
Temperature 80.0 °C		10200 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.5 MPa
@Strain 3.60 %,
Temperature 23.0 °C		10200 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 70.6 MPa
@Strain 10.0 %,
Temperature 80.0 °C		10200 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.6 MPa
@Strain 13.0 %,
Temperature 80.0 °C		10200 psi
@Strain 13.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.65 MPa
@Strain 11.0 %,
Temperature 80.0 °C		10250 psi
@Strain 11.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.7 MPa
@Strain 12.0 %,
Temperature 80.0 °C		10300 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 71.04 MPa
@Strain 1.50 %,
Temperature 23.0 °C		10300 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 71.158 MPa
@Strain 3.70 %,
Temperature 23.0 °C		10321 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.2 MPa
@Strain 2.80 %,
Temperature 60.0 °C		10300 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 71.91 MPa
@Strain 3.80 %,
Temperature 23.0 °C		10430 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.013 MPa
@Strain 1.30 %,
Temperature 0.000 °C		10445 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 72.4 MPa
@Strain 2.90 %,
Temperature 60.0 °C		10500 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 72.568 MPa
@Strain 3.90 %,
Temperature 23.0 °C		10525 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.944 MPa
@Strain 4.00 %,
Temperature 23.0 °C		10580 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.2 MPa
@Strain 1.20 %,
Temperature -40.0 °C		10600 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 73.226 MPa
@Strain 13.0 %,
Temperature 23.0 °C		10621 psi
@Strain 13.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.5 MPa
@Strain 3.00 %,
Temperature 60.0 °C		10700 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 73.508 MPa
@Strain 4.10 %,
Temperature 23.0 °C		10661 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.8 MPa
@Strain 1.50 %,
Temperature 0.000 °C		10700 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.884 MPa
@Strain 4.20 %,
Temperature 23.0 °C		10716 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.072 MPa
@Strain 12.0 %,
Temperature 23.0 °C		10743 psi
@Strain 12.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.26 MPa
@Strain 4.30 %,
Temperature 23.0 °C		10770 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.6 MPa
@Strain 3.10 %,
Temperature 60.0 °C		10800 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 74.636 MPa
@Strain 4.40 %,
Temperature 23.0 °C		10825 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.73 MPa
@Strain 4.50 %,
Temperature 23.0 °C		10840 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.73 MPa
@Strain 11.0 %,
Temperature 23.0 °C		10840 psi
@Strain 11.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.766 MPa
@Strain 1.20 %,
Temperature -40.0 °C		10844 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 75.012 MPa
@Strain 4.60 %,
Temperature 23.0 °C		10880 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.106 MPa
@Strain 4.70 %,
Temperature 23.0 °C		10893 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.27 MPa
@Strain 1.60 %,
Temperature 23.0 °C		10920 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.294 MPa
@Strain 4.80 %,
Temperature 23.0 °C		10920 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.294 MPa
@Strain 10.0 %,
Temperature 23.0 °C		10920 psi
@Strain 10.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.482 MPa
@Strain 9.50 %,
Temperature 23.0 °C		10948 psi
@Strain 9.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.482 MPa
@Strain 4.90 %,
Temperature 23.0 °C		10948 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.576 MPa
@Strain 5.00 %,
Temperature 23.0 °C		10961 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.6 MPa
@Strain 3.20 %,
Temperature 60.0 °C		11000 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.764 MPa
@Strain 9.00 %,
Temperature 23.0 °C		10989 psi
@Strain 9.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.858 MPa
@Strain 8.50 %,
Temperature 23.0 °C		11002 psi
@Strain 8.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.952 MPa
@Strain 5.50 %,
Temperature 23.0 °C		11016 psi
@Strain 5.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.046 MPa
@Strain 8.00 %,
Temperature 23.0 °C		11030 psi
@Strain 8.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.14 MPa
@Strain 6.00 %,
Temperature 23.0 °C		11040 psi
@Strain 6.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.14 MPa
@Strain 7.50 %,
Temperature 23.0 °C		11040 psi
@Strain 7.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.234 MPa
@Strain 6.50 %,
Temperature 23.0 °C		11057 psi
@Strain 6.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.234 MPa
@Strain 7.00 %,
Temperature 23.0 °C		11057 psi
@Strain 7.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.6 MPa
@Strain 3.30 %,
Temperature 60.0 °C		11100 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.962 MPa
@Strain 1.40 %,
Temperature 0.000 °C		11162 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.2 MPa
@Strain 1.60 %,
Temperature 0.000 °C		11200 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.5 MPa
@Strain 3.40 %,
Temperature 60.0 °C		11200 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 3.50 %,
Temperature 60.0 °C		11400 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 1.30 %,
Temperature -40.0 °C		11400 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 79.2 MPa
@Strain 3.60 %,
Temperature 60.0 °C		11500 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 79.3 MPa
@Strain 1.70 %,
Temperature 23.0 °C		11500 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.8 MPa
@Strain 3.70 %,
Temperature 60.0 °C		11600 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 80.07 MPa
@Strain 1.30 %,
Temperature -40.0 °C		11610 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.5 MPa
@Strain 3.80 %,
Temperature 60.0 °C		11700 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 80.6 MPa
@Strain 1.70 %,
Temperature 0.000 °C		11700 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 81.1 MPa
@Strain 3.90 %,
Temperature 60.0 °C		11800 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 81.6 MPa
@Strain 4.00 %,
Temperature 60.0 °C		11800 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 81.709 MPa
@Strain 1.50 %,
Temperature 0.000 °C		11851 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 82.0 MPa
@Strain 4.10 %,
Temperature 60.0 °C		11900 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.3 MPa
@Strain 4.20 %,
Temperature 60.0 °C		11900 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.4 MPa
@Strain 13.0 %,
Temperature 60.0 °C		12000 psi
@Strain 13.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.7 MPa
@Strain 4.30 %,
Temperature 60.0 °C		12000 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.8 MPa
@Strain 12.0 %,
Temperature 60.0 °C		12000 psi
@Strain 12.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.9 MPa
@Strain 4.40 %,
Temperature 60.0 °C		12000 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.1 MPa
@Strain 4.50 %,
Temperature 60.0 °C		12100 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.17 MPa
@Strain 1.80 %,
Temperature 23.0 °C		12060 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 11.0 %,
Temperature 60.0 °C		12100 psi
@Strain 11.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.3 MPa
@Strain 4.60 %,
Temperature 60.0 °C		12100 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.4 MPa
@Strain 4.70 %,
Temperature 60.0 °C		12100 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.5 MPa
@Strain 10.0 %,
Temperature 60.0 °C		12100 psi
@Strain 10.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.5 MPa
@Strain 1.40 %,
Temperature -40.0 °C		12100 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 83.6 MPa
@Strain 1.80 %,
Temperature 0.000 °C		12100 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 83.6 MPa
@Strain 4.80 %,
Temperature 60.0 °C		12100 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.7 MPa
@Strain 4.90 %,
Temperature 60.0 °C		12100 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.7 MPa
@Strain 9.00 %,
Temperature 60.0 °C		12100 psi
@Strain 9.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.7 MPa
@Strain 9.50 %,
Temperature 60.0 °C		12100 psi
@Strain 9.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.8 MPa
@Strain 5.00 %,
Temperature 60.0 °C		12200 psi
@Strain 5.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.9 MPa
@Strain 5.50 %,
Temperature 60.0 °C		12200 psi
@Strain 5.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.9 MPa
@Strain 8.50 %,
Temperature 60.0 °C		12200 psi
@Strain 8.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.0 MPa
@Strain 7.00 %,
Temperature 60.0 °C		12200 psi
@Strain 7.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.0 MPa
@Strain 7.50 %,
Temperature 60.0 °C		12200 psi
@Strain 7.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.0 MPa
@Strain 8.00 %,
Temperature 60.0 °C		12200 psi
@Strain 8.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.1 MPa
@Strain 6.00 %,
Temperature 60.0 °C		12200 psi
@Strain 6.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.1 MPa
@Strain 6.50 %,
Temperature 60.0 °C		12200 psi
@Strain 6.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 85.374 MPa
@Strain 1.40 %,
Temperature -40.0 °C		12382 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 86.3 MPa
@Strain 1.90 %,
Temperature 0.000 °C		12500 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 86.456 MPa
@Strain 1.60 %,
Temperature 0.000 °C		12539 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.01 MPa
@Strain 1.90 %,
Temperature 23.0 °C		12620 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 88.6 MPa
@Strain 1.50 %,
Temperature -40.0 °C		12900 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 89.0 MPa
@Strain 2.00 %,
Temperature 0.000 °C		12900 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 90.56 MPa
@Strain 2.00 %,
Temperature 23.0 °C		13130 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.576 MPa
@Strain 1.50 %,
Temperature -40.0 °C		13137 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.102 MPa
@Strain 1.70 %,
Temperature 0.000 °C		13213 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.5 MPa
@Strain 2.10 %,
Temperature 0.000 °C		13300 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 93.6 MPa
@Strain 1.60 %,
Temperature -40.0 °C		13600 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.9 MPa
@Strain 2.20 %,
Temperature 0.000 °C		13600 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 94.05 MPa
@Strain 2.10 %,
Temperature 23.0 °C		13640 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 95.546 MPa
@Strain 1.80 %,
Temperature 0.000 °C		13858 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.574 MPa
@Strain 1.60 %,
Temperature -40.0 °C		13862 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.2 MPa
@Strain 2.30 %,
Temperature 0.000 °C		14000 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.39 MPa
@Strain 2.20 %,
Temperature 23.0 °C		14130 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 98.1 MPa
@Strain 2.40 %,
Temperature 0.000 °C		14200 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.5 MPa
@Strain 1.70 %,
Temperature -40.0 °C		14300 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 99.788 MPa
@Strain 1.90 %,
Temperature 0.000 °C		14473 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 100.2 MPa
@Strain 2.50 %,
Temperature 0.000 °C		14530 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 100.53 MPa
@Strain 2.30 %,
Temperature 23.0 °C		14581 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 100.57 MPa
@Strain 1.70 %,
Temperature -40.0 °C		14586 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 102 MPa
@Strain 2.60 %,
Temperature 0.000 °C		14800 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.9 MPa
@Strain 1.80 %,
Temperature -40.0 °C		14920 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 103.51 MPa
@Strain 2.40 %,
Temperature 23.0 °C		15013 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.7 MPa
@Strain 2.70 %,
Temperature 0.000 °C		15040 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 104.13 MPa
@Strain 2.00 %,
Temperature 0.000 °C		15103 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 105.1 MPa
@Strain 2.80 %,
Temperature 0.000 °C		15240 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 105.37 MPa
@Strain 1.80 %,
Temperature -40.0 °C		15283 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 106.4 MPa
@Strain 2.90 %,
Temperature 0.000 °C		15430 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 106.43 MPa
@Strain 2.50 %,
Temperature 23.0 °C		15436 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 107.1 MPa
@Strain 1.90 %,
Temperature -40.0 °C		15530 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.87 MPa
@Strain 2.10 %,
Temperature 0.000 °C		15645 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 108 MPa
@Strain 3.00 %,
Temperature 0.000 °C		15700 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 109.15 MPa
@Strain 2.60 %,
Temperature 23.0 °C		15831 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 109.8 MPa
@Strain 3.10 %,
Temperature 0.000 °C		15930 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 110.26 MPa
@Strain 1.90 %,
Temperature -40.0 °C		15992 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.3 MPa
@Strain 3.20 %,
Temperature 0.000 °C		16140 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 111.5 MPa
@Strain 2.00 %,
Temperature -40.0 °C		16170 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.65 MPa
@Strain 2.70 %,
Temperature 23.0 °C		16193 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 111.81 MPa
@Strain 2.20 %,
Temperature 0.000 °C		16217 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 3.30 %,
Temperature 0.000 °C		16330 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 113.9 MPa
@Strain 3.40 %,
Temperature 0.000 °C		16520 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 113.92 MPa
@Strain 2.80 %,
Temperature 23.0 °C		16523 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114.34 MPa
@Strain 2.00 %,
Temperature -40.0 °C		16584 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.7 MPa
@Strain 3.50 %,
Temperature 0.000 °C		16640 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 115.2 MPa
@Strain 3.60 %,
Temperature 0.000 °C		16710 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 115.6 MPa
@Strain 2.10 %,
Temperature -40.0 °C		16770 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 115.95 MPa
@Strain 2.30 %,
Temperature 0.000 °C		16817 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 116.1 MPa
@Strain 2.90 %,
Temperature 23.0 °C		16840 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 116.3 MPa
@Strain 3.70 %,
Temperature 0.000 °C		16870 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 117.4 MPa
@Strain 3.80 %,
Temperature 0.000 °C		17030 psi
@Strain 3.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 118.08 MPa
@Strain 3.00 %,
Temperature 23.0 °C		17126 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 118.4 MPa
@Strain 3.90 %,
Temperature 0.000 °C		17170 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 118.73 MPa
@Strain 2.10 %,
Temperature -40.0 °C		17220 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 118.78 MPa
@Strain 2.40 %,
Temperature 0.000 °C		17228 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 119.3 MPa
@Strain 4.00 %,
Temperature 0.000 °C		17300 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 119.4 MPa
@Strain 2.20 %,
Temperature -40.0 °C		17320 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119.9 MPa
@Strain 4.10 %,
Temperature 0.000 °C		17390 psi
@Strain 4.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 119.91 MPa
@Strain 3.10 %,
Temperature 23.0 °C		17392 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 120.3 MPa
@Strain 5.00 %,
Temperature 0.000 °C		17450 psi
@Strain 5.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.4 MPa
@Strain 4.20 %,
Temperature 0.000 °C		17460 psi
@Strain 4.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.5 MPa
@Strain 4.90 %,
Temperature 0.000 °C		17480 psi
@Strain 4.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.7 MPa
@Strain 4.80 %,
Temperature 0.000 °C		17510 psi
@Strain 4.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.7 MPa
@Strain 4.30 %,
Temperature 0.000 °C		17510 psi
@Strain 4.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.9 MPa
@Strain 4.60 %,
Temperature 0.000 °C		17540 psi
@Strain 4.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.9 MPa
@Strain 4.70 %,
Temperature 0.000 °C		17540 psi
@Strain 4.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.9 MPa
@Strain 4.40 %,
Temperature 0.000 °C		17540 psi
@Strain 4.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 121 MPa
@Strain 4.50 %,
Temperature 0.000 °C		17500 psi
@Strain 4.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 122.82 MPa
@Strain 2.50 %,
Temperature 0.000 °C		17814 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 123.11 MPa
@Strain 2.20 %,
Temperature -40.0 °C		17856 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 123.4 MPa
@Strain 2.30 %,
Temperature -40.0 °C		17900 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 126.15 MPa
@Strain 2.60 %,
Temperature 0.000 °C		18297 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 127.19 MPa
@Strain 2.30 %,
Temperature -40.0 °C		18447 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 127.2 MPa
@Strain 2.40 %,
Temperature -40.0 °C		18450 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 130.8 MPa
@Strain 2.50 %,
Temperature -40.0 °C		18970 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 131.07 MPa
@Strain 2.40 %,
Temperature -40.0 °C		19010 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 134.1 MPa
@Strain 2.60 %,
Temperature -40.0 °C		19450 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 135.05 MPa
@Strain 2.50 %,
Temperature -40.0 °C		19587 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ISO 527
 8.0 %
@Temperature 23.0 °C		8.0 %
@Temperature 73.4 °F		50%RH; ASTM D638
 13 %
@Temperature 23.0 °C		13 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  3.50 GPa
@Temperature 23.0 °C		508 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 5.50 GPa
@Temperature 23.0 °C		798 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength  100 MPa
@Temperature 23.0 °C		14500 psi
@Temperature 73.4 °F		50%RH; ISO 178
 165 MPa
@Temperature 23.0 °C		23900 psi
@Temperature 73.4 °F		DAM; ASTM D790
 190 MPa
@Temperature 23.0 °C		27600 psi
@Temperature 73.4 °F		DAM; ISO 178
Flexural Modulus  2.76 GPa
@Temperature 23.0 °C		400 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 2.90 GPa
@Temperature 23.0 °C		421 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 4.83 GPa
@Temperature 23.0 °C		701 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 4.90 GPa
@Temperature 23.0 °C		711 ksi
@Temperature 73.4 °F		DAM; ISO 178
Shear Strength 76.0 MPa
@Temperature 23.0 °C		11000 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.480 J/cm
@Temperature 23.0 °C		0.899 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 0.530 J/cm
@Temperature 23.0 °C		0.993 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  3.00 kJ/m²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 3.00 kJ/m²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
 4.50 kJ/m²
@Temperature -40.0 °C		2.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature 23.0 °C		2.14 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  28.0 kJ/m²
@Temperature -30.0 °C		13.3 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 35.0 kJ/m²
@Temperature -30.0 °C		16.7 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 40.0 kJ/m²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 55.0 kJ/m²
@Temperature 23.0 °C		26.2 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  3.00 J/cm²
@Temperature -30.0 °C		14.3 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 3.00 J/cm²
@Temperature -30.0 °C		14.3 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 3.20 J/cm²
@Temperature 23.0 °C		15.2 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 7.00 J/cm²
@Temperature 23.0 °C		33.3 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.450 J/cm²
@Temperature -40.0 °C		2.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.500 J/cm²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 3300 MPa
@Temperature 23.0 °C		479000 psi
@Temperature 73.4 °F		50%RH; ISO 899
Tensile Creep Modulus, 1000 hours 2200 MPa
@Temperature 23.0 °C		319000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dissipation Factor  0.0070
@Frequency 100 Hz,
Temperature 23.0 °C		0.0070
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.0070
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.0070
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.24
@Frequency 100 Hz,
Temperature 23.0 °C		0.24
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.24
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.24
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index 600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; IEC 60112
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  77.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		42.8 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 77.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		42.8 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 96.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		53.3 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 96.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		53.3 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 158 µm/m-°C
@Temperature 55.0 - 160 °C		87.8 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 158 µm/m-°C
@Temperature 55.0 - 160 °C		87.8 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 258 °C496 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 238 °C460 °FDAM; ISO 75-1/-2
 243 °C469 °FDAM; ASTM D648
Glass Transition Temp, Tg 80.0 °C176 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		DAM; UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		DAM; UL 746B
 140 °C
@Thickness 0.710 mm		284 °F
@Thickness 0.0280 in		DAM; UL 746B
UL RTI, Mechanical with Impact  125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		DAM; UL 746B
 125 °C
@Thickness 0.710 mm		257 °F
@Thickness 0.0280 in		DAM; UL 746B
 125 °C
@Thickness 3.00 mm		257 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		DAM; UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		DAM; UL 746B
 140 °C
@Thickness 0.710 mm		284 °F
@Thickness 0.0280 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesGeneral PurposeDAM
 Heat StabilizedDAM
 Thermal Stability, GoodDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-GF13<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-GF13ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAutomotive ApplicationsDAM
 Industrial ApplicationsDAM
 Parts, EngineeringDAM
 Parts, Machine/MechanicalDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45448.html

免责声明: 本文 DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4