DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66

DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.14
  • 吸水率 [%]: 1.2
  • 成型收缩率 [%]: 0.014
  • 缺口冲击强度: 0.53
  • 拉伸强度 [MPa]: 55.0
  • 弯曲模量 [MPa]: 0.414
  • 硬度: 121.0
  • 热变形温度 [℃]: 200.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.14 g/cc1.14 g/ccDAM; ASTM D792
Density 1.14 g/cc0.0412 lb/in³DAM; ISO 1183
Water Absorption  1.2 %
@Temperature 23.0 °C		1.2 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 2.6 %
@Temperature 23.0 °C		2.6 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 8.5 %
@Temperature 23.0 °C		8.5 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
 8.6 %
@Temperature 23.0 °C		8.6 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
Linear Mold Shrinkage  0.014 cm/cm
@Thickness 1.60 mm		0.014 in/in
@Thickness 0.0630 in		Flow; DAM
 0.018 cm/cm
@Thickness 3.20 mm		0.018 in/in
@Thickness 0.126 in		Flow; DAM
Linear Mold Shrinkage, Flow 0.014 cm/cm
@Thickness 2.00 mm		0.014 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm
@Thickness 2.00 mm		0.013 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 121121DAM; ASTM D785
Tensile Strength  41.0 MPa
@Temperature 121 °C		5950 psi
@Temperature 250 °F		DAM; ASTM D638
 55.0 MPa
@Temperature 77.0 °C		7980 psi
@Temperature 171 °F		DAM; ASTM D638
 59.0 MPa
@Temperature 23.0 °C		8560 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  0.340 MPa
@Strain 0.100 %,
Temperature 150 °C		49.3 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.420 MPa
@Strain 0.100 %,
Temperature 150 °C		60.9 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.500 MPa
@Strain 0.100 %,
Temperature 120 °C		72.5 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.500 MPa
@Strain 0.100 %,
Temperature 120 °C		72.5 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 0.510 MPa
@Strain 0.100 %,
Temperature 100 °C		74.0 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 0.510 MPa
@Strain 0.100 %,
Temperature 80.0 °C		74.0 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 0.600 MPa
@Strain 0.100 %,
Temperature 100 °C		87.0 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 0.710 MPa
@Strain 0.200 %,
Temperature 150 °C		103 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.730 MPa
@Strain 0.100 %,
Temperature 80.0 °C		106 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 0.760 MPa
@Strain 0.100 %,
Temperature 60.0 °C		110 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.840 MPa
@Strain 0.200 %,
Temperature 150 °C		122 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.990 MPa
@Strain 0.200 %,
Temperature 120 °C		144 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.03 MPa
@Strain 0.200 %,
Temperature 120 °C		149 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.04 MPa
@Strain 0.300 %,
Temperature 150 °C		151 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.05 MPa
@Strain 0.200 %,
Temperature 100 °C		152 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.14 MPa
@Strain 0.200 %,
Temperature 80.0 °C		165 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.19 MPa
@Strain 0.200 %,
Temperature 100 °C		173 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.24 MPa
@Strain 0.400 %,
Temperature 150 °C		180 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.27 MPa
@Strain 0.300 %,
Temperature 150 °C		184 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.45 MPa
@Strain 0.300 %,
Temperature 120 °C		210 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.46 MPa
@Strain 0.200 %,
Temperature 80.0 °C		212 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 1.50 MPa
@Strain 0.200 %,
Temperature 60.0 °C		218 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 1.50 MPa
@Strain 0.100 %,
Temperature 23.0 °C		218 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.50 MPa
@Strain 0.400 %,
Temperature 150 °C		218 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.50 MPa
@Strain 0.300 %,
Temperature 120 °C		218 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.54 MPa
@Strain 0.300 %,
Temperature 100 °C		223 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.56 MPa
@Strain 0.500 %,
Temperature 150 °C		226 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 1.60 MPa
@Strain 0.100 %,
Temperature 60.0 °C		232 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 1.69 MPa
@Strain 0.300 %,
Temperature 80.0 °C		245 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 1.72 MPa
@Strain 0.300 %,
Temperature 100 °C		249 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 1.80 MPa
@Strain 0.400 %,
Temperature 120 °C		261 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.82 MPa
@Strain 0.400 %,
Temperature 120 °C		264 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.86 MPa
@Strain 0.400 %,
Temperature 100 °C		270 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 1.89 MPa
@Strain 0.500 %,
Temperature 150 °C		274 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.01 MPa
@Strain 0.600 %,
Temperature 150 °C		292 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.06 MPa
@Strain 0.400 %,
Temperature 80.0 °C		299 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.08 MPa
@Strain 0.400 %,
Temperature 100 °C		302 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.17 MPa
@Strain 0.300 %,
Temperature 80.0 °C		315 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.19 MPa
@Strain 0.300 %,
Temperature 60.0 °C		318 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.33 MPa
@Strain 0.600 %,
Temperature 150 °C		338 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.40 MPa
@Strain 0.500 %,
Temperature 120 °C		348 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.40 MPa
@Strain 0.700 %,
Temperature 150 °C		348 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.40 MPa
@Strain 0.500 %,
Temperature 120 °C		348 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.46 MPa
@Strain 0.500 %,
Temperature 100 °C		357 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.64 MPa
@Strain 0.400 %,
Temperature 80.0 °C		383 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.66 MPa
@Strain 0.100 %,
Temperature 0.000 °C		386 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 2.69 MPa
@Strain 0.400 %,
Temperature 60.0 °C		390 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.69 MPa
@Strain 0.500 %,
Temperature 100 °C		390 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.77 MPa
@Strain 0.700 %,
Temperature 150 °C		402 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.79 MPa
@Strain 0.600 %,
Temperature 120 °C		405 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.79 MPa
@Strain 0.800 %,
Temperature 150 °C		405 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.84 MPa
@Strain 0.500 %,
Temperature 80.0 °C		412 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.90 MPa
@Strain 0.600 %,
Temperature 120 °C		421 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.90 MPa
@Strain 0.100 %,
Temperature 23.0 °C		421 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 3.00 MPa
@Strain 0.100 %,
Temperature 0.000 °C		435 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 3.01 MPa
@Strain 0.600 %,
Temperature 100 °C		437 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.04 MPa
@Strain 0.200 %,
Temperature 23.0 °C		441 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.10 MPa
@Strain 0.200 %,
Temperature 60.0 °C		450 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 3.11 MPa
@Strain 0.800 %,
Temperature 150 °C		451 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.18 MPa
@Strain 0.900 %,
Temperature 150 °C		461 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.25 MPa
@Strain 0.600 %,
Temperature 100 °C		471 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 3.29 MPa
@Strain 0.700 %,
Temperature 120 °C		477 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.30 MPa
@Strain 0.100 %,
Temperature -40.0 °C		479 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 3.41 MPa
@Strain 0.700 %,
Temperature 120 °C		495 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.46 MPa
@Strain 0.600 %,
Temperature 80.0 °C		502 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 3.46 MPa
@Strain 1.00 %,
Temperature 150 °C		502 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.54 MPa
@Strain 0.500 %,
Temperature 80.0 °C		513 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 3.57 MPa
@Strain 0.500 %,
Temperature 60.0 °C		518 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.57 MPa
@Strain 0.700 %,
Temperature 100 °C		518 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 3.60 MPa
@Strain 0.900 %,
Temperature 150 °C		522 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.60 MPa
@Strain 0.100 %,
Temperature -40.0 °C		522 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 3.74 MPa
@Strain 0.800 %,
Temperature 120 °C		542 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.74 MPa
@Strain 1.10 %,
Temperature 150 °C		542 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.80 MPa
@Strain 0.800 %,
Temperature 120 °C		551 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 3.86 MPa
@Strain 0.700 %,
Temperature 100 °C		560 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 3.99 MPa
@Strain 1.00 %,
Temperature 150 °C		579 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.02 MPa
@Strain 0.800 %,
Temperature 100 °C		583 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.04 MPa
@Strain 0.700 %,
Temperature 80.0 °C		586 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.13 MPa
@Strain 1.20 %,
Temperature 150 °C		599 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.24 MPa
@Strain 0.600 %,
Temperature 60.0 °C		615 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.26 MPa
@Strain 0.600 %,
Temperature 80.0 °C		618 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 4.33 MPa
@Strain 1.10 %,
Temperature 150 °C		628 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.35 MPa
@Strain 0.900 %,
Temperature 120 °C		631 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.36 MPa
@Strain 0.900 %,
Temperature 120 °C		632 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.37 MPa
@Strain 0.800 %,
Temperature 100 °C		634 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.40 MPa
@Strain 1.30 %,
Temperature 150 °C		638 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.47 MPa
@Strain 0.900 %,
Temperature 100 °C		648 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.55 MPa
@Strain 0.800 %,
Temperature 80.0 °C		660 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.58 MPa
@Strain 0.300 %,
Temperature 23.0 °C		664 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 4.62 MPa
@Strain 0.300 %,
Temperature 60.0 °C		670 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 4.63 MPa
@Strain 1.40 %,
Temperature 150 °C		672 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.66 MPa
@Strain 1.20 %,
Temperature 150 °C		676 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.74 MPa
@Strain 1.00 %,
Temperature 120 °C		687 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.83 MPa
@Strain 1.00 %,
Temperature 100 °C		701 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 4.85 MPa
@Strain 0.700 %,
Temperature 60.0 °C		703 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.86 MPa
@Strain 1.00 %,
Temperature 120 °C		705 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.87 MPa
@Strain 0.900 %,
Temperature 100 °C		706 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 4.90 MPa
@Strain 0.900 %,
Temperature 80.0 °C		711 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.93 MPa
@Strain 1.50 %,
Temperature 150 °C		715 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 4.95 MPa
@Strain 0.700 %,
Temperature 80.0 °C		718 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.00 MPa
@Strain 0.400 %,
Temperature 60.0 °C		725 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 5.02 MPa
@Strain 1.30 %,
Temperature 150 °C		728 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.11 MPa
@Strain 1.10 %,
Temperature 120 °C		741 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.12 MPa
@Strain 0.400 %,
Temperature 23.0 °C		743 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 5.13 MPa
@Strain 1.10 %,
Temperature 120 °C		744 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.24 MPa
@Strain 1.60 %,
Temperature 150 °C		760 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.26 MPa
@Strain 1.00 %,
Temperature 100 °C		763 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.32 MPa
@Strain 1.40 %,
Temperature 150 °C		772 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.33 MPa
@Strain 0.800 %,
Temperature 60.0 °C		773 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.34 MPa
@Strain 0.200 %,
Temperature 0.000 °C		775 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 5.39 MPa
@Strain 1.10 %,
Temperature 100 °C		782 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.47 MPa
@Strain 1.00 %,
Temperature 80.0 °C		793 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.52 MPa
@Strain 1.70 %,
Temperature 150 °C		801 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.53 MPa
@Strain 1.20 %,
Temperature 120 °C		802 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.63 MPa
@Strain 1.20 %,
Temperature 120 °C		817 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.67 MPa
@Strain 0.800 %,
Temperature 80.0 °C		822 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.71 MPa
@Strain 1.50 %,
Temperature 150 °C		828 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.74 MPa
@Strain 1.30 %,
Temperature 120 °C		833 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.74 MPa
@Strain 1.80 %,
Temperature 150 °C		833 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.77 MPa
@Strain 1.10 %,
Temperature 100 °C		837 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.83 MPa
@Strain 0.200 %,
Temperature 23.0 °C		846 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.86 MPa
@Strain 0.900 %,
Temperature 60.0 °C		850 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.86 MPa
@Strain 1.20 %,
Temperature 100 °C		850 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.87 MPa
@Strain 1.30 %,
Temperature 120 °C		851 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.91 MPa
@Strain 0.200 %,
Temperature 0.000 °C		857 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 5.97 MPa
@Strain 1.90 %,
Temperature 150 °C		866 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.99 MPa
@Strain 1.60 %,
Temperature 150 °C		869 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.06 MPa
@Strain 1.10 %,
Temperature 80.0 °C		879 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.19 MPa
@Strain 2.00 %,
Temperature 150 °C		898 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.20 MPa
@Strain 1.40 %,
Temperature 120 °C		899 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.22 MPa
@Strain 1.40 %,
Temperature 120 °C		902 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.25 MPa
@Strain 1.30 %,
Temperature 100 °C		906 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.27 MPa
@Strain 1.70 %,
Temperature 150 °C		909 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.42 MPa
@Strain 1.00 %,
Temperature 60.0 °C		931 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 6.44 MPa
@Strain 1.20 %,
Temperature 100 °C		934 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 6.52 MPa
@Strain 2.10 %,
Temperature 150 °C		946 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.59 MPa
@Strain 1.50 %,
Temperature 120 °C		956 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 6.60 MPa
@Strain 1.80 %,
Temperature 150 °C		957 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.61 MPa
@Strain 0.200 %,
Temperature -40.0 °C		959 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.64 MPa
@Strain 0.900 %,
Temperature 80.0 °C		963 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 6.69 MPa
@Strain 1.20 %,
Temperature 80.0 °C		970 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.70 MPa
@Strain 1.40 %,
Temperature 100 °C		972 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 6.80 MPa
@Strain 1.50 %,
Temperature 120 °C		986 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.86 MPa
@Strain 2.20 %,
Temperature 150 °C		995 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.88 MPa
@Strain 1.90 %,
Temperature 150 °C		998 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.89 MPa
@Strain 1.30 %,
Temperature 100 °C		999 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.03 MPa
@Strain 1.10 %,
Temperature 60.0 °C		1020 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.04 MPa
@Strain 1.60 %,
Temperature 120 °C		1020 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.09 MPa
@Strain 1.50 %,
Temperature 100 °C		1030 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.14 MPa
@Strain 2.30 %,
Temperature 150 °C		1040 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.19 MPa
@Strain 1.70 %,
Temperature 120 °C		1040 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.20 MPa
@Strain 0.500 %,
Temperature 23.0 °C		1040 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 7.21 MPa
@Strain 2.00 %,
Temperature 150 °C		1050 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.22 MPa
@Strain 1.30 %,
Temperature 80.0 °C		1050 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.22 MPa
@Strain 0.500 %,
Temperature 60.0 °C		1050 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 7.30 MPa
@Strain 1.00 %,
Temperature 80.0 °C		1060 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.36 MPa
@Strain 2.40 %,
Temperature 150 °C		1070 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.39 MPa
@Strain 1.40 %,
Temperature 100 °C		1070 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.49 MPa
@Strain 1.70 %,
Temperature 120 °C		1090 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.54 MPa
@Strain 1.60 %,
Temperature 100 °C		1090 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.54 MPa
@Strain 2.10 %,
Temperature 150 °C		1090 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.58 MPa
@Strain 1.80 %,
Temperature 120 °C		1100 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.58 MPa
@Strain 2.50 %,
Temperature 150 °C		1100 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.59 MPa
@Strain 1.40 %,
Temperature 80.0 °C		1100 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.64 MPa
@Strain 1.20 %,
Temperature 60.0 °C		1110 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.69 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1120 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 7.73 MPa
@Strain 1.60 %,
Temperature 100 °C		1120 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.88 MPa
@Strain 1.80 %,
Temperature 120 °C		1140 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.88 MPa
@Strain 2.20 %,
Temperature 150 °C		1140 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.91 MPa
@Strain 1.10 %,
Temperature 80.0 °C		1150 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.92 MPa
@Strain 2.60 %,
Temperature 150 °C		1150 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.92 MPa
@Strain 1.50 %,
Temperature 80.0 °C		1150 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.03 MPa
@Strain 1.90 %,
Temperature 120 °C		1160 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.04 MPa
@Strain 1.70 %,
Temperature 100 °C		1170 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.14 MPa
@Strain 2.70 %,
Temperature 150 °C		1180 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.15 MPa
@Strain 2.30 %,
Temperature 150 °C		1180 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.23 MPa
@Strain 1.70 %,
Temperature 100 °C		1190 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.26 MPa
@Strain 1.30 %,
Temperature 60.0 °C		1200 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.27 MPa
@Strain 1.90 %,
Temperature 120 °C		1200 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.31 MPa
@Strain 2.00 %,
Temperature 120 °C		1210 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.36 MPa
@Strain 2.80 %,
Temperature 150 °C		1210 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.40 MPa
@Strain 1.60 %,
Temperature 80.0 °C		1220 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.40 MPa
@Strain 0.300 %,
Temperature 0.000 °C		1220 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 8.43 MPa
@Strain 1.80 %,
Temperature 100 °C		1220 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.46 MPa
@Strain 1.20 %,
Temperature 80.0 °C		1230 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 8.49 MPa
@Strain 2.50 %,
Temperature 150 °C		1230 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.55 MPa
@Strain 0.600 %,
Temperature 23.0 °C		1240 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 8.60 MPa
@Strain 2.00 %,
Temperature 120 °C		1250 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.62 MPa
@Strain 1.80 %,
Temperature 100 °C		1250 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.64 MPa
@Strain 3.00 %,
Temperature 150 °C		1250 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.70 MPa
@Strain 2.10 %,
Temperature 120 °C		1260 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.71 MPa
@Strain 2.60 %,
Temperature 150 °C		1260 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.74 MPa
@Strain 0.600 %,
Temperature 60.0 °C		1270 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 8.81 MPa
@Strain 1.40 %,
Temperature 60.0 °C		1280 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.92 MPa
@Strain 3.10 %,
Temperature 150 °C		1290 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.93 MPa
@Strain 1.90 %,
Temperature 100 °C		1300 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 8.99 MPa
@Strain 2.10 %,
Temperature 120 °C		1300 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.02 MPa
@Strain 1.90 %,
Temperature 100 °C		1310 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.03 MPa
@Strain 2.20 %,
Temperature 120 °C		1310 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.04 MPa
@Strain 1.70 %,
Temperature 80.0 °C		1310 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.10 MPa
@Strain 2.70 %,
Temperature 150 °C		1320 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.13 MPa
@Strain 1.30 %,
Temperature 80.0 °C		1320 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.14 MPa
@Strain 3.20 %,
Temperature 150 °C		1330 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.37 MPa
@Strain 2.80 %,
Temperature 150 °C		1360 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.37 MPa
@Strain 1.50 %,
Temperature 60.0 °C		1360 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.38 MPa
@Strain 2.00 %,
Temperature 100 °C		1360 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.40 MPa
@Strain 1.80 %,
Temperature 80.0 °C		1360 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.42 MPa
@Strain 2.30 %,
Temperature 120 °C		1370 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.42 MPa
@Strain 3.30 %,
Temperature 150 °C		1370 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.44 MPa
@Strain 2.20 %,
Temperature 120 °C		1370 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.46 MPa
@Strain 2.00 %,
Temperature 100 °C		1370 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.48 MPa
@Strain 3.40 %,
Temperature 150 °C		1370 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.62 MPa
@Strain 1.40 %,
Temperature 80.0 °C		1400 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.65 MPa
@Strain 2.90 %,
Temperature 150 °C		1400 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.72 MPa
@Strain 2.30 %,
Temperature 120 °C		1410 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.76 MPa
@Strain 2.40 %,
Temperature 120 °C		1420 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.76 MPa
@Strain 3.50 %,
Temperature 150 °C		1420 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.76 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1420 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 9.77 MPa
@Strain 2.10 %,
Temperature 100 °C		1420 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 9.85 MPa
@Strain 0.700 %,
Temperature 23.0 °C		1430 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.87 MPa
@Strain 1.60 %,
Temperature 60.0 °C		1430 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 9.87 MPa
@Strain 1.90 %,
Temperature 80.0 °C		1430 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.91 MPa
@Strain 2.10 %,
Temperature 100 °C		1440 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.93 MPa
@Strain 3.00 %,
Temperature 150 °C		1440 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.98 MPa
@Strain 3.60 %,
Temperature 150 °C		1450 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.09 MPa
@Strain 3.10 %,
Temperature 150 °C		1463 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.09 MPa
@Strain 2.50 %,
Temperature 120 °C		1463 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.11 MPa
@Strain 2.40 %,
Temperature 120 °C		1466 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.15 MPa
@Strain 3.70 %,
Temperature 150 °C		1472 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.15 MPa
@Strain 0.300 %,
Temperature 0.000 °C		1472 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 10.16 MPa
@Strain 2.20 %,
Temperature 100 °C		1474 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.18 MPa
@Strain 1.60 %,
Temperature 80.0 °C		1476 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.19 MPa
@Strain 0.700 %,
Temperature 60.0 °C		1478 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 10.25 MPa
@Strain 2.20 %,
Temperature 100 °C		1487 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.31 MPa
@Strain 3.80 %,
Temperature 150 °C		1495 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.35 MPa
@Strain 2.00 %,
Temperature 80.0 °C		1501 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.43 MPa
@Strain 2.60 %,
Temperature 120 °C		1513 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.43 MPa
@Strain 3.20 %,
Temperature 150 °C		1513 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.45 MPa
@Strain 2.50 %,
Temperature 120 °C		1516 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.46 MPa
@Strain 0.300 %,
Temperature -40.0 °C		1517 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 10.49 MPa
@Strain 1.70 %,
Temperature 60.0 °C		1521 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.5 MPa
@Strain 2.30 %,
Temperature 100 °C		1520 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.54 MPa
@Strain 3.90 %,
Temperature 150 °C		1529 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.62 MPa
@Strain 0.400 %,
Temperature 0.000 °C		1540 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 10.64 MPa
@Strain 2.30 %,
Temperature 100 °C		1543 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 10.65 MPa
@Strain 3.40 %,
Temperature 150 °C		1545 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.76 MPa
@Strain 2.70 %,
Temperature 120 °C		1561 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.76 MPa
@Strain 4.10 %,
Temperature 150 °C		1561 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.78 MPa
@Strain 2.70 %,
Temperature 120 °C		1564 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.79 MPa
@Strain 1.70 %,
Temperature 80.0 °C		1565 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.82 MPa
@Strain 2.10 %,
Temperature 80.0 °C		1569 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.87 MPa
@Strain 3.50 %,
Temperature 150 °C		1577 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.94 MPa
@Strain 2.40 %,
Temperature 100 °C		1587 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.98 MPa
@Strain 4.20 %,
Temperature 150 °C		1593 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.99 MPa
@Strain 1.80 %,
Temperature 60.0 °C		1594 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.03 MPa
@Strain 2.40 %,
Temperature 100 °C		1600 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.04 MPa
@Strain 2.80 %,
Temperature 120 °C		1601 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.1 MPa
@Strain 0.800 %,
Temperature 23.0 °C		1610 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 11.12 MPa
@Strain 2.80 %,
Temperature 120 °C		1613 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.15 MPa
@Strain 3.60 %,
Temperature 150 °C		1617 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.15 MPa
@Strain 4.30 %,
Temperature 150 °C		1617 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.16 MPa
@Strain 2.20 %,
Temperature 80.0 °C		1619 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.23 MPa
@Strain 1.80 %,
Temperature 80.0 °C		1629 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.32 MPa
@Strain 4.40 %,
Temperature 150 °C		1642 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.33 MPa
@Strain 2.60 %,
Temperature 100 °C		1643 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.37 MPa
@Strain 3.70 %,
Temperature 150 °C		1649 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.37 MPa
@Strain 3.00 %,
Temperature 120 °C		1649 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.42 MPa
@Strain 2.50 %,
Temperature 100 °C		1656 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.45 MPa
@Strain 2.90 %,
Temperature 120 °C		1661 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.46 MPa
@Strain 2.30 %,
Temperature 80.0 °C		1662 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.54 MPa
@Strain 4.50 %,
Temperature 150 °C		1674 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.55 MPa
@Strain 1.90 %,
Temperature 60.0 °C		1675 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.59 MPa
@Strain 3.80 %,
Temperature 150 °C		1681 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.65 MPa
@Strain 3.10 %,
Temperature 120 °C		1690 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.65 MPa
@Strain 4.60 %,
Temperature 150 °C		1690 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.65 MPa
@Strain 0.800 %,
Temperature 60.0 °C		1690 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 11.7 MPa
@Strain 2.60 %,
Temperature 100 °C		1700 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.72 MPa
@Strain 2.70 %,
Temperature 100 °C		1700 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 11.73 MPa
@Strain 3.00 %,
Temperature 120 °C		1701 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.73 MPa
@Strain 1.90 %,
Temperature 80.0 °C		1701 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.81 MPa
@Strain 3.90 %,
Temperature 150 °C		1713 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.85 MPa
@Strain 2.40 %,
Temperature 80.0 °C		1719 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.88 MPa
@Strain 4.70 %,
Temperature 150 °C		1723 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.91 MPa
@Strain 0.300 %,
Temperature -40.0 °C		1727 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 11.96 MPa
@Strain 0.400 %,
Temperature 23.0 °C		1735 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.99 MPa
@Strain 4.80 %,
Temperature 150 °C		1739 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.99 MPa
@Strain 3.20 %,
Temperature 120 °C		1739 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.03 MPa
@Strain 4.00 %,
Temperature 150 °C		1745 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.05 MPa
@Strain 2.00 %,
Temperature 60.0 °C		1748 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.06 MPa
@Strain 2.80 %,
Temperature 100 °C		1749 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.07 MPa
@Strain 3.10 %,
Temperature 120 °C		1751 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.15 MPa
@Strain 2.70 %,
Temperature 100 °C		1762 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.15 MPa
@Strain 5.00 %,
Temperature 150 °C		1762 psi
@Strain 5.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.2 MPa
@Strain 4.20 %,
Temperature 150 °C		1770 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.22 MPa
@Strain 2.00 %,
Temperature 80.0 °C		1772 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.27 MPa
@Strain 3.30 %,
Temperature 120 °C		1780 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.3 MPa
@Strain 2.50 %,
Temperature 80.0 °C		1780 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.34 MPa
@Strain 0.900 %,
Temperature 23.0 °C		1790 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 12.35 MPa
@Strain 3.20 %,
Temperature 120 °C		1791 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.39 MPa
@Strain 2.90 %,
Temperature 100 °C		1797 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.43 MPa
@Strain 2.80 %,
Temperature 100 °C		1803 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.48 MPa
@Strain 4.30 %,
Temperature 150 °C		1810 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.54 MPa
@Strain 3.40 %,
Temperature 120 °C		1819 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.55 MPa
@Strain 2.10 %,
Temperature 60.0 °C		1820 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.63 MPa
@Strain 0.400 %,
Temperature 0.000 °C		1832 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 12.67 MPa
@Strain 3.00 %,
Temperature 100 °C		1838 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.68 MPa
@Strain 3.30 %,
Temperature 120 °C		1839 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.7 MPa
@Strain 4.40 %,
Temperature 150 °C		1840 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.72 MPa
@Strain 2.60 %,
Temperature 80.0 °C		1845 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 12.72 MPa
@Strain 2.10 %,
Temperature 80.0 °C		1845 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.76 MPa
@Strain 5.50 %,
Temperature 150 °C		1851 psi
@Strain 5.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.77 MPa
@Strain 2.90 %,
Temperature 100 °C		1852 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.82 MPa
@Strain 3.50 %,
Temperature 120 °C		1859 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.87 MPa
@Strain 4.50 %,
Temperature 150 °C		1867 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.88 MPa
@Strain 0.900 %,
Temperature 60.0 °C		1868 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 12.9 MPa
@Strain 3.40 %,
Temperature 120 °C		1870 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.0 MPa
@Strain 2.70 %,
Temperature 80.0 °C		1890 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.05 MPa
@Strain 3.60 %,
Temperature 120 °C		1893 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.05 MPa
@Strain 2.20 %,
Temperature 60.0 °C		1893 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.06 MPa
@Strain 3.10 %,
Temperature 100 °C		1894 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.1 MPa
@Strain 3.10 %,
Temperature 100 °C		1900 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.13 MPa
@Strain 3.50 %,
Temperature 120 °C		1904 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.14 MPa
@Strain 4.60 %,
Temperature 150 °C		1906 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.16 MPa
@Strain 2.20 %,
Temperature 80.0 °C		1909 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.25 MPa
@Strain 4.70 %,
Temperature 150 °C		1922 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.28 MPa
@Strain 0.400 %,
Temperature -40.0 °C		1926 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 13.3 MPa
@Strain 2.80 %,
Temperature 80.0 °C		1930 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.32 MPa
@Strain 3.70 %,
Temperature 120 °C		1932 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.37 MPa
@Strain 4.80 %,
Temperature 150 °C		1939 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.38 MPa
@Strain 3.20 %,
Temperature 100 °C		1941 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.4 MPa
@Strain 3.20 %,
Temperature 100 °C		1940 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.44 MPa
@Strain 2.30 %,
Temperature 60.0 °C		1949 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 13.46 MPa
@Strain 3.60 %,
Temperature 120 °C		1952 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.47 MPa
@Strain 1.00 %,
Temperature 23.0 °C		1954 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 13.55 MPa
@Strain 3.80 %,
Temperature 120 °C		1965 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.55 MPa
@Strain 6.00 %,
Temperature 150 °C		1965 psi
@Strain 6.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.59 MPa
@Strain 5.00 %,
Temperature 150 °C		1971 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.66 MPa
@Strain 2.30 %,
Temperature 80.0 °C		1981 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.72 MPa
@Strain 3.30 %,
Temperature 100 °C		1990 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.73 MPa
@Strain 3.30 %,
Temperature 100 °C		1991 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 13.75 MPa
@Strain 2.90 %,
Temperature 80.0 °C		1994 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.8 MPa
@Strain 3.70 %,
Temperature 120 °C		2000 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.83 MPa
@Strain 4.00 %,
Temperature 120 °C		2006 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.95 MPa
@Strain 2.50 %,
Temperature 60.0 °C		2023 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.02 MPa
@Strain 3.90 %,
Temperature 120 °C		2033 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.05 MPa
@Strain 4.10 %,
Temperature 120 °C		2038 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.05 MPa
@Strain 2.40 %,
Temperature 80.0 °C		2038 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.06 MPa
@Strain 3.00 %,
Temperature 80.0 °C		2039 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.06 MPa
@Strain 3.40 %,
Temperature 100 °C		2039 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.07 MPa
@Strain 3.40 %,
Temperature 100 °C		2041 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.15 MPa
@Strain 6.50 %,
Temperature 150 °C		2052 psi
@Strain 6.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.17 MPa
@Strain 1.00 %,
Temperature 60.0 °C		2055 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 14.23 MPa
@Strain 5.50 %,
Temperature 150 °C		2064 psi
@Strain 5.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.27 MPa
@Strain 4.20 %,
Temperature 120 °C		2070 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.3 MPa
@Strain 4.00 %,
Temperature 120 °C		2070 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.34 MPa
@Strain 3.50 %,
Temperature 100 °C		2080 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.35 MPa
@Strain 3.50 %,
Temperature 100 °C		2081 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.44 MPa
@Strain 2.50 %,
Temperature 80.0 °C		2094 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.45 MPa
@Strain 2.60 %,
Temperature 60.0 °C		2096 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.48 MPa
@Strain 3.10 %,
Temperature 80.0 °C		2100 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.52 MPa
@Strain 4.10 %,
Temperature 120 °C		2106 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.55 MPa
@Strain 4.30 %,
Temperature 120 °C		2110 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.56 MPa
@Strain 0.400 %,
Temperature -40.0 °C		2112 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 14.62 MPa
@Strain 7.00 %,
Temperature 150 °C		2120 psi
@Strain 7.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.67 MPa
@Strain 3.20 %,
Temperature 80.0 °C		2128 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.67 MPa
@Strain 1.10 %,
Temperature 23.0 °C		2128 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 14.73 MPa
@Strain 3.60 %,
Temperature 100 °C		2136 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 14.74 MPa
@Strain 3.60 %,
Temperature 100 °C		2138 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.75 MPa
@Strain 4.20 %,
Temperature 120 °C		2139 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.76 MPa
@Strain 0.500 %,
Temperature 0.000 °C		2141 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 14.77 MPa
@Strain 4.40 %,
Temperature 120 °C		2142 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.84 MPa
@Strain 2.70 %,
Temperature 60.0 °C		2152 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.89 MPa
@Strain 3.30 %,
Temperature 80.0 °C		2160 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 14.93 MPa
@Strain 2.60 %,
Temperature 80.0 °C		2165 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.0 MPa
@Strain 4.50 %,
Temperature 120 °C		2180 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.02 MPa
@Strain 3.80 %,
Temperature 100 °C		2178 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.03 MPa
@Strain 4.30 %,
Temperature 120 °C		2180 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.03 MPa
@Strain 6.00 %,
Temperature 150 °C		2180 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.06 MPa
@Strain 3.70 %,
Temperature 100 °C		2184 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.13 MPa
@Strain 7.50 %,
Temperature 150 °C		2194 psi
@Strain 7.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.16 MPa
@Strain 4.60 %,
Temperature 120 °C		2199 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.29 MPa
@Strain 3.80 %,
Temperature 100 °C		2218 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.3 MPa
@Strain 3.90 %,
Temperature 100 °C		2220 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.31 MPa
@Strain 4.40 %,
Temperature 120 °C		2221 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.32 MPa
@Strain 2.70 %,
Temperature 80.0 °C		2222 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.37 MPa
@Strain 3.40 %,
Temperature 80.0 °C		2229 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.4 MPa
@Strain 2.80 %,
Temperature 60.0 °C		2230 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.4 MPa
@Strain 1.10 %,
Temperature 60.0 °C		2230 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 15.44 MPa
@Strain 4.70 %,
Temperature 120 °C		2239 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.47 MPa
@Strain 4.50 %,
Temperature 120 °C		2244 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.54 MPa
@Strain 8.00 %,
Temperature 150 °C		2254 psi
@Strain 8.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.58 MPa
@Strain 4.00 %,
Temperature 100 °C		2260 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.62 MPa
@Strain 3.90 %,
Temperature 100 °C		2265 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.67 MPa
@Strain 4.90 %,
Temperature 120 °C		2273 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.67 MPa
@Strain 6.50 %,
Temperature 150 °C		2273 psi
@Strain 6.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.69 MPa
@Strain 1.20 %,
Temperature 23.0 °C		2276 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.7 MPa
@Strain 4.60 %,
Temperature 120 °C		2280 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.73 MPa
@Strain 3.50 %,
Temperature 80.0 °C		2281 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.73 MPa
@Strain 2.90 %,
Temperature 60.0 °C		2281 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 15.76 MPa
@Strain 2.90 %,
Temperature 80.0 °C		2286 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.78 MPa
@Strain 5.00 %,
Temperature 120 °C		2289 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.85 MPa
@Strain 4.00 %,
Temperature 100 °C		2299 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.86 MPa
@Strain 4.10 %,
Temperature 100 °C		2300 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 15.87 MPa
@Strain 4.80 %,
Temperature 120 °C		2302 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.96 MPa
@Strain 8.50 %,
Temperature 150 °C		2315 psi
@Strain 8.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.02 MPa
@Strain 4.20 %,
Temperature 100 °C		2324 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.04 MPa
@Strain 3.00 %,
Temperature 80.0 °C		2326 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.09 MPa
@Strain 4.90 %,
Temperature 120 °C		2334 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.09 MPa
@Strain 3.60 %,
Temperature 80.0 °C		2334 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.13 MPa
@Strain 4.10 %,
Temperature 100 °C		2339 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.18 MPa
@Strain 3.00 %,
Temperature 60.0 °C		2347 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.23 MPa
@Strain 3.70 %,
Temperature 80.0 °C		2354 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.25 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2357 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 16.29 MPa
@Strain 7.00 %,
Temperature 150 °C		2363 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.34 MPa
@Strain 9.00 %,
Temperature 150 °C		2370 psi
@Strain 9.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.41 MPa
@Strain 4.20 %,
Temperature 100 °C		2380 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.41 MPa
@Strain 4.30 %,
Temperature 100 °C		2380 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.42 MPa
@Strain 5.00 %,
Temperature 120 °C		2382 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.43 MPa
@Strain 3.10 %,
Temperature 80.0 °C		2383 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.54 MPa
@Strain 5.50 %,
Temperature 120 °C		2399 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.6 MPa
@Strain 3.80 %,
Temperature 80.0 °C		2410 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.62 MPa
@Strain 3.10 %,
Temperature 60.0 °C		2411 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.63 MPa
@Strain 1.20 %,
Temperature 60.0 °C		2412 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 16.64 MPa
@Strain 9.50 %,
Temperature 150 °C		2413 psi
@Strain 9.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.69 MPa
@Strain 4.40 %,
Temperature 100 °C		2421 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.69 MPa
@Strain 4.40 %,
Temperature 100 °C		2421 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.72 MPa
@Strain 1.30 %,
Temperature 23.0 °C		2425 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 16.75 MPa
@Strain 0.500 %,
Temperature 0.000 °C		2429 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 16.78 MPa
@Strain 7.50 %,
Temperature 150 °C		2434 psi
@Strain 7.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.82 MPa
@Strain 3.20 %,
Temperature 80.0 °C		2440 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.92 MPa
@Strain 4.50 %,
Temperature 100 °C		2454 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 16.93 MPa
@Strain 3.90 %,
Temperature 80.0 °C		2455 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 16.97 MPa
@Strain 4.50 %,
Temperature 100 °C		2461 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.99 MPa
@Strain 10.0 %,
Temperature 150 °C		2464 psi
@Strain 10.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.01 MPa
@Strain 3.20 %,
Temperature 60.0 °C		2467 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.15 MPa
@Strain 5.50 %,
Temperature 120 °C		2487 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.2 MPa
@Strain 3.30 %,
Temperature 80.0 °C		2490 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.21 MPa
@Strain 8.00 %,
Temperature 150 °C		2496 psi
@Strain 8.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.25 MPa
@Strain 4.60 %,
Temperature 100 °C		2502 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.25 MPa
@Strain 4.60 %,
Temperature 100 °C		2502 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.27 MPa
@Strain 4.00 %,
Temperature 80.0 °C		2505 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.28 MPa
@Strain 0.500 %,
Temperature -40.0 °C		2506 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 17.4 MPa
@Strain 3.30 %,
Temperature 60.0 °C		2520 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.45 MPa
@Strain 6.00 %,
Temperature 120 °C		2531 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.47 MPa
@Strain 4.70 %,
Temperature 100 °C		2534 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.47 MPa
@Strain 4.80 %,
Temperature 100 °C		2534 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.48 MPa
@Strain 11.0 %,
Temperature 150 °C		2535 psi
@Strain 11.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.53 MPa
@Strain 3.40 %,
Temperature 80.0 °C		2543 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.57 MPa
@Strain 4.10 %,
Temperature 80.0 °C		2548 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.64 MPa
@Strain 4.90 %,
Temperature 100 °C		2558 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.66 MPa
@Strain 8.50 %,
Temperature 150 °C		2561 psi
@Strain 8.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.69 MPa
@Strain 1.40 %,
Temperature 23.0 °C		2566 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 17.7 MPa
@Strain 4.80 %,
Temperature 100 °C		2570 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.8 MPa
@Strain 4.20 %,
Temperature 80.0 °C		2580 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.8 MPa
@Strain 3.40 %,
Temperature 60.0 °C		2580 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.86 MPa
@Strain 4.90 %,
Temperature 100 °C		2590 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.87 MPa
@Strain 3.50 %,
Temperature 80.0 °C		2592 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 17.89 MPa
@Strain 0.600 %,
Temperature 0.000 °C		2595 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 17.92 MPa
@Strain 5.00 %,
Temperature 100 °C		2599 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.99 MPa
@Strain 4.30 %,
Temperature 80.0 °C		2609 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.04 MPa
@Strain 12.0 %,
Temperature 150 °C		2616 psi
@Strain 12.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.06 MPa
@Strain 6.00 %,
Temperature 120 °C		2619 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.11 MPa
@Strain 9.00 %,
Temperature 150 °C		2627 psi
@Strain 9.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.14 MPa
@Strain 3.60 %,
Temperature 80.0 °C		2631 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.16 MPa
@Strain 6.50 %,
Temperature 120 °C		2634 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.19 MPa
@Strain 3.50 %,
Temperature 60.0 °C		2638 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.28 MPa
@Strain 1.30 %,
Temperature 60.0 °C		2651 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 18.33 MPa
@Strain 4.40 %,
Temperature 80.0 °C		2659 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.43 MPa
@Strain 9.50 %,
Temperature 150 °C		2673 psi
@Strain 9.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.51 MPa
@Strain 13.0 %,
Temperature 150 °C		2685 psi
@Strain 13.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.58 MPa
@Strain 3.60 %,
Temperature 60.0 °C		2695 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.59 MPa
@Strain 3.70 %,
Temperature 80.0 °C		2696 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.61 MPa
@Strain 1.50 %,
Temperature 23.0 °C		2699 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 18.63 MPa
@Strain 4.50 %,
Temperature 80.0 °C		2702 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.75 MPa
@Strain 5.50 %,
Temperature 100 °C		2719 psi
@Strain 5.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.75 MPa
@Strain 10.0 %,
Temperature 150 °C		2719 psi
@Strain 10.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.8 MPa
@Strain 7.00 %,
Temperature 120 °C		2730 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.84 MPa
@Strain 5.40 %,
Temperature 100 °C		2733 psi
@Strain 5.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.86 MPa
@Strain 3.90 %,
Temperature 80.0 °C		2735 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.88 MPa
@Strain 4.60 %,
Temperature 80.0 °C		2738 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.91 MPa
@Strain 14.0 %,
Temperature 150 °C		2743 psi
@Strain 14.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.91 MPa
@Strain 3.80 %,
Temperature 60.0 °C		2743 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.93 MPa
@Strain 6.50 %,
Temperature 120 °C		2746 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.13 MPa
@Strain 4.70 %,
Temperature 80.0 °C		2775 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.19 MPa
@Strain 4.00 %,
Temperature 80.0 °C		2783 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.26 MPa
@Strain 15.0 %,
Temperature 150 °C		2793 psi
@Strain 15.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.29 MPa
@Strain 11.0 %,
Temperature 150 °C		2798 psi
@Strain 11.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.3 MPa
@Strain 3.90 %,
Temperature 60.0 °C		2800 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.33 MPa
@Strain 4.80 %,
Temperature 80.0 °C		2804 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.42 MPa
@Strain 7.50 %,
Temperature 120 °C		2817 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.5 MPa
@Strain 0.600 %,
Temperature 23.0 °C		2830 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 19.53 MPa
@Strain 4.10 %,
Temperature 80.0 °C		2833 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.56 MPa
@Strain 16.0 %,
Temperature 150 °C		2837 psi
@Strain 16.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.58 MPa
@Strain 1.60 %,
Temperature 23.0 °C		2840 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 19.64 MPa
@Strain 4.00 %,
Temperature 60.0 °C		2849 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.64 MPa
@Strain 4.90 %,
Temperature 80.0 °C		2849 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 19.65 MPa
@Strain 7.00 %,
Temperature 120 °C		2850 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.76 MPa
@Strain 0.500 %,
Temperature -40.0 °C		2866 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 19.79 MPa
@Strain 17.0 %,
Temperature 150 °C		2870 psi
@Strain 17.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.8 MPa
@Strain 4.20 %,
Temperature 80.0 °C		2870 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.83 MPa
@Strain 6.00 %,
Temperature 100 °C		2876 psi
@Strain 6.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 19.86 MPa
@Strain 0.600 %,
Temperature 0.000 °C		2880 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 19.88 MPa
@Strain 8.00 %,
Temperature 120 °C		2883 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.93 MPa
@Strain 12.0 %,
Temperature 150 °C		2891 psi
@Strain 12.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.93 MPa
@Strain 1.40 %,
Temperature 60.0 °C		2891 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.97 MPa
@Strain 4.10 %,
Temperature 60.0 °C		2896 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.98 MPa
@Strain 5.90 %,
Temperature 100 °C		2898 psi
@Strain 5.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.08 MPa
@Strain 18.0 %,
Temperature 150 °C		2912 psi
@Strain 18.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.13 MPa
@Strain 4.30 %,
Temperature 80.0 °C		2920 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.27 MPa
@Strain 7.50 %,
Temperature 120 °C		2940 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.31 MPa
@Strain 19.0 %,
Temperature 150 °C		2946 psi
@Strain 19.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.34 MPa
@Strain 1.70 %,
Temperature 23.0 °C		2950 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.36 MPa
@Strain 4.20 %,
Temperature 60.0 °C		2953 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.38 MPa
@Strain 8.50 %,
Temperature 120 °C		2956 psi
@Strain 8.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.39 MPa
@Strain 13.0 %,
Temperature 150 °C		2957 psi
@Strain 13.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.49 MPa
@Strain 20.0 %,
Temperature 150 °C		2972 psi
@Strain 20.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.52 MPa
@Strain 4.40 %,
Temperature 80.0 °C		2976 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.54 MPa
@Strain 0.600 %,
Temperature -40.0 °C		2979 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 20.64 MPa
@Strain 5.40 %,
Temperature 80.0 °C		2994 psi
@Strain 5.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.64 MPa
@Strain 4.30 %,
Temperature 60.0 °C		2994 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.68 MPa
@Strain 21.0 %,
Temperature 150 °C		2999 psi
@Strain 21.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.69 MPa
@Strain 6.50 %,
Temperature 100 °C		3001 psi
@Strain 6.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.74 MPa
@Strain 4.50 %,
Temperature 80.0 °C		3008 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.75 MPa
@Strain 14.0 %,
Temperature 150 °C		3010 psi
@Strain 14.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.84 MPa
@Strain 8.00 %,
Temperature 120 °C		3023 psi
@Strain 8.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.87 MPa
@Strain 9.00 %,
Temperature 120 °C		3027 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.87 MPa
@Strain 22.0 %,
Temperature 150 °C		3027 psi
@Strain 22.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.88 MPa
@Strain 6.40 %,
Temperature 100 °C		3028 psi
@Strain 6.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.92 MPa
@Strain 4.40 %,
Temperature 60.0 °C		3034 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.94 MPa
@Strain 1.50 %,
Temperature 60.0 °C		3037 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.96 MPa
@Strain 4.60 %,
Temperature 80.0 °C		3040 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.03 MPa
@Strain 0.700 %,
Temperature 0.000 °C		3050 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 21.03 MPa
@Strain 23.0 %,
Temperature 150 °C		3050 psi
@Strain 23.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.11 MPa
@Strain 1.80 %,
Temperature 23.0 °C		3062 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.14 MPa
@Strain 15.0 %,
Temperature 150 °C		3066 psi
@Strain 15.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.21 MPa
@Strain 24.0 %,
Temperature 150 °C		3076 psi
@Strain 24.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.3 MPa
@Strain 25.0 %,
Temperature 150 °C		3090 psi
@Strain 25.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.3 MPa
@Strain 9.50 %,
Temperature 120 °C		3090 psi
@Strain 9.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.31 MPa
@Strain 4.50 %,
Temperature 60.0 °C		3091 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.35 MPa
@Strain 4.70 %,
Temperature 80.0 °C		3097 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.41 MPa
@Strain 8.50 %,
Temperature 120 °C		3105 psi
@Strain 8.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.44 MPa
@Strain 26.0 %,
Temperature 150 °C		3110 psi
@Strain 26.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.48 MPa
@Strain 16.0 %,
Temperature 150 °C		3115 psi
@Strain 16.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.48 MPa
@Strain 7.00 %,
Temperature 100 °C		3115 psi
@Strain 7.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 21.58 MPa
@Strain 27.0 %,
Temperature 150 °C		3130 psi
@Strain 27.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.59 MPa
@Strain 4.60 %,
Temperature 60.0 °C		3131 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.63 MPa
@Strain 4.90 %,
Temperature 80.0 °C		3137 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.66 MPa
@Strain 10.0 %,
Temperature 120 °C		3142 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.71 MPa
@Strain 28.0 %,
Temperature 150 °C		3149 psi
@Strain 28.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.76 MPa
@Strain 17.0 %,
Temperature 150 °C		3156 psi
@Strain 17.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.8 MPa
@Strain 6.90 %,
Temperature 100 °C		3160 psi
@Strain 6.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.81 MPa
@Strain 5.90 %,
Temperature 80.0 °C		3163 psi
@Strain 5.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.81 MPa
@Strain 29.0 %,
Temperature 150 °C		3163 psi
@Strain 29.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.85 MPa
@Strain 5.00 %,
Temperature 80.0 °C		3169 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.94 MPa
@Strain 30.0 %,
Temperature 150 °C		3182 psi
@Strain 30.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.97 MPa
@Strain 1.90 %,
Temperature 23.0 °C		3186 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.98 MPa
@Strain 4.80 %,
Temperature 60.0 °C		3188 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.98 MPa
@Strain 9.00 %,
Temperature 120 °C		3188 psi
@Strain 9.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.03 MPa
@Strain 18.0 %,
Temperature 150 °C		3195 psi
@Strain 18.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.04 MPa
@Strain 31.0 %,
Temperature 150 °C		3197 psi
@Strain 31.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.11 MPa
@Strain 32.0 %,
Temperature 150 °C		3207 psi
@Strain 32.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.14 MPa
@Strain 7.50 %,
Temperature 100 °C		3211 psi
@Strain 7.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.23 MPa
@Strain 33.0 %,
Temperature 150 °C		3224 psi
@Strain 33.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.26 MPa
@Strain 19.0 %,
Temperature 150 °C		3229 psi
@Strain 19.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.26 MPa
@Strain 11.0 %,
Temperature 120 °C		3229 psi
@Strain 11.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.28 MPa
@Strain 34.0 %,
Temperature 150 °C		3231 psi
@Strain 34.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.34 MPa
@Strain 1.70 %,
Temperature 60.0 °C		3240 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.37 MPa
@Strain 4.90 %,
Temperature 60.0 °C		3245 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.37 MPa
@Strain 35.0 %,
Temperature 150 °C		3245 psi
@Strain 35.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.43 MPa
@Strain 36.0 %,
Temperature 150 °C		3253 psi
@Strain 36.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.43 MPa
@Strain 9.50 %,
Temperature 120 °C		3253 psi
@Strain 9.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.5 MPa
@Strain 20.0 %,
Temperature 150 °C		3260 psi
@Strain 20.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.53 MPa
@Strain 37.0 %,
Temperature 150 °C		3268 psi
@Strain 37.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.56 MPa
@Strain 7.40 %,
Temperature 100 °C		3272 psi
@Strain 7.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.56 MPa
@Strain 2.00 %,
Temperature 23.0 °C		3272 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.58 MPa
@Strain 38.0 %,
Temperature 150 °C		3275 psi
@Strain 38.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.59 MPa
@Strain 5.00 %,
Temperature 60.0 °C		3276 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.64 MPa
@Strain 39.0 %,
Temperature 150 °C		3284 psi
@Strain 39.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.67 MPa
@Strain 0.700 %,
Temperature 23.0 °C		3288 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 22.68 MPa
@Strain 40.0 %,
Temperature 150 °C		3289 psi
@Strain 40.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.71 MPa
@Strain 21.0 %,
Temperature 150 °C		3294 psi
@Strain 21.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.75 MPa
@Strain 8.00 %,
Temperature 100 °C		3300 psi
@Strain 8.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.76 MPa
@Strain 41.0 %,
Temperature 150 °C		3301 psi
@Strain 41.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.8 MPa
@Strain 6.40 %,
Temperature 80.0 °C		3310 psi
@Strain 6.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 22.81 MPa
@Strain 42.0 %,
Temperature 150 °C		3308 psi
@Strain 42.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.86 MPa
@Strain 43.0 %,
Temperature 150 °C		3316 psi
@Strain 43.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.89 MPa
@Strain 5.50 %,
Temperature 80.0 °C		3320 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.91 MPa
@Strain 44.0 %,
Temperature 150 °C		3323 psi
@Strain 44.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.91 MPa
@Strain 22.0 %,
Temperature 150 °C		3323 psi
@Strain 22.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.92 MPa
@Strain 10.0 %,
Temperature 120 °C		3324 psi
@Strain 10.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.94 MPa
@Strain 12.0 %,
Temperature 120 °C		3327 psi
@Strain 12.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.95 MPa
@Strain 45.0 %,
Temperature 150 °C		3329 psi
@Strain 45.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.0 MPa
@Strain 46.0 %,
Temperature 150 °C		3340 psi
@Strain 46.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.0 MPa
@Strain 47.0 %,
Temperature 150 °C		3340 psi
@Strain 47.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.07 MPa
@Strain 48.0 %,
Temperature 150 °C		3346 psi
@Strain 48.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.09 MPa
@Strain 49.0 %,
Temperature 150 °C		3349 psi
@Strain 49.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.12 MPa
@Strain 50.0 %,
Temperature 150 °C		3353 psi
@Strain 50.0 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.12 MPa
@Strain 23.0 %,
Temperature 150 °C		3353 psi
@Strain 23.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.22 MPa
@Strain 0.700 %,
Temperature 0.000 °C		3368 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 23.25 MPa
@Strain 24.0 %,
Temperature 150 °C		3372 psi
@Strain 24.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.27 MPa
@Strain 2.10 %,
Temperature 23.0 °C		3375 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 23.31 MPa
@Strain 7.90 %,
Temperature 100 °C		3381 psi
@Strain 7.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.35 MPa
@Strain 8.50 %,
Temperature 100 °C		3387 psi
@Strain 8.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.43 MPa
@Strain 13.0 %,
Temperature 120 °C		3398 psi
@Strain 13.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.44 MPa
@Strain 25.0 %,
Temperature 150 °C		3400 psi
@Strain 25.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.44 MPa
@Strain 0.700 %,
Temperature -40.0 °C		3400 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 23.49 MPa
@Strain 0.600 %,
Temperature -40.0 °C		3407 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 23.57 MPa
@Strain 26.0 %,
Temperature 150 °C		3419 psi
@Strain 26.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.61 MPa
@Strain 11.0 %,
Temperature 120 °C		3424 psi
@Strain 11.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.61 MPa
@Strain 5.50 %,
Temperature 60.0 °C		3424 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.69 MPa
@Strain 1.80 %,
Temperature 60.0 °C		3436 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.71 MPa
@Strain 27.0 %,
Temperature 150 °C		3439 psi
@Strain 27.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.79 MPa
@Strain 6.90 %,
Temperature 80.0 °C		3450 psi
@Strain 6.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.82 MPa
@Strain 28.0 %,
Temperature 150 °C		3455 psi
@Strain 28.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.86 MPa
@Strain 2.20 %,
Temperature 23.0 °C		3461 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 23.89 MPa
@Strain 14.0 %,
Temperature 120 °C		3465 psi
@Strain 14.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.94 MPa
@Strain 9.00 %,
Temperature 100 °C		3472 psi
@Strain 9.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 23.96 MPa
@Strain 8.40 %,
Temperature 100 °C		3475 psi
@Strain 8.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.97 MPa
@Strain 29.0 %,
Temperature 150 °C		3477 psi
@Strain 29.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.98 MPa
@Strain 0.800 %,
Temperature 0.000 °C		3478 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 24.06 MPa
@Strain 30.0 %,
Temperature 150 °C		3490 psi
@Strain 30.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.17 MPa
@Strain 31.0 %,
Temperature 150 °C		3506 psi
@Strain 31.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.27 MPa
@Strain 6.00 %,
Temperature 80.0 °C		3520 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.29 MPa
@Strain 15.0 %,
Temperature 120 °C		3523 psi
@Strain 15.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.31 MPa
@Strain 32.0 %,
Temperature 150 °C		3526 psi
@Strain 32.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.41 MPa
@Strain 33.0 %,
Temperature 150 °C		3540 psi
@Strain 33.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.42 MPa
@Strain 12.0 %,
Temperature 120 °C		3542 psi
@Strain 12.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.51 MPa
@Strain 9.50 %,
Temperature 100 °C		3555 psi
@Strain 9.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.51 MPa
@Strain 34.0 %,
Temperature 150 °C		3555 psi
@Strain 34.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.51 MPa
@Strain 2.40 %,
Temperature 23.0 °C		3555 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 24.53 MPa
@Strain 2.00 %,
Temperature 60.0 °C		3558 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.53 MPa
@Strain 8.90 %,
Temperature 100 °C		3558 psi
@Strain 8.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 24.58 MPa
@Strain 35.0 %,
Temperature 150 °C		3565 psi
@Strain 35.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.59 MPa
@Strain 7.40 %,
Temperature 80.0 °C		3566 psi
@Strain 7.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.65 MPa
@Strain 16.0 %,
Temperature 120 °C		3575 psi
@Strain 16.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.68 MPa
@Strain 36.0 %,
Temperature 150 °C		3580 psi
@Strain 36.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.74 MPa
@Strain 37.0 %,
Temperature 150 °C		3588 psi
@Strain 37.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.8 MPa
@Strain 38.0 %,
Temperature 150 °C		3600 psi
@Strain 38.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.89 MPa
@Strain 39.0 %,
Temperature 150 °C		3610 psi
@Strain 39.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.96 MPa
@Strain 17.0 %,
Temperature 120 °C		3620 psi
@Strain 17.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.96 MPa
@Strain 10.0 %,
Temperature 100 °C		3620 psi
@Strain 10.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.97 MPa
@Strain 40.0 %,
Temperature 150 °C		3622 psi
@Strain 40.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.01 MPa
@Strain 41.0 %,
Temperature 150 °C		3627 psi
@Strain 41.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.02 MPa
@Strain 13.0 %,
Temperature 120 °C		3629 psi
@Strain 13.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.1 MPa
@Strain 2.50 %,
Temperature 23.0 °C		3640 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.11 MPa
@Strain 42.0 %,
Temperature 150 °C		3642 psi
@Strain 42.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.12 MPa
@Strain 43.0 %,
Temperature 150 °C		3643 psi
@Strain 43.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.13 MPa
@Strain 6.00 %,
Temperature 60.0 °C		3645 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.17 MPa
@Strain 9.40 %,
Temperature 100 °C		3651 psi
@Strain 9.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.19 MPa
@Strain 44.0 %,
Temperature 150 °C		3654 psi
@Strain 44.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.22 MPa
@Strain 45.0 %,
Temperature 150 °C		3658 psi
@Strain 45.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.26 MPa
@Strain 18.0 %,
Temperature 120 °C		3664 psi
@Strain 18.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.3 MPa
@Strain 46.0 %,
Temperature 150 °C		3670 psi
@Strain 46.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.34 MPa
@Strain 47.0 %,
Temperature 150 °C		3675 psi
@Strain 47.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.35 MPa
@Strain 7.90 %,
Temperature 80.0 °C		3677 psi
@Strain 7.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.38 MPa
@Strain 6.50 %,
Temperature 80.0 °C		3681 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.39 MPa
@Strain 48.0 %,
Temperature 150 °C		3683 psi
@Strain 48.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.41 MPa
@Strain 49.0 %,
Temperature 150 °C		3685 psi
@Strain 49.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.43 MPa
@Strain 50.0 %,
Temperature 150 °C		3688 psi
@Strain 50.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.48 MPa
@Strain 2.10 %,
Temperature 60.0 °C		3696 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.49 MPa
@Strain 19.0 %,
Temperature 120 °C		3697 psi
@Strain 19.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.58 MPa
@Strain 14.0 %,
Temperature 120 °C		3710 psi
@Strain 14.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.67 MPa
@Strain 11.0 %,
Temperature 100 °C		3723 psi
@Strain 11.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 25.71 MPa
@Strain 2.60 %,
Temperature 23.0 °C		3729 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.74 MPa
@Strain 20.0 %,
Temperature 120 °C		3733 psi
@Strain 20.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.82 MPa
@Strain 9.90 %,
Temperature 100 °C		3745 psi
@Strain 9.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.9 MPa
@Strain 0.800 %,
Temperature 23.0 °C		3760 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 25.98 MPa
@Strain 21.0 %,
Temperature 120 °C		3768 psi
@Strain 21.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.03 MPa
@Strain 15.0 %,
Temperature 120 °C		3775 psi
@Strain 15.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.07 MPa
@Strain 8.40 %,
Temperature 80.0 °C		3781 psi
@Strain 8.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.09 MPa
@Strain 2.20 %,
Temperature 60.0 °C		3784 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.16 MPa
@Strain 22.0 %,
Temperature 120 °C		3794 psi
@Strain 22.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.19 MPa
@Strain 2.70 %,
Temperature 23.0 °C		3799 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.29 MPa
@Strain 6.50 %,
Temperature 60.0 °C		3813 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.32 MPa
@Strain 0.900 %,
Temperature 0.000 °C		3817 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 26.34 MPa
@Strain 7.00 %,
Temperature 80.0 °C		3820 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.36 MPa
@Strain 23.0 %,
Temperature 120 °C		3823 psi
@Strain 23.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.44 MPa
@Strain 16.0 %,
Temperature 120 °C		3835 psi
@Strain 16.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.46 MPa
@Strain 12.0 %,
Temperature 100 °C		3838 psi
@Strain 12.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.5 MPa
@Strain 24.0 %,
Temperature 120 °C		3840 psi
@Strain 24.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.51 MPa
@Strain 0.800 %,
Temperature 0.000 °C		3845 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 26.66 MPa
@Strain 10.9 %,
Temperature 100 °C		3867 psi
@Strain 10.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.68 MPa
@Strain 25.0 %,
Temperature 120 °C		3870 psi
@Strain 25.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.68 MPa
@Strain 2.80 %,
Temperature 23.0 °C		3870 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.68 MPa
@Strain 0.800 %,
Temperature -40.0 °C		3870 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 26.74 MPa
@Strain 8.90 %,
Temperature 80.0 °C		3878 psi
@Strain 8.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 26.81 MPa
@Strain 26.0 %,
Temperature 120 °C		3888 psi
@Strain 26.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.86 MPa
@Strain 17.0 %,
Temperature 120 °C		3896 psi
@Strain 17.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.88 MPa
@Strain 2.30 %,
Temperature 60.0 °C		3899 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.94 MPa
@Strain 27.0 %,
Temperature 120 °C		3907 psi
@Strain 27.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.07 MPa
@Strain 13.0 %,
Temperature 100 °C		3926 psi
@Strain 13.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.09 MPa
@Strain 28.0 %,
Temperature 120 °C		3929 psi
@Strain 28.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.16 MPa
@Strain 2.90 %,
Temperature 23.0 °C		3939 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.18 MPa
@Strain 7.00 %,
Temperature 60.0 °C		3942 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.18 MPa
@Strain 29.0 %,
Temperature 120 °C		3942 psi
@Strain 29.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.18 MPa
@Strain 0.700 %,
Temperature -40.0 °C		3942 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 27.21 MPa
@Strain 18.0 %,
Temperature 120 °C		3946 psi
@Strain 18.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.29 MPa
@Strain 30.0 %,
Temperature 120 °C		3958 psi
@Strain 30.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.3 MPa
@Strain 7.50 %,
Temperature 80.0 °C		3960 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.36 MPa
@Strain 9.40 %,
Temperature 80.0 °C		3968 psi
@Strain 9.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.41 MPa
@Strain 31.0 %,
Temperature 120 °C		3975 psi
@Strain 31.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.44 MPa
@Strain 2.40 %,
Temperature 60.0 °C		3980 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 27.49 MPa
@Strain 32.0 %,
Temperature 120 °C		3987 psi
@Strain 32.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.51 MPa
@Strain 19.0 %,
Temperature 120 °C		3990 psi
@Strain 19.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.58 MPa
@Strain 33.0 %,
Temperature 120 °C		4000 psi
@Strain 33.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.63 MPa
@Strain 11.9 %,
Temperature 100 °C		4007 psi
@Strain 11.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 27.64 MPa
@Strain 14.0 %,
Temperature 100 °C		4009 psi
@Strain 14.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.65 MPa
@Strain 3.00 %,
Temperature 23.0 °C		4010 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.66 MPa
@Strain 34.0 %,
Temperature 120 °C		4012 psi
@Strain 34.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.72 MPa
@Strain 35.0 %,
Temperature 120 °C		4020 psi
@Strain 35.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.8 MPa
@Strain 36.0 %,
Temperature 120 °C		4030 psi
@Strain 36.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.82 MPa
@Strain 20.0 %,
Temperature 120 °C		4035 psi
@Strain 20.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.86 MPa
@Strain 37.0 %,
Temperature 120 °C		4041 psi
@Strain 37.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.91 MPa
@Strain 38.0 %,
Temperature 120 °C		4048 psi
@Strain 38.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.91 MPa
@Strain 9.90 %,
Temperature 80.0 °C		4048 psi
@Strain 9.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.95 MPa
@Strain 39.0 %,
Temperature 120 °C		4054 psi
@Strain 39.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.02 MPa
@Strain 40.0 %,
Temperature 120 °C		4064 psi
@Strain 40.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.05 MPa
@Strain 41.0 %,
Temperature 120 °C		4068 psi
@Strain 41.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.07 MPa
@Strain 21.0 %,
Temperature 120 °C		4071 psi
@Strain 21.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.11 MPa
@Strain 42.0 %,
Temperature 120 °C		4077 psi
@Strain 42.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.11 MPa
@Strain 2.50 %,
Temperature 60.0 °C		4077 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.11 MPa
@Strain 8.00 %,
Temperature 80.0 °C		4077 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.13 MPa
@Strain 15.0 %,
Temperature 100 °C		4080 psi
@Strain 15.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.14 MPa
@Strain 3.20 %,
Temperature 23.0 °C		4081 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.18 MPa
@Strain 44.0 %,
Temperature 120 °C		4087 psi
@Strain 44.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.19 MPa
@Strain 43.0 %,
Temperature 120 °C		4089 psi
@Strain 43.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.22 MPa
@Strain 7.50 %,
Temperature 60.0 °C		4093 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.23 MPa
@Strain 45.0 %,
Temperature 120 °C		4094 psi
@Strain 45.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.25 MPa
@Strain 46.0 %,
Temperature 120 °C		4097 psi
@Strain 46.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.29 MPa
@Strain 22.0 %,
Temperature 120 °C		4103 psi
@Strain 22.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.3 MPa
@Strain 47.0 %,
Temperature 120 °C		4100 psi
@Strain 47.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.31 MPa
@Strain 48.0 %,
Temperature 120 °C		4106 psi
@Strain 48.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.35 MPa
@Strain 49.0 %,
Temperature 120 °C		4112 psi
@Strain 49.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.35 MPa
@Strain 50.0 %,
Temperature 120 °C		4112 psi
@Strain 50.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.39 MPa
@Strain 12.9 %,
Temperature 100 °C		4118 psi
@Strain 12.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.52 MPa
@Strain 16.0 %,
Temperature 100 °C		4136 psi
@Strain 16.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.52 MPa
@Strain 3.30 %,
Temperature 23.0 °C		4136 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.55 MPa
@Strain 23.0 %,
Temperature 120 °C		4141 psi
@Strain 23.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.72 MPa
@Strain 2.60 %,
Temperature 60.0 °C		4165 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.75 MPa
@Strain 24.0 %,
Temperature 120 °C		4170 psi
@Strain 24.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.83 MPa
@Strain 10.9 %,
Temperature 80.0 °C		4181 psi
@Strain 10.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.88 MPa
@Strain 17.0 %,
Temperature 100 °C		4189 psi
@Strain 17.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 28.93 MPa
@Strain 25.0 %,
Temperature 120 °C		4196 psi
@Strain 25.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.94 MPa
@Strain 3.40 %,
Temperature 23.0 °C		4197 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.96 MPa
@Strain 8.50 %,
Temperature 80.0 °C		4200 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.05 MPa
@Strain 0.900 %,
Temperature 23.0 °C		4213 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 29.08 MPa
@Strain 13.9 %,
Temperature 100 °C		4218 psi
@Strain 13.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.13 MPa
@Strain 8.00 %,
Temperature 60.0 °C		4225 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.16 MPa
@Strain 26.0 %,
Temperature 120 °C		4229 psi
@Strain 26.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.19 MPa
@Strain 18.0 %,
Temperature 100 °C		4234 psi
@Strain 18.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.23 MPa
@Strain 2.70 %,
Temperature 60.0 °C		4239 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.24 MPa
@Strain 1.00 %,
Temperature 0.000 °C		4241 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 29.31 MPa
@Strain 27.0 %,
Temperature 120 °C		4251 psi
@Strain 27.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.33 MPa
@Strain 3.50 %,
Temperature 23.0 °C		4254 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.42 MPa
@Strain 28.0 %,
Temperature 120 °C		4267 psi
@Strain 28.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.48 MPa
@Strain 19.0 %,
Temperature 100 °C		4276 psi
@Strain 19.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.59 MPa
@Strain 29.0 %,
Temperature 120 °C		4292 psi
@Strain 29.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.7 MPa
@Strain 30.0 %,
Temperature 120 °C		4310 psi
@Strain 30.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.7 MPa
@Strain 14.9 %,
Temperature 100 °C		4310 psi
@Strain 14.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.73 MPa
@Strain 20.0 %,
Temperature 100 °C		4312 psi
@Strain 20.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.78 MPa
@Strain 11.9 %,
Temperature 80.0 °C		4319 psi
@Strain 11.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.79 MPa
@Strain 2.80 %,
Temperature 60.0 °C		4321 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.8 MPa
@Strain 9.00 %,
Temperature 80.0 °C		4320 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.81 MPa
@Strain 0.900 %,
Temperature 0.000 °C		4324 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 29.82 MPa
@Strain 3.60 %,
Temperature 23.0 °C		4325 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.83 MPa
@Strain 31.0 %,
Temperature 120 °C		4326 psi
@Strain 31.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.86 MPa
@Strain 0.900 %,
Temperature -40.0 °C		4331 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 29.9 MPa
@Strain 8.50 %,
Temperature 60.0 °C		4340 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.95 MPa
@Strain 21.0 %,
Temperature 100 °C		4344 psi
@Strain 21.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.99 MPa
@Strain 32.0 %,
Temperature 120 °C		4350 psi
@Strain 32.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.09 MPa
@Strain 33.0 %,
Temperature 120 °C		4364 psi
@Strain 33.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.13 MPa
@Strain 22.0 %,
Temperature 100 °C		4370 psi
@Strain 22.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.2 MPa
@Strain 3.70 %,
Temperature 23.0 °C		4380 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.21 MPa
@Strain 34.0 %,
Temperature 120 °C		4382 psi
@Strain 34.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.24 MPa
@Strain 2.90 %,
Temperature 60.0 °C		4386 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.25 MPa
@Strain 15.9 %,
Temperature 100 °C		4387 psi
@Strain 15.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.32 MPa
@Strain 35.0 %,
Temperature 120 °C		4398 psi
@Strain 35.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.35 MPa
@Strain 23.0 %,
Temperature 100 °C		4402 psi
@Strain 23.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.39 MPa
@Strain 36.0 %,
Temperature 120 °C		4408 psi
@Strain 36.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.45 MPa
@Strain 9.50 %,
Temperature 80.0 °C		4416 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 30.48 MPa
@Strain 37.0 %,
Temperature 120 °C		4421 psi
@Strain 37.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.49 MPa
@Strain 24.0 %,
Temperature 100 °C		4422 psi
@Strain 24.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.52 MPa
@Strain 3.90 %,
Temperature 23.0 °C		4427 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.53 MPa
@Strain 38.0 %,
Temperature 120 °C		4428 psi
@Strain 38.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.59 MPa
@Strain 12.9 %,
Temperature 80.0 °C		4437 psi
@Strain 12.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.6 MPa
@Strain 9.00 %,
Temperature 60.0 °C		4440 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.61 MPa
@Strain 39.0 %,
Temperature 120 °C		4440 psi
@Strain 39.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.63 MPa
@Strain 25.0 %,
Temperature 100 °C		4443 psi
@Strain 25.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.72 MPa
@Strain 40.0 %,
Temperature 120 °C		4456 psi
@Strain 40.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.74 MPa
@Strain 16.9 %,
Temperature 100 °C		4458 psi
@Strain 16.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.74 MPa
@Strain 3.00 %,
Temperature 60.0 °C		4458 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.77 MPa
@Strain 41.0 %,
Temperature 120 °C		4463 psi
@Strain 41.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.78 MPa
@Strain 26.0 %,
Temperature 100 °C		4464 psi
@Strain 26.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.78 MPa
@Strain 0.800 %,
Temperature -40.0 °C		4464 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 30.85 MPa
@Strain 42.0 %,
Temperature 120 °C		4474 psi
@Strain 42.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.89 MPa
@Strain 43.0 %,
Temperature 120 °C		4480 psi
@Strain 43.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.91 MPa
@Strain 27.0 %,
Temperature 100 °C		4483 psi
@Strain 27.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.95 MPa
@Strain 4.00 %,
Temperature 23.0 °C		4489 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.99 MPa
@Strain 28.0 %,
Temperature 100 °C		4495 psi
@Strain 28.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 30.99 MPa
@Strain 44.0 %,
Temperature 120 °C		4495 psi
@Strain 44.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.04 MPa
@Strain 45.0 %,
Temperature 120 °C		4502 psi
@Strain 45.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.07 MPa
@Strain 46.0 %,
Temperature 120 °C		4506 psi
@Strain 46.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.11 MPa
@Strain 47.0 %,
Temperature 120 °C		4512 psi
@Strain 47.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.11 MPa
@Strain 29.0 %,
Temperature 100 °C		4512 psi
@Strain 29.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.11 MPa
@Strain 10.0 %,
Temperature 80.0 °C		4512 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.13 MPa
@Strain 3.10 %,
Temperature 60.0 °C		4515 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.15 MPa
@Strain 48.0 %,
Temperature 120 °C		4518 psi
@Strain 48.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.16 MPa
@Strain 49.0 %,
Temperature 120 °C		4519 psi
@Strain 49.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.16 MPa
@Strain 30.0 %,
Temperature 100 °C		4519 psi
@Strain 30.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.18 MPa
@Strain 17.9 %,
Temperature 100 °C		4522 psi
@Strain 17.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.22 MPa
@Strain 13.9 %,
Temperature 80.0 °C		4528 psi
@Strain 13.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.23 MPa
@Strain 31.0 %,
Temperature 100 °C		4530 psi
@Strain 31.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.27 MPa
@Strain 4.10 %,
Temperature 23.0 °C		4535 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.28 MPa
@Strain 50.0 %,
Temperature 120 °C		4537 psi
@Strain 50.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.31 MPa
@Strain 32.0 %,
Temperature 100 °C		4541 psi
@Strain 32.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.31 MPa
@Strain 9.50 %,
Temperature 60.0 °C		4541 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 31.4 MPa
@Strain 33.0 %,
Temperature 100 °C		4550 psi
@Strain 33.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.45 MPa
@Strain 1.00 %,
Temperature 23.0 °C		4561 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 31.48 MPa
@Strain 34.0 %,
Temperature 100 °C		4566 psi
@Strain 34.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.48 MPa
@Strain 35.0 %,
Temperature 100 °C		4566 psi
@Strain 35.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.53 MPa
@Strain 36.0 %,
Temperature 100 °C		4573 psi
@Strain 36.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.55 MPa
@Strain 18.9 %,
Temperature 100 °C		4576 psi
@Strain 18.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.58 MPa
@Strain 37.0 %,
Temperature 100 °C		4580 psi
@Strain 37.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.58 MPa
@Strain 3.30 %,
Temperature 60.0 °C		4580 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 31.63 MPa
@Strain 38.0 %,
Temperature 100 °C		4588 psi
@Strain 38.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.65 MPa
@Strain 39.0 %,
Temperature 100 °C		4590 psi
@Strain 39.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.65 MPa
@Strain 4.20 %,
Temperature 23.0 °C		4590 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.68 MPa
@Strain 41.0 %,
Temperature 100 °C		4595 psi
@Strain 41.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.69 MPa
@Strain 40.0 %,
Temperature 100 °C		4596 psi
@Strain 40.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.72 MPa
@Strain 42.0 %,
Temperature 100 °C		4601 psi
@Strain 42.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.73 MPa
@Strain 46.0 %,
Temperature 100 °C		4602 psi
@Strain 46.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.74 MPa
@Strain 43.0 %,
Temperature 100 °C		4604 psi
@Strain 43.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.75 MPa
@Strain 44.0 %,
Temperature 100 °C		4605 psi
@Strain 44.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.75 MPa
@Strain 45.0 %,
Temperature 100 °C		4605 psi
@Strain 45.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.75 MPa
@Strain 50.0 %,
Temperature 100 °C		4605 psi
@Strain 50.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.76 MPa
@Strain 49.0 %,
Temperature 100 °C		4606 psi
@Strain 49.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.79 MPa
@Strain 47.0 %,
Temperature 100 °C		4611 psi
@Strain 47.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.79 MPa
@Strain 48.0 %,
Temperature 100 °C		4611 psi
@Strain 48.0 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.81 MPa
@Strain 14.9 %,
Temperature 80.0 °C		4614 psi
@Strain 14.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.9 MPa
@Strain 19.9 %,
Temperature 100 °C		4630 psi
@Strain 19.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.96 MPa
@Strain 1.10 %,
Temperature 0.000 °C		4635 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 31.97 MPa
@Strain 3.40 %,
Temperature 60.0 °C		4637 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.0 MPa
@Strain 10.0 %,
Temperature 60.0 °C		4640 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.03 MPa
@Strain 4.30 %,
Temperature 23.0 °C		4646 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.22 MPa
@Strain 11.0 %,
Temperature 80.0 °C		4673 psi
@Strain 11.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.24 MPa
@Strain 20.9 %,
Temperature 100 °C		4676 psi
@Strain 20.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.25 MPa
@Strain 3.50 %,
Temperature 60.0 °C		4677 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.3 MPa
@Strain 15.9 %,
Temperature 80.0 °C		4680 psi
@Strain 15.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.36 MPa
@Strain 4.40 %,
Temperature 23.0 °C		4693 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.52 MPa
@Strain 21.9 %,
Temperature 100 °C		4717 psi
@Strain 21.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.64 MPa
@Strain 3.60 %,
Temperature 60.0 °C		4734 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.68 MPa
@Strain 4.60 %,
Temperature 23.0 °C		4740 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.75 MPa
@Strain 16.9 %,
Temperature 80.0 °C		4750 psi
@Strain 16.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.81 MPa
@Strain 22.9 %,
Temperature 100 °C		4759 psi
@Strain 22.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.9 MPa
@Strain 4.70 %,
Temperature 23.0 °C		4770 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.94 MPa
@Strain 1.00 %,
Temperature -40.0 °C		4778 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.98 MPa
@Strain 3.70 %,
Temperature 60.0 °C		4783 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.01 MPa
@Strain 1.00 %,
Temperature 0.000 °C		4788 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 33.05 MPa
@Strain 23.9 %,
Temperature 100 °C		4794 psi
@Strain 23.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.1 MPa
@Strain 17.9 %,
Temperature 80.0 °C		4800 psi
@Strain 17.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.14 MPa
@Strain 11.0 %,
Temperature 60.0 °C		4807 psi
@Strain 11.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.2 MPa
@Strain 3.80 %,
Temperature 60.0 °C		4820 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.29 MPa
@Strain 24.9 %,
Temperature 100 °C		4828 psi
@Strain 24.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.33 MPa
@Strain 4.80 %,
Temperature 23.0 °C		4834 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.44 MPa
@Strain 18.9 %,
Temperature 80.0 °C		4850 psi
@Strain 18.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.47 MPa
@Strain 12.0 %,
Temperature 80.0 °C		4854 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 33.48 MPa
@Strain 4.00 %,
Temperature 60.0 °C		4856 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.5 MPa
@Strain 25.9 %,
Temperature 100 °C		4860 psi
@Strain 25.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.69 MPa
@Strain 26.9 %,
Temperature 100 °C		4886 psi
@Strain 26.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.73 MPa
@Strain 19.9 %,
Temperature 80.0 °C		4892 psi
@Strain 19.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.77 MPa
@Strain 4.90 %,
Temperature 23.0 °C		4898 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.82 MPa
@Strain 4.10 %,
Temperature 60.0 °C		4905 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.87 MPa
@Strain 27.9 %,
Temperature 100 °C		4912 psi
@Strain 27.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.96 MPa
@Strain 20.9 %,
Temperature 80.0 °C		4925 psi
@Strain 20.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.06 MPa
@Strain 28.9 %,
Temperature 100 °C		4940 psi
@Strain 28.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.1 MPa
@Strain 4.20 %,
Temperature 60.0 °C		4950 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.11 MPa
@Strain 1.20 %,
Temperature 0.000 °C		4947 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 34.19 MPa
@Strain 21.9 %,
Temperature 80.0 °C		4959 psi
@Strain 21.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.21 MPa
@Strain 29.9 %,
Temperature 100 °C		4962 psi
@Strain 29.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.23 MPa
@Strain 0.900 %,
Temperature -40.0 °C		4965 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 34.27 MPa
@Strain 4.30 %,
Temperature 60.0 °C		4970 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.27 MPa
@Strain 12.0 %,
Temperature 60.0 °C		4970 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 34.36 MPa
@Strain 30.9 %,
Temperature 100 °C		4984 psi
@Strain 30.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.4 MPa
@Strain 22.9 %,
Temperature 80.0 °C		4990 psi
@Strain 22.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.49 MPa
@Strain 31.9 %,
Temperature 100 °C		5002 psi
@Strain 31.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.5 MPa
@Strain 13.0 %,
Temperature 80.0 °C		5000 psi
@Strain 13.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.55 MPa
@Strain 4.40 %,
Temperature 60.0 °C		5011 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.55 MPa
@Strain 1.10 %,
Temperature 23.0 °C		5011 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 34.55 MPa
@Strain 23.9 %,
Temperature 80.0 °C		5011 psi
@Strain 23.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.61 MPa
@Strain 32.9 %,
Temperature 100 °C		5020 psi
@Strain 32.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.69 MPa
@Strain 24.9 %,
Temperature 80.0 °C		5031 psi
@Strain 24.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.75 MPa
@Strain 33.9 %,
Temperature 100 °C		5040 psi
@Strain 33.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.76 MPa
@Strain 5.40 %,
Temperature 23.0 °C		5042 psi
@Strain 5.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 34.77 MPa
@Strain 4.50 %,
Temperature 60.0 °C		5043 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 34.82 MPa
@Strain 25.9 %,
Temperature 80.0 °C		5050 psi
@Strain 25.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.84 MPa
@Strain 34.9 %,
Temperature 100 °C		5053 psi
@Strain 34.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.9 MPa
@Strain 26.9 %,
Temperature 80.0 °C		5060 psi
@Strain 26.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.95 MPa
@Strain 35.9 %,
Temperature 100 °C		5069 psi
@Strain 35.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.0 MPa
@Strain 27.9 %,
Temperature 80.0 °C		5080 psi
@Strain 27.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.04 MPa
@Strain 36.9 %,
Temperature 100 °C		5082 psi
@Strain 36.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.05 MPa
@Strain 4.70 %,
Temperature 60.0 °C		5084 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.06 MPa
@Strain 28.9 %,
Temperature 80.0 °C		5085 psi
@Strain 28.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.14 MPa
@Strain 29.9 %,
Temperature 80.0 °C		5097 psi
@Strain 29.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.14 MPa
@Strain 13.0 %,
Temperature 60.0 °C		5097 psi
@Strain 13.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.15 MPa
@Strain 37.9 %,
Temperature 100 °C		5098 psi
@Strain 37.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.21 MPa
@Strain 30.9 %,
Temperature 80.0 °C		5107 psi
@Strain 30.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.22 MPa
@Strain 38.9 %,
Temperature 100 °C		5108 psi
@Strain 38.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.22 MPa
@Strain 4.80 %,
Temperature 60.0 °C		5108 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.25 MPa
@Strain 31.9 %,
Temperature 80.0 °C		5113 psi
@Strain 31.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.29 MPa
@Strain 39.9 %,
Temperature 100 °C		5118 psi
@Strain 39.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.3 MPa
@Strain 32.9 %,
Temperature 80.0 °C		5120 psi
@Strain 32.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.3 MPa
@Strain 49.9 %,
Temperature 80.0 °C		5120 psi
@Strain 49.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.3 MPa
@Strain 50.0 %,
Temperature 80.0 °C		5120 psi
@Strain 50.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.33 MPa
@Strain 33.9 %,
Temperature 80.0 °C		5124 psi
@Strain 33.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.33 MPa
@Strain 14.0 %,
Temperature 80.0 °C		5124 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.34 MPa
@Strain 47.9 %,
Temperature 80.0 °C		5126 psi
@Strain 47.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.34 MPa
@Strain 48.9 %,
Temperature 80.0 °C		5126 psi
@Strain 48.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.35 MPa
@Strain 34.9 %,
Temperature 80.0 °C		5127 psi
@Strain 34.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.37 MPa
@Strain 45.9 %,
Temperature 80.0 °C		5130 psi
@Strain 45.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.39 MPa
@Strain 44.9 %,
Temperature 80.0 °C		5133 psi
@Strain 44.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.39 MPa
@Strain 42.9 %,
Temperature 80.0 °C		5133 psi
@Strain 42.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.39 MPa
@Strain 35.9 %,
Temperature 80.0 °C		5133 psi
@Strain 35.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.39 MPa
@Strain 36.9 %,
Temperature 80.0 °C		5133 psi
@Strain 36.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.39 MPa
@Strain 40.9 %,
Temperature 100 °C		5133 psi
@Strain 40.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.4 MPa
@Strain 43.9 %,
Temperature 80.0 °C		5130 psi
@Strain 43.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 46.9 %,
Temperature 80.0 °C		5130 psi
@Strain 46.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.41 MPa
@Strain 38.9 %,
Temperature 80.0 °C		5136 psi
@Strain 38.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.41 MPa
@Strain 40.9 %,
Temperature 80.0 °C		5136 psi
@Strain 40.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.42 MPa
@Strain 39.9 %,
Temperature 80.0 °C		5137 psi
@Strain 39.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.42 MPa
@Strain 37.9 %,
Temperature 80.0 °C		5137 psi
@Strain 37.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.43 MPa
@Strain 41.9 %,
Temperature 80.0 °C		5139 psi
@Strain 41.9 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.43 MPa
@Strain 41.9 %,
Temperature 100 °C		5139 psi
@Strain 41.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.51 MPa
@Strain 42.9 %,
Temperature 100 °C		5150 psi
@Strain 42.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.55 MPa
@Strain 43.9 %,
Temperature 100 °C		5156 psi
@Strain 43.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.56 MPa
@Strain 4.90 %,
Temperature 60.0 °C		5158 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.6 MPa
@Strain 44.9 %,
Temperature 100 °C		5160 psi
@Strain 44.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.63 MPa
@Strain 45.9 %,
Temperature 100 °C		5168 psi
@Strain 45.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.67 MPa
@Strain 46.9 %,
Temperature 100 °C		5174 psi
@Strain 46.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.75 MPa
@Strain 47.9 %,
Temperature 100 °C		5185 psi
@Strain 47.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.76 MPa
@Strain 48.9 %,
Temperature 100 °C		5187 psi
@Strain 48.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.8 MPa
@Strain 49.9 %,
Temperature 100 °C		5190 psi
@Strain 49.9 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.8 MPa
@Strain 50.0 %,
Temperature 100 °C		5190 psi
@Strain 50.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.88 MPa
@Strain 14.0 %,
Temperature 60.0 °C		5204 psi
@Strain 14.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.11 MPa
@Strain 15.0 %,
Temperature 80.0 °C		5237 psi
@Strain 15.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 36.15 MPa
@Strain 1.10 %,
Temperature 0.000 °C		5243 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 36.27 MPa
@Strain 5.90 %,
Temperature 23.0 °C		5261 psi
@Strain 5.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 36.27 MPa
@Strain 1.10 %,
Temperature -40.0 °C		5261 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 36.34 MPa
@Strain 5.40 %,
Temperature 60.0 °C		5271 psi
@Strain 5.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.52 MPa
@Strain 15.0 %,
Temperature 60.0 °C		5297 psi
@Strain 15.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.75 MPa
@Strain 1.30 %,
Temperature 0.000 °C		5330 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 36.79 MPa
@Strain 16.0 %,
Temperature 80.0 °C		5336 psi
@Strain 16.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.13 MPa
@Strain 16.0 %,
Temperature 60.0 °C		5385 psi
@Strain 16.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.35 MPa
@Strain 6.40 %,
Temperature 23.0 °C		5417 psi
@Strain 6.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.36 MPa
@Strain 5.90 %,
Temperature 60.0 °C		5419 psi
@Strain 5.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.41 MPa
@Strain 17.0 %,
Temperature 80.0 °C		5426 psi
@Strain 17.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.48 MPa
@Strain 1.00 %,
Temperature -40.0 °C		5436 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 37.49 MPa
@Strain 1.20 %,
Temperature 23.0 °C		5437 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 37.63 MPa
@Strain 17.0 %,
Temperature 60.0 °C		5458 psi
@Strain 17.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 37.96 MPa
@Strain 18.0 %,
Temperature 80.0 °C		5506 psi
@Strain 18.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.06 MPa
@Strain 18.0 %,
Temperature 60.0 °C		5520 psi
@Strain 18.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.15 MPa
@Strain 6.40 %,
Temperature 60.0 °C		5533 psi
@Strain 6.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.4 MPa
@Strain 19.0 %,
Temperature 80.0 °C		5570 psi
@Strain 19.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.44 MPa
@Strain 19.0 %,
Temperature 60.0 °C		5575 psi
@Strain 19.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.47 MPa
@Strain 6.90 %,
Temperature 23.0 °C		5580 psi
@Strain 6.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.79 MPa
@Strain 20.0 %,
Temperature 60.0 °C		5626 psi
@Strain 20.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.86 MPa
@Strain 20.0 %,
Temperature 80.0 °C		5636 psi
@Strain 20.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.93 MPa
@Strain 6.90 %,
Temperature 60.0 °C		5646 psi
@Strain 6.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.96 MPa
@Strain 1.20 %,
Temperature 0.000 °C		5651 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 39.05 MPa
@Strain 21.0 %,
Temperature 60.0 °C		5664 psi
@Strain 21.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.19 MPa
@Strain 1.40 %,
Temperature 0.000 °C		5684 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 39.25 MPa
@Strain 22.0 %,
Temperature 60.0 °C		5693 psi
@Strain 22.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.26 MPa
@Strain 21.0 %,
Temperature 80.0 °C		5694 psi
@Strain 21.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.48 MPa
@Strain 23.0 %,
Temperature 60.0 °C		5726 psi
@Strain 23.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.49 MPa
@Strain 1.20 %,
Temperature -40.0 °C		5728 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 39.57 MPa
@Strain 22.0 %,
Temperature 80.0 °C		5739 psi
@Strain 22.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.6 MPa
@Strain 7.40 %,
Temperature 23.0 °C		5740 psi
@Strain 7.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.65 MPa
@Strain 24.0 %,
Temperature 60.0 °C		5751 psi
@Strain 24.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.7 MPa
@Strain 7.40 %,
Temperature 60.0 °C		5760 psi
@Strain 7.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.73 MPa
@Strain 25.0 %,
Temperature 60.0 °C		5762 psi
@Strain 25.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.9 MPa
@Strain 23.0 %,
Temperature 80.0 °C		5790 psi
@Strain 23.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 39.92 MPa
@Strain 26.0 %,
Temperature 60.0 °C		5790 psi
@Strain 26.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.02 MPa
@Strain 50.0 %,
Temperature 60.0 °C		5804 psi
@Strain 50.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.04 MPa
@Strain 27.0 %,
Temperature 60.0 °C		5807 psi
@Strain 27.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.05 MPa
@Strain 49.0 %,
Temperature 60.0 °C		5809 psi
@Strain 49.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.09 MPa
@Strain 48.0 %,
Temperature 60.0 °C		5815 psi
@Strain 48.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.12 MPa
@Strain 28.0 %,
Temperature 60.0 °C		5819 psi
@Strain 28.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.14 MPa
@Strain 47.0 %,
Temperature 60.0 °C		5822 psi
@Strain 47.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.15 MPa
@Strain 46.0 %,
Temperature 60.0 °C		5823 psi
@Strain 46.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.17 MPa
@Strain 45.0 %,
Temperature 60.0 °C		5826 psi
@Strain 45.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.19 MPa
@Strain 24.0 %,
Temperature 80.0 °C		5829 psi
@Strain 24.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.19 MPa
@Strain 29.0 %,
Temperature 60.0 °C		5829 psi
@Strain 29.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.2 MPa
@Strain 44.0 %,
Temperature 60.0 °C		5830 psi
@Strain 44.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.24 MPa
@Strain 30.0 %,
Temperature 60.0 °C		5836 psi
@Strain 30.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.26 MPa
@Strain 42.0 %,
Temperature 60.0 °C		5839 psi
@Strain 42.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.26 MPa
@Strain 43.0 %,
Temperature 60.0 °C		5839 psi
@Strain 43.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.28 MPa
@Strain 31.0 %,
Temperature 60.0 °C		5842 psi
@Strain 31.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.29 MPa
@Strain 40.0 %,
Temperature 60.0 °C		5844 psi
@Strain 40.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 41.0 %,
Temperature 60.0 °C		5850 psi
@Strain 41.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 32.0 %,
Temperature 60.0 °C		5850 psi
@Strain 32.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.34 MPa
@Strain 33.0 %,
Temperature 60.0 °C		5851 psi
@Strain 33.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.34 MPa
@Strain 34.0 %,
Temperature 60.0 °C		5851 psi
@Strain 34.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.34 MPa
@Strain 38.0 %,
Temperature 60.0 °C		5851 psi
@Strain 38.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.35 MPa
@Strain 39.0 %,
Temperature 60.0 °C		5852 psi
@Strain 39.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.36 MPa
@Strain 37.0 %,
Temperature 60.0 °C		5854 psi
@Strain 37.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.37 MPa
@Strain 35.0 %,
Temperature 60.0 °C		5855 psi
@Strain 35.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 36.0 %,
Temperature 60.0 °C		5860 psi
@Strain 36.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.44 MPa
@Strain 7.90 %,
Temperature 60.0 °C		5865 psi
@Strain 7.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.45 MPa
@Strain 1.30 %,
Temperature 23.0 °C		5867 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 40.46 MPa
@Strain 25.0 %,
Temperature 80.0 °C		5868 psi
@Strain 25.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.51 MPa
@Strain 7.90 %,
Temperature 23.0 °C		5875 psi
@Strain 7.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 40.67 MPa
@Strain 26.0 %,
Temperature 80.0 °C		5899 psi
@Strain 26.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.94 MPa
@Strain 27.0 %,
Temperature 80.0 °C		5938 psi
@Strain 27.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.13 MPa
@Strain 28.0 %,
Temperature 80.0 °C		5965 psi
@Strain 28.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.14 MPa
@Strain 8.40 %,
Temperature 60.0 °C		5967 psi
@Strain 8.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.16 MPa
@Strain 1.10 %,
Temperature -40.0 °C		5970 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 41.23 MPa
@Strain 8.40 %,
Temperature 23.0 °C		5980 psi
@Strain 8.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.33 MPa
@Strain 29.0 %,
Temperature 80.0 °C		5994 psi
@Strain 29.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.37 MPa
@Strain 1.50 %,
Temperature 0.000 °C		6000 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 41.53 MPa
@Strain 30.0 %,
Temperature 80.0 °C		6023 psi
@Strain 30.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.66 MPa
@Strain 1.30 %,
Temperature 0.000 °C		6042 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 41.67 MPa
@Strain 31.0 %,
Temperature 80.0 °C		6044 psi
@Strain 31.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.79 MPa
@Strain 32.0 %,
Temperature 80.0 °C		6061 psi
@Strain 32.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.85 MPa
@Strain 8.90 %,
Temperature 60.0 °C		6070 psi
@Strain 8.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.93 MPa
@Strain 33.0 %,
Temperature 80.0 °C		6081 psi
@Strain 33.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.03 MPa
@Strain 34.0 %,
Temperature 80.0 °C		6096 psi
@Strain 34.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.17 MPa
@Strain 35.0 %,
Temperature 80.0 °C		6116 psi
@Strain 35.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.17 MPa
@Strain 8.90 %,
Temperature 23.0 °C		6116 psi
@Strain 8.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 42.33 MPa
@Strain 36.0 %,
Temperature 80.0 °C		6139 psi
@Strain 36.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.39 MPa
@Strain 9.40 %,
Temperature 60.0 °C		6148 psi
@Strain 9.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.41 MPa
@Strain 37.0 %,
Temperature 80.0 °C		6151 psi
@Strain 37.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.54 MPa
@Strain 38.0 %,
Temperature 80.0 °C		6170 psi
@Strain 38.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.59 MPa
@Strain 39.0 %,
Temperature 80.0 °C		6177 psi
@Strain 39.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.7 MPa
@Strain 40.0 %,
Temperature 80.0 °C		6190 psi
@Strain 40.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.73 MPa
@Strain 41.0 %,
Temperature 80.0 °C		6197 psi
@Strain 41.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.81 MPa
@Strain 42.0 %,
Temperature 80.0 °C		6209 psi
@Strain 42.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.82 MPa
@Strain 1.30 %,
Temperature -40.0 °C		6211 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 42.91 MPa
@Strain 43.0 %,
Temperature 80.0 °C		6224 psi
@Strain 43.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.95 MPa
@Strain 44.0 %,
Temperature 80.0 °C		6229 psi
@Strain 44.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 42.99 MPa
@Strain 45.0 %,
Temperature 80.0 °C		6235 psi
@Strain 45.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.02 MPa
@Strain 9.90 %,
Temperature 60.0 °C		6240 psi
@Strain 9.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.03 MPa
@Strain 46.0 %,
Temperature 80.0 °C		6241 psi
@Strain 46.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.06 MPa
@Strain 9.40 %,
Temperature 23.0 °C		6245 psi
@Strain 9.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.11 MPa
@Strain 47.0 %,
Temperature 80.0 °C		6253 psi
@Strain 47.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.14 MPa
@Strain 48.0 %,
Temperature 80.0 °C		6257 psi
@Strain 48.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.18 MPa
@Strain 1.60 %,
Temperature 0.000 °C		6263 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 43.21 MPa
@Strain 1.40 %,
Temperature 23.0 °C		6267 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 43.24 MPa
@Strain 49.0 %,
Temperature 80.0 °C		6271 psi
@Strain 49.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.26 MPa
@Strain 50.0 %,
Temperature 80.0 °C		6274 psi
@Strain 50.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.81 MPa
@Strain 9.90 %,
Temperature 23.0 °C		6354 psi
@Strain 9.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.03 MPa
@Strain 1.20 %,
Temperature -40.0 °C		6386 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 44.25 MPa
@Strain 10.9 %,
Temperature 60.0 °C		6418 psi
@Strain 10.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 44.72 MPa
@Strain 1.40 %,
Temperature 0.000 °C		6486 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 44.76 MPa
@Strain 1.70 %,
Temperature 0.000 °C		6492 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 45.11 MPa
@Strain 10.9 %,
Temperature 23.0 °C		6543 psi
@Strain 10.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.26 MPa
@Strain 1.40 %,
Temperature -40.0 °C		6564 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 45.37 MPa
@Strain 1.50 %,
Temperature 23.0 °C		6580 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 45.61 MPa
@Strain 11.9 %,
Temperature 60.0 °C		6615 psi
@Strain 11.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.51 MPa
@Strain 11.9 %,
Temperature 23.0 °C		6746 psi
@Strain 11.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.67 MPa
@Strain 12.9 %,
Temperature 60.0 °C		6769 psi
@Strain 12.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.76 MPa
@Strain 1.80 %,
Temperature 0.000 °C		6782 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 47.47 MPa
@Strain 1.30 %,
Temperature -40.0 °C		6885 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 47.55 MPa
@Strain 12.9 %,
Temperature 23.0 °C		6897 psi
@Strain 12.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.59 MPa
@Strain 13.9 %,
Temperature 60.0 °C		6902 psi
@Strain 13.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.84 MPa
@Strain 1.50 %,
Temperature 0.000 °C		6939 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 48.17 MPa
@Strain 1.50 %,
Temperature -40.0 °C		6986 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 48.27 MPa
@Strain 1.90 %,
Temperature 0.000 °C		7001 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.41 MPa
@Strain 14.9 %,
Temperature 60.0 °C		7021 psi
@Strain 14.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.51 MPa
@Strain 13.9 %,
Temperature 23.0 °C		7036 psi
@Strain 13.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.79 MPa
@Strain 1.60 %,
Temperature 23.0 °C		7076 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.13 MPa
@Strain 15.9 %,
Temperature 60.0 °C		7126 psi
@Strain 15.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.31 MPa
@Strain 14.9 %,
Temperature 23.0 °C		7152 psi
@Strain 14.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.86 MPa
@Strain 16.9 %,
Temperature 60.0 °C		7232 psi
@Strain 16.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.04 MPa
@Strain 2.00 %,
Temperature 0.000 °C		7258 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 50.05 MPa
@Strain 15.9 %,
Temperature 23.0 °C		7259 psi
@Strain 15.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.33 MPa
@Strain 1.40 %,
Temperature -40.0 °C		7300 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 50.43 MPa
@Strain 17.9 %,
Temperature 60.0 °C		7314 psi
@Strain 17.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 50.43 MPa
@Strain 1.60 %,
Temperature 0.000 °C		7314 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.69 MPa
@Strain 16.9 %,
Temperature 23.0 °C		7352 psi
@Strain 16.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.93 MPa
@Strain 18.9 %,
Temperature 60.0 °C		7387 psi
@Strain 18.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.16 MPa
@Strain 1.60 %,
Temperature -40.0 °C		7420 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 51.22 MPa
@Strain 17.9 %,
Temperature 23.0 °C		7429 psi
@Strain 17.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.22 MPa
@Strain 1.70 %,
Temperature 23.0 °C		7429 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 51.35 MPa
@Strain 19.9 %,
Temperature 60.0 °C		7448 psi
@Strain 19.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.67 MPa
@Strain 2.10 %,
Temperature 0.000 °C		7494 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 51.7 MPa
@Strain 18.9 %,
Temperature 23.0 °C		7500 psi
@Strain 18.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.77 MPa
@Strain 20.9 %,
Temperature 60.0 °C		7509 psi
@Strain 20.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.08 MPa
@Strain 19.9 %,
Temperature 23.0 °C		7554 psi
@Strain 19.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.1 MPa
@Strain 21.9 %,
Temperature 60.0 °C		7560 psi
@Strain 21.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.35 MPa
@Strain 22.9 %,
Temperature 60.0 °C		7593 psi
@Strain 22.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.45 MPa
@Strain 20.9 %,
Temperature 23.0 °C		7607 psi
@Strain 20.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.66 MPa
@Strain 23.9 %,
Temperature 60.0 °C		7638 psi
@Strain 23.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.75 MPa
@Strain 21.9 %,
Temperature 23.0 °C		7651 psi
@Strain 21.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.84 MPa
@Strain 49.9 %,
Temperature 23.0 °C		7664 psi
@Strain 49.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.85 MPa
@Strain 50.0 %,
Temperature 23.0 °C		7665 psi
@Strain 50.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.86 MPa
@Strain 24.9 %,
Temperature 60.0 °C		7667 psi
@Strain 24.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.87 MPa
@Strain 48.9 %,
Temperature 23.0 °C		7668 psi
@Strain 48.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.87 MPa
@Strain 2.20 %,
Temperature 0.000 °C		7668 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 52.95 MPa
@Strain 47.9 %,
Temperature 23.0 °C		7680 psi
@Strain 47.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.97 MPa
@Strain 22.9 %,
Temperature 23.0 °C		7683 psi
@Strain 22.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.04 MPa
@Strain 46.9 %,
Temperature 23.0 °C		7693 psi
@Strain 46.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.05 MPa
@Strain 25.9 %,
Temperature 60.0 °C		7694 psi
@Strain 25.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.11 MPa
@Strain 45.9 %,
Temperature 23.0 °C		7703 psi
@Strain 45.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.17 MPa
@Strain 44.9 %,
Temperature 23.0 °C		7712 psi
@Strain 44.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.19 MPa
@Strain 23.9 %,
Temperature 23.0 °C		7715 psi
@Strain 23.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.2 MPa
@Strain 43.9 %,
Temperature 23.0 °C		7720 psi
@Strain 43.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.24 MPa
@Strain 26.9 %,
Temperature 60.0 °C		7722 psi
@Strain 26.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.27 MPa
@Strain 42.9 %,
Temperature 23.0 °C		7726 psi
@Strain 42.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.3 MPa
@Strain 1.70 %,
Temperature 0.000 °C		7730 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 53.33 MPa
@Strain 41.9 %,
Temperature 23.0 °C		7735 psi
@Strain 41.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.34 MPa
@Strain 24.9 %,
Temperature 23.0 °C		7736 psi
@Strain 24.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.35 MPa
@Strain 27.9 %,
Temperature 60.0 °C		7738 psi
@Strain 27.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.42 MPa
@Strain 40.9 %,
Temperature 23.0 °C		7748 psi
@Strain 40.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.47 MPa
@Strain 25.9 %,
Temperature 23.0 °C		7755 psi
@Strain 25.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.5 MPa
@Strain 39.9 %,
Temperature 23.0 °C		7760 psi
@Strain 39.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.51 MPa
@Strain 28.9 %,
Temperature 60.0 °C		7761 psi
@Strain 28.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.55 MPa
@Strain 38.9 %,
Temperature 23.0 °C		7767 psi
@Strain 38.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.56 MPa
@Strain 26.9 %,
Temperature 23.0 °C		7768 psi
@Strain 26.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.59 MPa
@Strain 29.9 %,
Temperature 60.0 °C		7773 psi
@Strain 29.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.59 MPa
@Strain 37.9 %,
Temperature 23.0 °C		7773 psi
@Strain 37.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.63 MPa
@Strain 36.9 %,
Temperature 23.0 °C		7778 psi
@Strain 36.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.63 MPa
@Strain 27.9 %,
Temperature 23.0 °C		7778 psi
@Strain 27.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.66 MPa
@Strain 35.9 %,
Temperature 23.0 °C		7783 psi
@Strain 35.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.66 MPa
@Strain 1.80 %,
Temperature 23.0 °C		7783 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 53.67 MPa
@Strain 30.9 %,
Temperature 60.0 °C		7784 psi
@Strain 30.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.67 MPa
@Strain 1.50 %,
Temperature -40.0 °C		7784 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 53.69 MPa
@Strain 34.9 %,
Temperature 23.0 °C		7787 psi
@Strain 34.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.7 MPa
@Strain 33.9 %,
Temperature 23.0 °C		7790 psi
@Strain 33.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.7 MPa
@Strain 28.9 %,
Temperature 23.0 °C		7790 psi
@Strain 28.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.73 MPa
@Strain 29.9 %,
Temperature 23.0 °C		7793 psi
@Strain 29.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.73 MPa
@Strain 30.9 %,
Temperature 23.0 °C		7793 psi
@Strain 30.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.74 MPa
@Strain 31.9 %,
Temperature 60.0 °C		7794 psi
@Strain 31.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.75 MPa
@Strain 31.9 %,
Temperature 23.0 °C		7796 psi
@Strain 31.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.76 MPa
@Strain 32.9 %,
Temperature 23.0 °C		7797 psi
@Strain 32.9 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.83 MPa
@Strain 32.9 %,
Temperature 60.0 °C		7807 psi
@Strain 32.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.88 MPa
@Strain 33.9 %,
Temperature 60.0 °C		7815 psi
@Strain 33.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.91 MPa
@Strain 34.9 %,
Temperature 60.0 °C		7819 psi
@Strain 34.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.96 MPa
@Strain 36.9 %,
Temperature 60.0 °C		7826 psi
@Strain 36.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.97 MPa
@Strain 35.9 %,
Temperature 60.0 °C		7828 psi
@Strain 35.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.0 MPa
@Strain 49.9 %,
Temperature 60.0 °C		7830 psi
@Strain 49.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.0 MPa
@Strain 50.0 %,
Temperature 60.0 °C		7830 psi
@Strain 50.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.01 MPa
@Strain 1.70 %,
Temperature -40.0 °C		7834 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 54.02 MPa
@Strain 48.9 %,
Temperature 60.0 °C		7835 psi
@Strain 48.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.05 MPa
@Strain 37.9 %,
Temperature 60.0 °C		7839 psi
@Strain 37.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.07 MPa
@Strain 38.9 %,
Temperature 60.0 °C		7842 psi
@Strain 38.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.07 MPa
@Strain 44.9 %,
Temperature 60.0 °C		7842 psi
@Strain 44.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.07 MPa
@Strain 41.9 %,
Temperature 60.0 °C		7842 psi
@Strain 41.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.07 MPa
@Strain 46.9 %,
Temperature 60.0 °C		7842 psi
@Strain 46.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.07 MPa
@Strain 47.9 %,
Temperature 60.0 °C		7842 psi
@Strain 47.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.08 MPa
@Strain 40.9 %,
Temperature 60.0 °C		7844 psi
@Strain 40.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.1 MPa
@Strain 45.9 %,
Temperature 60.0 °C		7850 psi
@Strain 45.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.1 MPa
@Strain 39.9 %,
Temperature 60.0 °C		7850 psi
@Strain 39.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.11 MPa
@Strain 43.9 %,
Temperature 60.0 °C		7848 psi
@Strain 43.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.12 MPa
@Strain 42.9 %,
Temperature 60.0 °C		7849 psi
@Strain 42.9 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.13 MPa
@Strain 2.30 %,
Temperature 0.000 °C		7851 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 55.19 MPa
@Strain 2.40 %,
Temperature 0.000 °C		8005 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 56.12 MPa
@Strain 1.80 %,
Temperature 0.000 °C		8140 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 56.17 MPa
@Strain 2.50 %,
Temperature 0.000 °C		8147 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 56.48 MPa
@Strain 1.90 %,
Temperature 23.0 °C		8192 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 56.63 MPa
@Strain 1.80 %,
Temperature -40.0 °C		8214 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 57.0 MPa
@Strain 1.60 %,
Temperature -40.0 °C		8270 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 57.06 MPa
@Strain 2.60 %,
Temperature 0.000 °C		8276 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.92 MPa
@Strain 2.70 %,
Temperature 0.000 °C		8401 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.65 MPa
@Strain 2.80 %,
Temperature 0.000 °C		8506 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.82 MPa
@Strain 2.00 %,
Temperature 23.0 °C		8531 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.96 MPa
@Strain 1.90 %,
Temperature 0.000 °C		8551 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 59.32 MPa
@Strain 2.90 %,
Temperature 0.000 °C		8604 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 59.37 MPa
@Strain 1.90 %,
Temperature -40.0 °C		8611 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 59.68 MPa
@Strain 1.70 %,
Temperature -40.0 °C		8656 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 59.99 MPa
@Strain 3.00 %,
Temperature 0.000 °C		8701 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.46 MPa
@Strain 3.10 %,
Temperature 0.000 °C		8769 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.83 MPa
@Strain 3.20 %,
Temperature 0.000 °C		8823 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.18 MPa
@Strain 2.10 %,
Temperature 23.0 °C		8873 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 61.25 MPa
@Strain 3.30 %,
Temperature 0.000 °C		8884 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.69 MPa
@Strain 3.40 %,
Temperature 0.000 °C		8947 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 61.73 MPa
@Strain 2.00 %,
Temperature 0.000 °C		8953 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 62.05 MPa
@Strain 42.9 %,
Temperature 23.0 °C		9000 psi
@Strain 42.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.08 MPa
@Strain 3.50 %,
Temperature 0.000 °C		9004 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.19 MPa
@Strain 2.00 %,
Temperature -40.0 °C		9020 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 62.22 MPa
@Strain 3.60 %,
Temperature 0.000 °C		9024 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.29 MPa
@Strain 1.80 %,
Temperature -40.0 °C		9034 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 62.56 MPa
@Strain 39.9 %,
Temperature 23.0 °C		9074 psi
@Strain 39.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.59 MPa
@Strain 3.70 %,
Temperature 0.000 °C		9078 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.72 MPa
@Strain 38.9 %,
Temperature 23.0 °C		9097 psi
@Strain 38.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.86 MPa
@Strain 3.80 %,
Temperature 0.000 °C		9117 psi
@Strain 3.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.99 MPa
@Strain 41.9 %,
Temperature 23.0 °C		9136 psi
@Strain 41.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 63.05 MPa
@Strain 40.9 %,
Temperature 23.0 °C		9145 psi
@Strain 40.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 63.17 MPa
@Strain 3.90 %,
Temperature 0.000 °C		9162 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.31 MPa
@Strain 4.00 %,
Temperature 0.000 °C		9182 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.41 MPa
@Strain 2.20 %,
Temperature 23.0 °C		9197 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 63.53 MPa
@Strain 4.10 %,
Temperature 0.000 °C		9214 psi
@Strain 4.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.76 MPa
@Strain 4.20 %,
Temperature 0.000 °C		9248 psi
@Strain 4.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.93 MPa
@Strain 4.30 %,
Temperature 0.000 °C		9272 psi
@Strain 4.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.07 MPa
@Strain 4.40 %,
Temperature 0.000 °C		9293 psi
@Strain 4.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.26 MPa
@Strain 4.50 %,
Temperature 0.000 °C		9320 psi
@Strain 4.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.36 MPa
@Strain 2.10 %,
Temperature 0.000 °C		9335 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 64.51 MPa
@Strain 4.60 %,
Temperature 0.000 °C		9356 psi
@Strain 4.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.71 MPa
@Strain 4.70 %,
Temperature 0.000 °C		9385 psi
@Strain 4.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.79 MPa
@Strain 4.80 %,
Temperature 0.000 °C		9397 psi
@Strain 4.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.79 MPa
@Strain 2.10 %,
Temperature -40.0 °C		9397 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 64.99 MPa
@Strain 4.90 %,
Temperature 0.000 °C		9426 psi
@Strain 4.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.1 MPa
@Strain 5.00 %,
Temperature 0.000 °C		9440 psi
@Strain 5.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.4 MPa
@Strain 1.90 %,
Temperature -40.0 °C		9490 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 65.58 MPa
@Strain 2.30 %,
Temperature 23.0 °C		9512 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 65.7 MPa
@Strain 5.50 %,
Temperature 0.000 °C		9530 psi
@Strain 5.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.77 MPa
@Strain 37.9 %,
Temperature 23.0 °C		9539 psi
@Strain 37.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.54 MPa
@Strain 6.00 %,
Temperature 0.000 °C		9651 psi
@Strain 6.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.77 MPa
@Strain 2.20 %,
Temperature 0.000 °C		9684 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 67.28 MPa
@Strain 6.50 %,
Temperature 0.000 °C		9758 psi
@Strain 6.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.3 MPa
@Strain 2.20 %,
Temperature -40.0 °C		9760 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 67.73 MPa
@Strain 2.40 %,
Temperature 23.0 °C		9823 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 67.92 MPa
@Strain 7.00 %,
Temperature 0.000 °C		9851 psi
@Strain 7.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.96 MPa
@Strain 2.00 %,
Temperature -40.0 °C		9857 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 68.65 MPa
@Strain 7.50 %,
Temperature 0.000 °C		9957 psi
@Strain 7.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.17 MPa
@Strain 2.30 %,
Temperature 0.000 °C		10030 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 69.32 MPa
@Strain 8.00 %,
Temperature 0.000 °C		10050 psi
@Strain 8.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.71 MPa
@Strain 2.30 %,
Temperature -40.0 °C		10110 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 69.76 MPa
@Strain 2.50 %,
Temperature 23.0 °C		10120 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 69.76 MPa
@Strain 36.9 %,
Temperature 23.0 °C		10120 psi
@Strain 36.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 69.85 MPa
@Strain 8.50 %,
Temperature 0.000 °C		10130 psi
@Strain 8.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.94 MPa
@Strain 2.10 %,
Temperature -40.0 °C		10140 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 70.41 MPa
@Strain 9.00 %,
Temperature 0.000 °C		10210 psi
@Strain 9.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.88 MPa
@Strain 9.50 %,
Temperature 0.000 °C		10280 psi
@Strain 9.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.43 MPa
@Strain 10.0 %,
Temperature 0.000 °C		10360 psi
@Strain 10.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 71.53 MPa
@Strain 2.40 %,
Temperature 0.000 °C		10370 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 71.68 MPa
@Strain 2.60 %,
Temperature 23.0 °C		10400 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.3 MPa
@Strain 11.0 %,
Temperature 0.000 °C		10500 psi
@Strain 11.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.36 MPa
@Strain 2.40 %,
Temperature -40.0 °C		10490 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 72.42 MPa
@Strain 2.20 %,
Temperature -40.0 °C		10500 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 72.82 MPa
@Strain 35.9 %,
Temperature 23.0 °C		10560 psi
@Strain 35.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.22 MPa
@Strain 2.70 %,
Temperature 23.0 °C		10620 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.38 MPa
@Strain 23.0 %,
Temperature 0.000 °C		10640 psi
@Strain 23.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 73.39 MPa
@Strain 12.0 %,
Temperature 0.000 °C		10640 psi
@Strain 12.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.85 MPa
@Strain 2.50 %,
Temperature 0.000 °C		10710 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 74.2 MPa
@Strain 13.0 %,
Temperature 0.000 °C		10800 psi
@Strain 13.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.3 MPa
@Strain 50.0 %,
Temperature 0.000 °C		10800 psi
@Strain 50.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.47 MPa
@Strain 49.0 %,
Temperature 0.000 °C		10800 psi
@Strain 49.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.64 MPa
@Strain 48.0 %,
Temperature 0.000 °C		10830 psi
@Strain 48.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.7 MPa
@Strain 2.80 %,
Temperature 23.0 °C		10800 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 74.71 MPa
@Strain 2.30 %,
Temperature -40.0 °C		10840 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 74.76 MPa
@Strain 2.50 %,
Temperature -40.0 °C		10840 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 74.9 MPa
@Strain 47.0 %,
Temperature 0.000 °C		10900 psi
@Strain 47.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 74.92 MPa
@Strain 14.0 %,
Temperature 0.000 °C		10870 psi
@Strain 14.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.1 MPa
@Strain 34.9 %,
Temperature 23.0 °C		10900 psi
@Strain 34.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.15 MPa
@Strain 46.0 %,
Temperature 0.000 °C		10900 psi
@Strain 46.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.29 MPa
@Strain 24.0 %,
Temperature 0.000 °C		10920 psi
@Strain 24.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.43 MPa
@Strain 45.0 %,
Temperature 0.000 °C		10940 psi
@Strain 45.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.52 MPa
@Strain 15.0 %,
Temperature 0.000 °C		10950 psi
@Strain 15.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.6 MPa
@Strain 44.0 %,
Temperature 0.000 °C		11000 psi
@Strain 44.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.61 MPa
@Strain 29.0 %,
Temperature 0.000 °C		10970 psi
@Strain 29.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 75.76 MPa
@Strain 43.0 %,
Temperature 0.000 °C		10990 psi
@Strain 43.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.87 MPa
@Strain 42.0 %,
Temperature 0.000 °C		11000 psi
@Strain 42.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.0 MPa
@Strain 16.0 %,
Temperature 0.000 °C		11000 psi
@Strain 16.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.05 MPa
@Strain 2.60 %,
Temperature 0.000 °C		11030 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.13 MPa
@Strain 41.0 %,
Temperature 0.000 °C		11040 psi
@Strain 41.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.33 MPa
@Strain 40.0 %,
Temperature 0.000 °C		11070 psi
@Strain 40.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.33 MPa
@Strain 2.90 %,
Temperature 23.0 °C		11070 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.34 MPa
@Strain 17.0 %,
Temperature 0.000 °C		11070 psi
@Strain 17.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.36 MPa
@Strain 28.0 %,
Temperature 0.000 °C		11080 psi
@Strain 28.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.4 MPa
@Strain 26.0 %,
Temperature 0.000 °C		11100 psi
@Strain 26.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.49 MPa
@Strain 27.0 %,
Temperature 0.000 °C		11090 psi
@Strain 27.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.54 MPa
@Strain 18.0 %,
Temperature 0.000 °C		11100 psi
@Strain 18.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.54 MPa
@Strain 39.0 %,
Temperature 0.000 °C		11100 psi
@Strain 39.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.55 MPa
@Strain 2.40 %,
Temperature -40.0 °C		11100 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 76.63 MPa
@Strain 38.0 %,
Temperature 0.000 °C		11110 psi
@Strain 38.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.63 MPa
@Strain 36.0 %,
Temperature 0.000 °C		11110 psi
@Strain 36.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.64 MPa
@Strain 37.0 %,
Temperature 0.000 °C		11120 psi
@Strain 37.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.71 MPa
@Strain 33.9 %,
Temperature 23.0 °C		11130 psi
@Strain 33.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.77 MPa
@Strain 35.0 %,
Temperature 0.000 °C		11130 psi
@Strain 35.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.8 MPa
@Strain 19.0 %,
Temperature 0.000 °C		11100 psi
@Strain 19.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 76.81 MPa
@Strain 25.0 %,
Temperature 0.000 °C		11140 psi
@Strain 25.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.9 MPa
@Strain 2.60 %,
Temperature -40.0 °C		11200 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 76.92 MPa
@Strain 34.0 %,
Temperature 0.000 °C		11160 psi
@Strain 34.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.02 MPa
@Strain 20.0 %,
Temperature 0.000 °C		11170 psi
@Strain 20.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.06 MPa
@Strain 33.0 %,
Temperature 0.000 °C		11180 psi
@Strain 33.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.2 MPa
@Strain 21.0 %,
Temperature 0.000 °C		11200 psi
@Strain 21.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.21 MPa
@Strain 32.0 %,
Temperature 0.000 °C		11200 psi
@Strain 32.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.43 MPa
@Strain 31.0 %,
Temperature 0.000 °C		11230 psi
@Strain 31.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.46 MPa
@Strain 22.0 %,
Temperature 0.000 °C		11230 psi
@Strain 22.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.62 MPa
@Strain 30.0 %,
Temperature 0.000 °C		11260 psi
@Strain 30.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.71 MPa
@Strain 23.0 %,
Temperature 0.000 °C		11270 psi
@Strain 23.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.74 MPa
@Strain 29.0 %,
Temperature 0.000 °C		11280 psi
@Strain 29.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.76 MPa
@Strain 32.9 %,
Temperature 23.0 °C		11280 psi
@Strain 32.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 77.78 MPa
@Strain 28.0 %,
Temperature 0.000 °C		11280 psi
@Strain 28.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.85 MPa
@Strain 27.0 %,
Temperature 0.000 °C		11290 psi
@Strain 27.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.85 MPa
@Strain 25.0 %,
Temperature 0.000 °C		11290 psi
@Strain 25.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.87 MPa
@Strain 24.0 %,
Temperature 0.000 °C		11290 psi
@Strain 24.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.88 MPa
@Strain 26.0 %,
Temperature 0.000 °C		11300 psi
@Strain 26.0 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.88 MPa
@Strain 22.0 %,
Temperature 0.000 °C		11300 psi
@Strain 22.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.99 MPa
@Strain 3.00 %,
Temperature 23.0 °C		11310 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.2 MPa
@Strain 2.70 %,
Temperature 0.000 °C		11300 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 78.43 MPa
@Strain 31.9 %,
Temperature 23.0 °C		11380 psi
@Strain 31.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.7 MPa
@Strain 2.50 %,
Temperature -40.0 °C		11400 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 79.0 MPa
@Strain 30.9 %,
Temperature 23.0 °C		11500 psi
@Strain 30.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.18 MPa
@Strain 3.10 %,
Temperature 23.0 °C		11480 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.21 MPa
@Strain 2.70 %,
Temperature -40.0 °C		11490 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 79.42 MPa
@Strain 29.9 %,
Temperature 23.0 °C		11520 psi
@Strain 29.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.75 MPa
@Strain 28.9 %,
Temperature 23.0 °C		11570 psi
@Strain 28.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.06 MPa
@Strain 2.80 %,
Temperature 0.000 °C		11610 psi
@Strain 2.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 80.07 MPa
@Strain 27.9 %,
Temperature 23.0 °C		11610 psi
@Strain 27.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.3 MPa
@Strain 3.20 %,
Temperature 23.0 °C		11600 psi
@Strain 3.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.33 MPa
@Strain 26.9 %,
Temperature 23.0 °C		11650 psi
@Strain 26.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.51 MPa
@Strain 25.9 %,
Temperature 23.0 °C		11680 psi
@Strain 25.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.64 MPa
@Strain 24.9 %,
Temperature 23.0 °C		11700 psi
@Strain 24.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.78 MPa
@Strain 23.9 %,
Temperature 23.0 °C		11720 psi
@Strain 23.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.79 MPa
@Strain 2.60 %,
Temperature -40.0 °C		11720 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 80.9 MPa
@Strain 22.9 %,
Temperature 23.0 °C		11700 psi
@Strain 22.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.01 MPa
@Strain 21.9 %,
Temperature 23.0 °C		11750 psi
@Strain 21.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.09 MPa
@Strain 20.9 %,
Temperature 23.0 °C		11760 psi
@Strain 20.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.11 MPa
@Strain 13.9 %,
Temperature 23.0 °C		11760 psi
@Strain 13.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.11 MPa
@Strain 11.9 %,
Temperature 23.0 °C		11760 psi
@Strain 11.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.14 MPa
@Strain 12.9 %,
Temperature 23.0 °C		11770 psi
@Strain 12.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.14 MPa
@Strain 15.9 %,
Temperature 23.0 °C		11770 psi
@Strain 15.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.15 MPa
@Strain 14.9 %,
Temperature 23.0 °C		11770 psi
@Strain 14.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.16 MPa
@Strain 10.9 %,
Temperature 23.0 °C		11770 psi
@Strain 10.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.16 MPa
@Strain 19.9 %,
Temperature 23.0 °C		11770 psi
@Strain 19.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.19 MPa
@Strain 16.9 %,
Temperature 23.0 °C		11780 psi
@Strain 16.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.19 MPa
@Strain 17.9 %,
Temperature 23.0 °C		11780 psi
@Strain 17.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.19 MPa
@Strain 18.9 %,
Temperature 23.0 °C		11780 psi
@Strain 18.9 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.24 MPa
@Strain 9.90 %,
Temperature 23.0 °C		11780 psi
@Strain 9.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.29 MPa
@Strain 9.40 %,
Temperature 23.0 °C		11790 psi
@Strain 9.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.31 MPa
@Strain 3.30 %,
Temperature 23.0 °C		11790 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.36 MPa
@Strain 8.90 %,
Temperature 23.0 °C		11800 psi
@Strain 8.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.49 MPa
@Strain 8.40 %,
Temperature 23.0 °C		11820 psi
@Strain 8.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.49 MPa
@Strain 2.80 %,
Temperature -40.0 °C		11820 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 81.67 MPa
@Strain 7.90 %,
Temperature 23.0 °C		11850 psi
@Strain 7.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 81.91 MPa
@Strain 2.90 %,
Temperature 0.000 °C		11880 psi
@Strain 2.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 81.97 MPa
@Strain 3.40 %,
Temperature 23.0 °C		11890 psi
@Strain 3.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.15 MPa
@Strain 6.90 %,
Temperature 23.0 °C		11910 psi
@Strain 6.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.46 MPa
@Strain 2.70 %,
Temperature -40.0 °C		11960 psi
@Strain 2.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 82.64 MPa
@Strain 3.50 %,
Temperature 23.0 °C		11990 psi
@Strain 3.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.02 MPa
@Strain 5.90 %,
Temperature 23.0 °C		12040 psi
@Strain 5.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.34 MPa
@Strain 3.60 %,
Temperature 23.0 °C		12090 psi
@Strain 3.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.73 MPa
@Strain 2.90 %,
Temperature -40.0 °C		12140 psi
@Strain 2.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 83.82 MPa
@Strain 3.70 %,
Temperature 23.0 °C		12160 psi
@Strain 3.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.82 MPa
@Strain 21.0 %,
Temperature 0.000 °C		12160 psi
@Strain 21.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 83.92 MPa
@Strain 3.00 %,
Temperature 0.000 °C		12170 psi
@Strain 3.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.23 MPa
@Strain 3.80 %,
Temperature 23.0 °C		12220 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.34 MPa
@Strain 4.90 %,
Temperature 23.0 °C		12230 psi
@Strain 4.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.43 MPa
@Strain 2.80 %,
Temperature -40.0 °C		12250 psi
@Strain 2.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 84.47 MPa
@Strain 4.80 %,
Temperature 23.0 °C		12250 psi
@Strain 4.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.47 MPa
@Strain 3.90 %,
Temperature 23.0 °C		12250 psi
@Strain 3.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.69 MPa
@Strain 4.00 %,
Temperature 23.0 °C		12280 psi
@Strain 4.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.69 MPa
@Strain 4.70 %,
Temperature 23.0 °C		12280 psi
@Strain 4.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.76 MPa
@Strain 4.60 %,
Temperature 23.0 °C		12290 psi
@Strain 4.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.81 MPa
@Strain 4.50 %,
Temperature 23.0 °C		12300 psi
@Strain 4.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.87 MPa
@Strain 4.10 %,
Temperature 23.0 °C		12310 psi
@Strain 4.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.87 MPa
@Strain 4.30 %,
Temperature 23.0 °C		12310 psi
@Strain 4.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.9 MPa
@Strain 4.20 %,
Temperature 23.0 °C		12300 psi
@Strain 4.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.92 MPa
@Strain 4.40 %,
Temperature 23.0 °C		12320 psi
@Strain 4.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 85.66 MPa
@Strain 3.10 %,
Temperature 0.000 °C		12420 psi
@Strain 3.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 85.89 MPa
@Strain 3.00 %,
Temperature -40.0 °C		12460 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 86.33 MPa
@Strain 2.90 %,
Temperature -40.0 °C		12520 psi
@Strain 2.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 87.27 MPa
@Strain 3.20 %,
Temperature 0.000 °C		12660 psi
@Strain 3.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.81 MPa
@Strain 3.00 %,
Temperature -40.0 °C		12740 psi
@Strain 3.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 88.02 MPa
@Strain 3.10 %,
Temperature -40.0 °C		12770 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 88.19 MPa
@Strain 20.0 %,
Temperature 0.000 °C		12790 psi
@Strain 20.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 88.85 MPa
@Strain 3.30 %,
Temperature 0.000 °C		12890 psi
@Strain 3.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.18 MPa
@Strain 3.10 %,
Temperature -40.0 °C		12930 psi
@Strain 3.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 89.91 MPa
@Strain 3.20 %,
Temperature -40.0 °C		13040 psi
@Strain 3.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 90.19 MPa
@Strain 3.40 %,
Temperature 0.000 °C		13080 psi
@Strain 3.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.51 MPa
@Strain 3.20 %,
Temperature -40.0 °C		13130 psi
@Strain 3.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 90.79 MPa
@Strain 19.0 %,
Temperature 0.000 °C		13170 psi
@Strain 19.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.43 MPa
@Strain 3.50 %,
Temperature 0.000 °C		13260 psi
@Strain 3.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.77 MPa
@Strain 3.30 %,
Temperature -40.0 °C		13310 psi
@Strain 3.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.85 MPa
@Strain 3.30 %,
Temperature -40.0 °C		13320 psi
@Strain 3.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 92.18 MPa
@Strain 18.0 %,
Temperature 0.000 °C		13370 psi
@Strain 18.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 92.64 MPa
@Strain 3.60 %,
Temperature 0.000 °C		13440 psi
@Strain 3.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.02 MPa
@Strain 17.0 %,
Temperature 0.000 °C		13490 psi
@Strain 17.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.05 MPa
@Strain 3.40 %,
Temperature -40.0 °C		13500 psi
@Strain 3.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.47 MPa
@Strain 16.0 %,
Temperature 0.000 °C		13560 psi
@Strain 16.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.79 MPa
@Strain 15.0 %,
Temperature 0.000 °C		13600 psi
@Strain 15.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.79 MPa
@Strain 3.40 %,
Temperature -40.0 °C		13600 psi
@Strain 3.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 93.9 MPa
@Strain 3.70 %,
Temperature 0.000 °C		13600 psi
@Strain 3.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.05 MPa
@Strain 14.0 %,
Temperature 0.000 °C		13640 psi
@Strain 14.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.22 MPa
@Strain 3.50 %,
Temperature -40.0 °C		13670 psi
@Strain 3.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 94.24 MPa
@Strain 13.0 %,
Temperature 0.000 °C		13670 psi
@Strain 13.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.39 MPa
@Strain 12.0 %,
Temperature 0.000 °C		13690 psi
@Strain 12.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.68 MPa
@Strain 11.0 %,
Temperature 0.000 °C		13730 psi
@Strain 11.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.88 MPa
@Strain 3.80 %,
Temperature 0.000 °C		13760 psi
@Strain 3.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.98 MPa
@Strain 10.0 %,
Temperature 0.000 °C		13780 psi
@Strain 10.0 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.18 MPa
@Strain 9.50 %,
Temperature 0.000 °C		13800 psi
@Strain 9.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.36 MPa
@Strain 3.60 %,
Temperature -40.0 °C		13830 psi
@Strain 3.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 95.45 MPa
@Strain 9.00 %,
Temperature 0.000 °C		13840 psi
@Strain 9.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.54 MPa
@Strain 3.50 %,
Temperature -40.0 °C		13860 psi
@Strain 3.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 95.68 MPa
@Strain 8.50 %,
Temperature 0.000 °C		13880 psi
@Strain 8.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.7 MPa
@Strain 3.90 %,
Temperature 0.000 °C		13900 psi
@Strain 3.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.09 MPa
@Strain 8.00 %,
Temperature 0.000 °C		13940 psi
@Strain 8.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.41 MPa
@Strain 4.00 %,
Temperature 0.000 °C		13980 psi
@Strain 4.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.47 MPa
@Strain 7.50 %,
Temperature 0.000 °C		13990 psi
@Strain 7.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.48 MPa
@Strain 3.70 %,
Temperature -40.0 °C		13990 psi
@Strain 3.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 96.93 MPa
@Strain 4.10 %,
Temperature 0.000 °C		14060 psi
@Strain 4.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.99 MPa
@Strain 7.00 %,
Temperature 0.000 °C		14070 psi
@Strain 7.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 97.05 MPa
@Strain 3.60 %,
Temperature -40.0 °C		14080 psi
@Strain 3.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 97.46 MPa
@Strain 3.80 %,
Temperature -40.0 °C		14140 psi
@Strain 3.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 97.5 MPa
@Strain 4.20 %,
Temperature 0.000 °C		14100 psi
@Strain 4.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 97.56 MPa
@Strain 6.50 %,
Temperature 0.000 °C		14150 psi
@Strain 6.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 97.92 MPa
@Strain 4.30 %,
Temperature 0.000 °C		14200 psi
@Strain 4.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 98.13 MPa
@Strain 6.00 %,
Temperature 0.000 °C		14230 psi
@Strain 6.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 98.37 MPa
@Strain 4.40 %,
Temperature 0.000 °C		14270 psi
@Strain 4.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 98.38 MPa
@Strain 3.90 %,
Temperature -40.0 °C		14270 psi
@Strain 3.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 98.69 MPa
@Strain 4.50 %,
Temperature 0.000 °C		14310 psi
@Strain 4.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 98.74 MPa
@Strain 3.70 %,
Temperature -40.0 °C		14320 psi
@Strain 3.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 98.83 MPa
@Strain 5.50 %,
Temperature 0.000 °C		14330 psi
@Strain 5.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 98.87 MPa
@Strain 4.60 %,
Temperature 0.000 °C		14340 psi
@Strain 4.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.01 MPa
@Strain 4.70 %,
Temperature 0.000 °C		14360 psi
@Strain 4.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.07 MPa
@Strain 4.80 %,
Temperature 0.000 °C		14370 psi
@Strain 4.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.07 MPa
@Strain 4.00 %,
Temperature -40.0 °C		14370 psi
@Strain 4.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 99.09 MPa
@Strain 4.90 %,
Temperature 0.000 °C		14370 psi
@Strain 4.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.09 MPa
@Strain 5.00 %,
Temperature 0.000 °C		14370 psi
@Strain 5.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.52 MPa
@Strain 34.0 %,
Temperature -40.0 °C		14430 psi
@Strain 34.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 99.69 MPa
@Strain 4.10 %,
Temperature -40.0 °C		14460 psi
@Strain 4.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 100.37 MPa
@Strain 3.80 %,
Temperature -40.0 °C		14557 psi
@Strain 3.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 100.61 MPa
@Strain 4.20 %,
Temperature -40.0 °C		14592 psi
@Strain 4.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 101.19 MPa
@Strain 4.30 %,
Temperature -40.0 °C		14676 psi
@Strain 4.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 101.72 MPa
@Strain 4.40 %,
Temperature -40.0 °C		14753 psi
@Strain 4.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 101.84 MPa
@Strain 3.90 %,
Temperature -40.0 °C		14771 psi
@Strain 3.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 102.39 MPa
@Strain 4.50 %,
Temperature -40.0 °C		14850 psi
@Strain 4.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 102.47 MPa
@Strain 33.0 %,
Temperature -40.0 °C		14862 psi
@Strain 33.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 102.81 MPa
@Strain 4.60 %,
Temperature -40.0 °C		14911 psi
@Strain 4.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 103.23 MPa
@Strain 4.70 %,
Temperature -40.0 °C		14972 psi
@Strain 4.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 103.28 MPa
@Strain 4.00 %,
Temperature -40.0 °C		14980 psi
@Strain 4.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 103.59 MPa
@Strain 4.80 %,
Temperature -40.0 °C		15024 psi
@Strain 4.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.06 MPa
@Strain 4.90 %,
Temperature -40.0 °C		15093 psi
@Strain 4.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.48 MPa
@Strain 5.00 %,
Temperature -40.0 °C		15154 psi
@Strain 5.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 104.57 MPa
@Strain 4.10 %,
Temperature -40.0 °C		15167 psi
@Strain 4.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 105.58 MPa
@Strain 5.50 %,
Temperature -40.0 °C		15313 psi
@Strain 5.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 105.77 MPa
@Strain 4.20 %,
Temperature -40.0 °C		15341 psi
@Strain 4.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 106.19 MPa
@Strain 32.0 %,
Temperature -40.0 °C		15402 psi
@Strain 32.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.73 MPa
@Strain 6.00 %,
Temperature -40.0 °C		15480 psi
@Strain 6.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 106.85 MPa
@Strain 4.30 %,
Temperature -40.0 °C		15497 psi
@Strain 4.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.32 MPa
@Strain 6.50 %,
Temperature -40.0 °C		15565 psi
@Strain 6.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.76 MPa
@Strain 7.00 %,
Temperature -40.0 °C		15629 psi
@Strain 7.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.86 MPa
@Strain 4.40 %,
Temperature -40.0 °C		15644 psi
@Strain 4.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.02 MPa
@Strain 7.50 %,
Temperature -40.0 °C		15667 psi
@Strain 7.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.26 MPa
@Strain 31.0 %,
Temperature -40.0 °C		15702 psi
@Strain 31.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.3 MPa
@Strain 8.00 %,
Temperature -40.0 °C		15710 psi
@Strain 8.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.47 MPa
@Strain 8.50 %,
Temperature -40.0 °C		15732 psi
@Strain 8.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.64 MPa
@Strain 9.00 %,
Temperature -40.0 °C		15757 psi
@Strain 9.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.71 MPa
@Strain 9.50 %,
Temperature -40.0 °C		15767 psi
@Strain 9.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.83 MPa
@Strain 10.0 %,
Temperature -40.0 °C		15784 psi
@Strain 10.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 108.98 MPa
@Strain 4.50 %,
Temperature -40.0 °C		15806 psi
@Strain 4.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 109.3 MPa
@Strain 11.0 %,
Temperature -40.0 °C		15850 psi
@Strain 11.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.52 MPa
@Strain 12.0 %,
Temperature -40.0 °C		15885 psi
@Strain 12.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.55 MPa
@Strain 30.0 %,
Temperature -40.0 °C		15889 psi
@Strain 30.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 109.99 MPa
@Strain 13.0 %,
Temperature -40.0 °C		15953 psi
@Strain 13.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.04 MPa
@Strain 4.60 %,
Temperature -40.0 °C		15960 psi
@Strain 4.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 110.67 MPa
@Strain 29.0 %,
Temperature -40.0 °C		16051 psi
@Strain 29.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 110.97 MPa
@Strain 14.0 %,
Temperature -40.0 °C		16095 psi
@Strain 14.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.04 MPa
@Strain 4.70 %,
Temperature -40.0 °C		16105 psi
@Strain 4.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.18 MPa
@Strain 24.0 %,
Temperature -40.0 °C		16125 psi
@Strain 24.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.54 MPa
@Strain 23.0 %,
Temperature -40.0 °C		16178 psi
@Strain 23.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.64 MPa
@Strain 28.0 %,
Temperature -40.0 °C		16192 psi
@Strain 28.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.81 MPa
@Strain 15.0 %,
Temperature -40.0 °C		16217 psi
@Strain 15.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.86 MPa
@Strain 4.80 %,
Temperature -40.0 °C		16224 psi
@Strain 4.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.12 MPa
@Strain 22.0 %,
Temperature -40.0 °C		16262 psi
@Strain 22.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.26 MPa
@Strain 16.0 %,
Temperature -40.0 °C		16282 psi
@Strain 16.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.26 MPa
@Strain 27.0 %,
Temperature -40.0 °C		16282 psi
@Strain 27.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.55 MPa
@Strain 17.0 %,
Temperature -40.0 °C		16324 psi
@Strain 17.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.62 MPa
@Strain 21.0 %,
Temperature -40.0 °C		16334 psi
@Strain 21.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.65 MPa
@Strain 4.90 %,
Temperature -40.0 °C		16339 psi
@Strain 4.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 112.73 MPa
@Strain 26.0 %,
Temperature -40.0 °C		16350 psi
@Strain 26.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.75 MPa
@Strain 18.0 %,
Temperature -40.0 °C		16353 psi
@Strain 18.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 112.89 MPa
@Strain 19.0 %,
Temperature -40.0 °C		16373 psi
@Strain 19.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113 MPa
@Strain 20.0 %,
Temperature -40.0 °C		16400 psi
@Strain 20.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.05 MPa
@Strain 25.0 %,
Temperature -40.0 °C		16397 psi
@Strain 25.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.05 MPa
@Strain 20.0 %,
Temperature -40.0 °C		16397 psi
@Strain 20.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.19 MPa
@Strain 21.0 %,
Temperature -40.0 °C		16417 psi
@Strain 21.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.33 MPa
@Strain 5.00 %,
Temperature -40.0 °C		16437 psi
@Strain 5.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.34 MPa
@Strain 22.0 %,
Temperature -40.0 °C		16439 psi
@Strain 22.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.38 MPa
@Strain 24.0 %,
Temperature -40.0 °C		16444 psi
@Strain 24.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.48 MPa
@Strain 19.0 %,
Temperature -40.0 °C		16459 psi
@Strain 19.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.5 MPa
@Strain 23.0 %,
Temperature -40.0 °C		16460 psi
@Strain 23.0 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 113.91 MPa
@Strain 18.0 %,
Temperature -40.0 °C		16521 psi
@Strain 18.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.38 MPa
@Strain 17.0 %,
Temperature -40.0 °C		16589 psi
@Strain 17.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.81 MPa
@Strain 16.0 %,
Temperature -40.0 °C		16652 psi
@Strain 16.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.28 MPa
@Strain 15.0 %,
Temperature -40.0 °C		16720 psi
@Strain 15.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.58 MPa
@Strain 5.50 %,
Temperature -40.0 °C		16763 psi
@Strain 5.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 115.8 MPa
@Strain 14.0 %,
Temperature -40.0 °C		16800 psi
@Strain 14.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 116.35 MPa
@Strain 13.0 %,
Temperature -40.0 °C		16875 psi
@Strain 13.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 117.01 MPa
@Strain 12.0 %,
Temperature -40.0 °C		16971 psi
@Strain 12.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 117.74 MPa
@Strain 11.0 %,
Temperature -40.0 °C		17077 psi
@Strain 11.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 117.98 MPa
@Strain 6.00 %,
Temperature -40.0 °C		17112 psi
@Strain 6.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 118.36 MPa
@Strain 10.0 %,
Temperature -40.0 °C		17167 psi
@Strain 10.0 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 118.73 MPa
@Strain 9.50 %,
Temperature -40.0 °C		17220 psi
@Strain 9.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 119.01 MPa
@Strain 9.00 %,
Temperature -40.0 °C		17261 psi
@Strain 9.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 119.05 MPa
@Strain 6.50 %,
Temperature -40.0 °C		17267 psi
@Strain 6.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 119.33 MPa
@Strain 8.50 %,
Temperature -40.0 °C		17307 psi
@Strain 8.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 119.49 MPa
@Strain 7.00 %,
Temperature -40.0 °C		17331 psi
@Strain 7.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 119.5 MPa
@Strain 8.00 %,
Temperature -40.0 °C		17330 psi
@Strain 8.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 119.63 MPa
@Strain 7.50 %,
Temperature -40.0 °C		17351 psi
@Strain 7.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Tensile Strength, Yield  55.0 MPa
@Temperature 23.0 °C		7980 psi
@Temperature 73.4 °F		50%RH; ISO 527
 85.0 MPa
@Temperature 23.0 °C		12300 psi
@Temperature 73.4 °F		DAM; ISO 527
Elongation at Break  20 %
@Temperature 23.0 °C		20 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 50 %
@Temperature 23.0 °C		50 %
@Temperature 73.4 °F		DAM; ASTM D638
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 >= 100 %
@Temperature 23.0 °C		>= 100 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 190 %
@Temperature 77.0 °C		190 %
@Temperature 171 °F		DAM; ASTM D638
 >= 250 %
@Temperature 23.0 °C		>= 250 %
@Temperature 73.4 °F		50%RH; ASTM D638
 >= 250 %
@Temperature 121 °C		>= 250 %
@Temperature 250 °F		DAM; ASTM D638
Elongation at Yield  4.5 %
@Temperature 23.0 °C		4.5 %
@Temperature 73.4 °F		DAM; ISO 527
 25 %
@Temperature 23.0 °C		25 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  1.40 GPa
@Temperature 23.0 °C		203 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 3.10 GPa
@Temperature 23.0 °C		450 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  0.414 GPa
@Temperature 130 °C		60.0 ksi
@Temperature 266 °F		DAM; ASTM D790
 0.415 GPa
@Temperature 121 °C		60.2 ksi
@Temperature 250 °F		50%RH; ASTM D790
 0.538 GPa
@Temperature 121 °C		78.0 ksi
@Temperature 250 °F		DAM; ASTM D790
 0.565 GPa
@Temperature 77.0 °C		81.9 ksi
@Temperature 171 °F		50%RH; ASTM D790
 1.10 GPa
@Temperature 77.0 °C		160 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.21 GPa
@Temperature 23.0 °C		175 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 1.30 GPa
@Temperature 23.0 °C		189 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 2.80 GPa
@Temperature 23.0 °C		406 ksi
@Temperature 73.4 °F		DAM; ISO 178
 2.83 GPa
@Temperature 23.0 °C		410 ksi
@Temperature 73.4 °F		DAM; ASTM D790
Shear Strength  65.0 MPa
@Temperature 23.0 °C		9430 psi
@Temperature 73.4 °F		50%RH; ASTM D732
 73.8 MPa
@Temperature 23.0 °C		10700 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.530 J/cm
@Temperature 23.0 °C		0.993 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 0.800 J/cm
@Temperature 23.0 °C		1.50 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
 1.30 J/cm
@Temperature 77.0 °C		2.44 ft-lb/in
@Temperature 171 °F		DAM; ASTM D256
 1.90 J/cm
@Temperature 77.0 °C		3.56 ft-lb/in
@Temperature 171 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  5.00 kJ/m²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 5.50 kJ/m²
@Temperature -40.0 °C		2.62 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 5.50 kJ/m²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 6.00 kJ/m²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 11.0 kJ/m²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  300 kJ/m²
@Temperature -30.0 °C		143 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 300 kJ/m²
@Temperature 23.0 °C		143 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 180/1U
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  35.0 J/cm²
@Temperature -30.0 °C		167 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  0.300 J/cm²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.300 J/cm²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.450 J/cm²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.550 J/cm²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.10 J/cm²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Impact Strength  440 kJ/m²
@Temperature 23.0 °C		209 ft-lb/in²
@Temperature 73.4 °F		DAM; Long specimen; ASTM D1822
 510 kJ/m²
@Temperature 121 °C		243 ft-lb/in²
@Temperature 250 °F		DAM; Long specimen; ASTM D1822
 NB
@Temperature 121 °C		NB
@Temperature 250 °F		50%RH; Long specimen; ASTM D1822
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+11 ohm-cm
@Temperature 23.0 °C		1.00e+11 ohm-cm
@Temperature 73.4 °F		50%RH; ASTM D257
 1.00e+11 ohm-cm
@Temperature 23.0 °C		1.00e+11 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+14 ohm-cm
@Temperature 23.0 °C		1.00e+14 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 1.00e+14 ohm-cm
@Temperature 23.0 °C		1.00e+14 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.4
@Frequency 100 Hz,
Temperature 23.0 °C		3.4
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.4
@Frequency 1000 Hz,
Temperature 23.0 °C		3.4
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.6
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.6
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 5.6
@Frequency 1000 Hz,
Temperature 23.0 °C		5.6
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 7.0
@Frequency 100 Hz,
Temperature 23.0 °C		7.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
Dissipation Factor  0.010
@Frequency 100 Hz,
Temperature 23.0 °C		0.010
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.010
@Frequency 1000 Hz,
Temperature 23.0 °C		0.010
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.060
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.060
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.15
@Frequency 1000 Hz,
Temperature 23.0 °C		0.15
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.20
@Frequency 100 Hz,
Temperature 23.0 °C		0.20
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
Comparative Tracking Index 600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; IEC 60112
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 200 °C392 °FDAM; ISO 75-1/-2
 210 °C410 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C149 °FDAM; ASTM D648
 70.0 °C158 °FDAM; ISO 75-1/-2
Glass Transition Temp, Tg 60.0 °C140 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  140 °C
@Thickness 0.710 mm		284 °F
@Thickness 0.0280 in		DAM; UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		DAM; UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical with Impact  95.0 °C
@Thickness 0.710 mm		203 °F
@Thickness 0.0280 in		DAM; UL 746B
 110 °C
@Thickness 3.00 mm		230 °F
@Thickness 0.118 in		DAM; UL 746B
 110 °C
@Thickness 1.50 mm		230 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical without Impact  115 °C
@Thickness 0.710 mm		239 °F
@Thickness 0.0280 in		DAM; UL 746B
 125 °C
@Thickness 3.00 mm		257 °F
@Thickness 0.118 in		DAM; UL 746B
 125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		DAM; UL 746B
Flammability, UL94  V-2
@Thickness 0.710 mm		V-2
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-2
@Thickness 0.710 mm		V-2
@Thickness 0.0280 in		DAM; UL94
 V-2
@Thickness 1.50 mm		V-2
@Thickness 0.0591 in		DAM; UL94
 V-2
@Thickness 3.00 mm		V-2
@Thickness 0.118 in		DAM; UL94
Oxygen Index 28 %28 %DAM; ISO 4589-1/-2
Glow Wire Test  725 °C
@Thickness 0.710 mm		1340 °F
@Thickness 0.0280 in		DAM; Ignition; IEC 60695-2-13
 725 °C
@Thickness 1.50 mm		1340 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 725 °C
@Thickness 3.00 mm		1340 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 850 °C
@Thickness 0.710 mm		1560 °F
@Thickness 0.0280 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 1.50 mm		1760 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 290 °C554 °FDAM; Optimum
 280 - 300 °C536 - 572 °FDAM
Mold Temperature 70.0 °C158 °FDAM; optimum
 50.0 - 90.0 °C122 - 194 °FDAM
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
 LubricantDAM
 Mold ReleaseDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesChemical Resistance, GoodDAM
 Cycle (Production), FastDAM
 Electrical Properties, GoodDAM
 Fatigue ResistantDAM
 Flow, HighDAM
 Fuel ResistantDAM
 Grease ResistantDAM
 Heat Aging Resistance, GoodDAM
 LubricatedDAM
 Mold Release, GoodDAM
 Moldability, GoodDAM
 Molding Cycle, FastDAM
 Oil ResistantDAM
 Processability, GoodDAM
 Wear Resistance, GoodDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryUnreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAutomotive ApplicationsDAM
 ConnectorsDAM
 Electrical/Electronic ApplicationsDAM
 FastenersDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45442.html

免责声明: 本文 DuPont Performance Polymers Zytel® 103FHS NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4