  4. DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66

DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66

DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66 物性表: DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.23
  • 缺口冲击强度: 0.48
  • 弯曲模量 [MPa]: 4.83
  • 热变形温度 [℃]: 258.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.22 g/cc1.22 g/ccDAM; ASTM D792
Density 1.23 g/cc0.0444 lb/in³DAM; ISO 1183
Filler Content 13 %13 %DAM
Linear Mold Shrinkage, Flow 0.0050 cm/cm
@Thickness 2.00 mm		0.0050 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
@Thickness 2.00 mm		0.010 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  75.0 MPa
@Temperature 23.0 °C		10900 psi
@Temperature 73.4 °F		50%RH; ISO 527
 120 MPa
@Temperature 23.0 °C		17400 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength 117 MPa
@Temperature 23.0 °C		17000 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  1.45 MPa
@Strain 0.100 %,
Temperature 150 °C		210 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 1.80 MPa
@Strain 0.100 %,
Temperature 150 °C		261 psi
@Strain 0.100 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 2.20 MPa
@Strain 0.100 %,
Temperature 120 °C		319 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.30 MPa
@Strain 0.100 %,
Temperature 120 °C		334 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.40 MPa
@Strain 0.100 %,
Temperature 100 °C		348 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 2.50 MPa
@Strain 0.100 %,
Temperature 80.0 °C		363 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.50 MPa
@Strain 0.100 %,
Temperature 100 °C		363 psi
@Strain 0.100 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 2.70 MPa
@Strain 0.100 %,
Temperature 80.0 °C		392 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.80 MPa
@Strain 0.100 %,
Temperature 60.0 °C		406 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 2.80 MPa
@Strain 0.100 %,
Temperature 60.0 °C		406 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 3.00 MPa
@Strain 0.100 %,
Temperature 23.0 °C		435 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.50 MPa
@Strain 0.200 %,
Temperature 150 °C		508 psi
@Strain 0.200 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.80 MPa
@Strain 0.200 %,
Temperature 150 °C		551 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 4.30 MPa
@Strain 0.200 %,
Temperature 120 °C		624 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 4.30 MPa
@Strain 0.100 %,
Temperature 0.000 °C		624 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 4.60 MPa
@Strain 0.200 %,
Temperature 120 °C		667 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.80 MPa
@Strain 0.200 %,
Temperature 100 °C		696 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 5.00 MPa
@Strain 0.200 %,
Temperature 80.0 °C		725 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.00 MPa
@Strain 0.200 %,
Temperature 100 °C		725 psi
@Strain 0.200 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 5.10 MPa
@Strain 0.300 %,
Temperature 150 °C		740 psi
@Strain 0.300 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.30 MPa
@Strain 0.200 %,
Temperature 80.0 °C		769 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 5.40 MPa
@Strain 0.100 %,
Temperature -40.0 °C		783 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 5.60 MPa
@Strain 0.100 %,
Temperature 23.0 °C		812 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.60 MPa
@Strain 0.200 %,
Temperature 60.0 °C		812 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 5.60 MPa
@Strain 0.200 %,
Temperature 60.0 °C		812 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.65 MPa
@Strain 0.300 %,
Temperature 150 °C		819 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 5.80 MPa
@Strain 0.100 %,
Temperature 0.000 °C		841 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 6.00 MPa
@Strain 0.200 %,
Temperature 23.0 °C		870 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 6.20 MPa
@Strain 0.400 %,
Temperature 150 °C		899 psi
@Strain 0.400 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.40 MPa
@Strain 0.300 %,
Temperature 120 °C		928 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 6.60 MPa
@Strain 0.100 %,
Temperature -40.0 °C		957 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.70 MPa
@Strain 0.300 %,
Temperature 120 °C		972 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.20 MPa
@Strain 0.400 %,
Temperature 150 °C		1040 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.25 MPa
@Strain 0.300 %,
Temperature 100 °C		1050 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 7.40 MPa
@Strain 0.300 %,
Temperature 100 °C		1070 psi
@Strain 0.300 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 7.80 MPa
@Strain 0.400 %,
Temperature 120 °C		1130 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.80 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1130 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 8.00 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1160 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 8.10 MPa
@Strain 0.500 %,
Temperature 150 °C		1170 psi
@Strain 0.500 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.30 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1200 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 8.60 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1250 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.70 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1260 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 8.90 MPa
@Strain 0.400 %,
Temperature 120 °C		1290 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.20 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1330 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.35 MPa
@Strain 0.500 %,
Temperature 150 °C		1360 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.50 MPa
@Strain 0.400 %,
Temperature 100 °C		1380 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 9.60 MPa
@Strain 0.600 %,
Temperature 150 °C		1390 psi
@Strain 0.600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.80 MPa
@Strain 0.400 %,
Temperature 100 °C		1420 psi
@Strain 0.400 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 10.1 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1460 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 10.2 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1480 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 10.3 MPa
@Strain 0.500 %,
Temperature 120 °C		1490 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.6 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1540 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.8 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1570 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 10.9 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1580 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 11.0 MPa
@Strain 0.500 %,
Temperature 120 °C		1600 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.1 MPa
@Strain 0.700 %,
Temperature 150 °C		1610 psi
@Strain 0.700 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.1 MPa
@Strain 0.600 %,
Temperature 150 °C		1610 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.4 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1650 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.45 MPa
@Strain 0.500 %,
Temperature 100 °C		1661 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 11.65 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1690 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 11.9 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1730 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 11.9 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1730 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 12.1 MPa
@Strain 0.400 %,
Temperature 23.0 °C		1750 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 12.2 MPa
@Strain 0.500 %,
Temperature 100 °C		1770 psi
@Strain 0.500 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 12.4 MPa
@Strain 0.800 %,
Temperature 150 °C		1800 psi
@Strain 0.800 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.7 MPa
@Strain 0.600 %,
Temperature 120 °C		1840 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.75 MPa
@Strain 0.700 %,
Temperature 150 °C		1849 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.9 MPa
@Strain 0.600 %,
Temperature 120 °C		1870 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.0 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1890 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.25 MPa
@Strain 0.600 %,
Temperature 100 °C		1922 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 13.6 MPa
@Strain 0.900 %,
Temperature 150 °C		1970 psi
@Strain 0.900 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.6 MPa
@Strain 0.300 %,
Temperature 0.000 °C		1970 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 13.8 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2000 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 13.8 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2000 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.3 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2070 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 14.3 MPa
@Strain 0.800 %,
Temperature 150 °C		2070 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 14.5 MPa
@Strain 0.700 %,
Temperature 120 °C		2100 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.5 MPa
@Strain 0.600 %,
Temperature 100 °C		2100 psi
@Strain 0.600 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 14.7 MPa
@Strain 0.700 %,
Temperature 120 °C		2130 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.9 MPa
@Strain 1.00 %,
Temperature 150 °C		2160 psi
@Strain 1.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.15 MPa
@Strain 0.700 %,
Temperature 100 °C		2197 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 15.3 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2220 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.4 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2230 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 15.8 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2290 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 15.9 MPa
@Strain 0.900 %,
Temperature 150 °C		2310 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.0 MPa
@Strain 0.800 %,
Temperature 120 °C		2320 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.0 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2320 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 16.2 MPa
@Strain 1.10 %,
Temperature 150 °C		2350 psi
@Strain 1.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 16.4 MPa
@Strain 0.800 %,
Temperature 120 °C		2380 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.4 MPa
@Strain 0.600 %,
Temperature 60.0 °C		2380 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.5 MPa
@Strain 0.700 %,
Temperature 100 °C		2390 psi
@Strain 0.700 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 17.05 MPa
@Strain 0.800 %,
Temperature 100 °C		2473 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 17.1 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2480 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 17.3 MPa
@Strain 0.600 %,
Temperature 60.0 °C		2510 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 17.3 MPa
@Strain 1.20 %,
Temperature 150 °C		2510 psi
@Strain 1.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 17.4 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2520 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 17.45 MPa
@Strain 1.00 %,
Temperature 150 °C		2531 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 17.7 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2570 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 17.7 MPa
@Strain 0.900 %,
Temperature 120 °C		2570 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.7 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2570 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.7 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2570 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.0 MPa
@Strain 0.600 %,
Temperature 23.0 °C		2610 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 18.3 MPa
@Strain 0.400 %,
Temperature 0.000 °C		2650 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 18.4 MPa
@Strain 0.700 %,
Temperature 60.0 °C		2670 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.5 MPa
@Strain 0.800 %,
Temperature 100 °C		2680 psi
@Strain 0.800 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 18.5 MPa
@Strain 1.30 %,
Temperature 150 °C		2680 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 18.7 MPa
@Strain 0.900 %,
Temperature 100 °C		2710 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.8 MPa
@Strain 0.900 %,
Temperature 120 °C		2730 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.95 MPa
@Strain 1.10 %,
Temperature 150 °C		2748 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.3 MPa
@Strain 1.00 %,
Temperature 120 °C		2800 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.6 MPa
@Strain 1.40 %,
Temperature 150 °C		2840 psi
@Strain 1.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 19.7 MPa
@Strain 0.900 %,
Temperature 80.0 °C		2860 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 19.9 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2890 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.1 MPa
@Strain 0.700 %,
Temperature 60.0 °C		2920 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.45 MPa
@Strain 1.00 %,
Temperature 100 °C		2966 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.5 MPa
@Strain 1.20 %,
Temperature 150 °C		2970 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 20.5 MPa
@Strain 1.00 %,
Temperature 120 °C		2970 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.5 MPa
@Strain 0.900 %,
Temperature 100 °C		2970 psi
@Strain 0.900 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 20.6 MPa
@Strain 0.700 %,
Temperature 23.0 °C		2990 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 20.7 MPa
@Strain 0.800 %,
Temperature 60.0 °C		3000 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.7 MPa
@Strain 1.50 %,
Temperature 150 °C		3000 psi
@Strain 1.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 20.8 MPa
@Strain 1.10 %,
Temperature 120 °C		3020 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.1 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3060 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 21.6 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3130 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.6 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3130 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 21.7 MPa
@Strain 1.60 %,
Temperature 150 °C		3150 psi
@Strain 1.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.9 MPa
@Strain 1.30 %,
Temperature 150 °C		3180 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 22.0 MPa
@Strain 1.10 %,
Temperature 100 °C		3190 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 22.1 MPa
@Strain 1.20 %,
Temperature 120 °C		3210 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 22.4 MPa
@Strain 0.400 %,
Temperature 23.0 °C		3250 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 22.5 MPa
@Strain 1.00 %,
Temperature 100 °C		3260 psi
@Strain 1.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 22.6 MPa
@Strain 0.500 %,
Temperature 0.000 °C		3280 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 22.7 MPa
@Strain 1.70 %,
Temperature 150 °C		3290 psi
@Strain 1.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 22.8 MPa
@Strain 0.800 %,
Temperature 60.0 °C		3310 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.9 MPa
@Strain 0.900 %,
Temperature 60.0 °C		3320 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.9 MPa
@Strain 1.10 %,
Temperature 120 °C		3320 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.95 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3329 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 23.2 MPa
@Strain 1.40 %,
Temperature 150 °C		3360 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.2 MPa
@Strain 1.10 %,
Temperature 80.0 °C		3360 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 23.5 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3410 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 23.6 MPa
@Strain 1.30 %,
Temperature 120 °C		3420 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.6 MPa
@Strain 1.20 %,
Temperature 100 °C		3420 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 23.6 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3420 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.6 MPa
@Strain 0.800 %,
Temperature 23.0 °C		3420 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 23.8 MPa
@Strain 1.80 %,
Temperature 150 °C		3450 psi
@Strain 1.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 23.9 MPa
@Strain 1.20 %,
Temperature 120 °C		3470 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.5 MPa
@Strain 1.10 %,
Temperature 100 °C		3550 psi
@Strain 1.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 24.5 MPa
@Strain 1.50 %,
Temperature 150 °C		3550 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 24.7 MPa
@Strain 1.90 %,
Temperature 150 °C		3580 psi
@Strain 1.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 24.8 MPa
@Strain 1.00 %,
Temperature 60.0 °C		3600 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.1 MPa
@Strain 1.20 %,
Temperature 80.0 °C		3640 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 1.30 %,
Temperature 100 °C		3650 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 1.40 %,
Temperature 120 °C		3650 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.3 MPa
@Strain 0.900 %,
Temperature 60.0 °C		3670 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.4 MPa
@Strain 1.30 %,
Temperature 120 °C		3680 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.6 MPa
@Strain 1.10 %,
Temperature 80.0 °C		3710 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.7 MPa
@Strain 2.00 %,
Temperature 150 °C		3730 psi
@Strain 2.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 25.75 MPa
@Strain 1.60 %,
Temperature 150 °C		3735 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 26.1 MPa
@Strain 1.20 %,
Temperature 100 °C		3790 psi
@Strain 1.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 26.1 MPa
@Strain 0.900 %,
Temperature 23.0 °C		3790 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.2 MPa
@Strain 0.500 %,
Temperature -40.0 °C		3800 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 26.5 MPa
@Strain 0.600 %,
Temperature 0.000 °C		3840 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 26.5 MPa
@Strain 2.10 %,
Temperature 150 °C		3840 psi
@Strain 2.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.7 MPa
@Strain 1.50 %,
Temperature 120 °C		3870 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.7 MPa
@Strain 1.10 %,
Temperature 60.0 °C		3870 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.7 MPa
@Strain 1.40 %,
Temperature 100 °C		3870 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 26.8 MPa
@Strain 1.30 %,
Temperature 80.0 °C		3890 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 27.0 MPa
@Strain 1.40 %,
Temperature 120 °C		3920 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.05 MPa
@Strain 1.70 %,
Temperature 150 °C		3923 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.4 MPa
@Strain 2.20 %,
Temperature 150 °C		3970 psi
@Strain 2.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 27.5 MPa
@Strain 1.20 %,
Temperature 80.0 °C		3990 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.7 MPa
@Strain 1.30 %,
Temperature 100 °C		4020 psi
@Strain 1.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 27.8 MPa
@Strain 1.60 %,
Temperature 120 °C		4030 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.9 MPa
@Strain 1.00 %,
Temperature 60.0 °C		4050 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 27.9 MPa
@Strain 0.500 %,
Temperature 23.0 °C		4050 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.15 MPa
@Strain 1.50 %,
Temperature 100 °C		4083 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 28.2 MPa
@Strain 2.30 %,
Temperature 150 °C		4090 psi
@Strain 2.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 28.2 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4090 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.3 MPa
@Strain 1.80 %,
Temperature 150 °C		4100 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.5 MPa
@Strain 1.20 %,
Temperature 60.0 °C		4130 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.55 MPa
@Strain 0.500 %,
Temperature 0.000 °C		4141 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 28.6 MPa
@Strain 1.00 %,
Temperature 23.0 °C		4150 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.6 MPa
@Strain 1.50 %,
Temperature 120 °C		4150 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.0 MPa
@Strain 2.40 %,
Temperature 150 °C		4210 psi
@Strain 2.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.2 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4240 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 29.2 MPa
@Strain 1.70 %,
Temperature 120 °C		4240 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.3 MPa
@Strain 1.40 %,
Temperature 100 °C		4250 psi
@Strain 1.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 29.3 MPa
@Strain 1.30 %,
Temperature 80.0 °C		4250 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.45 MPa
@Strain 1.90 %,
Temperature 150 °C		4271 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.55 MPa
@Strain 1.60 %,
Temperature 100 °C		4286 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 29.6 MPa
@Strain 1.50 %,
Temperature 80.0 °C		4290 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.7 MPa
@Strain 2.50 %,
Temperature 150 °C		4310 psi
@Strain 2.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 29.9 MPa
@Strain 1.30 %,
Temperature 60.0 °C		4340 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.2 MPa
@Strain 1.60 %,
Temperature 120 °C		4380 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.3 MPa
@Strain 1.80 %,
Temperature 120 °C		4390 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 30.4 MPa
@Strain 2.60 %,
Temperature 150 °C		4410 psi
@Strain 2.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 30.5 MPa
@Strain 2.00 %,
Temperature 150 °C		4420 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 30.5 MPa
@Strain 1.10 %,
Temperature 60.0 °C		4420 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.7 MPa
@Strain 0.700 %,
Temperature 0.000 °C		4450 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 31.0 MPa
@Strain 2.70 %,
Temperature 150 °C		4500 psi
@Strain 2.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.1 MPa
@Strain 1.70 %,
Temperature 100 °C		4510 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 31.1 MPa
@Strain 1.50 %,
Temperature 100 °C		4510 psi
@Strain 1.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 31.1 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4510 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 31.2 MPa
@Strain 1.10 %,
Temperature 23.0 °C		4530 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.3 MPa
@Strain 1.60 %,
Temperature 80.0 °C		4540 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.6 MPa
@Strain 1.70 %,
Temperature 120 °C		4580 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 31.6 MPa
@Strain 2.80 %,
Temperature 150 °C		4580 psi
@Strain 2.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.6 MPa
@Strain 2.10 %,
Temperature 150 °C		4580 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 31.6 MPa
@Strain 0.600 %,
Temperature -40.0 °C		4580 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 31.7 MPa
@Strain 1.90 %,
Temperature 120 °C		4600 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.0 MPa
@Strain 1.40 %,
Temperature 60.0 °C		4640 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.1 MPa
@Strain 2.90 %,
Temperature 150 °C		4660 psi
@Strain 2.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.35 MPa
@Strain 1.80 %,
Temperature 100 °C		4692 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.6 MPa
@Strain 3.00 %,
Temperature 150 °C		4730 psi
@Strain 3.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 32.65 MPa
@Strain 2.20 %,
Temperature 150 °C		4735 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.8 MPa
@Strain 1.60 %,
Temperature 100 °C		4760 psi
@Strain 1.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 32.8 MPa
@Strain 1.20 %,
Temperature 60.0 °C		4760 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.9 MPa
@Strain 1.50 %,
Temperature 80.0 °C		4770 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.9 MPa
@Strain 2.00 %,
Temperature 120 °C		4770 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.0 MPa
@Strain 1.70 %,
Temperature 80.0 °C		4790 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 33.1 MPa
@Strain 3.10 %,
Temperature 150 °C		4800 psi
@Strain 3.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 1.80 %,
Temperature 120 °C		4830 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.3 MPa
@Strain 1.20 %,
Temperature 23.0 °C		4830 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 33.5 MPa
@Strain 3.20 %,
Temperature 150 °C		4860 psi
@Strain 3.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 33.6 MPa
@Strain 0.600 %,
Temperature 23.0 °C		4870 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 33.65 MPa
@Strain 1.90 %,
Temperature 100 °C		4881 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 33.7 MPa
@Strain 2.30 %,
Temperature 150 °C		4890 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.8 MPa
@Strain 1.50 %,
Temperature 60.0 °C		4900 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.9 MPa
@Strain 3.30 %,
Temperature 150 °C		4920 psi
@Strain 3.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.1 MPa
@Strain 2.10 %,
Temperature 120 °C		4950 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.2 MPa
@Strain 1.70 %,
Temperature 100 °C		4960 psi
@Strain 1.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 34.2 MPa
@Strain 3.40 %,
Temperature 150 °C		4960 psi
@Strain 3.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.25 MPa
@Strain 0.600 %,
Temperature 0.000 °C		4968 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.4 MPa
@Strain 1.80 %,
Temperature 80.0 °C		4990 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.5 MPa
@Strain 3.50 %,
Temperature 150 °C		5000 psi
@Strain 3.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.5 MPa
@Strain 1.90 %,
Temperature 120 °C		5000 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.6 MPa
@Strain 1.60 %,
Temperature 80.0 °C		5020 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.65 MPa
@Strain 2.40 %,
Temperature 150 °C		5026 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.7 MPa
@Strain 3.60 %,
Temperature 150 °C		5030 psi
@Strain 3.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 34.7 MPa
@Strain 0.800 %,
Temperature 0.000 °C		5030 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 34.9 MPa
@Strain 0.600 %,
Temperature -40.0 °C		5060 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 34.95 MPa
@Strain 2.00 %,
Temperature 100 °C		5069 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 35.0 MPa
@Strain 3.70 %,
Temperature 150 °C		5080 psi
@Strain 3.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.1 MPa
@Strain 1.30 %,
Temperature 60.0 °C		5090 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.2 MPa
@Strain 3.80 %,
Temperature 150 °C		5110 psi
@Strain 3.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 3.90 %,
Temperature 150 °C		5130 psi
@Strain 3.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 8.50 %,
Temperature 150 °C		5130 psi
@Strain 8.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.4 MPa
@Strain 2.20 %,
Temperature 120 °C		5130 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.5 MPa
@Strain 2.00 %,
Temperature 120 °C		5150 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.5 MPa
@Strain 1.60 %,
Temperature 60.0 °C		5150 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.6 MPa
@Strain 1.90 %,
Temperature 80.0 °C		5160 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.6 MPa
@Strain 1.80 %,
Temperature 100 °C		5160 psi
@Strain 1.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 35.6 MPa
@Strain 4.00 %,
Temperature 150 °C		5160 psi
@Strain 4.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.6 MPa
@Strain 2.50 %,
Temperature 150 °C		5160 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.7 MPa
@Strain 1.30 %,
Temperature 23.0 °C		5180 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.8 MPa
@Strain 4.10 %,
Temperature 150 °C		5190 psi
@Strain 4.10 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.9 MPa
@Strain 4.20 %,
Temperature 150 °C		5210 psi
@Strain 4.20 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.9 MPa
@Strain 8.00 %,
Temperature 150 °C		5210 psi
@Strain 8.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.1 MPa
@Strain 4.30 %,
Temperature 150 °C		5240 psi
@Strain 4.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.1 MPa
@Strain 1.70 %,
Temperature 80.0 °C		5240 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.2 MPa
@Strain 4.40 %,
Temperature 150 °C		5250 psi
@Strain 4.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.2 MPa
@Strain 2.10 %,
Temperature 100 °C		5250 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.3 MPa
@Strain 4.50 %,
Temperature 150 °C		5260 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.4 MPa
@Strain 4.60 %,
Temperature 150 °C		5280 psi
@Strain 4.60 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.4 MPa
@Strain 7.50 %,
Temperature 150 °C		5280 psi
@Strain 7.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.5 MPa
@Strain 4.70 %,
Temperature 150 °C		5290 psi
@Strain 4.70 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.55 MPa
@Strain 2.60 %,
Temperature 150 °C		5301 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.6 MPa
@Strain 2.10 %,
Temperature 120 °C		5310 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.6 MPa
@Strain 4.80 %,
Temperature 150 °C		5310 psi
@Strain 4.80 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.6 MPa
@Strain 2.30 %,
Temperature 120 °C		5310 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.7 MPa
@Strain 4.90 %,
Temperature 150 °C		5320 psi
@Strain 4.90 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.7 MPa
@Strain 7.00 %,
Temperature 150 °C		5320 psi
@Strain 7.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.8 MPa
@Strain 5.00 %,
Temperature 150 °C		5340 psi
@Strain 5.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.8 MPa
@Strain 1.70 %,
Temperature 60.0 °C		5340 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.9 MPa
@Strain 6.50 %,
Temperature 150 °C		5350 psi
@Strain 6.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.9 MPa
@Strain 5.50 %,
Temperature 150 °C		5350 psi
@Strain 5.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 36.9 MPa
@Strain 1.90 %,
Temperature 100 °C		5350 psi
@Strain 1.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 37.0 MPa
@Strain 6.00 %,
Temperature 150 °C		5370 psi
@Strain 6.00 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 37.0 MPa
@Strain 2.00 %,
Temperature 80.0 °C		5370 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.3 MPa
@Strain 1.40 %,
Temperature 60.0 °C		5410 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 37.4 MPa
@Strain 2.20 %,
Temperature 120 °C		5420 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.4 MPa
@Strain 2.70 %,
Temperature 150 °C		5420 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.4 MPa
@Strain 0.700 %,
Temperature -40.0 °C		5420 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 37.5 MPa
@Strain 1.40 %,
Temperature 23.0 °C		5440 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.7 MPa
@Strain 1.80 %,
Temperature 80.0 °C		5470 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.7 MPa
@Strain 2.20 %,
Temperature 100 °C		5470 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 37.8 MPa
@Strain 2.40 %,
Temperature 120 °C		5480 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.15 MPa
@Strain 2.80 %,
Temperature 150 °C		5533 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 38.2 MPa
@Strain 1.80 %,
Temperature 60.0 °C		5540 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.3 MPa
@Strain 2.10 %,
Temperature 80.0 °C		5550 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.3 MPa
@Strain 2.30 %,
Temperature 120 °C		5550 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.3 MPa
@Strain 2.00 %,
Temperature 100 °C		5550 psi
@Strain 2.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 38.4 MPa
@Strain 0.900 %,
Temperature 0.000 °C		5570 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 38.8 MPa
@Strain 2.50 %,
Temperature 120 °C		5630 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.9 MPa
@Strain 0.700 %,
Temperature 23.0 °C		5640 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 39.0 MPa
@Strain 2.90 %,
Temperature 150 °C		5660 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.05 MPa
@Strain 2.30 %,
Temperature 100 °C		5664 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 39.2 MPa
@Strain 2.40 %,
Temperature 120 °C		5690 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.2 MPa
@Strain 1.90 %,
Temperature 80.0 °C		5690 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 39.5 MPa
@Strain 1.50 %,
Temperature 23.0 °C		5730 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.6 MPa
@Strain 1.50 %,
Temperature 60.0 °C		5740 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.7 MPa
@Strain 2.50 %,
Temperature 120 °C		5760 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.7 MPa
@Strain 2.10 %,
Temperature 100 °C		5760 psi
@Strain 2.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 39.75 MPa
@Strain 3.00 %,
Temperature 150 °C		5765 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.8 MPa
@Strain 2.60 %,
Temperature 120 °C		5770 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.8 MPa
@Strain 1.90 %,
Temperature 60.0 °C		5770 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.95 MPa
@Strain 0.700 %,
Temperature 0.000 °C		5794 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 40.0 MPa
@Strain 2.20 %,
Temperature 80.0 °C		5800 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.1 MPa
@Strain 2.60 %,
Temperature 120 °C		5820 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 2.70 %,
Temperature 120 °C		5860 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.4 MPa
@Strain 2.40 %,
Temperature 100 °C		5860 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 40.45 MPa
@Strain 3.10 %,
Temperature 150 °C		5867 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.6 MPa
@Strain 2.80 %,
Temperature 120 °C		5890 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.6 MPa
@Strain 2.00 %,
Temperature 80.0 °C		5890 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 40.7 MPa
@Strain 2.20 %,
Temperature 100 °C		5900 psi
@Strain 2.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 40.8 MPa
@Strain 2.70 %,
Temperature 120 °C		5920 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.0 MPa
@Strain 0.700 %,
Temperature -40.0 °C		5950 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 41.1 MPa
@Strain 2.90 %,
Temperature 120 °C		5960 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.1 MPa
@Strain 3.20 %,
Temperature 150 °C		5960 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.4 MPa
@Strain 2.00 %,
Temperature 60.0 °C		6000 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.45 MPa
@Strain 2.50 %,
Temperature 100 °C		6012 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.5 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6020 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.5 MPa
@Strain 1.60 %,
Temperature 60.0 °C		6020 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.6 MPa
@Strain 3.00 %,
Temperature 120 °C		6030 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.65 MPa
@Strain 3.30 %,
Temperature 150 °C		6041 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.7 MPa
@Strain 2.30 %,
Temperature 100 °C		6050 psi
@Strain 2.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 41.8 MPa
@Strain 3.10 %,
Temperature 120 °C		6060 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.8 MPa
@Strain 1.60 %,
Temperature 23.0 °C		6060 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.9 MPa
@Strain 2.80 %,
Temperature 120 °C		6080 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.0 MPa
@Strain 3.20 %,
Temperature 120 °C		6090 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.0 MPa
@Strain 2.10 %,
Temperature 80.0 °C		6090 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.1 MPa
@Strain 1.00 %,
Temperature 0.000 °C		6110 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 42.2 MPa
@Strain 3.30 %,
Temperature 120 °C		6120 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.2 MPa
@Strain 3.40 %,
Temperature 150 °C		6120 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.3 MPa
@Strain 3.40 %,
Temperature 120 °C		6140 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.5 MPa
@Strain 3.50 %,
Temperature 120 °C		6160 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.6 MPa
@Strain 3.60 %,
Temperature 120 °C		6180 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.6 MPa
@Strain 2.60 %,
Temperature 100 °C		6180 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 42.6 MPa
@Strain 2.10 %,
Temperature 60.0 °C		6180 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 42.7 MPa
@Strain 3.50 %,
Temperature 150 °C		6190 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.8 MPa
@Strain 3.70 %,
Temperature 120 °C		6210 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.9 MPa
@Strain 3.80 %,
Temperature 120 °C		6220 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.9 MPa
@Strain 3.90 %,
Temperature 120 °C		6220 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.9 MPa
@Strain 2.40 %,
Temperature 100 °C		6220 psi
@Strain 2.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 42.9 MPa
@Strain 2.90 %,
Temperature 120 °C		6220 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.0 MPa
@Strain 4.00 %,
Temperature 120 °C		6240 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.0 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6240 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.1 MPa
@Strain 4.10 %,
Temperature 120 °C		6250 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.1 MPa
@Strain 4.20 %,
Temperature 120 °C		6250 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.2 MPa
@Strain 4.30 %,
Temperature 120 °C		6270 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.2 MPa
@Strain 4.40 %,
Temperature 120 °C		6270 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.2 MPa
@Strain 3.60 %,
Temperature 150 °C		6270 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.2 MPa
@Strain 0.800 %,
Temperature -40.0 °C		6270 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.3 MPa
@Strain 4.50 %,
Temperature 120 °C		6280 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.3 MPa
@Strain 4.60 %,
Temperature 120 °C		6280 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.3 MPa
@Strain 2.20 %,
Temperature 80.0 °C		6280 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.4 MPa
@Strain 4.70 %,
Temperature 120 °C		6290 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.4 MPa
@Strain 4.80 %,
Temperature 120 °C		6290 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.5 MPa
@Strain 4.90 %,
Temperature 120 °C		6310 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.5 MPa
@Strain 5.00 %,
Temperature 120 °C		6310 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.6 MPa
@Strain 5.50 %,
Temperature 120 °C		6320 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.6 MPa
@Strain 1.70 %,
Temperature 60.0 °C		6320 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.65 MPa
@Strain 3.70 %,
Temperature 150 °C		6331 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 43.7 MPa
@Strain 6.00 %,
Temperature 120 °C		6340 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.7 MPa
@Strain 3.00 %,
Temperature 120 °C		6340 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.75 MPa
@Strain 2.70 %,
Temperature 100 °C		6345 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 43.8 MPa
@Strain 6.50 %,
Temperature 120 °C		6350 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 43.8 MPa
@Strain 1.70 %,
Temperature 23.0 °C		6350 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.8 MPa
@Strain 2.20 %,
Temperature 60.0 °C		6350 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 43.9 MPa
@Strain 2.50 %,
Temperature 100 °C		6370 psi
@Strain 2.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.0 MPa
@Strain 7.00 %,
Temperature 120 °C		6380 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 44.05 MPa
@Strain 3.80 %,
Temperature 150 °C		6389 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.1 MPa
@Strain 2.50 %,
Temperature 80.0 °C		6400 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.1 MPa
@Strain 0.800 %,
Temperature 23.0 °C		6400 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.4 MPa
@Strain 3.90 %,
Temperature 150 °C		6440 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.5 MPa
@Strain 3.10 %,
Temperature 120 °C		6450 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.5 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6450 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.65 MPa
@Strain 2.80 %,
Temperature 100 °C		6476 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.7 MPa
@Strain 2.60 %,
Temperature 100 °C		6480 psi
@Strain 2.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 44.75 MPa
@Strain 4.00 %,
Temperature 150 °C		6490 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.9 MPa
@Strain 2.30 %,
Temperature 60.0 °C		6510 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 44.95 MPa
@Strain 0.800 %,
Temperature 0.000 °C		6519 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 45.05 MPa
@Strain 4.10 %,
Temperature 150 °C		6534 psi
@Strain 4.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.3 MPa
@Strain 3.20 %,
Temperature 120 °C		6570 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.35 MPa
@Strain 4.20 %,
Temperature 150 °C		6577 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.4 MPa
@Strain 2.70 %,
Temperature 100 °C		6580 psi
@Strain 2.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 45.4 MPa
@Strain 2.60 %,
Temperature 80.0 °C		6580 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.6 MPa
@Strain 1.80 %,
Temperature 60.0 °C		6610 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.6 MPa
@Strain 4.30 %,
Temperature 150 °C		6610 psi
@Strain 4.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.7 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6630 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.75 MPa
@Strain 2.90 %,
Temperature 100 °C		6635 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.8 MPa
@Strain 4.40 %,
Temperature 150 °C		6640 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.8 MPa
@Strain 0.800 %,
Temperature -40.0 °C		6640 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 45.9 MPa
@Strain 1.10 %,
Temperature 0.000 °C		6660 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 45.9 MPa
@Strain 2.40 %,
Temperature 60.0 °C		6660 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 46.0 MPa
@Strain 2.80 %,
Temperature 100 °C		6670 psi
@Strain 2.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 46.05 MPa
@Strain 4.50 %,
Temperature 150 °C		6679 psi
@Strain 4.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.1 MPa
@Strain 1.80 %,
Temperature 23.0 °C		6690 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.2 MPa
@Strain 3.30 %,
Temperature 120 °C		6700 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.25 MPa
@Strain 4.60 %,
Temperature 150 °C		6708 psi
@Strain 4.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.5 MPa
@Strain 4.70 %,
Temperature 150 °C		6740 psi
@Strain 4.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.5 MPa
@Strain 2.90 %,
Temperature 100 °C		6740 psi
@Strain 2.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 46.65 MPa
@Strain 4.80 %,
Temperature 150 °C		6766 psi
@Strain 4.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.7 MPa
@Strain 2.70 %,
Temperature 80.0 °C		6770 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.8 MPa
@Strain 2.50 %,
Temperature 80.0 °C		6790 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.8 MPa
@Strain 4.90 %,
Temperature 150 °C		6790 psi
@Strain 4.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.8 MPa
@Strain 3.00 %,
Temperature 100 °C		6790 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 46.8 MPa
@Strain 9.00 %,
Temperature 100 °C		6790 psi
@Strain 9.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 46.9 MPa
@Strain 3.40 %,
Temperature 120 °C		6800 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.9 MPa
@Strain 3.00 %,
Temperature 100 °C		6800 psi
@Strain 3.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.0 MPa
@Strain 5.00 %,
Temperature 150 °C		6820 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.0 MPa
@Strain 2.50 %,
Temperature 60.0 °C		6820 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.3 MPa
@Strain 3.10 %,
Temperature 100 °C		6860 psi
@Strain 3.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.4 MPa
@Strain 2.80 %,
Temperature 80.0 °C		6870 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 47.5 MPa
@Strain 1.90 %,
Temperature 60.0 °C		6890 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.5 MPa
@Strain 5.50 %,
Temperature 150 °C		6890 psi
@Strain 5.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.6 MPa
@Strain 3.20 %,
Temperature 100 °C		6900 psi
@Strain 3.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.6 MPa
@Strain 3.50 %,
Temperature 120 °C		6900 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.7 MPa
@Strain 8.50 %,
Temperature 100 °C		6920 psi
@Strain 8.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 47.8 MPa
@Strain 2.60 %,
Temperature 80.0 °C		6930 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.85 MPa
@Strain 3.10 %,
Temperature 100 °C		6940 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.0 MPa
@Strain 3.30 %,
Temperature 100 °C		6960 psi
@Strain 3.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.0 MPa
@Strain 1.90 %,
Temperature 23.0 °C		6960 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.1 MPa
@Strain 2.60 %,
Temperature 60.0 °C		6980 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.1 MPa
@Strain 6.00 %,
Temperature 150 °C		6980 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.2 MPa
@Strain 3.40 %,
Temperature 100 °C		6990 psi
@Strain 3.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.2 MPa
@Strain 3.60 %,
Temperature 120 °C		6990 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.35 MPa
@Strain 10.0 %,
Temperature 150 °C		7013 psi
@Strain 10.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.4 MPa
@Strain 8.00 %,
Temperature 100 °C		7020 psi
@Strain 8.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.4 MPa
@Strain 2.70 %,
Temperature 80.0 °C		7020 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.45 MPa
@Strain 6.50 %,
Temperature 150 °C		7027 psi
@Strain 6.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.5 MPa
@Strain 3.50 %,
Temperature 100 °C		7030 psi
@Strain 3.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.6 MPa
@Strain 7.00 %,
Temperature 150 °C		7050 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.6 MPa
@Strain 2.90 %,
Temperature 80.0 °C		7050 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 48.7 MPa
@Strain 3.60 %,
Temperature 100 °C		7060 psi
@Strain 3.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.7 MPa
@Strain 0.900 %,
Temperature -40.0 °C		7060 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 48.75 MPa
@Strain 9.50 %,
Temperature 150 °C		7071 psi
@Strain 9.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.8 MPa
@Strain 3.20 %,
Temperature 100 °C		7080 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 48.8 MPa
@Strain 7.50 %,
Temperature 150 °C		7080 psi
@Strain 7.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.9 MPa
@Strain 8.00 %,
Temperature 150 °C		7090 psi
@Strain 8.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.9 MPa
@Strain 3.70 %,
Temperature 100 °C		7090 psi
@Strain 3.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.9 MPa
@Strain 7.50 %,
Temperature 100 °C		7090 psi
@Strain 7.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 48.9 MPa
@Strain 9.00 %,
Temperature 150 °C		7090 psi
@Strain 9.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.9 MPa
@Strain 3.70 %,
Temperature 120 °C		7090 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.95 MPa
@Strain 8.50 %,
Temperature 150 °C		7100 psi
@Strain 8.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 49.0 MPa
@Strain 3.80 %,
Temperature 100 °C		7110 psi
@Strain 3.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.0 MPa
@Strain 2.70 %,
Temperature 60.0 °C		7110 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.2 MPa
@Strain 2.80 %,
Temperature 80.0 °C		7140 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.2 MPa
@Strain 0.900 %,
Temperature 23.0 °C		7140 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.2 MPa
@Strain 3.90 %,
Temperature 100 °C		7140 psi
@Strain 3.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.2 MPa
@Strain 1.20 %,
Temperature 0.000 °C		7140 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 49.3 MPa
@Strain 7.00 %,
Temperature 100 °C		7150 psi
@Strain 7.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.3 MPa
@Strain 2.00 %,
Temperature 60.0 °C		7150 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.4 MPa
@Strain 3.80 %,
Temperature 120 °C		7160 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.4 MPa
@Strain 4.00 %,
Temperature 100 °C		7160 psi
@Strain 4.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 4.10 %,
Temperature 100 °C		7180 psi
@Strain 4.10 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 2.90 %,
Temperature 80.0 °C		7180 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.6 MPa
@Strain 4.20 %,
Temperature 100 °C		7190 psi
@Strain 4.20 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.6 MPa
@Strain 4.40 %,
Temperature 100 °C		7190 psi
@Strain 4.40 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.6 MPa
@Strain 6.50 %,
Temperature 100 °C		7190 psi
@Strain 6.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.7 MPa
@Strain 4.50 %,
Temperature 100 °C		7210 psi
@Strain 4.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.7 MPa
@Strain 4.30 %,
Temperature 100 °C		7210 psi
@Strain 4.30 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.7 MPa
@Strain 2.00 %,
Temperature 23.0 °C		7210 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 49.8 MPa
@Strain 2.80 %,
Temperature 60.0 °C		7220 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.8 MPa
@Strain 4.60 %,
Temperature 100 °C		7220 psi
@Strain 4.60 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.8 MPa
@Strain 4.70 %,
Temperature 100 °C		7220 psi
@Strain 4.70 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.8 MPa
@Strain 4.80 %,
Temperature 100 °C		7220 psi
@Strain 4.80 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.8 MPa
@Strain 6.00 %,
Temperature 100 °C		7220 psi
@Strain 6.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.8 MPa
@Strain 5.00 %,
Temperature 100 °C		7220 psi
@Strain 5.00 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.85 MPa
@Strain 3.30 %,
Temperature 100 °C		7230 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.9 MPa
@Strain 5.50 %,
Temperature 100 °C		7240 psi
@Strain 5.50 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 49.9 MPa
@Strain 3.00 %,
Temperature 80.0 °C		7240 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 50.0 MPa
@Strain 3.90 %,
Temperature 120 °C		7250 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.0 MPa
@Strain 4.90 %,
Temperature 100 °C		7250 psi
@Strain 4.90 %,
Temperature 212 °F		50%RH; ISO 11403-1/-2
 50.2 MPa
@Strain 3.00 %,
Temperature 80.0 °C		7280 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.35 MPa
@Strain 0.900 %,
Temperature 0.000 °C		7303 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.5 MPa
@Strain 4.00 %,
Temperature 120 °C		7320 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.6 MPa
@Strain 9.50 %,
Temperature 80.0 °C		7340 psi
@Strain 9.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.6 MPa
@Strain 2.90 %,
Temperature 60.0 °C		7340 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.65 MPa
@Strain 3.40 %,
Temperature 100 °C		7346 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 50.8 MPa
@Strain 3.10 %,
Temperature 80.0 °C		7370 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.9 MPa
@Strain 4.10 %,
Temperature 120 °C		7380 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.1 MPa
@Strain 3.20 %,
Temperature 80.0 °C		7410 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 2.10 %,
Temperature 60.0 °C		7410 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.2 MPa
@Strain 3.10 %,
Temperature 80.0 °C		7430 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 51.2 MPa
@Strain 4.20 %,
Temperature 120 °C		7430 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.3 MPa
@Strain 9.00 %,
Temperature 80.0 °C		7440 psi
@Strain 9.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.4 MPa
@Strain 3.00 %,
Temperature 60.0 °C		7450 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.45 MPa
@Strain 3.50 %,
Temperature 100 °C		7462 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.5 MPa
@Strain 3.30 %,
Temperature 80.0 °C		7470 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.5 MPa
@Strain 2.10 %,
Temperature 23.0 °C		7470 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 51.5 MPa
@Strain 0.900 %,
Temperature -40.0 °C		7470 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 51.6 MPa
@Strain 12.0 %,
Temperature 60.0 °C		7480 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.7 MPa
@Strain 3.40 %,
Temperature 80.0 °C		7500 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.7 MPa
@Strain 4.30 %,
Temperature 120 °C		7500 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.9 MPa
@Strain 4.40 %,
Temperature 120 °C		7530 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.9 MPa
@Strain 3.50 %,
Temperature 80.0 °C		7530 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.9 MPa
@Strain 8.50 %,
Temperature 80.0 °C		7530 psi
@Strain 8.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.9 MPa
@Strain 3.10 %,
Temperature 60.0 °C		7530 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.1 MPa
@Strain 3.60 %,
Temperature 80.0 °C		7560 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.1 MPa
@Strain 1.30 %,
Temperature 0.000 °C		7560 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 52.2 MPa
@Strain 4.50 %,
Temperature 120 °C		7570 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.3 MPa
@Strain 3.70 %,
Temperature 80.0 °C		7590 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.3 MPa
@Strain 8.00 %,
Temperature 80.0 °C		7590 psi
@Strain 8.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.3 MPa
@Strain 3.20 %,
Temperature 80.0 °C		7590 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.35 MPa
@Strain 3.60 %,
Temperature 100 °C		7593 psi
@Strain 3.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.4 MPa
@Strain 4.60 %,
Temperature 120 °C		7600 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.5 MPa
@Strain 3.80 %,
Temperature 80.0 °C		7610 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.6 MPa
@Strain 7.50 %,
Temperature 80.0 °C		7630 psi
@Strain 7.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.6 MPa
@Strain 3.20 %,
Temperature 60.0 °C		7630 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.7 MPa
@Strain 3.90 %,
Temperature 80.0 °C		7640 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.7 MPa
@Strain 4.00 %,
Temperature 80.0 °C		7640 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.7 MPa
@Strain 4.70 %,
Temperature 120 °C		7640 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.8 MPa
@Strain 2.20 %,
Temperature 60.0 °C		7660 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 52.9 MPa
@Strain 2.20 %,
Temperature 23.0 °C		7670 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.9 MPa
@Strain 4.10 %,
Temperature 80.0 °C		7670 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 52.9 MPa
@Strain 4.80 %,
Temperature 120 °C		7670 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.0 MPa
@Strain 4.20 %,
Temperature 80.0 °C		7690 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.0 MPa
@Strain 7.00 %,
Temperature 80.0 °C		7690 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.0 MPa
@Strain 3.30 %,
Temperature 60.0 °C		7690 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.1 MPa
@Strain 11.0 %,
Temperature 60.0 °C		7700 psi
@Strain 11.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.1 MPa
@Strain 4.30 %,
Temperature 80.0 °C		7700 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.1 MPa
@Strain 4.90 %,
Temperature 120 °C		7700 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.15 MPa
@Strain 3.70 %,
Temperature 100 °C		7709 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.2 MPa
@Strain 5.00 %,
Temperature 120 °C		7720 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.2 MPa
@Strain 4.40 %,
Temperature 80.0 °C		7720 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.2 MPa
@Strain 4.50 %,
Temperature 80.0 °C		7720 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.2 MPa
@Strain 4.60 %,
Temperature 80.0 °C		7720 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.3 MPa
@Strain 4.70 %,
Temperature 80.0 °C		7730 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.3 MPa
@Strain 6.50 %,
Temperature 80.0 °C		7730 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.4 MPa
@Strain 5.00 %,
Temperature 80.0 °C		7750 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.4 MPa
@Strain 5.50 %,
Temperature 80.0 °C		7750 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.4 MPa
@Strain 6.00 %,
Temperature 80.0 °C		7750 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.4 MPa
@Strain 4.80 %,
Temperature 80.0 °C		7750 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.4 MPa
@Strain 4.90 %,
Temperature 80.0 °C		7750 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 53.4 MPa
@Strain 11.0 %,
Temperature 120 °C		7750 psi
@Strain 11.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.5 MPa
@Strain 3.40 %,
Temperature 60.0 °C		7760 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.5 MPa
@Strain 3.30 %,
Temperature 80.0 °C		7760 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.7 MPa
@Strain 1.00 %,
Temperature -40.0 °C		7790 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 53.8 MPa
@Strain 5.50 %,
Temperature 120 °C		7800 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.9 MPa
@Strain 3.80 %,
Temperature 100 °C		7820 psi
@Strain 3.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 53.9 MPa
@Strain 3.50 %,
Temperature 60.0 °C		7820 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.1 MPa
@Strain 3.60 %,
Temperature 60.0 °C		7850 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.1 MPa
@Strain 10.0 %,
Temperature 60.0 °C		7850 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.1 MPa
@Strain 10.0 %,
Temperature 120 °C		7850 psi
@Strain 10.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.3 MPa
@Strain 3.70 %,
Temperature 60.0 °C		7880 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.4 MPa
@Strain 3.40 %,
Temperature 80.0 °C		7890 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.4 MPa
@Strain 2.30 %,
Temperature 23.0 °C		7890 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 54.4 MPa
@Strain 6.00 %,
Temperature 120 °C		7890 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.4 MPa
@Strain 9.50 %,
Temperature 120 °C		7890 psi
@Strain 9.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.4 MPa
@Strain 1.40 %,
Temperature 0.000 °C		7890 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 54.5 MPa
@Strain 1.00 %,
Temperature 23.0 °C		7900 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 54.5 MPa
@Strain 2.30 %,
Temperature 60.0 °C		7900 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.5 MPa
@Strain 9.50 %,
Temperature 60.0 °C		7900 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.6 MPa
@Strain 3.80 %,
Temperature 60.0 °C		7920 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.6 MPa
@Strain 9.00 %,
Temperature 120 °C		7920 psi
@Strain 9.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.6 MPa
@Strain 6.50 %,
Temperature 120 °C		7920 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.65 MPa
@Strain 3.90 %,
Temperature 100 °C		7926 psi
@Strain 3.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.7 MPa
@Strain 3.90 %,
Temperature 60.0 °C		7930 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.8 MPa
@Strain 7.00 %,
Temperature 120 °C		7950 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.8 MPa
@Strain 8.50 %,
Temperature 120 °C		7950 psi
@Strain 8.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.9 MPa
@Strain 7.50 %,
Temperature 120 °C		7960 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.9 MPa
@Strain 8.00 %,
Temperature 120 °C		7960 psi
@Strain 8.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.9 MPa
@Strain 4.00 %,
Temperature 60.0 °C		7960 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.9 MPa
@Strain 9.00 %,
Temperature 60.0 °C		7960 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.1 MPa
@Strain 4.10 %,
Temperature 60.0 °C		7990 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.1 MPa
@Strain 4.20 %,
Temperature 60.0 °C		7990 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.2 MPa
@Strain 8.50 %,
Temperature 60.0 °C		8010 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.25 MPa
@Strain 4.00 %,
Temperature 100 °C		8013 psi
@Strain 4.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.3 MPa
@Strain 4.30 %,
Temperature 60.0 °C		8020 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.3 MPa
@Strain 4.40 %,
Temperature 60.0 °C		8020 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.3 MPa
@Strain 3.50 %,
Temperature 80.0 °C		8020 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.4 MPa
@Strain 4.50 %,
Temperature 60.0 °C		8040 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.5 MPa
@Strain 4.60 %,
Temperature 60.0 °C		8050 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.5 MPa
@Strain 8.00 %,
Temperature 60.0 °C		8050 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.6 MPa
@Strain 4.70 %,
Temperature 60.0 °C		8060 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.7 MPa
@Strain 4.80 %,
Temperature 60.0 °C		8080 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.7 MPa
@Strain 5.00 %,
Temperature 60.0 °C		8080 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.7 MPa
@Strain 7.50 %,
Temperature 60.0 °C		8080 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.75 MPa
@Strain 1.00 %,
Temperature 0.000 °C		8086 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 55.8 MPa
@Strain 4.90 %,
Temperature 60.0 °C		8090 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.9 MPa
@Strain 5.50 %,
Temperature 60.0 °C		8110 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.9 MPa
@Strain 7.00 %,
Temperature 60.0 °C		8110 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.9 MPa
@Strain 4.10 %,
Temperature 100 °C		8110 psi
@Strain 4.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.0 MPa
@Strain 2.40 %,
Temperature 60.0 °C		8120 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 56.0 MPa
@Strain 2.40 %,
Temperature 23.0 °C		8120 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 56.0 MPa
@Strain 6.00 %,
Temperature 60.0 °C		8120 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.0 MPa
@Strain 6.50 %,
Temperature 60.0 °C		8120 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.4 MPa
@Strain 4.20 %,
Temperature 100 °C		8180 psi
@Strain 4.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 56.5 MPa
@Strain 3.60 %,
Temperature 80.0 °C		8190 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.85 MPa
@Strain 4.30 %,
Temperature 100 °C		8245 psi
@Strain 4.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 57.0 MPa
@Strain 1.00 %,
Temperature -40.0 °C		8270 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 57.15 MPa
@Strain 4.40 %,
Temperature 100 °C		8289 psi
@Strain 4.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 57.4 MPa
@Strain 3.70 %,
Temperature 80.0 °C		8330 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.55 MPa
@Strain 4.50 %,
Temperature 100 °C		8347 psi
@Strain 4.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 57.7 MPa
@Strain 2.50 %,
Temperature 60.0 °C		8370 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 57.95 MPa
@Strain 4.60 %,
Temperature 100 °C		8405 psi
@Strain 4.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 58.1 MPa
@Strain 2.50 %,
Temperature 23.0 °C		8430 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.3 MPa
@Strain 4.70 %,
Temperature 100 °C		8460 psi
@Strain 4.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 58.4 MPa
@Strain 3.80 %,
Temperature 80.0 °C		8470 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 58.6 MPa
@Strain 4.80 %,
Temperature 100 °C		8500 psi
@Strain 4.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 58.7 MPa
@Strain 1.50 %,
Temperature 0.000 °C		8510 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 58.85 MPa
@Strain 4.90 %,
Temperature 100 °C		8535 psi
@Strain 4.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.0 MPa
@Strain 5.00 %,
Temperature 100 °C		8560 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.2 MPa
@Strain 1.10 %,
Temperature -40.0 °C		8590 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 59.3 MPa
@Strain 3.90 %,
Temperature 80.0 °C		8600 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.3 MPa
@Strain 1.10 %,
Temperature 23.0 °C		8600 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 59.3 MPa
@Strain 2.60 %,
Temperature 60.0 °C		8600 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 59.65 MPa
@Strain 11.0 %,
Temperature 100 °C		8652 psi
@Strain 11.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.7 MPa
@Strain 5.50 %,
Temperature 100 °C		8660 psi
@Strain 5.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.7 MPa
@Strain 2.60 %,
Temperature 23.0 °C		8660 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 60.0 MPa
@Strain 4.00 %,
Temperature 80.0 °C		8700 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.2 MPa
@Strain 10.0 %,
Temperature 100 °C		8730 psi
@Strain 10.0 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.35 MPa
@Strain 6.00 %,
Temperature 100 °C		8753 psi
@Strain 6.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.45 MPa
@Strain 9.50 %,
Temperature 100 °C		8768 psi
@Strain 9.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.6 MPa
@Strain 9.00 %,
Temperature 100 °C		8790 psi
@Strain 9.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.6 MPa
@Strain 6.50 %,
Temperature 100 °C		8790 psi
@Strain 6.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.7 MPa
@Strain 2.70 %,
Temperature 60.0 °C		8800 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 60.75 MPa
@Strain 7.00 %,
Temperature 100 °C		8811 psi
@Strain 7.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.75 MPa
@Strain 8.50 %,
Temperature 100 °C		8811 psi
@Strain 8.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.85 MPa
@Strain 7.50 %,
Temperature 100 °C		8826 psi
@Strain 7.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.85 MPa
@Strain 8.00 %,
Temperature 100 °C		8826 psi
@Strain 8.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.85 MPa
@Strain 1.10 %,
Temperature 0.000 °C		8826 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 60.9 MPa
@Strain 4.10 %,
Temperature 80.0 °C		8830 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.3 MPa
@Strain 2.70 %,
Temperature 23.0 °C		8890 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 61.6 MPa
@Strain 4.20 %,
Temperature 80.0 °C		8930 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.0 MPa
@Strain 4.30 %,
Temperature 80.0 °C		8990 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.0 MPa
@Strain 2.80 %,
Temperature 60.0 °C		8990 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 62.0 MPa
@Strain 1.60 %,
Temperature 0.000 °C		8990 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.4 MPa
@Strain 1.10 %,
Temperature -40.0 °C		9050 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 62.4 MPa
@Strain 2.80 %,
Temperature 23.0 °C		9050 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.4 MPa
@Strain 4.40 %,
Temperature 80.0 °C		9050 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.9 MPa
@Strain 4.50 %,
Temperature 80.0 °C		9120 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.4 MPa
@Strain 2.90 %,
Temperature 60.0 °C		9200 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 63.5 MPa
@Strain 4.60 %,
Temperature 80.0 °C		9210 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.9 MPa
@Strain 4.70 %,
Temperature 80.0 °C		9270 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.9 MPa
@Strain 14.0 %,
Temperature 80.0 °C		9270 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.9 MPa
@Strain 2.90 %,
Temperature 23.0 °C		9270 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 64.0 MPa
@Strain 1.20 %,
Temperature 23.0 °C		9280 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 64.3 MPa
@Strain 4.80 %,
Temperature 80.0 °C		9330 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.4 MPa
@Strain 1.20 %,
Temperature -40.0 °C		9340 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 64.6 MPa
@Strain 4.90 %,
Temperature 80.0 °C		9370 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.6 MPa
@Strain 13.0 %,
Temperature 80.0 °C		9370 psi
@Strain 13.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.8 MPa
@Strain 5.00 %,
Temperature 80.0 °C		9400 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.8 MPa
@Strain 3.00 %,
Temperature 60.0 °C		9400 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.9 MPa
@Strain 1.70 %,
Temperature 0.000 °C		9410 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.3 MPa
@Strain 12.0 %,
Temperature 80.0 °C		9470 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.5 MPa
@Strain 3.00 %,
Temperature 23.0 °C		9500 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 65.6 MPa
@Strain 5.50 %,
Temperature 80.0 °C		9510 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.9 MPa
@Strain 11.0 %,
Temperature 80.0 °C		9560 psi
@Strain 11.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.9 MPa
@Strain 3.10 %,
Temperature 60.0 °C		9560 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 65.95 MPa
@Strain 1.20 %,
Temperature 0.000 °C		9565 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 66.3 MPa
@Strain 6.00 %,
Temperature 80.0 °C		9620 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.3 MPa
@Strain 10.0 %,
Temperature 80.0 °C		9620 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.5 MPa
@Strain 9.50 %,
Temperature 80.0 °C		9650 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.6 MPa
@Strain 9.00 %,
Temperature 80.0 °C		9660 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.6 MPa
@Strain 6.50 %,
Temperature 80.0 °C		9660 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.6 MPa
@Strain 3.10 %,
Temperature 23.0 °C		9660 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 66.7 MPa
@Strain 8.50 %,
Temperature 80.0 °C		9670 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.7 MPa
@Strain 7.00 %,
Temperature 80.0 °C		9670 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.8 MPa
@Strain 7.50 %,
Temperature 80.0 °C		9690 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.8 MPa
@Strain 8.00 %,
Temperature 80.0 °C		9690 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.9 MPa
@Strain 13.0 %,
Temperature 23.0 °C		9700 psi
@Strain 13.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 67.2 MPa
@Strain 3.20 %,
Temperature 60.0 °C		9750 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.5 MPa
@Strain 3.20 %,
Temperature 23.0 °C		9790 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 67.5 MPa
@Strain 1.80 %,
Temperature 0.000 °C		9790 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.9 MPa
@Strain 1.20 %,
Temperature -40.0 °C		9850 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 68.2 MPa
@Strain 3.30 %,
Temperature 23.0 °C		9890 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.4 MPa
@Strain 12.0 %,
Temperature 23.0 °C		9920 psi
@Strain 12.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.5 MPa
@Strain 3.30 %,
Temperature 60.0 °C		9940 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 68.8 MPa
@Strain 1.30 %,
Temperature 23.0 °C		9980 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 69.2 MPa
@Strain 3.40 %,
Temperature 23.0 °C		10000 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 69.5 MPa
@Strain 3.40 %,
Temperature 60.0 °C		10100 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 69.5 MPa
@Strain 1.30 %,
Temperature -40.0 °C		10100 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 69.8 MPa
@Strain 11.0 %,
Temperature 23.0 °C		10100 psi
@Strain 11.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 70.0 MPa
@Strain 3.50 %,
Temperature 23.0 °C		10200 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 70.3 MPa
@Strain 1.90 %,
Temperature 0.000 °C		10200 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.5 MPa
@Strain 3.50 %,
Temperature 60.0 °C		10200 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 70.6 MPa
@Strain 10.0 %,
Temperature 23.0 °C		10200 psi
@Strain 10.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 70.8 MPa
@Strain 3.60 %,
Temperature 23.0 °C		10300 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.0 MPa
@Strain 9.50 %,
Temperature 23.0 °C		10300 psi
@Strain 9.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.0 MPa
@Strain 1.30 %,
Temperature 0.000 °C		10300 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 71.3 MPa
@Strain 3.70 %,
Temperature 23.0 °C		10300 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.4 MPa
@Strain 9.00 %,
Temperature 23.0 °C		10400 psi
@Strain 9.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.4 MPa
@Strain 3.60 %,
Temperature 60.0 °C		10400 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 71.7 MPa
@Strain 3.80 %,
Temperature 23.0 °C		10400 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.8 MPa
@Strain 8.50 %,
Temperature 23.0 °C		10400 psi
@Strain 8.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.0 MPa
@Strain 3.90 %,
Temperature 23.0 °C		10400 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.1 MPa
@Strain 4.10 %,
Temperature 23.0 °C		10500 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.1 MPa
@Strain 8.00 %,
Temperature 23.0 °C		10500 psi
@Strain 8.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.2 MPa
@Strain 4.20 %,
Temperature 23.0 °C		10500 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.3 MPa
@Strain 7.50 %,
Temperature 23.0 °C		10500 psi
@Strain 7.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.3 MPa
@Strain 3.70 %,
Temperature 60.0 °C		10500 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 72.4 MPa
@Strain 4.00 %,
Temperature 23.0 °C		10500 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.6 MPa
@Strain 7.00 %,
Temperature 23.0 °C		10500 psi
@Strain 7.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.6 MPa
@Strain 4.30 %,
Temperature 23.0 °C		10500 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.7 MPa
@Strain 2.00 %,
Temperature 0.000 °C		10500 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 72.8 MPa
@Strain 4.40 %,
Temperature 23.0 °C		10600 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.8 MPa
@Strain 6.50 %,
Temperature 23.0 °C		10600 psi
@Strain 6.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.0 MPa
@Strain 4.50 %,
Temperature 23.0 °C		10600 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.1 MPa
@Strain 4.60 %,
Temperature 23.0 °C		10600 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.1 MPa
@Strain 6.00 %,
Temperature 23.0 °C		10600 psi
@Strain 6.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.1 MPa
@Strain 4.80 %,
Temperature 23.0 °C		10600 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.2 MPa
@Strain 4.90 %,
Temperature 23.0 °C		10600 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.2 MPa
@Strain 5.00 %,
Temperature 23.0 °C		10600 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.2 MPa
@Strain 5.50 %,
Temperature 23.0 °C		10600 psi
@Strain 5.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.2 MPa
@Strain 1.30 %,
Temperature -40.0 °C		10600 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 73.3 MPa
@Strain 3.80 %,
Temperature 60.0 °C		10600 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 73.3 MPa
@Strain 4.70 %,
Temperature 23.0 °C		10600 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.4 MPa
@Strain 1.40 %,
Temperature 23.0 °C		10600 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 73.8 MPa
@Strain 12.0 %,
Temperature 60.0 °C		10700 psi
@Strain 12.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 73.9 MPa
@Strain 3.90 %,
Temperature 60.0 °C		10700 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 74.5 MPa
@Strain 4.00 %,
Temperature 60.0 °C		10800 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 74.5 MPa
@Strain 1.40 %,
Temperature -40.0 °C		10800 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 74.7 MPa
@Strain 11.0 %,
Temperature 60.0 °C		10800 psi
@Strain 11.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.1 MPa
@Strain 4.10 %,
Temperature 60.0 °C		10900 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.4 MPa
@Strain 10.0 %,
Temperature 60.0 °C		10900 psi
@Strain 10.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.4 MPa
@Strain 2.10 %,
Temperature 0.000 °C		10900 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.5 MPa
@Strain 4.20 %,
Temperature 60.0 °C		11000 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.7 MPa
@Strain 9.50 %,
Temperature 60.0 °C		11000 psi
@Strain 9.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.9 MPa
@Strain 1.40 %,
Temperature 0.000 °C		11000 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.0 MPa
@Strain 4.30 %,
Temperature 60.0 °C		11000 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.1 MPa
@Strain 9.00 %,
Temperature 60.0 °C		11000 psi
@Strain 9.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.3 MPa
@Strain 4.40 %,
Temperature 60.0 °C		11100 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.4 MPa
@Strain 8.50 %,
Temperature 60.0 °C		11100 psi
@Strain 8.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.6 MPa
@Strain 4.50 %,
Temperature 60.0 °C		11100 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.7 MPa
@Strain 8.00 %,
Temperature 60.0 °C		11100 psi
@Strain 8.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.8 MPa
@Strain 4.60 %,
Temperature 60.0 °C		11100 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.9 MPa
@Strain 4.70 %,
Temperature 60.0 °C		11200 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.9 MPa
@Strain 7.50 %,
Temperature 60.0 °C		11200 psi
@Strain 7.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.1 MPa
@Strain 7.00 %,
Temperature 60.0 °C		11200 psi
@Strain 7.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.1 MPa
@Strain 4.80 %,
Temperature 60.0 °C		11200 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.3 MPa
@Strain 4.90 %,
Temperature 60.0 °C		11200 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.3 MPa
@Strain 5.00 %,
Temperature 60.0 °C		11200 psi
@Strain 5.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.3 MPa
@Strain 6.50 %,
Temperature 60.0 °C		11200 psi
@Strain 6.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.5 MPa
@Strain 5.50 %,
Temperature 60.0 °C		11200 psi
@Strain 5.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.5 MPa
@Strain 6.00 %,
Temperature 60.0 °C		11200 psi
@Strain 6.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.8 MPa
@Strain 1.50 %,
Temperature 23.0 °C		11300 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.1 MPa
@Strain 2.20 %,
Temperature 0.000 °C		11300 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 78.4 MPa
@Strain 1.40 %,
Temperature -40.0 °C		11400 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 79.1 MPa
@Strain 1.50 %,
Temperature -40.0 °C		11500 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 80.2 MPa
@Strain 2.30 %,
Temperature 0.000 °C		11600 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 80.65 MPa
@Strain 1.50 %,
Temperature 0.000 °C		11700 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 82.0 MPa
@Strain 1.60 %,
Temperature 23.0 °C		11900 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 82.3 MPa
@Strain 2.40 %,
Temperature 0.000 °C		11900 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 83.5 MPa
@Strain 1.50 %,
Temperature -40.0 °C		12100 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 83.7 MPa
@Strain 1.60 %,
Temperature -40.0 °C		12100 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 84.5 MPa
@Strain 2.50 %,
Temperature 0.000 °C		12300 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 85.3 MPa
@Strain 1.60 %,
Temperature 0.000 °C		12400 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 86.1 MPa
@Strain 1.70 %,
Temperature 23.0 °C		12500 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 86.4 MPa
@Strain 2.60 %,
Temperature 0.000 °C		12500 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 88.0 MPa
@Strain 2.70 %,
Temperature 0.000 °C		12800 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 88.4 MPa
@Strain 1.70 %,
Temperature -40.0 °C		12800 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 88.6 MPa
@Strain 1.60 %,
Temperature -40.0 °C		12900 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 89.8 MPa
@Strain 2.80 %,
Temperature 0.000 °C		13000 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 89.85 MPa
@Strain 1.70 %,
Temperature 0.000 °C		13030 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 90.2 MPa
@Strain 1.80 %,
Temperature 23.0 °C		13100 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 91.6 MPa
@Strain 2.90 %,
Temperature 0.000 °C		13300 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 92.9 MPa
@Strain 1.80 %,
Temperature -40.0 °C		13500 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.4 MPa
@Strain 3.00 %,
Temperature 0.000 °C		13500 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 93.6 MPa
@Strain 1.70 %,
Temperature -40.0 °C		13600 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 94.1 MPa
@Strain 1.90 %,
Temperature 23.0 °C		13600 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 94.3 MPa
@Strain 1.80 %,
Temperature 0.000 °C		13700 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 94.7 MPa
@Strain 3.10 %,
Temperature 0.000 °C		13700 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 94.9 MPa
@Strain 8.00 %,
Temperature 0.000 °C		13800 psi
@Strain 8.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 95.3 MPa
@Strain 7.50 %,
Temperature 0.000 °C		13800 psi
@Strain 7.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 95.9 MPa
@Strain 3.20 %,
Temperature 0.000 °C		13900 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 96.3 MPa
@Strain 7.00 %,
Temperature 0.000 °C		14000 psi
@Strain 7.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.2 MPa
@Strain 3.30 %,
Temperature 0.000 °C		14100 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.2 MPa
@Strain 1.90 %,
Temperature -40.0 °C		14100 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 97.3 MPa
@Strain 6.50 %,
Temperature 0.000 °C		14100 psi
@Strain 6.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.9 MPa
@Strain 2.00 %,
Temperature 23.0 °C		14200 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 98.3 MPa
@Strain 6.00 %,
Temperature 0.000 °C		14300 psi
@Strain 6.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.3 MPa
@Strain 3.40 %,
Temperature 0.000 °C		14300 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.4 MPa
@Strain 1.80 %,
Temperature -40.0 °C		14300 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 98.6 MPa
@Strain 1.90 %,
Temperature 0.000 °C		14300 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.4 MPa
@Strain 3.50 %,
Temperature 0.000 °C		14400 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 99.8 MPa
@Strain 5.50 %,
Temperature 0.000 °C		14500 psi
@Strain 5.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 100.3 MPa
@Strain 3.60 %,
Temperature 0.000 °C		14550 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 100.8 MPa
@Strain 5.00 %,
Temperature 0.000 °C		14620 psi
@Strain 5.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 101.1 MPa
@Strain 4.90 %,
Temperature 0.000 °C		14660 psi
@Strain 4.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 101.1 MPa
@Strain 3.70 %,
Temperature 0.000 °C		14660 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 101.4 MPa
@Strain 4.80 %,
Temperature 0.000 °C		14710 psi
@Strain 4.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 101.5 MPa
@Strain 2.00 %,
Temperature -40.0 °C		14720 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 101.6 MPa
@Strain 4.70 %,
Temperature 0.000 °C		14740 psi
@Strain 4.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 101.6 MPa
@Strain 2.10 %,
Temperature 23.0 °C		14740 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 101.7 MPa
@Strain 3.80 %,
Temperature 0.000 °C		14750 psi
@Strain 3.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 101.9 MPa
@Strain 4.60 %,
Temperature 0.000 °C		14780 psi
@Strain 4.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102 MPa
@Strain 3.90 %,
Temperature 0.000 °C		14800 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.2 MPa
@Strain 4.50 %,
Temperature 0.000 °C		14820 psi
@Strain 4.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.3 MPa
@Strain 4.00 %,
Temperature 0.000 °C		14840 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.4 MPa
@Strain 4.10 %,
Temperature 0.000 °C		14850 psi
@Strain 4.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.4 MPa
@Strain 4.20 %,
Temperature 0.000 °C		14850 psi
@Strain 4.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.4 MPa
@Strain 4.40 %,
Temperature 0.000 °C		14850 psi
@Strain 4.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.5 MPa
@Strain 4.30 %,
Temperature 0.000 °C		14870 psi
@Strain 4.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.85 MPa
@Strain 2.00 %,
Temperature 0.000 °C		14917 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 103.1 MPa
@Strain 1.90 %,
Temperature -40.0 °C		14950 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 105.2 MPa
@Strain 2.20 %,
Temperature 23.0 °C		15260 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 105.4 MPa
@Strain 2.10 %,
Temperature -40.0 °C		15290 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.05 MPa
@Strain 2.10 %,
Temperature 0.000 °C		15526 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 107.8 MPa
@Strain 2.00 %,
Temperature -40.0 °C		15640 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.5 MPa
@Strain 2.30 %,
Temperature 23.0 °C		15740 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 109.5 MPa
@Strain 2.20 %,
Temperature -40.0 °C		15880 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.05 MPa
@Strain 2.20 %,
Temperature 0.000 °C		16106 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 111.6 MPa
@Strain 2.40 %,
Temperature 23.0 °C		16190 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 112.5 MPa
@Strain 2.10 %,
Temperature -40.0 °C		16320 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 113.1 MPa
@Strain 2.30 %,
Temperature -40.0 °C		16400 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 114.7 MPa
@Strain 2.50 %,
Temperature 23.0 °C		16640 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114.85 MPa
@Strain 2.30 %,
Temperature 0.000 °C		16658 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 116.8 MPa
@Strain 2.40 %,
Temperature -40.0 °C		16940 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 116.9 MPa
@Strain 2.20 %,
Temperature -40.0 °C		16950 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 117.3 MPa
@Strain 2.60 %,
Temperature 23.0 °C		17010 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 118.6 MPa
@Strain 2.40 %,
Temperature 0.000 °C		17200 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 120 MPa
@Strain 2.70 %,
Temperature 23.0 °C		17400 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 120.1 MPa
@Strain 2.50 %,
Temperature -40.0 °C		17420 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 121.2 MPa
@Strain 2.30 %,
Temperature -40.0 °C		17580 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 122.15 MPa
@Strain 2.50 %,
Temperature 0.000 °C		17716 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 122.6 MPa
@Strain 2.80 %,
Temperature 23.0 °C		17780 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 125.45 MPa
@Strain 2.60 %,
Temperature 0.000 °C		18195 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 125.6 MPa
@Strain 2.40 %,
Temperature -40.0 °C		18220 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 129.6 MPa
@Strain 2.50 %,
Temperature -40.0 °C		18800 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 133.6 MPa
@Strain 2.60 %,
Temperature -40.0 °C		19380 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 136.2 MPa
@Strain 2.70 %,
Temperature -40.0 °C		19750 psi
@Strain 2.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  2.7 %
@Temperature 23.0 °C		2.7 %
@Temperature 73.4 °F		DAM; ISO 527
 2.7 %
@Temperature 23.0 °C		2.7 %
@Temperature 73.4 °F		DAM; ASTM D638
 12 %
@Temperature 23.0 °C		12 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  3.50 GPa
@Temperature 23.0 °C		508 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 5.50 GPa
@Temperature 23.0 °C		798 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength  100 MPa
@Temperature 23.0 °C		14500 psi
@Temperature 73.4 °F		50%RH; ISO 178
 165 MPa
@Temperature 23.0 °C		23900 psi
@Temperature 73.4 °F		DAM; ASTM D790
 190 MPa
@Temperature 23.0 °C		27600 psi
@Temperature 73.4 °F		DAM; ISO 178
Flexural Modulus  4.83 GPa
@Temperature 23.0 °C		701 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 4.90 GPa
@Temperature 23.0 °C		711 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched 0.480 J/cm
@Temperature 23.0 °C		0.899 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
Izod Impact, Unnotched 5.30 J/cm
@Temperature 23.0 °C		9.93 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
Izod Impact, Notched (ISO)  4.50 kJ/m²
@Temperature -40.0 °C		2.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature 23.0 °C		2.14 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Charpy Impact, Notched  0.450 J/cm²
@Temperature -40.0 °C		2.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.500 J/cm²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index  >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  77.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		42.8 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 77.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		42.8 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 96.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		53.3 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 96.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		53.3 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 158 µm/m-°C
@Temperature 55.0 - 160 °C		87.8 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
 158 µm/m-°C
@Temperature 55.0 - 160 °C		87.8 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 258 °C496 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 238 °C460 °FDAM; ISO 75-1/-2
 242 °C468 °FDAM; ASTM D648
UL RTI, Electrical  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		DAM; UL 746B
 140 °C
@Thickness 0.710 mm		284 °F
@Thickness 0.0280 in		DAM; UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical with Impact  125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		DAM; UL 746B
 125 °C
@Thickness 0.710 mm		257 °F
@Thickness 0.0280 in		DAM; UL 746B
 125 °C
@Thickness 3.00 mm		257 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		DAM; UL 746B
 140 °C
@Thickness 0.710 mm		284 °F
@Thickness 0.0280 in		DAM; UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
AppearanceBlack ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesGeneral PurposeDAM
 Heat StabilizedDAM
 Thermal Stability, GoodDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA66-GF13<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-GF13ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAutomotive ApplicationsDAM
 Industrial ApplicationsDAM
 Parts, EngineeringDAM
 Parts, Machine/MechanicalDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45443.html

免责声明: 本文 DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4