  4. DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66

DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66

DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66 物性表: DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.23
  • 吸水率 [%]: 1.7
  • 成型收缩率 [%]: 0.006
  • 缺口冲击强度: 0.48
  • 弯曲模量 [MPa]: 2.76
  • 硬度: 113.0
  • 热变形温度 [℃]: 258.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.22 g/cc1.22 g/ccDAM; ASTM D792
Density 1.23 g/cc0.0444 lb/in³DAM; ISO 1183
Filler Content 13 %13 %DAM
Water Absorption  1.7 %
@Temperature 23.0 °C		1.7 %
@Temperature 73.4 °F		Immersion 24h; DAM; ISO 62, Similar to
 2.2 %
@Temperature 23.0 °C		2.2 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 7.1 %
@Temperature 23.0 °C		7.1 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 7.6 %
@Temperature 23.0 °C		7.6 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.0060 cm/cm
@Thickness 1.60 mm		0.0060 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0070 cm/cm
@Thickness 3.20 mm		0.0070 in/in
@Thickness 0.126 in		Flow; DAM
 0.0090 cm/cm
@Thickness 6.40 mm		0.0090 in/in
@Thickness 0.252 in		Flow; DAM
 0.012 cm/cm
@Thickness 1.60 mm		0.012 in/in
@Thickness 0.0630 in		Transverse; DAM
 0.014 cm/cm
@Thickness 3.20 mm		0.014 in/in
@Thickness 0.126 in		Transverse; DAM
 0.017 cm/cm
@Thickness 6.40 mm		0.017 in/in
@Thickness 0.252 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.012 cm/cm
@Thickness 2.00 mm		0.012 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 848450%RH; ASTM D785
 9595DAM; ASTM D785
Hardness, Rockwell R 11311350%RH; ASTM D785
 122122DAM; ASTM D785
Tensile Strength at Break  75.0 MPa
@Temperature 23.0 °C		10900 psi
@Temperature 73.4 °F		50%RH; ISO 527
 120 MPa
@Temperature 23.0 °C		17400 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  83.0 MPa
@Temperature 23.0 °C		12000 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 121 MPa
@Temperature 23.0 °C		17500 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  1.60 MPa
@Strain 0.100 %,
Temperature 120 °C		232 psi
@Strain 0.100 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.00 MPa
@Strain 0.100 %,
Temperature 80.0 °C		290 psi
@Strain 0.100 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 2.05 MPa
@Strain 0.100 %,
Temperature 120 °C		297 psi
@Strain 0.100 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 2.50 MPa
@Strain 0.100 %,
Temperature 80.0 °C		363 psi
@Strain 0.100 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 2.50 MPa
@Strain 0.100 %,
Temperature 60.0 °C		363 psi
@Strain 0.100 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 3.432 MPa
@Strain 0.200 %,
Temperature 120 °C		497.8 psi
@Strain 0.200 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.50 MPa
@Strain 0.100 %,
Temperature 23.0 °C		508 psi
@Strain 0.100 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 3.70 MPa
@Strain 0.100 %,
Temperature 60.0 °C		537 psi
@Strain 0.100 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 3.998 MPa
@Strain 0.200 %,
Temperature 120 °C		579.9 psi
@Strain 0.200 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.00 MPa
@Strain 0.200 %,
Temperature 80.0 °C		580 psi
@Strain 0.200 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 4.80 MPa
@Strain 0.200 %,
Temperature 60.0 °C		696 psi
@Strain 0.200 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 5.104 MPa
@Strain 0.300 %,
Temperature 120 °C		740.3 psi
@Strain 0.300 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.20 MPa
@Strain 0.200 %,
Temperature 80.0 °C		754 psi
@Strain 0.200 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 5.50 MPa
@Strain 0.100 %,
Temperature 23.0 °C		798 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 5.50 MPa
@Strain 0.100 %,
Temperature 0.000 °C		798 psi
@Strain 0.100 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 5.60 MPa
@Strain 0.100 %,
Temperature 0.000 °C		812 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 5.807 MPa
@Strain 0.300 %,
Temperature 120 °C		842.2 psi
@Strain 0.300 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.92 MPa
@Strain 0.300 %,
Temperature 80.0 °C		859 psi
@Strain 0.300 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 6.10 MPa
@Strain 0.100 %,
Temperature -40.0 °C		885 psi
@Strain 0.100 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 6.486 MPa
@Strain 0.200 %,
Temperature 23.0 °C		940.7 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 6.50 MPa
@Strain 0.100 %,
Temperature -40.0 °C		943 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 6.60 MPa
@Strain 0.400 %,
Temperature 120 °C		957 psi
@Strain 0.400 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.10 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1030 psi
@Strain 0.300 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.40 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1070 psi
@Strain 0.300 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 7.50 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1090 psi
@Strain 0.400 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 7.50 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1090 psi
@Strain 0.200 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 8.092 MPa
@Strain 0.400 %,
Temperature 120 °C		1174 psi
@Strain 0.400 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.448 MPa
@Strain 0.500 %,
Temperature 120 °C		1225 psi
@Strain 0.500 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.70 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1260 psi
@Strain 0.400 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 8.90 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1290 psi
@Strain 0.400 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 9.70 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1410 psi
@Strain 0.500 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 9.776 MPa
@Strain 0.300 %,
Temperature 23.0 °C		1418 psi
@Strain 0.300 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.901 MPa
@Strain 0.500 %,
Temperature 120 °C		1436 psi
@Strain 0.500 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.12 MPa
@Strain 0.600 %,
Temperature 120 °C		1468 psi
@Strain 0.600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.15 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1472 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.2 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1620 psi
@Strain 0.200 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 11.2 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1620 psi
@Strain 0.300 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 11.413 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1655.3 psi
@Strain 0.200 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 11.64 MPa
@Strain 0.600 %,
Temperature 80.0 °C		1688 psi
@Strain 0.600 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 11.704 MPa
@Strain 0.700 %,
Temperature 120 °C		1697.5 psi
@Strain 0.700 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.8 MPa
@Strain 0.500 %,
Temperature 60.0 °C		1710 psi
@Strain 0.500 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.805 MPa
@Strain 0.600 %,
Temperature 120 °C		1712.2 psi
@Strain 0.600 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.1 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1750 psi
@Strain 0.500 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 12.4 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1800 psi
@Strain 0.200 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 12.69 MPa
@Strain 0.400 %,
Temperature 23.0 °C		1841 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 13.112 MPa
@Strain 0.800 %,
Temperature 120 °C		1901.7 psi
@Strain 0.800 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.386 MPa
@Strain 0.700 %,
Temperature 80.0 °C		1941.5 psi
@Strain 0.700 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 13.464 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1952.8 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 13.709 MPa
@Strain 0.700 %,
Temperature 120 °C		1988.3 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.9 MPa
@Strain 0.600 %,
Temperature 60.0 °C		2020 psi
@Strain 0.600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.0 MPa
@Strain 0.400 %,
Temperature 60.0 °C		2030 psi
@Strain 0.400 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 14.4 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2090 psi
@Strain 0.600 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 14.52 MPa
@Strain 0.900 %,
Temperature 120 °C		2106 psi
@Strain 0.900 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.07 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2186 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 15.132 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2194.7 psi
@Strain 0.800 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 15.518 MPa
@Strain 0.800 %,
Temperature 120 °C		2250.7 psi
@Strain 0.800 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.928 MPa
@Strain 1.00 %,
Temperature 120 °C		2310.2 psi
@Strain 1.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.074 MPa
@Strain 0.500 %,
Temperature 23.0 °C		2331.3 psi
@Strain 0.500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 16.1 MPa
@Strain 0.700 %,
Temperature 60.0 °C		2340 psi
@Strain 0.700 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 16.6 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2410 psi
@Strain 0.700 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 16.8 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2440 psi
@Strain 0.300 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 16.878 MPa
@Strain 0.900 %,
Temperature 80.0 °C		2448.0 psi
@Strain 0.900 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 17.069 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2475.7 psi
@Strain 0.300 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 17.136 MPa
@Strain 0.900 %,
Temperature 120 °C		2485.4 psi
@Strain 0.900 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 17.248 MPa
@Strain 1.10 %,
Temperature 120 °C		2501.6 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.3 MPa
@Strain 0.800 %,
Temperature 60.0 °C		2650 psi
@Strain 0.800 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.392 MPa
@Strain 1.20 %,
Temperature 120 °C		2667.5 psi
@Strain 1.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.43 MPa
@Strain 1.00 %,
Temperature 80.0 °C		2673 psi
@Strain 1.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 18.659 MPa
@Strain 1.00 %,
Temperature 120 °C		2706.3 psi
@Strain 1.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 18.7 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2710 psi
@Strain 0.800 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 18.7 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2710 psi
@Strain 0.300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2760 psi
@Strain 0.500 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.176 MPa
@Strain 0.600 %,
Temperature 23.0 °C		2781.2 psi
@Strain 0.600 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 19.62 MPa
@Strain 0.400 %,
Temperature 23.0 °C		2846 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 19.624 MPa
@Strain 1.30 %,
Temperature 120 °C		2846.2 psi
@Strain 1.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.982 MPa
@Strain 1.10 %,
Temperature 80.0 °C		2898.1 psi
@Strain 1.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 20.094 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2914.4 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 20.278 MPa
@Strain 1.10 %,
Temperature 120 °C		2941.1 psi
@Strain 1.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.3 MPa
@Strain 0.900 %,
Temperature 60.0 °C		2940 psi
@Strain 0.900 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.8 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3020 psi
@Strain 0.900 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 20.856 MPa
@Strain 1.40 %,
Temperature 120 °C		3024.9 psi
@Strain 1.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.534 MPa
@Strain 1.20 %,
Temperature 80.0 °C		3123.2 psi
@Strain 1.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 21.6 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3130 psi
@Strain 0.400 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 21.706 MPa
@Strain 1.20 %,
Temperature 120 °C		3148.2 psi
@Strain 1.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.912 MPa
@Strain 1.50 %,
Temperature 120 °C		3178.1 psi
@Strain 1.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.0 MPa
@Strain 1.00 %,
Temperature 60.0 °C		3190 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.09 MPa
@Strain 0.700 %,
Temperature 23.0 °C		3204 psi
@Strain 0.700 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 22.422 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3252.0 psi
@Strain 0.400 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 22.5 MPa
@Strain 0.600 %,
Temperature 60.0 °C		3260 psi
@Strain 0.600 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.7 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3290 psi
@Strain 1.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 22.88 MPa
@Strain 1.60 %,
Temperature 120 °C		3318 psi
@Strain 1.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 23.086 MPa
@Strain 1.30 %,
Temperature 80.0 °C		3348.3 psi
@Strain 1.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 23.134 MPa
@Strain 1.30 %,
Temperature 120 °C		3355.3 psi
@Strain 1.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.8 MPa
@Strain 1.10 %,
Temperature 60.0 °C		3450 psi
@Strain 1.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.024 MPa
@Strain 1.70 %,
Temperature 120 °C		3484.4 psi
@Strain 1.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 24.347 MPa
@Strain 1.40 %,
Temperature 80.0 °C		3531.2 psi
@Strain 1.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 24.4 MPa
@Strain 1.10 %,
Temperature 80.0 °C		3540 psi
@Strain 1.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 24.4 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3540 psi
@Strain 0.400 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 24.466 MPa
@Strain 1.40 %,
Temperature 120 °C		3548.5 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.91 MPa
@Strain 0.800 %,
Temperature 23.0 °C		3613 psi
@Strain 0.800 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.09 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3639 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 25.168 MPa
@Strain 1.80 %,
Temperature 120 °C		3650.3 psi
@Strain 1.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 25.6 MPa
@Strain 1.20 %,
Temperature 60.0 °C		3710 psi
@Strain 1.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.705 MPa
@Strain 1.50 %,
Temperature 80.0 °C		3728.2 psi
@Strain 1.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 25.799 MPa
@Strain 1.50 %,
Temperature 120 °C		3741.8 psi
@Strain 1.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.8 MPa
@Strain 0.700 %,
Temperature 60.0 °C		3740 psi
@Strain 0.700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.136 MPa
@Strain 1.90 %,
Temperature 120 °C		3790.7 psi
@Strain 1.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.2 MPa
@Strain 1.20 %,
Temperature 80.0 °C		3800 psi
@Strain 1.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 26.214 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3802.0 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 27.063 MPa
@Strain 1.60 %,
Temperature 80.0 °C		3925.2 psi
@Strain 1.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 27.104 MPa
@Strain 2.00 %,
Temperature 120 °C		3931.1 psi
@Strain 2.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 27.132 MPa
@Strain 1.60 %,
Temperature 120 °C		3935.2 psi
@Strain 1.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.2 MPa
@Strain 1.30 %,
Temperature 60.0 °C		3950 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.636 MPa
@Strain 0.900 %,
Temperature 23.0 °C		4008.3 psi
@Strain 0.900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.984 MPa
@Strain 2.10 %,
Temperature 120 °C		4058.7 psi
@Strain 2.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 28.0 MPa
@Strain 1.30 %,
Temperature 80.0 °C		4060 psi
@Strain 1.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 28.078 MPa
@Strain 0.500 %,
Temperature 0.000 °C		4072.4 psi
@Strain 0.500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 28.1 MPa
@Strain 0.500 %,
Temperature 0.000 °C		4080 psi
@Strain 0.500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 28.227 MPa
@Strain 1.70 %,
Temperature 80.0 °C		4094.0 psi
@Strain 1.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 28.274 MPa
@Strain 1.70 %,
Temperature 120 °C		4100.8 psi
@Strain 1.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 28.9 MPa
@Strain 1.40 %,
Temperature 60.0 °C		4190 psi
@Strain 1.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.952 MPa
@Strain 2.20 %,
Temperature 120 °C		4199.1 psi
@Strain 2.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 29.2 MPa
@Strain 0.800 %,
Temperature 60.0 °C		4240 psi
@Strain 0.800 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 29.585 MPa
@Strain 1.80 %,
Temperature 80.0 °C		4290.9 psi
@Strain 1.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 29.607 MPa
@Strain 1.80 %,
Temperature 120 °C		4294.1 psi
@Strain 1.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 29.7 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4310 psi
@Strain 1.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 29.744 MPa
@Strain 2.30 %,
Temperature 120 °C		4314.0 psi
@Strain 2.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.0 MPa
@Strain 0.600 %,
Temperature 23.0 °C		4350 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.174 MPa
@Strain 1.00 %,
Temperature 23.0 °C		4376.4 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 30.5 MPa
@Strain 1.50 %,
Temperature 60.0 °C		4420 psi
@Strain 1.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.536 MPa
@Strain 2.40 %,
Temperature 120 °C		4428.9 psi
@Strain 2.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 30.749 MPa
@Strain 1.90 %,
Temperature 80.0 °C		4459.8 psi
@Strain 1.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 30.75 MPa
@Strain 1.90 %,
Temperature 120 °C		4460 psi
@Strain 1.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.3 MPa
@Strain 1.50 %,
Temperature 80.0 °C		4540 psi
@Strain 1.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 31.328 MPa
@Strain 2.50 %,
Temperature 120 °C		4543.8 psi
@Strain 2.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 31.4 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4550 psi
@Strain 0.500 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 31.892 MPa
@Strain 2.00 %,
Temperature 120 °C		4625.6 psi
@Strain 2.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 31.913 MPa
@Strain 2.00 %,
Temperature 80.0 °C		4628.6 psi
@Strain 2.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 32.1 MPa
@Strain 1.60 %,
Temperature 60.0 °C		4660 psi
@Strain 1.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.208 MPa
@Strain 2.60 %,
Temperature 120 °C		4671.4 psi
@Strain 2.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.4 MPa
@Strain 0.900 %,
Temperature 60.0 °C		4700 psi
@Strain 0.900 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 32.43 MPa
@Strain 1.10 %,
Temperature 23.0 °C		4704 psi
@Strain 1.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 32.8 MPa
@Strain 1.60 %,
Temperature 80.0 °C		4760 psi
@Strain 1.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 32.844 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4763.6 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.912 MPa
@Strain 2.70 %,
Temperature 120 °C		4773.5 psi
@Strain 2.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.939 MPa
@Strain 2.10 %,
Temperature 120 °C		4777.4 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 33.077 MPa
@Strain 2.10 %,
Temperature 80.0 °C		4797.4 psi
@Strain 2.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 33.1 MPa
@Strain 0.600 %,
Temperature 0.000 °C		4800 psi
@Strain 0.600 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.6 MPa
@Strain 1.70 %,
Temperature 60.0 °C		4870 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.616 MPa
@Strain 2.80 %,
Temperature 120 °C		4875.6 psi
@Strain 2.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 33.835 MPa
@Strain 0.600 %,
Temperature 0.000 °C		4907.4 psi
@Strain 0.600 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.082 MPa
@Strain 2.20 %,
Temperature 120 °C		4943.2 psi
@Strain 2.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.144 MPa
@Strain 2.20 %,
Temperature 80.0 °C		4952.2 psi
@Strain 2.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 34.2 MPa
@Strain 1.70 %,
Temperature 80.0 °C		4960 psi
@Strain 1.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 34.232 MPa
@Strain 2.90 %,
Temperature 120 °C		4964.9 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.686 MPa
@Strain 1.20 %,
Temperature 23.0 °C		5030.8 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 34.848 MPa
@Strain 3.00 %,
Temperature 120 °C		5054.3 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 34.87 MPa
@Strain 0.700 %,
Temperature 23.0 °C		5057 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 35.0 MPa
@Strain 1.80 %,
Temperature 60.0 °C		5080 psi
@Strain 1.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 35.211 MPa
@Strain 2.30 %,
Temperature 80.0 °C		5106.9 psi
@Strain 2.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 35.224 MPa
@Strain 2.30 %,
Temperature 120 °C		5108.8 psi
@Strain 2.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 35.4 MPa
@Strain 1.00 %,
Temperature 60.0 °C		5130 psi
@Strain 1.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 35.464 MPa
@Strain 3.10 %,
Temperature 120 °C		5143.6 psi
@Strain 3.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 35.8 MPa
@Strain 1.80 %,
Temperature 80.0 °C		5190 psi
@Strain 1.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 35.904 MPa
@Strain 3.20 %,
Temperature 120 °C		5207.4 psi
@Strain 3.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.084 MPa
@Strain 2.40 %,
Temperature 80.0 °C		5233.6 psi
@Strain 2.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 36.176 MPa
@Strain 2.40 %,
Temperature 120 °C		5246.9 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 36.3 MPa
@Strain 1.90 %,
Temperature 60.0 °C		5260 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 36.432 MPa
@Strain 3.30 %,
Temperature 120 °C		5284.0 psi
@Strain 3.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.872 MPa
@Strain 3.40 %,
Temperature 120 °C		5347.8 psi
@Strain 3.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 36.942 MPa
@Strain 1.30 %,
Temperature 23.0 °C		5358.0 psi
@Strain 1.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.054 MPa
@Strain 2.50 %,
Temperature 80.0 °C		5374.2 psi
@Strain 2.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 37.128 MPa
@Strain 2.50 %,
Temperature 120 °C		5385.0 psi
@Strain 2.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 37.2 MPa
@Strain 1.90 %,
Temperature 80.0 °C		5400 psi
@Strain 1.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 37.312 MPa
@Strain 3.50 %,
Temperature 120 °C		5411.7 psi
@Strain 3.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.6 MPa
@Strain 0.600 %,
Temperature -40.0 °C		5450 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 37.664 MPa
@Strain 3.60 %,
Temperature 120 °C		5462.7 psi
@Strain 3.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.8 MPa
@Strain 2.00 %,
Temperature 60.0 °C		5480 psi
@Strain 2.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 38.024 MPa
@Strain 2.60 %,
Temperature 80.0 °C		5514.9 psi
@Strain 2.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.08 MPa
@Strain 2.60 %,
Temperature 120 °C		5523 psi
@Strain 2.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.104 MPa
@Strain 3.70 %,
Temperature 120 °C		5526.5 psi
@Strain 3.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.2 MPa
@Strain 0.700 %,
Temperature 0.000 °C		5540 psi
@Strain 0.700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 38.3 MPa
@Strain 1.10 %,
Temperature 60.0 °C		5550 psi
@Strain 1.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.456 MPa
@Strain 3.80 %,
Temperature 120 °C		5577.6 psi
@Strain 3.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.6 MPa
@Strain 2.00 %,
Temperature 80.0 °C		5600 psi
@Strain 2.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 38.632 MPa
@Strain 3.90 %,
Temperature 120 °C		5603.1 psi
@Strain 3.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 38.897 MPa
@Strain 2.70 %,
Temperature 80.0 °C		5641.5 psi
@Strain 2.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 38.984 MPa
@Strain 4.00 %,
Temperature 120 °C		5654.2 psi
@Strain 4.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.01 MPa
@Strain 1.40 %,
Temperature 23.0 °C		5658 psi
@Strain 1.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 39.032 MPa
@Strain 2.70 %,
Temperature 120 °C		5661.1 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 39.1 MPa
@Strain 2.10 %,
Temperature 60.0 °C		5670 psi
@Strain 2.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 39.168 MPa
@Strain 0.600 %,
Temperature -40.0 °C		5680.8 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 39.248 MPa
@Strain 4.10 %,
Temperature 120 °C		5692.5 psi
@Strain 4.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.491 MPa
@Strain 0.700 %,
Temperature 0.000 °C		5727.7 psi
@Strain 0.700 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 39.512 MPa
@Strain 4.20 %,
Temperature 120 °C		5730.7 psi
@Strain 4.20 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.58 MPa
@Strain 0.800 %,
Temperature 23.0 °C		5741 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 39.77 MPa
@Strain 2.80 %,
Temperature 80.0 °C		5768 psi
@Strain 2.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 39.776 MPa
@Strain 4.30 %,
Temperature 120 °C		5769.0 psi
@Strain 4.30 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.952 MPa
@Strain 4.40 %,
Temperature 120 °C		5794.6 psi
@Strain 4.40 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 39.984 MPa
@Strain 2.80 %,
Temperature 120 °C		5799.2 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.0 MPa
@Strain 2.10 %,
Temperature 80.0 °C		5800 psi
@Strain 2.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 40.128 MPa
@Strain 4.50 %,
Temperature 120 °C		5820.1 psi
@Strain 4.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.3 MPa
@Strain 2.20 %,
Temperature 60.0 °C		5850 psi
@Strain 2.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 40.304 MPa
@Strain 4.60 %,
Temperature 120 °C		5845.6 psi
@Strain 4.60 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.48 MPa
@Strain 4.70 %,
Temperature 120 °C		5871 psi
@Strain 4.70 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.546 MPa
@Strain 2.90 %,
Temperature 80.0 °C		5880.7 psi
@Strain 2.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 40.656 MPa
@Strain 4.80 %,
Temperature 120 °C		5896.7 psi
@Strain 4.80 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.746 MPa
@Strain 2.90 %,
Temperature 120 °C		5909.7 psi
@Strain 2.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.832 MPa
@Strain 4.90 %,
Temperature 120 °C		5922.2 psi
@Strain 4.90 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 40.92 MPa
@Strain 5.00 %,
Temperature 120 °C		5935 psi
@Strain 5.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.1 MPa
@Strain 1.20 %,
Temperature 60.0 °C		5960 psi
@Strain 1.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 41.172 MPa
@Strain 1.50 %,
Temperature 23.0 °C		5971.5 psi
@Strain 1.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.225 MPa
@Strain 3.00 %,
Temperature 80.0 °C		5979.2 psi
@Strain 3.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 41.3 MPa
@Strain 2.20 %,
Temperature 80.0 °C		5990 psi
@Strain 2.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 41.36 MPa
@Strain 5.50 %,
Temperature 120 °C		5999 psi
@Strain 5.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.5 MPa
@Strain 2.30 %,
Temperature 60.0 °C		6020 psi
@Strain 2.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.602 MPa
@Strain 3.00 %,
Temperature 120 °C		6033.9 psi
@Strain 3.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 41.8 MPa
@Strain 10.0 %,
Temperature 120 °C		6060 psi
@Strain 10.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.8 MPa
@Strain 6.00 %,
Temperature 120 °C		6060 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 41.904 MPa
@Strain 3.10 %,
Temperature 80.0 °C		6077.7 psi
@Strain 3.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.064 MPa
@Strain 6.50 %,
Temperature 120 °C		6100.9 psi
@Strain 6.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.064 MPa
@Strain 9.50 %,
Temperature 120 °C		6100.9 psi
@Strain 9.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.152 MPa
@Strain 9.00 %,
Temperature 120 °C		6113.6 psi
@Strain 9.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.24 MPa
@Strain 7.00 %,
Temperature 120 °C		6126 psi
@Strain 7.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.24 MPa
@Strain 8.50 %,
Temperature 120 °C		6126 psi
@Strain 8.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.328 MPa
@Strain 7.50 %,
Temperature 120 °C		6139.2 psi
@Strain 7.50 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.328 MPa
@Strain 8.00 %,
Temperature 120 °C		6139.2 psi
@Strain 8.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.459 MPa
@Strain 3.10 %,
Temperature 120 °C		6158.2 psi
@Strain 3.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.583 MPa
@Strain 3.20 %,
Temperature 80.0 °C		6176.2 psi
@Strain 3.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 42.6 MPa
@Strain 2.40 %,
Temperature 60.0 °C		6180 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 42.7 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6190 psi
@Strain 2.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 43.126 MPa
@Strain 3.20 %,
Temperature 120 °C		6254.9 psi
@Strain 3.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.146 MPa
@Strain 1.60 %,
Temperature 23.0 °C		6257.8 psi
@Strain 1.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.262 MPa
@Strain 3.30 %,
Temperature 80.0 °C		6274.6 psi
@Strain 3.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.3 MPa
@Strain 0.800 %,
Temperature 0.000 °C		6280 psi
@Strain 0.800 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 43.7 MPa
@Strain 2.50 %,
Temperature 60.0 °C		6340 psi
@Strain 2.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 43.747 MPa
@Strain 3.40 %,
Temperature 80.0 °C		6345.0 psi
@Strain 3.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 43.8 MPa
@Strain 1.30 %,
Temperature 60.0 °C		6350 psi
@Strain 1.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.8 MPa
@Strain 0.700 %,
Temperature -40.0 °C		6350 psi
@Strain 0.700 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.887 MPa
@Strain 3.30 %,
Temperature 120 °C		6365.3 psi
@Strain 3.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 43.9 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6370 psi
@Strain 2.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 44.232 MPa
@Strain 3.50 %,
Temperature 80.0 °C		6415.3 psi
@Strain 3.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.3 MPa
@Strain 0.900 %,
Temperature 23.0 °C		6430 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.554 MPa
@Strain 3.40 %,
Temperature 120 °C		6462.0 psi
@Strain 3.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.717 MPa
@Strain 3.60 %,
Temperature 80.0 °C		6485.7 psi
@Strain 3.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 44.8 MPa
@Strain 2.60 %,
Temperature 60.0 °C		6500 psi
@Strain 2.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 44.945 MPa
@Strain 0.800 %,
Temperature 0.000 °C		6518.7 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 45.026 MPa
@Strain 1.70 %,
Temperature 23.0 °C		6530.5 psi
@Strain 1.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 45.1 MPa
@Strain 2.50 %,
Temperature 80.0 °C		6540 psi
@Strain 2.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 45.186 MPa
@Strain 0.700 %,
Temperature -40.0 °C		6553.7 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 45.202 MPa
@Strain 3.70 %,
Temperature 80.0 °C		6556.0 psi
@Strain 3.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.22 MPa
@Strain 3.50 %,
Temperature 120 °C		6559 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.59 MPa
@Strain 3.80 %,
Temperature 80.0 °C		6612 psi
@Strain 3.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 45.8 MPa
@Strain 2.70 %,
Temperature 60.0 °C		6640 psi
@Strain 2.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 45.886 MPa
@Strain 3.60 %,
Temperature 120 °C		6655.2 psi
@Strain 3.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 45.978 MPa
@Strain 3.90 %,
Temperature 80.0 °C		6668.6 psi
@Strain 3.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.2 MPa
@Strain 1.40 %,
Temperature 60.0 °C		6700 psi
@Strain 1.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.3 MPa
@Strain 2.60 %,
Temperature 80.0 °C		6720 psi
@Strain 2.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 46.362 MPa
@Strain 3.70 %,
Temperature 120 °C		6724.3 psi
@Strain 3.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.366 MPa
@Strain 4.00 %,
Temperature 80.0 °C		6724.8 psi
@Strain 4.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.657 MPa
@Strain 4.10 %,
Temperature 80.0 °C		6767.0 psi
@Strain 4.10 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 46.718 MPa
@Strain 1.80 %,
Temperature 23.0 °C		6775.9 psi
@Strain 1.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.8 MPa
@Strain 2.80 %,
Temperature 60.0 °C		6790 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 46.934 MPa
@Strain 3.80 %,
Temperature 120 °C		6807.2 psi
@Strain 3.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.948 MPa
@Strain 4.20 %,
Temperature 80.0 °C		6809.2 psi
@Strain 4.20 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.239 MPa
@Strain 4.30 %,
Temperature 80.0 °C		6851.4 psi
@Strain 4.30 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.41 MPa
@Strain 3.90 %,
Temperature 120 °C		6876 psi
@Strain 3.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.5 MPa
@Strain 2.70 %,
Temperature 80.0 °C		6890 psi
@Strain 2.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 47.53 MPa
@Strain 4.40 %,
Temperature 80.0 °C		6894 psi
@Strain 4.40 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.8 MPa
@Strain 2.90 %,
Temperature 60.0 °C		6930 psi
@Strain 2.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.821 MPa
@Strain 4.50 %,
Temperature 80.0 °C		6935.9 psi
@Strain 4.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 47.886 MPa
@Strain 4.00 %,
Temperature 120 °C		6945.3 psi
@Strain 4.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.918 MPa
@Strain 4.60 %,
Temperature 80.0 °C		6949.9 psi
@Strain 4.60 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.209 MPa
@Strain 4.70 %,
Temperature 80.0 °C		6992.1 psi
@Strain 4.70 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.3 MPa
@Strain 0.900 %,
Temperature 0.000 °C		7010 psi
@Strain 0.900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 48.362 MPa
@Strain 4.10 %,
Temperature 120 °C		7014.3 psi
@Strain 4.10 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.403 MPa
@Strain 4.80 %,
Temperature 80.0 °C		7020.3 psi
@Strain 4.80 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 4.90 %,
Temperature 80.0 °C		7030 psi
@Strain 4.90 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.5 MPa
@Strain 1.50 %,
Temperature 60.0 °C		7030 psi
@Strain 1.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 48.504 MPa
@Strain 1.90 %,
Temperature 23.0 °C		7034.9 psi
@Strain 1.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 48.6 MPa
@Strain 3.00 %,
Temperature 60.0 °C		7050 psi
@Strain 3.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 48.694 MPa
@Strain 5.00 %,
Temperature 80.0 °C		7062.5 psi
@Strain 5.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 48.8 MPa
@Strain 2.80 %,
Temperature 80.0 °C		7080 psi
@Strain 2.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 48.838 MPa
@Strain 4.20 %,
Temperature 120 °C		7083.4 psi
@Strain 4.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.01 MPa
@Strain 1.00 %,
Temperature 23.0 °C		7108 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 49.218 MPa
@Strain 4.30 %,
Temperature 120 °C		7138.5 psi
@Strain 4.30 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.28 MPa
@Strain 5.50 %,
Temperature 80.0 °C		7147 psi
@Strain 5.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 49.5 MPa
@Strain 3.10 %,
Temperature 60.0 °C		7180 psi
@Strain 3.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 49.504 MPa
@Strain 4.40 %,
Temperature 120 °C		7180.0 psi
@Strain 4.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.79 MPa
@Strain 4.50 %,
Temperature 120 °C		7221 psi
@Strain 4.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.9 MPa
@Strain 2.90 %,
Temperature 80.0 °C		7240 psi
@Strain 2.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 49.9 MPa
@Strain 0.800 %,
Temperature -40.0 °C		7240 psi
@Strain 0.800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 50.0 MPa
@Strain 6.00 %,
Temperature 80.0 °C		7250 psi
@Strain 6.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.17 MPa
@Strain 4.60 %,
Temperature 120 °C		7277 psi
@Strain 4.60 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.29 MPa
@Strain 2.00 %,
Temperature 23.0 °C		7294 psi
@Strain 2.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 50.3 MPa
@Strain 3.20 %,
Temperature 60.0 °C		7300 psi
@Strain 3.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 50.3 MPa
@Strain 6.50 %,
Temperature 80.0 °C		7300 psi
@Strain 6.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.456 MPa
@Strain 4.70 %,
Temperature 120 °C		7318.0 psi
@Strain 4.70 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.5 MPa
@Strain 12.0 %,
Temperature 80.0 °C		7320 psi
@Strain 12.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.601 MPa
@Strain 0.900 %,
Temperature 0.000 °C		7339.1 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 50.7 MPa
@Strain 7.00 %,
Temperature 80.0 °C		7350 psi
@Strain 7.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.742 MPa
@Strain 4.80 %,
Temperature 120 °C		7359.5 psi
@Strain 4.80 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.8 MPa
@Strain 11.0 %,
Temperature 80.0 °C		7370 psi
@Strain 11.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.9 MPa
@Strain 7.50 %,
Temperature 80.0 °C		7380 psi
@Strain 7.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 50.932 MPa
@Strain 4.90 %,
Temperature 120 °C		7387.1 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.0 MPa
@Strain 8.00 %,
Temperature 80.0 °C		7400 psi
@Strain 8.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.0 MPa
@Strain 10.0 %,
Temperature 80.0 °C		7400 psi
@Strain 10.0 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.0 MPa
@Strain 1.60 %,
Temperature 60.0 °C		7400 psi
@Strain 1.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 51.1 MPa
@Strain 3.30 %,
Temperature 60.0 °C		7410 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 3.00 %,
Temperature 80.0 °C		7410 psi
@Strain 3.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 51.1 MPa
@Strain 8.50 %,
Temperature 80.0 °C		7410 psi
@Strain 8.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 9.00 %,
Temperature 80.0 °C		7410 psi
@Strain 9.00 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.1 MPa
@Strain 9.50 %,
Temperature 80.0 °C		7410 psi
@Strain 9.50 %,
Temperature 176 °F		50%RH; ISO 11403-1/-2
 51.218 MPa
@Strain 5.00 %,
Temperature 120 °C		7428.6 psi
@Strain 5.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.306 MPa
@Strain 0.800 %,
Temperature -40.0 °C		7441.3 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 51.8 MPa
@Strain 3.40 %,
Temperature 60.0 °C		7510 psi
@Strain 3.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 51.979 MPa
@Strain 5.50 %,
Temperature 120 °C		7538.9 psi
@Strain 5.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.982 MPa
@Strain 2.10 %,
Temperature 23.0 °C		7539.4 psi
@Strain 2.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.1 MPa
@Strain 3.10 %,
Temperature 80.0 °C		7560 psi
@Strain 3.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 52.5 MPa
@Strain 3.50 %,
Temperature 60.0 °C		7610 psi
@Strain 3.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 52.931 MPa
@Strain 6.00 %,
Temperature 120 °C		7677.0 psi
@Strain 6.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.0 MPa
@Strain 3.60 %,
Temperature 60.0 °C		7690 psi
@Strain 3.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.1 MPa
@Strain 3.20 %,
Temperature 80.0 °C		7700 psi
@Strain 3.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 53.2 MPa
@Strain 1.70 %,
Temperature 60.0 °C		7720 psi
@Strain 1.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 53.2 MPa
@Strain 1.00 %,
Temperature 0.000 °C		7720 psi
@Strain 1.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 53.47 MPa
@Strain 1.10 %,
Temperature 23.0 °C		7755 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 53.486 MPa
@Strain 2.20 %,
Temperature 23.0 °C		7757.5 psi
@Strain 2.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.5 MPa
@Strain 3.70 %,
Temperature 60.0 °C		7760 psi
@Strain 3.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.598 MPa
@Strain 6.50 %,
Temperature 120 °C		7773.7 psi
@Strain 6.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.978 MPa
@Strain 7.00 %,
Temperature 120 °C		7828.9 psi
@Strain 7.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.0 MPa
@Strain 3.80 %,
Temperature 60.0 °C		7830 psi
@Strain 3.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.2 MPa
@Strain 3.30 %,
Temperature 80.0 °C		7860 psi
@Strain 3.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 54.359 MPa
@Strain 7.50 %,
Temperature 120 °C		7884.1 psi
@Strain 7.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.4 MPa
@Strain 3.90 %,
Temperature 60.0 °C		7890 psi
@Strain 3.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.645 MPa
@Strain 8.00 %,
Temperature 120 °C		7925.6 psi
@Strain 8.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.8 MPa
@Strain 4.00 %,
Temperature 60.0 °C		7950 psi
@Strain 4.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 54.835 MPa
@Strain 8.50 %,
Temperature 120 °C		7953.2 psi
@Strain 8.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.835 MPa
@Strain 12.0 %,
Temperature 120 °C		7953.2 psi
@Strain 12.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.93 MPa
@Strain 9.00 %,
Temperature 120 °C		7967 psi
@Strain 9.00 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.99 MPa
@Strain 2.30 %,
Temperature 23.0 °C		7976 psi
@Strain 2.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 55.026 MPa
@Strain 9.50 %,
Temperature 120 °C		7980.9 psi
@Strain 9.50 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.026 MPa
@Strain 10.0 %,
Temperature 120 °C		7980.9 psi
@Strain 10.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.026 MPa
@Strain 11.0 %,
Temperature 120 °C		7980.9 psi
@Strain 11.0 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.1 MPa
@Strain 1.80 %,
Temperature 60.0 °C		7990 psi
@Strain 1.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 55.2 MPa
@Strain 3.40 %,
Temperature 80.0 °C		8010 psi
@Strain 3.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 55.2 MPa
@Strain 4.10 %,
Temperature 60.0 °C		8010 psi
@Strain 4.10 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.5 MPa
@Strain 4.20 %,
Temperature 60.0 °C		8050 psi
@Strain 4.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.8 MPa
@Strain 4.30 %,
Temperature 60.0 °C		8090 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 55.8 MPa
@Strain 0.900 %,
Temperature -40.0 °C		8090 psi
@Strain 0.900 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 56.0 MPa
@Strain 4.40 %,
Temperature 60.0 °C		8120 psi
@Strain 4.40 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.156 MPa
@Strain 1.00 %,
Temperature 0.000 °C		8144.8 psi
@Strain 1.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 56.2 MPa
@Strain 3.50 %,
Temperature 80.0 °C		8150 psi
@Strain 3.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 56.3 MPa
@Strain 4.50 %,
Temperature 60.0 °C		8170 psi
@Strain 4.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.494 MPa
@Strain 2.40 %,
Temperature 23.0 °C		8193.8 psi
@Strain 2.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 56.5 MPa
@Strain 4.60 %,
Temperature 60.0 °C		8190 psi
@Strain 4.60 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 56.8 MPa
@Strain 4.70 %,
Temperature 60.0 °C		8240 psi
@Strain 4.70 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.0 MPa
@Strain 4.80 %,
Temperature 60.0 °C		8270 psi
@Strain 4.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.1 MPa
@Strain 4.90 %,
Temperature 60.0 °C		8280 psi
@Strain 4.90 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.1 MPa
@Strain 1.90 %,
Temperature 60.0 °C		8280 psi
@Strain 1.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 57.2 MPa
@Strain 3.60 %,
Temperature 80.0 °C		8300 psi
@Strain 3.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 57.4 MPa
@Strain 5.00 %,
Temperature 60.0 °C		8330 psi
@Strain 5.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.426 MPa
@Strain 0.900 %,
Temperature -40.0 °C		8329.0 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 57.7 MPa
@Strain 1.10 %,
Temperature 0.000 °C		8370 psi
@Strain 1.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 57.7 MPa
@Strain 14.0 %,
Temperature 60.0 °C		8370 psi
@Strain 14.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.9 MPa
@Strain 5.50 %,
Temperature 60.0 °C		8400 psi
@Strain 5.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 57.904 MPa
@Strain 2.50 %,
Temperature 23.0 °C		8398.3 psi
@Strain 2.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 58.02 MPa
@Strain 1.20 %,
Temperature 23.0 °C		8415 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.1 MPa
@Strain 3.70 %,
Temperature 80.0 °C		8430 psi
@Strain 3.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 58.5 MPa
@Strain 6.00 %,
Temperature 60.0 °C		8480 psi
@Strain 6.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 58.5 MPa
@Strain 13.0 %,
Temperature 60.0 °C		8480 psi
@Strain 13.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 58.9 MPa
@Strain 2.00 %,
Temperature 60.0 °C		8540 psi
@Strain 2.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 58.9 MPa
@Strain 3.80 %,
Temperature 80.0 °C		8540 psi
@Strain 3.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 59.0 MPa
@Strain 6.50 %,
Temperature 60.0 °C		8560 psi
@Strain 6.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.0 MPa
@Strain 12.0 %,
Temperature 60.0 °C		8560 psi
@Strain 12.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.3 MPa
@Strain 11.0 %,
Temperature 60.0 °C		8600 psi
@Strain 11.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.3 MPa
@Strain 7.00 %,
Temperature 60.0 °C		8600 psi
@Strain 7.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.314 MPa
@Strain 2.60 %,
Temperature 23.0 °C		8602.8 psi
@Strain 2.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 59.4 MPa
@Strain 7.50 %,
Temperature 60.0 °C		8620 psi
@Strain 7.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.5 MPa
@Strain 8.00 %,
Temperature 60.0 °C		8630 psi
@Strain 8.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.5 MPa
@Strain 10.0 %,
Temperature 60.0 °C		8630 psi
@Strain 10.0 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.6 MPa
@Strain 8.50 %,
Temperature 60.0 °C		8640 psi
@Strain 8.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.6 MPa
@Strain 9.50 %,
Temperature 60.0 °C		8640 psi
@Strain 9.50 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.7 MPa
@Strain 9.00 %,
Temperature 60.0 °C		8660 psi
@Strain 9.00 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.7 MPa
@Strain 3.90 %,
Temperature 80.0 °C		8660 psi
@Strain 3.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.5 MPa
@Strain 4.00 %,
Temperature 80.0 °C		8770 psi
@Strain 4.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 60.536 MPa
@Strain 2.70 %,
Temperature 23.0 °C		8780.0 psi
@Strain 2.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 60.6 MPa
@Strain 2.10 %,
Temperature 60.0 °C		8790 psi
@Strain 2.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 61.0 MPa
@Strain 4.10 %,
Temperature 80.0 °C		8850 psi
@Strain 4.10 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.61 MPa
@Strain 1.10 %,
Temperature 0.000 °C		8936 psi
@Strain 1.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 61.7 MPa
@Strain 4.20 %,
Temperature 80.0 °C		8950 psi
@Strain 4.20 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 61.9 MPa
@Strain 1.00 %,
Temperature -40.0 °C		8980 psi
@Strain 1.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 61.946 MPa
@Strain 2.80 %,
Temperature 23.0 °C		8984.5 psi
@Strain 2.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 62.0 MPa
@Strain 1.20 %,
Temperature 0.000 °C		8990 psi
@Strain 1.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 62.3 MPa
@Strain 4.30 %,
Temperature 80.0 °C		9040 psi
@Strain 4.30 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 62.34 MPa
@Strain 1.30 %,
Temperature 23.0 °C		9042 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.5 MPa
@Strain 2.20 %,
Temperature 60.0 °C		9060 psi
@Strain 2.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 62.9 MPa
@Strain 4.40 %,
Temperature 80.0 °C		9120 psi
@Strain 4.40 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.24 MPa
@Strain 1.00 %,
Temperature -40.0 °C		9172 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 63.262 MPa
@Strain 2.90 %,
Temperature 23.0 °C		9175.4 psi
@Strain 2.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.4 MPa
@Strain 4.50 %,
Temperature 80.0 °C		9200 psi
@Strain 4.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 63.9 MPa
@Strain 4.60 %,
Temperature 80.0 °C		9270 psi
@Strain 4.60 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.2 MPa
@Strain 2.30 %,
Temperature 60.0 °C		9310 psi
@Strain 2.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 64.39 MPa
@Strain 3.00 %,
Temperature 23.0 °C		9339 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 64.4 MPa
@Strain 4.70 %,
Temperature 80.0 °C		9340 psi
@Strain 4.70 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 64.7 MPa
@Strain 4.80 %,
Temperature 80.0 °C		9380 psi
@Strain 4.80 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.0 MPa
@Strain 4.90 %,
Temperature 80.0 °C		9430 psi
@Strain 4.90 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.5 MPa
@Strain 5.00 %,
Temperature 80.0 °C		9500 psi
@Strain 5.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 65.612 MPa
@Strain 3.10 %,
Temperature 23.0 °C		9516.2 psi
@Strain 3.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 65.8 MPa
@Strain 2.40 %,
Temperature 60.0 °C		9540 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.2 MPa
@Strain 1.30 %,
Temperature 0.000 °C		9600 psi
@Strain 1.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 66.7 MPa
@Strain 5.50 %,
Temperature 80.0 °C		9670 psi
@Strain 5.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 66.74 MPa
@Strain 3.20 %,
Temperature 23.0 °C		9680 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 66.76 MPa
@Strain 1.40 %,
Temperature 23.0 °C		9683 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.761 MPa
@Strain 1.20 %,
Temperature 0.000 °C		9682.9 psi
@Strain 1.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 67.1 MPa
@Strain 2.50 %,
Temperature 60.0 °C		9730 psi
@Strain 2.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 67.68 MPa
@Strain 3.30 %,
Temperature 23.0 °C		9816 psi
@Strain 3.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 67.8 MPa
@Strain 1.10 %,
Temperature -40.0 °C		9830 psi
@Strain 1.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 67.8 MPa
@Strain 6.00 %,
Temperature 80.0 °C		9830 psi
@Strain 6.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 68.4 MPa
@Strain 6.50 %,
Temperature 80.0 °C		9920 psi
@Strain 6.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 68.5 MPa
@Strain 2.60 %,
Temperature 60.0 °C		9940 psi
@Strain 2.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 68.62 MPa
@Strain 3.40 %,
Temperature 23.0 °C		9953 psi
@Strain 3.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 68.952 MPa
@Strain 1.10 %,
Temperature -40.0 °C		10001 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 69.0 MPa
@Strain 7.00 %,
Temperature 80.0 °C		10000 psi
@Strain 7.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.5 MPa
@Strain 7.50 %,
Temperature 80.0 °C		10100 psi
@Strain 7.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 69.56 MPa
@Strain 3.50 %,
Temperature 23.0 °C		10090 psi
@Strain 3.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 69.8 MPa
@Strain 8.00 %,
Temperature 80.0 °C		10100 psi
@Strain 8.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.0 MPa
@Strain 2.70 %,
Temperature 60.0 °C		10200 psi
@Strain 2.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 70.1 MPa
@Strain 8.50 %,
Temperature 80.0 °C		10200 psi
@Strain 8.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.2 MPa
@Strain 1.40 %,
Temperature 0.000 °C		10200 psi
@Strain 1.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.4 MPa
@Strain 9.00 %,
Temperature 80.0 °C		10200 psi
@Strain 9.00 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.4 MPa
@Strain 15.0 %,
Temperature 80.0 °C		10200 psi
@Strain 15.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.5 MPa
@Strain 14.0 %,
Temperature 80.0 °C		10200 psi
@Strain 14.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.5 MPa
@Strain 9.50 %,
Temperature 80.0 °C		10200 psi
@Strain 9.50 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.5 MPa
@Strain 3.60 %,
Temperature 23.0 °C		10200 psi
@Strain 3.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 70.6 MPa
@Strain 10.0 %,
Temperature 80.0 °C		10200 psi
@Strain 10.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.6 MPa
@Strain 13.0 %,
Temperature 80.0 °C		10200 psi
@Strain 13.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.65 MPa
@Strain 11.0 %,
Temperature 80.0 °C		10250 psi
@Strain 11.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 70.7 MPa
@Strain 12.0 %,
Temperature 80.0 °C		10300 psi
@Strain 12.0 %,
Temperature 176 °F		DAM; ISO 11403-1/-2
 71.04 MPa
@Strain 1.50 %,
Temperature 23.0 °C		10300 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 71.158 MPa
@Strain 3.70 %,
Temperature 23.0 °C		10321 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 71.2 MPa
@Strain 2.80 %,
Temperature 60.0 °C		10300 psi
@Strain 2.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 71.91 MPa
@Strain 3.80 %,
Temperature 23.0 °C		10430 psi
@Strain 3.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.013 MPa
@Strain 1.30 %,
Temperature 0.000 °C		10445 psi
@Strain 1.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 72.4 MPa
@Strain 2.90 %,
Temperature 60.0 °C		10500 psi
@Strain 2.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 72.568 MPa
@Strain 3.90 %,
Temperature 23.0 °C		10525 psi
@Strain 3.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 72.944 MPa
@Strain 4.00 %,
Temperature 23.0 °C		10580 psi
@Strain 4.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.2 MPa
@Strain 1.20 %,
Temperature -40.0 °C		10600 psi
@Strain 1.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 73.226 MPa
@Strain 13.0 %,
Temperature 23.0 °C		10621 psi
@Strain 13.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.5 MPa
@Strain 3.00 %,
Temperature 60.0 °C		10700 psi
@Strain 3.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 73.508 MPa
@Strain 4.10 %,
Temperature 23.0 °C		10661 psi
@Strain 4.10 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 73.8 MPa
@Strain 1.50 %,
Temperature 0.000 °C		10700 psi
@Strain 1.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 73.884 MPa
@Strain 4.20 %,
Temperature 23.0 °C		10716 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.072 MPa
@Strain 12.0 %,
Temperature 23.0 °C		10743 psi
@Strain 12.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.26 MPa
@Strain 4.30 %,
Temperature 23.0 °C		10770 psi
@Strain 4.30 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.6 MPa
@Strain 3.10 %,
Temperature 60.0 °C		10800 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 74.636 MPa
@Strain 4.40 %,
Temperature 23.0 °C		10825 psi
@Strain 4.40 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.73 MPa
@Strain 4.50 %,
Temperature 23.0 °C		10840 psi
@Strain 4.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.73 MPa
@Strain 11.0 %,
Temperature 23.0 °C		10840 psi
@Strain 11.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 74.766 MPa
@Strain 1.20 %,
Temperature -40.0 °C		10844 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 75.012 MPa
@Strain 4.60 %,
Temperature 23.0 °C		10880 psi
@Strain 4.60 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.106 MPa
@Strain 4.70 %,
Temperature 23.0 °C		10893 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.27 MPa
@Strain 1.60 %,
Temperature 23.0 °C		10920 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 75.294 MPa
@Strain 4.80 %,
Temperature 23.0 °C		10920 psi
@Strain 4.80 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.294 MPa
@Strain 10.0 %,
Temperature 23.0 °C		10920 psi
@Strain 10.0 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.482 MPa
@Strain 9.50 %,
Temperature 23.0 °C		10948 psi
@Strain 9.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.482 MPa
@Strain 4.90 %,
Temperature 23.0 °C		10948 psi
@Strain 4.90 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.576 MPa
@Strain 5.00 %,
Temperature 23.0 °C		10961 psi
@Strain 5.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.6 MPa
@Strain 3.20 %,
Temperature 60.0 °C		11000 psi
@Strain 3.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 75.764 MPa
@Strain 9.00 %,
Temperature 23.0 °C		10989 psi
@Strain 9.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.858 MPa
@Strain 8.50 %,
Temperature 23.0 °C		11002 psi
@Strain 8.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 75.952 MPa
@Strain 5.50 %,
Temperature 23.0 °C		11016 psi
@Strain 5.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.046 MPa
@Strain 8.00 %,
Temperature 23.0 °C		11030 psi
@Strain 8.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.14 MPa
@Strain 7.50 %,
Temperature 23.0 °C		11040 psi
@Strain 7.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.14 MPa
@Strain 6.00 %,
Temperature 23.0 °C		11040 psi
@Strain 6.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.234 MPa
@Strain 6.50 %,
Temperature 23.0 °C		11057 psi
@Strain 6.50 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.234 MPa
@Strain 7.00 %,
Temperature 23.0 °C		11057 psi
@Strain 7.00 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 76.6 MPa
@Strain 3.30 %,
Temperature 60.0 °C		11100 psi
@Strain 3.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 76.962 MPa
@Strain 1.40 %,
Temperature 0.000 °C		11162 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 77.2 MPa
@Strain 1.60 %,
Temperature 0.000 °C		11200 psi
@Strain 1.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 77.5 MPa
@Strain 3.40 %,
Temperature 60.0 °C		11200 psi
@Strain 3.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 3.50 %,
Temperature 60.0 °C		11400 psi
@Strain 3.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 78.4 MPa
@Strain 1.30 %,
Temperature -40.0 °C		11400 psi
@Strain 1.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 79.2 MPa
@Strain 3.60 %,
Temperature 60.0 °C		11500 psi
@Strain 3.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 79.3 MPa
@Strain 1.70 %,
Temperature 23.0 °C		11500 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.8 MPa
@Strain 3.70 %,
Temperature 60.0 °C		11600 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 80.07 MPa
@Strain 1.30 %,
Temperature -40.0 °C		11610 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.5 MPa
@Strain 3.80 %,
Temperature 60.0 °C		11700 psi
@Strain 3.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 80.6 MPa
@Strain 1.70 %,
Temperature 0.000 °C		11700 psi
@Strain 1.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 81.1 MPa
@Strain 3.90 %,
Temperature 60.0 °C		11800 psi
@Strain 3.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 81.6 MPa
@Strain 4.00 %,
Temperature 60.0 °C		11800 psi
@Strain 4.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 81.709 MPa
@Strain 1.50 %,
Temperature 0.000 °C		11851 psi
@Strain 1.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 82.0 MPa
@Strain 4.10 %,
Temperature 60.0 °C		11900 psi
@Strain 4.10 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.3 MPa
@Strain 4.20 %,
Temperature 60.0 °C		11900 psi
@Strain 4.20 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.4 MPa
@Strain 13.0 %,
Temperature 60.0 °C		12000 psi
@Strain 13.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.7 MPa
@Strain 4.30 %,
Temperature 60.0 °C		12000 psi
@Strain 4.30 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.8 MPa
@Strain 12.0 %,
Temperature 60.0 °C		12000 psi
@Strain 12.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 82.9 MPa
@Strain 4.40 %,
Temperature 60.0 °C		12000 psi
@Strain 4.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.1 MPa
@Strain 4.50 %,
Temperature 60.0 °C		12100 psi
@Strain 4.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.17 MPa
@Strain 1.80 %,
Temperature 23.0 °C		12060 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 83.2 MPa
@Strain 11.0 %,
Temperature 60.0 °C		12100 psi
@Strain 11.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.3 MPa
@Strain 4.60 %,
Temperature 60.0 °C		12100 psi
@Strain 4.60 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.4 MPa
@Strain 4.70 %,
Temperature 60.0 °C		12100 psi
@Strain 4.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.5 MPa
@Strain 10.0 %,
Temperature 60.0 °C		12100 psi
@Strain 10.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.5 MPa
@Strain 1.40 %,
Temperature -40.0 °C		12100 psi
@Strain 1.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 83.6 MPa
@Strain 1.80 %,
Temperature 0.000 °C		12100 psi
@Strain 1.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 83.6 MPa
@Strain 4.80 %,
Temperature 60.0 °C		12100 psi
@Strain 4.80 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.7 MPa
@Strain 4.90 %,
Temperature 60.0 °C		12100 psi
@Strain 4.90 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.7 MPa
@Strain 9.00 %,
Temperature 60.0 °C		12100 psi
@Strain 9.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.7 MPa
@Strain 9.50 %,
Temperature 60.0 °C		12100 psi
@Strain 9.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.8 MPa
@Strain 5.00 %,
Temperature 60.0 °C		12200 psi
@Strain 5.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.9 MPa
@Strain 5.50 %,
Temperature 60.0 °C		12200 psi
@Strain 5.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 83.9 MPa
@Strain 8.50 %,
Temperature 60.0 °C		12200 psi
@Strain 8.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.0 MPa
@Strain 7.00 %,
Temperature 60.0 °C		12200 psi
@Strain 7.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.0 MPa
@Strain 7.50 %,
Temperature 60.0 °C		12200 psi
@Strain 7.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.0 MPa
@Strain 8.00 %,
Temperature 60.0 °C		12200 psi
@Strain 8.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.1 MPa
@Strain 6.00 %,
Temperature 60.0 °C		12200 psi
@Strain 6.00 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 84.1 MPa
@Strain 6.50 %,
Temperature 60.0 °C		12200 psi
@Strain 6.50 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 85.374 MPa
@Strain 1.40 %,
Temperature -40.0 °C		12382 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 86.3 MPa
@Strain 1.90 %,
Temperature 0.000 °C		12500 psi
@Strain 1.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 86.456 MPa
@Strain 1.60 %,
Temperature 0.000 °C		12539 psi
@Strain 1.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 87.01 MPa
@Strain 1.90 %,
Temperature 23.0 °C		12620 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 88.6 MPa
@Strain 1.50 %,
Temperature -40.0 °C		12900 psi
@Strain 1.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 89.0 MPa
@Strain 2.00 %,
Temperature 0.000 °C		12900 psi
@Strain 2.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 90.56 MPa
@Strain 2.00 %,
Temperature 23.0 °C		13130 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 90.576 MPa
@Strain 1.50 %,
Temperature -40.0 °C		13137 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 91.102 MPa
@Strain 1.70 %,
Temperature 0.000 °C		13213 psi
@Strain 1.70 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 91.5 MPa
@Strain 2.10 %,
Temperature 0.000 °C		13300 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 93.6 MPa
@Strain 1.60 %,
Temperature -40.0 °C		13600 psi
@Strain 1.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 93.9 MPa
@Strain 2.20 %,
Temperature 0.000 °C		13600 psi
@Strain 2.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 94.05 MPa
@Strain 2.10 %,
Temperature 23.0 °C		13640 psi
@Strain 2.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 95.546 MPa
@Strain 1.80 %,
Temperature 0.000 °C		13858 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 95.574 MPa
@Strain 1.60 %,
Temperature -40.0 °C		13862 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 96.2 MPa
@Strain 2.30 %,
Temperature 0.000 °C		14000 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 97.39 MPa
@Strain 2.20 %,
Temperature 23.0 °C		14130 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 98.1 MPa
@Strain 2.40 %,
Temperature 0.000 °C		14200 psi
@Strain 2.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 98.5 MPa
@Strain 1.70 %,
Temperature -40.0 °C		14300 psi
@Strain 1.70 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 99.788 MPa
@Strain 1.90 %,
Temperature 0.000 °C		14473 psi
@Strain 1.90 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 100.2 MPa
@Strain 2.50 %,
Temperature 0.000 °C		14530 psi
@Strain 2.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 100.53 MPa
@Strain 2.30 %,
Temperature 23.0 °C		14581 psi
@Strain 2.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 100.57 MPa
@Strain 1.70 %,
Temperature -40.0 °C		14586 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 102 MPa
@Strain 2.60 %,
Temperature 0.000 °C		14800 psi
@Strain 2.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 102.9 MPa
@Strain 1.80 %,
Temperature -40.0 °C		14920 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 103.51 MPa
@Strain 2.40 %,
Temperature 23.0 °C		15013 psi
@Strain 2.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.7 MPa
@Strain 2.70 %,
Temperature 0.000 °C		15040 psi
@Strain 2.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 104.13 MPa
@Strain 2.00 %,
Temperature 0.000 °C		15103 psi
@Strain 2.00 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 105.1 MPa
@Strain 2.80 %,
Temperature 0.000 °C		15240 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 105.37 MPa
@Strain 1.80 %,
Temperature -40.0 °C		15283 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 106.4 MPa
@Strain 2.90 %,
Temperature 0.000 °C		15430 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 106.43 MPa
@Strain 2.50 %,
Temperature 23.0 °C		15436 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 107.1 MPa
@Strain 1.90 %,
Temperature -40.0 °C		15530 psi
@Strain 1.90 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 107.87 MPa
@Strain 2.10 %,
Temperature 0.000 °C		15645 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 108 MPa
@Strain 3.00 %,
Temperature 0.000 °C		15700 psi
@Strain 3.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 109.15 MPa
@Strain 2.60 %,
Temperature 23.0 °C		15831 psi
@Strain 2.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 109.8 MPa
@Strain 3.10 %,
Temperature 0.000 °C		15930 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 110.26 MPa
@Strain 1.90 %,
Temperature -40.0 °C		15992 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 111.3 MPa
@Strain 3.20 %,
Temperature 0.000 °C		16140 psi
@Strain 3.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 111.5 MPa
@Strain 2.00 %,
Temperature -40.0 °C		16170 psi
@Strain 2.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 111.65 MPa
@Strain 2.70 %,
Temperature 23.0 °C		16193 psi
@Strain 2.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 111.81 MPa
@Strain 2.20 %,
Temperature 0.000 °C		16217 psi
@Strain 2.20 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 112.6 MPa
@Strain 3.30 %,
Temperature 0.000 °C		16330 psi
@Strain 3.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 113.9 MPa
@Strain 3.40 %,
Temperature 0.000 °C		16520 psi
@Strain 3.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 113.92 MPa
@Strain 2.80 %,
Temperature 23.0 °C		16523 psi
@Strain 2.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114.34 MPa
@Strain 2.00 %,
Temperature -40.0 °C		16584 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.7 MPa
@Strain 3.50 %,
Temperature 0.000 °C		16640 psi
@Strain 3.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 115.2 MPa
@Strain 3.60 %,
Temperature 0.000 °C		16710 psi
@Strain 3.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 115.6 MPa
@Strain 2.10 %,
Temperature -40.0 °C		16770 psi
@Strain 2.10 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 115.95 MPa
@Strain 2.30 %,
Temperature 0.000 °C		16817 psi
@Strain 2.30 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 116.1 MPa
@Strain 2.90 %,
Temperature 23.0 °C		16840 psi
@Strain 2.90 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 116.3 MPa
@Strain 3.70 %,
Temperature 0.000 °C		16870 psi
@Strain 3.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 117.4 MPa
@Strain 3.80 %,
Temperature 0.000 °C		17030 psi
@Strain 3.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 118.08 MPa
@Strain 3.00 %,
Temperature 23.0 °C		17126 psi
@Strain 3.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 118.4 MPa
@Strain 3.90 %,
Temperature 0.000 °C		17170 psi
@Strain 3.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 118.73 MPa
@Strain 2.10 %,
Temperature -40.0 °C		17220 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 118.78 MPa
@Strain 2.40 %,
Temperature 0.000 °C		17228 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 119.3 MPa
@Strain 4.00 %,
Temperature 0.000 °C		17300 psi
@Strain 4.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 119.4 MPa
@Strain 2.20 %,
Temperature -40.0 °C		17320 psi
@Strain 2.20 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 119.9 MPa
@Strain 4.10 %,
Temperature 0.000 °C		17390 psi
@Strain 4.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 119.91 MPa
@Strain 3.10 %,
Temperature 23.0 °C		17392 psi
@Strain 3.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 120.3 MPa
@Strain 5.00 %,
Temperature 0.000 °C		17450 psi
@Strain 5.00 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.4 MPa
@Strain 4.20 %,
Temperature 0.000 °C		17460 psi
@Strain 4.20 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.5 MPa
@Strain 4.90 %,
Temperature 0.000 °C		17480 psi
@Strain 4.90 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.7 MPa
@Strain 4.80 %,
Temperature 0.000 °C		17510 psi
@Strain 4.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.7 MPa
@Strain 4.30 %,
Temperature 0.000 °C		17510 psi
@Strain 4.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.9 MPa
@Strain 4.60 %,
Temperature 0.000 °C		17540 psi
@Strain 4.60 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.9 MPa
@Strain 4.70 %,
Temperature 0.000 °C		17540 psi
@Strain 4.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 120.9 MPa
@Strain 4.40 %,
Temperature 0.000 °C		17540 psi
@Strain 4.40 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 121 MPa
@Strain 4.50 %,
Temperature 0.000 °C		17500 psi
@Strain 4.50 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 122.82 MPa
@Strain 2.50 %,
Temperature 0.000 °C		17814 psi
@Strain 2.50 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 123.11 MPa
@Strain 2.20 %,
Temperature -40.0 °C		17856 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 123.4 MPa
@Strain 2.30 %,
Temperature -40.0 °C		17900 psi
@Strain 2.30 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 126.15 MPa
@Strain 2.60 %,
Temperature 0.000 °C		18297 psi
@Strain 2.60 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 127.19 MPa
@Strain 2.30 %,
Temperature -40.0 °C		18447 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 127.2 MPa
@Strain 2.40 %,
Temperature -40.0 °C		18450 psi
@Strain 2.40 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 130.8 MPa
@Strain 2.50 %,
Temperature -40.0 °C		18970 psi
@Strain 2.50 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 131.07 MPa
@Strain 2.40 %,
Temperature -40.0 °C		19010 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 134.1 MPa
@Strain 2.60 %,
Temperature -40.0 °C		19450 psi
@Strain 2.60 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 135.05 MPa
@Strain 2.50 %,
Temperature -40.0 °C		19587 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ISO 527
 8.0 %
@Temperature 23.0 °C		8.0 %
@Temperature 73.4 °F		50%RH; ASTM D638
 13 %
@Temperature 23.0 °C		13 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  3.50 GPa
@Temperature 23.0 °C		508 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 5.50 GPa
@Temperature 23.0 °C		798 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength  100 MPa
@Temperature 23.0 °C		14500 psi
@Temperature 73.4 °F		50%RH; ISO 178
 165 MPa
@Temperature 23.0 °C		23900 psi
@Temperature 73.4 °F		DAM; ASTM D790
 190 MPa
@Temperature 23.0 °C		27600 psi
@Temperature 73.4 °F		DAM; ISO 178
Flexural Modulus  2.76 GPa
@Temperature 23.0 °C		400 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 2.90 GPa
@Temperature 23.0 °C		421 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 4.80 GPa
@Temperature 23.0 °C		696 ksi
@Temperature 73.4 °F		DAM; ISO 178
 4.83 GPa
@Temperature 23.0 °C		701 ksi
@Temperature 73.4 °F		DAM; ASTM D790
Shear Strength 76.0 MPa
@Temperature 23.0 °C		11000 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.480 J/cm
@Temperature 23.0 °C		0.899 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 0.530 J/cm
@Temperature 23.0 °C		0.993 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  3.00 kJ/m²
@Temperature -40.0 °C		1.43 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 180/1A
 3.00 kJ/m²
@Temperature -30.0 °C		1.43 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
 4.50 kJ/m²
@Temperature -40.0 °C		2.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature 23.0 °C		2.14 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)  28.0 kJ/m²
@Temperature -30.0 °C		13.3 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1U
 35.0 kJ/m²
@Temperature -30.0 °C		16.7 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 40.0 kJ/m²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
 55.0 kJ/m²
@Temperature 23.0 °C		26.2 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1U
Charpy Impact Unnotched  3.00 J/cm²
@Temperature -30.0 °C		14.3 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 4.00 J/cm²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 4.00 J/cm²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 7.00 J/cm²
@Temperature 23.0 °C		33.3 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -40.0 °C		1.90 ft-lb/in²
@Temperature -40.0 °F		50%RH; ISO 179/1eA
 0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.450 J/cm²
@Temperature -40.0 °C		2.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 0.450 J/cm²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.500 J/cm²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 3300 MPa
@Temperature 23.0 °C		479000 psi
@Temperature 73.4 °F		50%RH; ISO 899
Tensile Creep Modulus, 1000 hours 2200 MPa
@Temperature 23.0 °C		319000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
 1.00e+16 ohm-cm
@Temperature 23.0 °C		1.00e+16 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Surface Resistance 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		50%RH; IEC 60093
Dielectric Constant  3.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.9
@Frequency 100 Hz,
Temperature 23.0 °C		3.9
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
Dielectric Strength 25.0 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		635 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		DAM; IEC 60243-1
Dissipation Factor  0.013
@Frequency 100 Hz,
Temperature 23.0 °C		0.013
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.015
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.015
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
Comparative Tracking Index  >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; IEC 60112
 600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; IEC 60112
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Thickness 3.00 mm,
Temperature 23.0 °C		>= 600 V
@Thickness 0.118 in,
Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  77.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		42.8 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 77.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		42.8 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 96.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		53.3 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 96.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		53.3 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 158 µm/m-°C
@Temperature 55.0 - 160 °C		87.8 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 158 µm/m-°C
@Temperature 55.0 - 160 °C		87.8 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Melting Point 263 °C505 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 258 °C496 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 238 °C460 °FDAM; ISO 75-1/-2
 243 °C469 °FDAM; ASTM D648
Glass Transition Temp, Tg 80.0 °C176 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  125 °C
@Thickness 0.710 mm		257 °F
@Thickness 0.0280 in		DAM; UL 746B
 125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		DAM; UL 746B
 125 °C
@Thickness 3.00 mm		257 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		DAM; UL 746B
 120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		DAM; UL 746B
 120 °C
@Thickness 0.710 mm		248 °F
@Thickness 0.0280 in		DAM; UL 746B
UL RTI, Mechanical without Impact  125 °C
@Thickness 3.00 mm		257 °F
@Thickness 0.118 in		DAM; UL 746B
 125 °C
@Thickness 1.50 mm		257 °F
@Thickness 0.0591 in		DAM; UL 746B
 125 °C
@Thickness 0.710 mm		257 °F
@Thickness 0.0280 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.710 mm		HB
@Thickness 0.0280 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
Oxygen Index 24 %24 %DAM; ISO 4589-1/-2
Glow Wire Test  650 °C
@Thickness 0.750 mm		1200 °F
@Thickness 0.0295 in		DAM; IEC 60695-2-12
 650 °C
@Thickness 1.50 mm		1200 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 675 °C
@Thickness 3.00 mm		1250 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 675 °C
@Thickness 1.50 mm		1250 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 675 °C
@Thickness 0.750 mm		1250 °F
@Thickness 0.0295 in		DAM; Ignition; IEC 60695-2-13
 800 °C
@Thickness 3.00 mm		1470 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesGeneral PurposeDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-GF13<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-GF13ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 Electrical/Electronic ApplicationsDAM
 Industrial ApplicationsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45450.html

免责声明: 本文 DuPont Performance Polymers Zytel® 70G13L NC010 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4