- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 9.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 20 % | 20 % | DAM | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 70.0 MPa @Temperature 23.0 °C | 10200 psi @Temperature 73.4 °F | 5mm/min; 50%RH; ISO 527 | ||
| 120 MPa @Temperature 23.0 °C | 17400 psi @Temperature 73.4 °F | 5mm/min; DAM; ISO 527 | |||
| Elongation at Break | 3.9 % @Temperature 23.0 °C | 3.9 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 13.5 % @Temperature 23.0 °C | 13.5 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 4.00 GPa @Temperature 23.0 °C | 580 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 6.40 GPa @Temperature 23.0 °C | 928 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 7.20 J/cm² @Temperature 23.0 °C | 34.3 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| 7.20 J/cm² @Temperature 23.0 °C | 34.3 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.40 J/cm² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 237 °C | 459 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum; Blow Molding | |||
| 285 - 305 °C | 545 - 581 °F | DAM; Blow Molding | |||
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | DAM; Blow Molding | ||
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | DAM; Blow Molding | ||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Blow Molding | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA66-IGF20< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Blow Molding | DAM | |||
| Product Category | Blow Moldable Resins | DAM | |||
| Glass Reinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-IGF20 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||