- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 1.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.5 % @Thickness 1.00 mm, Temperature 23.0 °C | 1.5 % @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 5.0 % @Thickness 1.00 mm, Temperature 23.0 °C | 5.0 % @Thickness 0.0394 in, Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 145 MPa @Temperature 23.0 °C | 21000 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 2.6 % @Temperature 23.0 °C | 2.6 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 7.80 GPa @Temperature 23.0 °C | 1130 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 8.80 GPa @Temperature 23.0 °C | 1280 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Charpy Impact Unnotched | 4.10 J/cm² @Temperature 23.0 °C | 19.5 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| 4.10 J/cm² @Temperature 23.0 °C | 19.5 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | ||
| 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+12 ohm-cm @Temperature 23.0 °C | 2.00e+12 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 8.00e+14 ohm-cm @Temperature 23.0 °C | 8.00e+14 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 3.00e+14 ohm @Temperature 23.0 °C | 3.00e+14 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 33.3 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 90.0 °C | 194 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 245 °C | 473 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Glass/Mineral Reinforced Resins | DAM | ||||
| RoHS Compliance | Contact Manufacturer | DAM | |||