- 密度 [g/cm3]: 1.34
- 缺口冲击强度: 12.0
- 弯曲模量 [MPa]: 3.167
- 硬度: 113.0
- 热变形温度 [℃]: 247.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 2.00 mm | 0.0010 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 2.00 mm | 0.0060 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 53 | 53 | 50%RH; ISO 2039/2 | ||
| 81 | 81 | DAM; ISO 2039/2 | |||
| Hardness, Rockwell R | 113 | 113 | 50%RH; ISO 2039/2 | ||
| 116 | 116 | DAM; ISO 2039/2 | |||
| Tensile Strength at Break | 60.0 MPa @Temperature 150 °C | 8700 psi @Temperature 302 °F | 50%RH; ISO 527 | ||
| 66.0 MPa @Temperature 120 °C | 9570 psi @Temperature 248 °F | 50%RH; ISO 527 | |||
| 67.0 MPa @Temperature 150 °C | 9720 psi @Temperature 302 °F | DAM; ISO 527 | |||
| 71.0 MPa @Temperature 100 °C | 10300 psi @Temperature 212 °F | 50%RH; ISO 527 | |||
| 75.0 MPa @Temperature 120 °C | 10900 psi @Temperature 248 °F | DAM; ISO 527 | |||
| 77.0 MPa @Temperature 80.0 °C | 11200 psi @Temperature 176 °F | 50%RH; ISO 527 | |||
| 82.0 MPa @Temperature 100 °C | 11900 psi @Temperature 212 °F | DAM; ISO 527 | |||
| 84.0 MPa @Temperature 60.0 °C | 12200 psi @Temperature 140 °F | 50%RH; ISO 527 | |||
| 90.0 MPa @Temperature 80.0 °C | 13100 psi @Temperature 176 °F | DAM; ISO 527 | |||
| 102 MPa @Temperature 60.0 °C | 14800 psi @Temperature 140 °F | DAM; ISO 527 | |||
| 115 MPa @Temperature 23.0 °C | 16700 psi @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 144 MPa @Temperature 0.000 °C | 20900 psi @Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 150 MPa @Temperature 23.0 °C | 21800 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| 167 MPa @Temperature 0.000 °C | 24200 psi @Temperature 32.0 °F | DAM; ISO 527 | |||
| 205 MPa @Temperature -40.0 °C | 29700 psi @Temperature -40.0 °F | 50%RH; ISO 527 | |||
| 220 MPa @Temperature -40.0 °C | 31900 psi @Temperature -40.0 °F | DAM; ISO 527 | |||
| Elongation at Break | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 5.4 % @Temperature -40.0 °C | 5.4 % @Temperature -40.0 °F | 50%RH; ISO 527 | |||
| 5.5 % @Temperature 0.000 °C | 5.5 % @Temperature 32.0 °F | DAM; ISO 527 | |||
| 5.7 % @Temperature 0.000 °C | 5.7 % @Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 6.0 % @Temperature -40.0 °C | 6.0 % @Temperature -40.0 °F | DAM; ISO 527 | |||
| 8.5 % @Temperature 60.0 °C | 8.5 % @Temperature 140 °F | DAM; ISO 527 | |||
| 8.6 % @Temperature 23.0 °C | 8.6 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 9.2 % @Temperature 60.0 °C | 9.2 % @Temperature 140 °F | 50%RH; ISO 527 | |||
| 9.5 % @Temperature 80.0 °C | 9.5 % @Temperature 176 °F | 50%RH; ISO 527 | |||
| 9.5 % @Temperature 100 °C | 9.5 % @Temperature 212 °F | 50%RH; ISO 527 | |||
| 9.6 % @Temperature 80.0 °C | 9.6 % @Temperature 176 °F | DAM; ISO 527 | |||
| 10 % @Temperature 100 °C | 10 % @Temperature 212 °F | DAM; ISO 527 | |||
| 10.3 % @Temperature 120 °C | 10.3 % @Temperature 248 °F | 50%RH; ISO 527 | |||
| 10.7 % @Temperature 120 °C | 10.7 % @Temperature 248 °F | DAM; ISO 527 | |||
| 11.2 % @Temperature 150 °C | 11.2 % @Temperature 302 °F | 50%RH; ISO 527 | |||
| 11.6 % @Temperature 150 °C | 11.6 % @Temperature 302 °F | DAM; ISO 527 | |||
| Tensile Modulus | 3.746 GPa @Temperature 150 °C | 543.3 ksi @Temperature 302 °F | 50%RH; ISO 527 | ||
| 4.052 GPa @Temperature 150 °C | 587.7 ksi @Temperature 302 °F | DAM; ISO 527 | |||
| 4.223 GPa @Temperature 120 °C | 612.5 ksi @Temperature 248 °F | 50%RH; ISO 527 | |||
| 4.384 GPa @Temperature 120 °C | 635.8 ksi @Temperature 248 °F | DAM; ISO 527 | |||
| 4.70 GPa @Temperature 100 °C | 682 ksi @Temperature 212 °F | 50%RH; ISO 527 | |||
| 4.956 GPa @Temperature 100 °C | 718.8 ksi @Temperature 212 °F | DAM; ISO 527 | |||
| 5.182 GPa @Temperature 80.0 °C | 751.6 ksi @Temperature 176 °F | 50%RH; ISO 527 | |||
| 5.518 GPa @Temperature 60.0 °C | 800.3 ksi @Temperature 140 °F | 50%RH; ISO 527 | |||
| 5.614 GPa @Temperature 80.0 °C | 814.2 ksi @Temperature 176 °F | DAM; ISO 527 | |||
| 6.905 GPa @Temperature 60.0 °C | 1001 ksi @Temperature 140 °F | DAM; ISO 527 | |||
| 6.929 GPa @Temperature 23.0 °C | 1005 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| 9.074 GPa @Temperature 0.000 °C | 1316 ksi @Temperature 32.0 °F | DAM; ISO 527 | |||
| 9.286 GPa @Temperature 0.000 °C | 1347 ksi @Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 9.426 GPa @Temperature -40.0 °C | 1367 ksi @Temperature -40.0 °F | DAM; ISO 527 | |||
| 10.234 GPa @Temperature -40.0 °C | 1484.3 ksi @Temperature -40.0 °F | 50%RH; ISO 527 | |||
| Flexural Modulus | 3.167 GPa @Temperature 150 °C | 459.3 ksi @Temperature 302 °F | 50%RH; ISO 178 | ||
| 3.33 GPa @Temperature 150 °C | 483 ksi @Temperature 302 °F | DAM; ISO 178 | |||
| 3.461 GPa @Temperature 120 °C | 502.0 ksi @Temperature 248 °F | 50%RH; ISO 178 | |||
| 3.502 GPa @Temperature 120 °C | 507.9 ksi @Temperature 248 °F | DAM; ISO 178 | |||
| 3.633 GPa @Temperature 100 °C | 526.9 ksi @Temperature 212 °F | 50%RH; ISO 178 | |||
| 3.651 GPa @Temperature 100 °C | 529.5 ksi @Temperature 212 °F | DAM; ISO 178 | |||
| 3.737 GPa @Temperature 80.0 °C | 542.0 ksi @Temperature 176 °F | 50%RH; ISO 178 | |||
| 3.982 GPa @Temperature 80.0 °C | 577.5 ksi @Temperature 176 °F | DAM; ISO 178 | |||
| 4.006 GPa @Temperature 60.0 °C | 581.0 ksi @Temperature 140 °F | 50%RH; ISO 178 | |||
| 4.461 GPa @Temperature 60.0 °C | 647.0 ksi @Temperature 140 °F | DAM; ISO 178 | |||
| 5.60 GPa @Temperature 23.0 °C | 812 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | |||
| 7.683 GPa @Temperature 23.0 °C | 1114 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| 7.723 GPa @Temperature -40.0 °C | 1120 ksi @Temperature -40.0 °F | DAM; ISO 178 | |||
| 7.859 GPa @Temperature 0.000 °C | 1140 ksi @Temperature 32.0 °F | DAM; ISO 178 | |||
| 8.042 GPa @Temperature -40.0 °C | 1166 ksi @Temperature -40.0 °F | 50%RH; ISO 178 | |||
| 8.082 GPa @Temperature 0.000 °C | 1172 ksi @Temperature 32.0 °F | 50%RH; ISO 178 | |||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -40.0 °C | 5.71 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 180/1A | ||
| 15.0 kJ/m² @Temperature -40.0 °C | 7.14 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | |||
| 21.0 kJ/m² @Temperature 23.0 °C | 9.99 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 23.0 kJ/m² @Temperature 23.0 °C | 10.9 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -40.0 °C | 4.76 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 179/1eA | ||
| 1.10 J/cm² @Temperature -40.0 °C | 5.23 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | |||
| 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| 2.10 J/cm² @Temperature 23.0 °C | 9.99 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -30.0 - 30.0 °C | 278 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature -30.0 - 30.0 °C | 278 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -30.0 - 30.0 °C | 55.6 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ASTM E 831 | ||
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |||
| 100 µm/m-°C @Temperature -30.0 - 30.0 °C | 55.6 µin/in-°F @Temperature -22.0 - 86.0 °F | DAM; ISO 11359-1/-2 | |||
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C | 55.6 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 120 µm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 120 µm/m-°C @Temperature 55.0 - 160 °C | 66.7 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 120 µm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 120 µm/m-°C @Temperature 55.0 - 160 °C | 66.7 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 222 °C | 432 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 105 °C @Thickness 0.750 mm | 221 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 90.0 °C @Thickness 3.00 mm | 194 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 90.0 °C @Thickness 1.50 mm | 194 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 120 °C @Thickness 0.750 mm | 248 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 °C | 482 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM | ||
| 80.0 °C | 176 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | PA66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA66+PA6-IGF33< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Resin Identification | PA66+PA6-IGF33 | ISO 1043; DAM | |||