  4. DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66

DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66

DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66 物性表: DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.6
  • 吸水率 [%]: 0.7
  • 弯曲模量 [MPa]: 9.446
 
Physical PropertiesMetricEnglishComments
Density 1.60 g/cc0.0578 lb/in³DAM; ISO 1183
Filler Content 25 %25 %DAM
Water Absorption 0.70 %
@Thickness 1.00 mm,
Temperature 23.0 °C		0.70 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
@Thickness 2.00 mm		0.0080 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 170 MPa
@Temperature 23.0 °C		24700 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  3.79 MPa
@Strain 0.100 %,
Temperature 150 °C		550 psi
@Strain 0.100 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.60 MPa
@Strain 0.100 %,
Temperature 100 °C		957 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.28 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1200 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 9.09 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1320 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 10.03 MPa
@Strain 0.200 %,
Temperature 150 °C		1455 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.8 MPa
@Strain 0.200 %,
Temperature 100 °C		1860 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 16.02 MPa
@Strain 0.300 %,
Temperature 150 °C		2324 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.47 MPa
@Strain 0.200 %,
Temperature -40.0 °C		2389 psi
@Strain 0.200 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 18.09 MPa
@Strain 0.200 %,
Temperature 23.0 °C		2624 psi
@Strain 0.200 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 18.64 MPa
@Strain 0.300 %,
Temperature 100 °C		2704 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 20.87 MPa
@Strain 0.400 %,
Temperature 150 °C		3027 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.52 MPa
@Strain 0.400 %,
Temperature 100 °C		3411 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 24.91 MPa
@Strain 0.300 %,
Temperature -40.0 °C		3613 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 25.24 MPa
@Strain 0.500 %,
Temperature 150 °C		3661 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 27.19 MPa
@Strain 0.300 %,
Temperature 23.0 °C		3944 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 29.2 MPa
@Strain 0.600 %,
Temperature 150 °C		4240 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.46 MPa
@Strain 0.500 %,
Temperature 100 °C		4273 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 32.28 MPa
@Strain 0.400 %,
Temperature -40.0 °C		4682 psi
@Strain 0.400 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 32.69 MPa
@Strain 0.700 %,
Temperature 150 °C		4741 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 33.81 MPa
@Strain 0.600 %,
Temperature 100 °C		4904 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.85 MPa
@Strain 0.400 %,
Temperature 23.0 °C		5055 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 35.81 MPa
@Strain 0.800 %,
Temperature 150 °C		5194 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.91 MPa
@Strain 0.700 %,
Temperature 100 °C		5498 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 38.62 MPa
@Strain 0.900 %,
Temperature 150 °C		5601 psi
@Strain 0.900 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.07 MPa
@Strain 1.00 %,
Temperature 150 °C		5957 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.1 MPa
@Strain 0.800 %,
Temperature 100 °C		5960 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 41.95 MPa
@Strain 0.500 %,
Temperature -40.0 °C		6084 psi
@Strain 0.500 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 43.54 MPa
@Strain 1.10 %,
Temperature 150 °C		6315 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.27 MPa
@Strain 0.500 %,
Temperature 23.0 °C		6421 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 44.92 MPa
@Strain 0.900 %,
Temperature 100 °C		6515 psi
@Strain 0.900 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 45.97 MPa
@Strain 1.20 %,
Temperature 150 °C		6667 psi
@Strain 1.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.98 MPa
@Strain 1.30 %,
Temperature 150 °C		6959 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.18 MPa
@Strain 1.00 %,
Temperature 100 °C		6988 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 49.8 MPa
@Strain 1.40 %,
Temperature 150 °C		7220 psi
@Strain 1.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 51.13 MPa
@Strain 1.10 %,
Temperature 100 °C		7416 psi
@Strain 1.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 51.6 MPa
@Strain 1.50 %,
Temperature 150 °C		7480 psi
@Strain 1.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 51.77 MPa
@Strain 0.600 %,
Temperature -40.0 °C		7509 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 53.3 MPa
@Strain 1.60 %,
Temperature 150 °C		7730 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 53.87 MPa
@Strain 1.20 %,
Temperature 100 °C		7813 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.55 MPa
@Strain 0.600 %,
Temperature 23.0 °C		7912 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 54.8 MPa
@Strain 1.70 %,
Temperature 150 °C		7950 psi
@Strain 1.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 55.86 MPa
@Strain 1.80 %,
Temperature 150 °C		8102 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 56.58 MPa
@Strain 1.30 %,
Temperature 100 °C		8206 psi
@Strain 1.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 57.17 MPa
@Strain 1.90 %,
Temperature 150 °C		8292 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 58.63 MPa
@Strain 2.00 %,
Temperature 150 °C		8504 psi
@Strain 2.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 59.11 MPa
@Strain 1.40 %,
Temperature 100 °C		8573 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 59.84 MPa
@Strain 2.10 %,
Temperature 150 °C		8679 psi
@Strain 2.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 60.85 MPa
@Strain 2.20 %,
Temperature 150 °C		8826 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.31 MPa
@Strain 0.700 %,
Temperature -40.0 °C		8892 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 61.39 MPa
@Strain 1.50 %,
Temperature 100 °C		8904 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 61.77 MPa
@Strain 2.30 %,
Temperature 150 °C		8959 psi
@Strain 2.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 62.52 MPa
@Strain 2.40 %,
Temperature 150 °C		9068 psi
@Strain 2.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.02 MPa
@Strain 0.700 %,
Temperature 23.0 °C		9140 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 63.12 MPa
@Strain 2.50 %,
Temperature 150 °C		9155 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.62 MPa
@Strain 1.60 %,
Temperature 100 °C		9227 psi
@Strain 1.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 63.66 MPa
@Strain 2.60 %,
Temperature 150 °C		9233 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 64.34 MPa
@Strain 2.70 %,
Temperature 150 °C		9332 psi
@Strain 2.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.02 MPa
@Strain 2.80 %,
Temperature 150 °C		9430 psi
@Strain 2.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.53 MPa
@Strain 2.90 %,
Temperature 150 °C		9504 psi
@Strain 2.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 65.71 MPa
@Strain 1.70 %,
Temperature 100 °C		9530 psi
@Strain 1.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 66.1 MPa
@Strain 3.00 %,
Temperature 150 °C		9590 psi
@Strain 3.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.54 MPa
@Strain 3.10 %,
Temperature 150 °C		9651 psi
@Strain 3.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 67.03 MPa
@Strain 3.20 %,
Temperature 150 °C		9722 psi
@Strain 3.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 67.34 MPa
@Strain 3.30 %,
Temperature 150 °C		9767 psi
@Strain 3.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 67.51 MPa
@Strain 1.80 %,
Temperature 100 °C		9792 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 67.81 MPa
@Strain 3.40 %,
Temperature 150 °C		9835 psi
@Strain 3.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.15 MPa
@Strain 3.50 %,
Temperature 150 °C		9884 psi
@Strain 3.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.29 MPa
@Strain 3.60 %,
Temperature 150 °C		9905 psi
@Strain 3.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.67 MPa
@Strain 3.70 %,
Temperature 150 °C		9960 psi
@Strain 3.70 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.96 MPa
@Strain 3.80 %,
Temperature 150 °C		10000 psi
@Strain 3.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.15 MPa
@Strain 4.00 %,
Temperature 150 °C		10030 psi
@Strain 4.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.16 MPa
@Strain 3.90 %,
Temperature 150 °C		10030 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 69.28 MPa
@Strain 1.90 %,
Temperature 100 °C		10050 psi
@Strain 1.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 70.75 MPa
@Strain 0.800 %,
Temperature -40.0 °C		10260 psi
@Strain 0.800 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 70.93 MPa
@Strain 2.00 %,
Temperature 100 °C		10290 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 71.8 MPa
@Strain 0.800 %,
Temperature 23.0 °C		10400 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.4 MPa
@Strain 2.10 %,
Temperature 100 °C		10500 psi
@Strain 2.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 73.87 MPa
@Strain 2.20 %,
Temperature 100 °C		10710 psi
@Strain 2.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 75.12 MPa
@Strain 2.30 %,
Temperature 100 °C		10900 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.24 MPa
@Strain 2.40 %,
Temperature 100 °C		11060 psi
@Strain 2.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 77.19 MPa
@Strain 2.50 %,
Temperature 100 °C		11200 psi
@Strain 2.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 78.28 MPa
@Strain 2.60 %,
Temperature 100 °C		11350 psi
@Strain 2.60 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 79.11 MPa
@Strain 2.70 %,
Temperature 100 °C		11470 psi
@Strain 2.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 79.51 MPa
@Strain 2.80 %,
Temperature 100 °C		11530 psi
@Strain 2.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 79.87 MPa
@Strain 0.900 %,
Temperature -40.0 °C		11580 psi
@Strain 0.900 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 80.01 MPa
@Strain 0.900 %,
Temperature 23.0 °C		11600 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.31 MPa
@Strain 2.90 %,
Temperature 100 °C		11650 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 81.01 MPa
@Strain 3.00 %,
Temperature 100 °C		11750 psi
@Strain 3.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 81.5 MPa
@Strain 3.10 %,
Temperature 100 °C		11800 psi
@Strain 3.10 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 81.88 MPa
@Strain 3.20 %,
Temperature 100 °C		11880 psi
@Strain 3.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.22 MPa
@Strain 3.30 %,
Temperature 100 °C		11930 psi
@Strain 3.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.45 MPa
@Strain 3.40 %,
Temperature 100 °C		11960 psi
@Strain 3.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 82.63 MPa
@Strain 3.50 %,
Temperature 100 °C		11980 psi
@Strain 3.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 87.65 MPa
@Strain 1.00 %,
Temperature 23.0 °C		12710 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 88.75 MPa
@Strain 1.00 %,
Temperature -40.0 °C		12870 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 94.83 MPa
@Strain 1.10 %,
Temperature 23.0 °C		13750 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 97.35 MPa
@Strain 1.10 %,
Temperature -40.0 °C		14120 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 101.56 MPa
@Strain 1.20 %,
Temperature 23.0 °C		14730 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 105.72 MPa
@Strain 1.20 %,
Temperature -40.0 °C		15333 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 107.96 MPa
@Strain 1.30 %,
Temperature 23.0 °C		15658 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 113.56 MPa
@Strain 1.30 %,
Temperature -40.0 °C		16471 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 114.01 MPa
@Strain 1.40 %,
Temperature 23.0 °C		16536 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 119.61 MPa
@Strain 1.50 %,
Temperature 23.0 °C		17348 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 121.02 MPa
@Strain 1.40 %,
Temperature -40.0 °C		17552 psi
@Strain 1.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 124.73 MPa
@Strain 1.60 %,
Temperature 23.0 °C		18091 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 128.23 MPa
@Strain 1.50 %,
Temperature -40.0 °C		18598 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 129.47 MPa
@Strain 1.70 %,
Temperature 23.0 °C		18778 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 133.96 MPa
@Strain 1.80 %,
Temperature 23.0 °C		19429 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 134.9 MPa
@Strain 1.60 %,
Temperature -40.0 °C		19570 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 141.26 MPa
@Strain 1.70 %,
Temperature -40.0 °C		20488 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 141.41 MPa
@Strain 2.00 %,
Temperature 23.0 °C		20510 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 147.36 MPa
@Strain 1.80 %,
Temperature -40.0 °C		21373 psi
@Strain 1.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 153.04 MPa
@Strain 1.90 %,
Temperature -40.0 °C		22197 psi
@Strain 1.90 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 158.49 MPa
@Strain 2.00 %,
Temperature -40.0 °C		22987 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 163.73 MPa
@Strain 2.10 %,
Temperature -40.0 °C		23747 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 168.8 MPa
@Strain 2.20 %,
Temperature -40.0 °C		24480 psi
@Strain 2.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 173.66 MPa
@Strain 2.30 %,
Temperature -40.0 °C		25187 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 178.45 MPa
@Strain 2.40 %,
Temperature -40.0 °C		25882 psi
@Strain 2.40 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 182.88 MPa
@Strain 2.50 %,
Temperature -40.0 °C		26525 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 186.16 MPa
@Strain 2.60 %,
Temperature -40.0 °C		27000 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break 2.5 %
@Temperature 23.0 °C		2.5 %
@Temperature 73.4 °F		DAM; ISO 527
Tensile Modulus  7.50 GPa
@Temperature 23.0 °C		1090 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 10.64 GPa
@Temperature 23.0 °C		1543 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus 9.446 GPa
@Temperature 23.0 °C		1370 ksi
@Temperature 73.4 °F		DAM; ISO 178
Charpy Impact Unnotched 4.00 J/cm²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  1.08 J/cm²
@Temperature -40.0 °C		5.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 1.13 J/cm²
@Temperature 23.0 °C		5.38 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+16 ohm-cm
@Temperature 23.0 °C		1.00e+16 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant 3.8
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.8
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
Dissipation Factor  0.018
@Frequency 100 Hz,
Temperature 23.0 °C		0.018
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.018
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.018
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
Comparative Tracking Index  285 V
@Temperature 23.0 °C		285 V
@Temperature 73.4 °F		DAM; IEC 60112
 250 - 400 V
@Temperature 23.0 °C		250 - 400 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 1.8 MPa (264 psi) 246 °C475 °FDAM; ISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		DAM; UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		DAM; UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  105 °C
@Thickness 0.750 mm		221 °F
@Thickness 0.0295 in		DAM; UL 746B
 115 °C
@Thickness 1.50 mm		239 °F
@Thickness 0.0591 in		DAM; UL 746B
 115 °C
@Thickness 3.00 mm		239 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical without Impact  105 °C
@Thickness 0.750 mm		221 °F
@Thickness 0.0295 in		DAM; UL 746B
 115 °C
@Thickness 1.50 mm		239 °F
@Thickness 0.0591 in		DAM; UL 746B
 120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		DAM; UL 746B
Flammability, UL94  V-0
@Thickness 3.00 mm		V-0
@Thickness 0.118 in		DAM; IEC 60695-11-10
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		DAM; IEC 60695-11-10
 V-0
@Thickness 1.50 mm		V-0
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 V-0
@Thickness 0.350 mm		V-0
@Thickness 0.0138 in		DAM; IEC 60695-11-10
 V-0
@Thickness 0.350 mm		V-0
@Thickness 0.0138 in		DAM; UL94
 V-0
@Thickness 0.750 mm		V-0
@Thickness 0.0295 in		DAM; UL94
 5VA
@Thickness 1.50 mm		5VA
@Thickness 0.0591 in		DAM; IEC 60695-11-20
 5VA
@Thickness 1.50 mm		5VA
@Thickness 0.0591 in		DAM; UL94
 5VA
@Thickness 3.00 mm		5VA
@Thickness 0.118 in		DAM; UL94
Glow Wire Test  900 °C
@Thickness 0.750 mm		1650 °F
@Thickness 0.0295 in		DAM; Ignition; IEC 60695-2-13
 900 °C
@Thickness 1.50 mm		1650 °F
@Thickness 0.0591 in		DAM; Ignition; IEC 60695-2-13
 930 °C
@Thickness 3.00 mm		1710 °F
@Thickness 0.118 in		DAM; Ignition; IEC 60695-2-13
 960 °C
@Thickness 3.00 mm		1760 °F
@Thickness 0.118 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 1.50 mm		1760 °F
@Thickness 0.0591 in		DAM; IEC 60695-2-12
 960 °C
@Thickness 0.750 mm		1760 °F
@Thickness 0.0295 in		DAM; IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 261 °C502 °F10°C/min; DAM; ISO 11357-1/-3
 290 °C554 °FDAM; Optimum
 280 - 300 °C536 - 572 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveFlame RetardantDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesFlame RetardantDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-GF25FR(17)<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryFlame Retardant ResinsDAM
 Glass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-GF25FR(17)ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
UsesConnectorsDAM
 Electrical PartsDAM
 Electrical/Electronic ApplicationsDAM
 Housing, ElectricalDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45524.html

免责声明: 本文 DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4