- 吸水率 [%]: 1.2
- 拉伸强度 [MPa]: 77.0
- 弯曲模量 [MPa]: 1.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm @Thickness 2.00 mm | 0.016 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 77.0 MPa | 11200 psi | ISO 527 |
| Elongation at Break | 60 % | 60 % | ISO 527 |
| Elongation at Yield | 25 % | 25 % | ISO 527 |
| Tensile Modulus | 1.55 GPa | 225 ksi | ISO 527 |
| Flexural Strength | 22.0 MPa | 3190 psi | ISO 178 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ISO 3146 |