- 吸水率 [%]: 1.3
- 缺口冲击强度: 5.5
- 拉伸强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 2.90
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Water Absorption | 1.3 % @Time 86400 sec | 1.3 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 45 % | 45 % | ISO 527 |
| Elongation at Yield | 11 % | 11 % | ISO 527 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 |
| Flexural Strength | 33.0 MPa | 4790 psi | ISO 178 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 |
| Poissons Ratio | 0.40 | 0.40 | ISO 527 |
| Shear Modulus | 1.07 GPa | 155 ksi | Calculated |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179 |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | ISO 179 |
| 0.650 J/cm² @Temperature 23.0 °C | 3.09 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.00e+15 ohm-cm @Thickness 3.00 mm | 6.00e+15 ohm-cm @Thickness 0.118 in | IEC 60093 |
| Dielectric Strength | 12.0 kV/mm @Thickness 3.00 mm | 305 kV/in @Thickness 0.118 in | IEC 60243 |
| Arc Resistance | 120 - 180 sec @Thickness 3.00 mm | 120 - 180 sec @Thickness 0.118 in | UL 746A |
| Comparative Tracking Index | >= 600 V @Thickness 3.00 mm | >= 600 V @Thickness 0.118 in | IEC 60112 |
| Hot Wire Ignition, HWI | 7.0 - 15 sec @Thickness 0.710 mm | 7.0 - 15 sec @Thickness 0.0280 in | UL 746B |
| 15 - 30 sec @Thickness 1.50 mm | 15 - 30 sec @Thickness 0.0591 in | UL 746B | |
| 30 - 60 sec @Thickness 3.00 mm | 30 - 60 sec @Thickness 0.118 in | UL 746B | |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 0.710 mm | >= 120 arcs @Thickness 0.0280 in | UL 746A |
| >= 120 arcs @Thickness 1.50 mm | >= 120 arcs @Thickness 0.0591 in | UL 746A | |
| >= 120 arcs @Thickness 3.00 mm | >= 120 arcs @Thickness 0.118 in | UL 746A | |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min @Thickness 3.00 mm | 0.000 - 0.394 in/min @Thickness 0.118 in | UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 6.11 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359 |
| CTE, linear, Transverse to Flow | 12.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 6.67 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359 |
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Vicat Softening Point | 237 °C @Load 5.10 kg | 459 °F @Load 11.2 lb | ISO 306 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.400 mm | 149 °F @Thickness 0.0157 in | UL 746B |
| 130 °C @Thickness 0.710 mm | 266 °F @Thickness 0.0280 in | UL 746B | |
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.400 mm | 149 °F @Thickness 0.0157 in | UL 746B |
| 75.0 °C @Thickness 0.710 mm | 167 °F @Thickness 0.0280 in | UL 746B | |
| 75.0 °C @Thickness 1.50 mm | 167 °F @Thickness 0.0591 in | UL 746B | |
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | UL 746B | |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.400 mm | 149 °F @Thickness 0.0157 in | UL 746B |
| 85.0 °C @Thickness 0.710 mm | 185 °F @Thickness 0.0280 in | UL 746B | |
| 85.0 °C @Thickness 1.50 mm | 185 °F @Thickness 0.0591 in | UL 746B | |
| 85.0 °C @Thickness 3.00 mm | 185 °F @Thickness 0.118 in | UL 746B | |
| Flammability, UL94 | V-2 @Thickness 0.400 mm | V-2 @Thickness 0.0157 in | |
| V-2 @Thickness 0.710 mm | V-2 @Thickness 0.0280 in | ||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | ||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||
| Oxygen Index | 27 % | 27 % | ASTM D2863 |
| Glow Wire Test | 725 °C @Thickness 0.710 mm | 1340 °F @Thickness 0.0280 in | Ignition Temperature; IEC 60695-2-12 |
| 725 °C @Thickness 1.50 mm | 1340 °F @Thickness 0.0591 in | Ignition Temperature; IEC 60695-2-12 | |
| 725 °C @Thickness 3.00 mm | 1340 °F @Thickness 0.118 in | Ignition Temperature; IEC 60695-2-12 | |
| 825 °C @Thickness 0.710 mm | 1520 °F @Thickness 0.0280 in | Flame Index; IEC 60695-2-12 | |
| 825 °C @Thickness 1.50 mm | 1520 °F @Thickness 0.0591 in | Flame Index; IEC 60695-2-12 | |
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | Flame Index; IEC 60695-2-12 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 310 °C | 518 - 590 °F | |
| Melt Temperature | 275 - 305 °C | 527 - 581 °F | |
| Mold Temperature | 15.0 - 95.0 °C | 59.0 - 203 °F | |
| Injection Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Hold Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Back Pressure | 0.200 - 1.00 MPa | 29.0 - 145 psi | |
| Clamp Pressure | 29.43 - 68.67 MPa | 4268 - 9960 psi | |
| Cushion | 0.300 - 0.640 cm | 0.118 - 0.252 in | |
| Screw Speed | 50 - 150 rpm | 50 - 150 rpm | |