- 吸水率 [%]: 0.9
- 缺口冲击强度: 0.481
- 拉伸强度 [MPa]: 86.2
- 弯曲模量 [MPa]: 3.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 0.90 % @Time 86400 sec | 0.90 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.018 cm/cm @Thickness 3.17 mm | 0.012 - 0.018 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |