- 密度 [g/cm3]: 1.51
- 吸水率 [%]: 0.6
- 缺口冲击强度: 0.5
- 拉伸强度 [MPa]: 95.0
- 断裂伸长率 [%]: 143
- 弯曲模量 [MPa]: 7.20
- 硬度: 122.0
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 122 | 122 | ASTM D786 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Yield Strength | 143 MPa | 20700 psi | ASTM D790 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 - 40.0 µm/m-°C @Temperature 20.0 °C | 16.7 - 22.2 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |