- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.785
- 弯曲模量 [MPa]: 5.96448
- 热变形温度 [℃]: 254.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec | 0.50 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 122.625 MPa | 17785.3 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 194.24 MPa | 28172 psi | ASTM D790 |
| Flexural Modulus | 5.96448 GPa | 865.076 ksi | ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm | 1.47 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 305 °C | 536 - 581 °F | |
| Mold Temperature | 75.0 - 120 °C | 167 - 248 °F | |