E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM

E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM 物性表: E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM物性表及特性介绍,E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM注塑参数详情,如需E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.56
  • 吸水率 [%]: 0.6
  • 缺口冲击强度: 1.0
  • 拉伸强度 [MPa]: 157.0
  • 断裂伸长率 [%]: 220
  • 弯曲模量 [MPa]: 8.50
  • 硬度: 120.0
  • 热变形温度 [℃]: 260.0
 
Physical PropertiesMetricEnglishComments
Density 1.56 g/cc0.0564 lb/in³ASTM D792
Water Absorption 0.60 %0.60 %23°C/24 hr; ASTM D570
Linear Mold Shrinkage 0.0050 cm/cm0.0050 in/in
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 120120ASTM D786
Tensile Strength, Yield 157 MPa22800 psiASTM D638
Elongation at Break 3.0 %3.0 %ASTM D638
Flexural Yield Strength 220 MPa31900 psiASTM D790
Flexural Modulus 8.50 GPa1230 ksiASTM D790
Izod Impact, Notched 1.00 J/cm1.87 ft-lb/inASTM D256
 
Thermal PropertiesMetricEnglishComments
CTE, linear 60.0 µm/m-°C
@Temperature 20.0 °C
33.3 µin/in-°F
@Temperature 68.0 °F
ASTM D696
Melting Point 260 °C500 °FASTM D2133
Deflection Temperature at 0.46 MPa (66 psi) 260 °C500 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 250 °C482 °FASTM D648
Flammability, UL94 V-0V-0
 
Processing PropertiesMetricEnglishComments
Processing Temperature 270 - 290 °C518 - 554 °F
Mold Temperature 80.0 - 120 °C176 - 248 °F

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45698.html

免责声明: 本文 E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4