- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.981
- 弯曲模量 [MPa]: 4.2183
- 热变形温度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec | 0.50 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 64.746 MPa | 9390.6 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 107.91 MPa | 15651 psi | ASTM D790 |
| Flexural Modulus | 4.2183 GPa | 611.81 ksi | ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm | 1.84 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 305 °C | 536 - 581 °F | |
| Mold Temperature | 75.0 - 120 °C | 167 - 248 °F | |