- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 拉伸强度 [MPa]: 90.0
- 断裂伸长率 [%]: 130
- 弯曲强度 [MPa]: 75.0
- 弯曲模量 [MPa]: 3.17
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO data |
| Water Absorption | 1.6 % | 1.6 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | |
| Water Absorption at Saturation | 9.3 % | 9.3 % | |
| Viscosity Measurement | 48 | 48 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM data MD |
| 0.013 cm/cm | 0.013 in/in | ISO data | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Break | 10 % | 10 % | Strain at break, ASTM, 5 mm/min |
| 10 % | 10 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO Value at 50 mm/min. |
| 4.0 % | 4.0 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 3.50 GPa | 508 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 130 MPa | 18900 psi | ASTM Data |
| Flexural Modulus | 3.17 GPa | 460 ksi | ASTM Value |
| 3.20 GPa | 464 ksi | ISO Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 1.30 GPa | 189 ksi | calculated |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 81.0 µm/m-°C @Temperature 20.0 °C | 45.0 µin/in-°F @Temperature 68.0 °F | ASTM data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO Data |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 °C | 500 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |