- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.45
- 拉伸强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 2.62
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Volatiles | 0.80 % | 0.80 % | Extractable | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hr.; ISO 62 | ||
| 9.5 % | 9.5 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 0.080 % | 0.080 % | ASTM D570 | ||
| 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 | |||
| Oxygen Transmission Rate | 40.3 cc/m²/day | 2.60 cc/100 in²/day | |||
| Nitrogen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | cc/m2/day (Thickness not reported) | ||
| Carbon Dioxide Transmission | 72.8 cc-mm/m²-24hr-atm | 185 cc-mil/100 in²-24hr-atm | cc/m2/day (Thickness not reported) | ||
| Viscosity Measurement | 3.7 | 3.7 | Relative Viscosity (95% SAV) | ||
| 3.88 | 3.88 | Relative Viscosity (96% SAV) | |||
| 3.9 | 3.9 | Relative Viscosity (98% SAV) | |||
| 135 | 135 | Formic Acid; ASTM D789 | |||
| Viscosity Test | 239 cm³/g | 239 cm³/g | Viscosity number | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 2 in/min; ASTM D638 | ||
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 | ||
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM D3418 | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status (March 2007) | Active America | ||||
| FDA | 21 CFR 177.1500 | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Film Extrusion | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.