- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.6
- 拉伸强度 [MPa]: 79.0
- 弯曲模量 [MPa]: 2.83
- 硬度: 119.0
- 热变形温度 [℃]: 178.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hr.; ISO 62 | ||
| 9.5 % | 9.5 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 64 | 64 | Formic Acid; ASTM D789 | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM Test | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM D785 | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 0.2 in/min; ASTM D638 | ||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 50 mm/min; ISO 527 | ||
| 79.0 MPa | 11500 psi | 2 in/min; ASTM D638 | |||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ASTM D638 | |||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ISO 527 | |||
| 35.0 MPa @Temperature 80.0 °C | 5080 psi @Temperature 176 °F | ASTM D638 | |||
| 35.0 MPa @Temperature 80.0 °C | 5080 psi @Temperature 176 °F | ISO 527 | |||
| 125 MPa @Temperature -40.0 °C | 18100 psi @Temperature -40.0 °F | ASTM D638 | |||
| 125 MPa @Temperature -40.0 °C | 18100 psi @Temperature -40.0 °F | ISO 527 | |||
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; Nominal; ISO 527 | ||
| 55 % | 55 % | 2 in/min; ASTM D638 | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 2 in/min; ASTM D638 | |||
| Modulus of Elasticity | 0.360 GPa @Temperature 120 °C | 52.2 ksi @Temperature 248 °F | ISO 527 | ||
| 0.485 GPa @Temperature 80.0 °C | 70.3 ksi @Temperature 176 °F | ISO 527 | |||
| Tensile Modulus | 3.10 GPa | 450 ksi | 1 mm/min; ISO 527 | ||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 | ||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ASTM D790 | |||
| 20.0 MPa @Temperature 93.0 °C | 2900 psi @Temperature 199 °F | ASTM D790 | |||
| 30.0 MPa @Temperature 65.0 °C | 4350 psi @Temperature 149 °F | ASTM D790 | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 | ||
| 0.305 GPa @Temperature 120 °C | 44.2 ksi @Temperature 248 °F | ASTM D790 | |||
| 0.350 GPa @Temperature 93.0 °C | 50.8 ksi @Temperature 199 °F | ASTM D790 | |||
| 0.500 GPa @Temperature 65.0 °C | 72.5 ksi @Temperature 149 °F | ASTM D790 | |||
| 3.01 GPa @Temperature -40.0 °C | 437 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 | ||
| 0.500 J/cm @Temperature -40.0 °C | 0.937 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 83.0 µm/m-°C @Temperature 20.0 °C | 46.1 µin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C | 352 °F | ISO 75 | ||
| 178 °C | 352 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 | ||
| 65.0 °C | 149 °F | ASTM D648 | |||
| Descriptive Properties | |||||
| Additive | Unfilled | ||||
| Color | Natural | ||||
| Commercial Status (March 2007) | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Injection molding | Processable | ||||
| Primary Processing Technique | Film Extrusion | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.