- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 拉伸强度 [MPa]: 90.0
- 断裂伸长率 [%]: 110
- 弯曲模量 [MPa]: 3.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO data |
| Water Absorption | 1.6 % | 1.6 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 9.2 % | 9.2 % | in water; 23°C; ISO data |
| Viscosity Measurement | 64 | 64 | Formic Acid Viscosity; ISO data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Yield | 4.0 % | 4.0 % | ISO Value at 50 mm/min. |
| 4.0 % | 4.0 % | ASTM Value at 50 mm/min. | |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM Data |
| Flexural Modulus | 3.17 GPa | 460 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ASTM Data |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |