- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.3
- 拉伸强度 [MPa]: 59.0
- 断裂伸长率 [%]: 75.0
- 弯曲模量 [MPa]: 2.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO data |
| Water Absorption | 1.3 % | 1.3 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 7.1 % | 7.1 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | ISO value at 50 mm/min. |
| 60.0 MPa | 8700 psi | ASTM value at 50 mm/min. | |
| Elongation at Break | >= 100 % | >= 100 % | Nominal strain at break, ASTM, 50 mm/min |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | ASTM Data |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM Data |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |