- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.5
- 拉伸强度 [MPa]: 65.0
- 断裂伸长率 [%]: 90.0
- 弯曲强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 2.165
- 热变形温度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO data |
| Water Absorption | 1.5 % | 1.5 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 8.1 % | 8.1 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ISO data |
| 0.012 cm/cm | 0.012 in/in | ASTM data MD | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break, ISO data, 50 mm/min |
| >= 100 % | >= 100 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO Value at 50 mm/min. |
| 4.0 % | 4.0 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 2.53 GPa | 367 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | ASTM Data |
| Flexural Modulus | 2.165 GPa | 314.0 ksi | ISO Value |
| 2.21 GPa | 321 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 0.900 GPa | 131 ksi | calculated |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO Data |
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO data | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Comparative Tracking Index | 600 V | 600 V | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 88.0 µm/m-°C @Temperature 20.0 °C | 48.9 µin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 93.0 µm/m-°C @Temperature 20.0 °C | 51.7 µin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ISO data |
| 168 °C | 334 °F | ASTM Data | |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO data |
| 60.0 °C | 140 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 °C | 536 °F | See Materials Notes |
| Mold Temperature | 70.0 °C | 158 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |