- 密度 [g/cm3]: 1.13
- 拉伸强度 [MPa]: 40.0
- 断裂伸长率 [%]: 30.0
- 弯曲模量 [MPa]: 0.840
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data MD (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM test; 50 mm/min. |
| Elongation at Break | >= 100 % | >= 100 % | Nominal strain at break, ASTM, 50 mm/min |
| Elongation at Yield | 15 % | 15 % | ASTM test at 50 mm/min. |
| Flexural Yield Strength | 30.0 MPa | 4350 psi | ASTM Data |
| Flexural Modulus | 0.840 GPa | 122 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | temperatures as low as 10°C (50°F) can be used where applicable. |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |
| Injection Pressure | 3.45 - 10.3 MPa | 500 - 1500 psi | |