- 密度 [g/cm3]: 1.49
- 拉伸强度 [MPa]: 60.0
- 弯曲强度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Break | 25 % | 25 % | Strain at break, ASTM, 5 mm/min |
| 25 % | 25 % | Nominal strain at break, ISO, 50 mm/min | |
| Elongation at Yield | 13 % | 13 % | ISO Value at 50 mm/min. |
| 15 % | 15 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 3.80 GPa | 551 ksi | same value from ASTM and ISO test. |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |