- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 1.1
- 拉伸强度 [MPa]: 86.0
- 弯曲模量 [MPa]: 5.00
- 热变形温度 [℃]: 197.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO data |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.7 % | 5.7 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ISO data |
| 0.0090 cm/cm | 0.0090 in/in | ASTM data MD | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | ISO value at 50 mm/min. |
| 90.0 MPa | 13100 psi | ASTM value at 50 mm/min. | |
| Elongation at Break | 10 % | 10 % | Nominal strain at break, ISO, 50 mm/min |
| 10 % | 10 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM Value at 50 mm/min. |
| 3.2 % | 3.2 % | ISO Value at 50 mm/min. | |
| Tensile Modulus | 6.63 GPa | 962 ksi | same value from ASTM and ISO test. |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 2.50 GPa | 363 ksi | calculated |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | ASTM data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 197 °C | 387 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO Data |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |