- 密度 [g/cm3]: 1.136
- 吸水率 [%]: 1.1
- 缺口冲击强度: 1.07
- 弯曲强度 [MPa]: 185.0
- 弯曲模量 [MPa]: 8.20
- 硬度: 121.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.136 g/cc | 0.04104 lb/in³ | Melt; ISO 1183 | ||
| 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | |||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 6.4 % | 6.4 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 195 MPa | 28300 psi | 0.2 in/min; ASTM Test | ||
| 83.0 MPa @Temperature 120 °C | 12000 psi @Temperature 248 °F | ASTM Test | |||
| 83.0 MPa @Temperature 120 °C | 12000 psi @Temperature 248 °F | ISO Data | |||
| 110 MPa @Temperature 80.0 °C | 16000 psi @Temperature 176 °F | ISO Data | |||
| 110 MPa @Temperature 80.0 °C | 16000 psi @Temperature 176 °F | ASTM Test | |||
| 283 MPa @Temperature -40.0 °C | 41000 psi @Temperature -40.0 °F | ASTM Test | |||
| 283 MPa @Temperature -40.0 °C | 41000 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 185 MPa | 26800 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 | ||
| 3.5 % | 3.5 % | 0.2 in/min; ASTM Test | |||
| 3.6 % @Temperature -40.0 °C | 3.6 % @Temperature -40.0 °F | ASTM Test | |||
| 3.6 % @Temperature -40.0 °C | 3.6 % @Temperature -40.0 °F | ISO Data | |||
| 7.0 % @Temperature 120 °C | 7.0 % @Temperature 248 °F | ISO Data | |||
| 7.0 % @Temperature 80.0 °C | 7.0 % @Temperature 176 °F | ISO Data | |||
| 7.0 % @Temperature 120 °C | 7.0 % @Temperature 248 °F | ASTM Test | |||
| 7.0 % @Temperature 80.0 °C | 7.0 % @Temperature 176 °F | ASTM Test | |||
| Tensile Modulus | 10.1 GPa | 1460 ksi | 1mm/min; ISO 527 | ||
| 3.55 GPa @Temperature 120 °C | 515 ksi @Temperature 248 °F | ISO Data | |||
| 4.43 GPa @Temperature 80.0 °C | 643 ksi @Temperature 176 °F | ISO Data | |||
| 10.5 GPa @Temperature -40.0 °C | 1520 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 260 MPa | 37700 psi | ISO Data | ||
| 297 MPa | 43100 psi | ASTM Test | |||
| 112 MPa @Temperature 120 °C | 16200 psi @Temperature 248 °F | ASTM Test | |||
| 140 MPa @Temperature 93.0 °C | 20300 psi @Temperature 199 °F | ASTM Test | |||
| 160 MPa @Temperature 65.0 °C | 23200 psi @Temperature 149 °F | ASTM Test | |||
| 380 MPa @Temperature -40.0 °C | 55100 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 8.20 GPa | 1190 ksi | ISO Data | ||
| 9.04 GPa | 1310 ksi | ASTM Test | |||
| 3.32 GPa @Temperature 120 °C | 482 ksi @Temperature 248 °F | ASTM Test | |||
| 3.75 GPa @Temperature 93.0 °C | 544 ksi @Temperature 199 °F | ASTM Test | |||
| 4.02 GPa @Temperature 65.0 °C | 583 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 1.07 J/cm @Temperature -40.0 °C | 2.00 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 1.48 J/cm @Thickness 3.17 mm | 2.77 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Unnotched | 13.7 J/cm | 25.7 ft-lb/in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO Test | ||
| 8.50 kJ/m² @Temperature -40.0 °C | 4.04 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 8.80 J/cm² | 41.9 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 | ||
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | ASTM Data | |||
| 3.8 @Frequency 1e+9 Hz | 3.8 @Frequency 1e+9 Hz | ASTM Data | |||
| 4.2 @Frequency 100 Hz | 4.2 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 44.0 kV/mm | 1120 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 1e+9 Hz | 0.010 @Frequency 1e+9 Hz | ASTM Data | ||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM Data | |||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 38.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 21.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C | 11.7 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359 | ||
| Specific Heat Capacity | 2.434 J/g-°C | 0.5817 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.275 W/m-K | 1.91 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| 218 °C | 424 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| 210 °C | 410 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||