- 密度 [g/cm3]: 1.291
- 吸水率 [%]: 1.1
- 缺口冲击强度: 0.53
- 弯曲强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 5.20
- 硬度: 119.0
- 热变形温度 [℃]: 195.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.291 g/cc | 0.04664 lb/in³ | Melt; ISO 1183 | ||
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM Test | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 10 % | 10 % | 5mm/min; ISO 527 | ||
| 10 % | 10 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 6.40 GPa | 928 ksi | 1mm/min; ISO 527 | ||
| 0.970 GPa @Temperature 120 °C | 141 ksi @Temperature 248 °F | ISO Data | |||
| 1.36 GPa @Temperature 80.0 °C | 197 ksi @Temperature 176 °F | ISO Data | |||
| 8.31 GPa @Temperature -40.0 °C | 1210 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 138 MPa | 20000 psi | ASTM Test | ||
| 140 MPa | 20300 psi | ISO Data | |||
| 34.0 MPa @Temperature 120 °C | 4930 psi @Temperature 248 °F | ASTM Test | |||
| 35.0 MPa @Temperature 93.0 °C | 5080 psi @Temperature 199 °F | ASTM Test | |||
| 55.0 MPa @Temperature 65.0 °C | 7980 psi @Temperature 149 °F | ASTM Test | |||
| 207 MPa @Temperature -40.0 °C | 30000 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO Data | ||
| 5.76 GPa | 835 ksi | ASTM Test | |||
| 0.810 GPa @Temperature 93.0 °C | 117 ksi @Temperature 199 °F | ASTM Test | |||
| 0.815 GPa @Temperature 120 °C | 118 ksi @Temperature 248 °F | ASTM Test | |||
| 1.54 GPa @Temperature 65.0 °C | 223 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Unnotched | 16.4 J/cm | 30.7 ft-lb/in | ASTM Test | ||
| Charpy Impact Unnotched | 11.5 J/cm² | 54.7 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 | ||
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 27.8 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C | 25.6 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C | 32.2 µin/in-°F | ISO 11359 | ||
| Specific Heat Capacity | 1.999 J/g-°C | 0.4778 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.281 W/m-K | 1.95 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ASTM Test | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | X | ||||