- 密度 [g/cm3]: 1.291
- 吸水率 [%]: 5.7
- 弯曲强度 [MPa]: 85.0
- 热变形温度 [℃]: 195.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.291 g/cc | 0.04664 lb/in³ | Melt; ISO 1183 | ||
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |||
| Water Absorption | 5.7 % | 5.7 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 23°C/50% R.H.; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 10 % | 10 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 6.40 GPa | 928 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 11.5 J/cm² | 54.7 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 | ||
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C | 25.6 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C | 32.2 µin/in-°F | ISO 11359 | ||
| Specific Heat Capacity | 1.999 J/g-°C | 0.4778 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.281 W/m-K | 1.95 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | ISO 75 | ||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| X | |||||