BASF Ultramid® 8253 HS PA6 (Conditioned)物性表参数

吸水率 [%]: 1.5
缺口冲击强度: 0.64
拉伸强度 [MPa]: 32.0
弯曲模量 [MPa]: 0.670

Physical Properties	Metric	English	Comments

Water Absorption	1.5 %	1.5 %	24 hour; ISO Test
Linear Mold Shrinkage	0.012 cm/cm	0.012 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	70.0 MPa @Temperature -40.0 °C	10200 psi @Temperature -40.0 °F	ISO Data
	70.0 MPa @Temperature -40.0 °C	10200 psi @Temperature -40.0 °F	ASTM Test
Tensile Strength, Yield	32.0 MPa	4640 psi	2 in/min; ASTM Test
	20.0 MPa @Temperature 80.0 °C	2900 psi @Temperature 176 °F	ASTM Test
	20.0 MPa @Temperature 80.0 °C	2900 psi @Temperature 176 °F	ISO Data
	116 MPa @Temperature -40.0 °C	16800 psi @Temperature -40.0 °F	ASTM Test
	116 MPa @Temperature -40.0 °C	16800 psi @Temperature -40.0 °F	ISO Data
Elongation at Break	>= 100 %	>= 100 %	2 in/min; ASTM Test
	20 % @Temperature -40.0 °C	20 % @Temperature -40.0 °F	ASTM Test
	20 % @Temperature -40.0 °C	20 % @Temperature -40.0 °F	ISO Data
Elongation at Yield	15 %	15 %	2 in/min; ASTM Test
	30 % @Temperature 120 °C	30 % @Temperature 248 °F	ASTM Test
	30 % @Temperature 80.0 °C	30 % @Temperature 176 °F	ISO Data
Tensile Modulus	0.220 GPa @Temperature 120 °C	31.9 ksi @Temperature 248 °F	ISO Data
	0.370 GPa @Temperature 80.0 °C	53.7 ksi @Temperature 176 °F	ISO Data
	3.30 GPa @Temperature -40.0 °C	479 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	32.0 MPa	4640 psi	ASTM Test
	141 MPa @Temperature -40.0 °C	20500 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	0.670 GPa	97.2 ksi	ASTM Test
Izod Impact, Notched	0.640 J/cm @Temperature -40.0 °C	1.20 ft-lb/in @Temperature -40.0 °F	ASTM Test
	NB @Thickness 3.17 mm	NB @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ASTM Test

Descriptive Properties
Color	Natural
Commercial Status	Active America
Impact Modified	Yes
Primary Processing Technique	Injection Molding
UL.UL-C	Yes