- 吸水率 [%]: 1.5
- 缺口冲击强度: 0.8
- 拉伸强度 [MPa]: 65.0
- 弯曲模量 [MPa]: 1.90
- 硬度: 82.0
- 热变形温度 [℃]: 168.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 1.5 % | 1.5 % | 24 hour; ISO Test | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 82 | 82 | ASTM Test | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 0.2 in/min; ASTM Test | ||
| 100 MPa @Temperature -40.0 °C | 14500 psi @Temperature -40.0 °F | ASTM Test | |||
| 100 MPa @Temperature -40.0 °C | 14500 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 2 in/min; ASTM Test | ||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ASTM Test | |||
| 20.0 MPa @Temperature 120 °C | 2900 psi @Temperature 248 °F | ISO Data | |||
| 25.0 MPa @Temperature 80.0 °C | 3630 psi @Temperature 176 °F | ISO Data | |||
| 25.0 MPa @Temperature 80.0 °C | 3630 psi @Temperature 176 °F | ASTM Test | |||
| 117 MPa @Temperature -40.0 °C | 17000 psi @Temperature -40.0 °F | ASTM Test | |||
| 117 MPa @Temperature -40.0 °C | 17000 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | >= 100 % | >= 100 % | 2 in/min; ASTM Test | ||
| 9.0 % @Temperature -40.0 °C | 9.0 % @Temperature -40.0 °F | ASTM Test | |||
| 9.0 % @Temperature -40.0 °C | 9.0 % @Temperature -40.0 °F | ISO Data | |||
| Elongation at Yield | 4.0 % | 4.0 % | 2 in/min; ASTM Test | ||
| 7.0 % @Temperature -40.0 °C | 7.0 % @Temperature -40.0 °F | ASTM Test | |||
| 7.0 % @Temperature -40.0 °C | 7.0 % @Temperature -40.0 °F | ISO Data | |||
| 29 % @Temperature 80.0 °C | 29 % @Temperature 176 °F | ISO Data | |||
| 29 % @Temperature 80.0 °C | 29 % @Temperature 176 °F | ASTM Test | |||
| 34 % @Temperature 120 °C | 34 % @Temperature 248 °F | ASTM Test | |||
| 34 % @Temperature 120 °C | 34 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 0.295 GPa @Temperature 120 °C | 42.8 ksi @Temperature 248 °F | ISO Data | ||
| 0.400 GPa @Temperature 80.0 °C | 58.0 ksi @Temperature 176 °F | ISO Data | |||
| 2.835 GPa @Temperature -40.0 °C | 411.2 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 65.0 MPa | 9430 psi | ISO Data | ||
| 87.0 MPa | 12600 psi | ASTM Test | |||
| 14.0 MPa @Temperature 120 °C | 2030 psi @Temperature 248 °F | ASTM Test | |||
| 20.0 MPa @Temperature 93.0 °C | 2900 psi @Temperature 199 °F | ASTM Test | |||
| 25.0 MPa @Temperature 65.0 °C | 3630 psi @Temperature 149 °F | ASTM Test | |||
| 148 MPa @Temperature -40.0 °C | 21500 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO Data | ||
| 2.21 GPa | 321 ksi | ASTM Test | |||
| 0.260 GPa @Temperature 120 °C | 37.7 ksi @Temperature 248 °F | ASTM Test | |||
| 0.325 GPa @Temperature 93.0 °C | 47.1 ksi @Temperature 199 °F | ASTM Test | |||
| 0.415 GPa @Temperature 65.0 °C | 60.2 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.800 J/cm @Temperature -40.0 °C | 1.50 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 1.48 J/cm @Thickness 3.17 mm | 2.77 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 99.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 55.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | ASTM Test | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | ASTM Test | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM Test | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| UL.UL-C | Yes | ||||