- 熔体流动速率 [g/10min]: 46.92
- 密度 [g/cm3]: 1.38
- 缺口冲击强度: 6.5
- 弯曲模量 [MPa]: 9.09
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH | ||
| 6.7 % | 6.7 % | Saturation | |||
| Melt Flow | 46.92 g/10 min | 46.92 g/10 min | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 157 MPa | 22800 psi | ISO 527 | ||
| Elongation at Break | 2.8 % | 2.8 % | ISO 527 | ||
| Tensile Modulus | 9.33 GPa | 1350 ksi | ISO 527 | ||
| Flexural Strength | 241 MPa | 35000 psi | ISO 178 | ||
| Flexural Modulus | 9.09 GPa | 1320 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180 | ||
| Charpy Impact Unnotched | 5.10 J/cm² | 24.3 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.640 J/cm² | 3.05 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |||
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | 0.10 % | 0.10 % | |||
| Descriptive Properties | |||||
| Color | BK 5830 | ||||
| Commercial Status | North America | ||||