- 熔体流动速率 [g/10min]: 17.3
- 密度 [g/cm3]: 1.12
- 拉伸强度 [MPa]: 65.0
- 断裂伸长率 [%]: 78.0
- 弯曲模量 [MPa]: 1.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 - 1.14 g/cc | 0.0405 - 0.0412 lb/in³ | ASTM D792 | ||
| Apparent Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | circa | ||
| Viscosity Measurement | 2.95 - 3.05 | 2.95 - 3.05 | Relative Viscosity | ||
| Melt Flow | 17.3 g/10 min @Load 2.16 kg, Temperature 230 °C | 17.3 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D638 | ||
| Elongation at Yield | 7.6 % | 7.6 % | ASTM D638 | ||
| Flexural Yield Strength | 78.0 MPa | 11300 psi | ASTM D790 | ||
| Flexural Modulus | 1.70 GPa | 247 ksi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 224 °C | 435 °F | ASTM DSC | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Moisture Content | <= 0.10 % | <= 0.10 % | |||
| Descriptive Properties | |||||
| Extractables, wt% | <0.5 | ||||