- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 1.0
- 缺口冲击强度: 1.3
- 弯曲强度 [MPa]: 179.0
- 弯曲模量 [MPa]: 9.70
- 硬度: 122.0
- 热变形温度 [℃]: 218.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 92 | 92 | ASTM D785 |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 179 MPa | 26000 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 228 MPa | 33100 psi | ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Compressive Yield Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 222 °C | 432 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |