- 缺口冲击强度: 0.98
- 弯曲模量 [MPa]: 7.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 3.17 mm | 0.0040 in/in @Thickness 0.125 in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 157 MPa | 22800 psi | ASTM D882 |
| Elongation at Break | 3.4 % | 3.4 % | ASTM D882 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched | 0.980 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 1.84 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 227 °C | 441 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 219 °C | 426 °F | 0.125";; ASTM D648 |