- 密度 [g/cm3]: 1.1
- 缺口冲击强度: 35.0
- 弯曲强度 [MPa]: 49.0
- 弯曲模量 [MPa]: 1.163
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 3.1 % | 3.1 % | DIN 53714: 23°C, 50% Relative Humidity |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 74 | 74 | ISO 868 |
| Tensile Strength, Ultimate | 49.0 MPa | 7110 psi | ISO 527 |
| Elongation at Break | 250 % | 250 % | ISO 527 |
| Modulus of Elasticity | 1.197 GPa | 173.6 ksi | ISO 527 |
| Flexural Modulus | 1.163 GPa | 168.7 ksi | ISO 178 |
| Shear Modulus | 0.520 GPa | 75.4 ksi | torsional |
| Izod Impact, Notched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | ISO 180, Ductile break |
| 4.00 kJ/m² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | Brittle break; ISO 180 | |
| Charpy Impact, Notched | 3.10 J/cm² | 14.8 ft-lb/in² | DIN 53453, Ductile break |
| 0.800 J/cm² @Temperature -40.0 °C | 3.81 ft-lb/in² @Temperature -40.0 °F | Brittle break; DIN 53453 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.00e+9 ohm-cm | 5.00e+9 ohm-cm | DIN 53482 |
| Surface Resistance | 4.00e+8 ohm | 4.00e+8 ohm | DIN 53482 |
| Dielectric Constant | 4.1 @Frequency 1e+6 Hz | 4.1 @Frequency 1e+6 Hz | DIN 53483 |
| 15.3 @Frequency 50 Hz | 15.3 @Frequency 50 Hz | DIN 53483 | |
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | DIN 53481 |
| Dissipation Factor | 0.10 @Frequency 1e+6 Hz | 0.10 @Frequency 1e+6 Hz | DIN 53483 |
| Comparative Tracking Index | 400 V | 400 V | DIN IEC 112 / VDE 030 t1 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 214 °C | 417 °F | |