- 密度 [g/cm3]: 1.12
- 缺口冲击强度: 19.0
- 弯曲强度 [MPa]: 54.0
- 弯曲模量 [MPa]: 2.279
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 77 | 77 | ISO 868 |
| Tensile Strength, Ultimate | 54.0 MPa | 7830 psi | ISO 527 |
| Elongation at Break | 90 % | 90 % | ISO 527 |
| Modulus of Elasticity | 2.106 GPa | 305.5 ksi | ISO 527 |
| Flexural Modulus | 2.279 GPa | 330.5 ksi | ISO 178 |
| Poissons Ratio | 0.32 | 0.32 | Calculated |
| Shear Modulus | 0.800 GPa | 116 ksi | torsional |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | ISO 180, Ductile break |
| 9.00 kJ/m² @Temperature -40.0 °C | 4.28 ft-lb/in² @Temperature -40.0 °F | Brittle break; ISO 180 | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | DIN 53453, Brittle break |
| 1.40 J/cm² @Temperature -40.0 °C | 6.66 ft-lb/in² @Temperature -40.0 °F | Brittle break; DIN 53453 | |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 500 V | 500 V | DIN IEC 112 / VDE 030 t1 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 214 °C | 417 °F | DSC |