  4. DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6

DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6

DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6 物性表: DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6物性表及特性介绍,DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6注塑参数详情,如需DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.35
  • 吸水率 [%]: 2.1
  • 缺口冲击强度: 4.0
  • 弯曲模量 [MPa]: 1.80
  • 热变形温度 [℃]: 196.0
 
Physical PropertiesMetricEnglishComments
Density 1.35 g/cc0.0488 lb/in³DAM; ISO 1183
Filler Content 30 %30 %DAM
Water Absorption  2.1 %
@Temperature 23.0 °C		2.1 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 6.3 %
@Temperature 23.0 °C		6.3 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
@Thickness 2.00 mm		0.0090 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  55.0 MPa
@Temperature 23.0 °C		7980 psi
@Temperature 73.4 °F		50%RH; ISO 527
 82.0 MPa
@Temperature 23.0 °C		11900 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  5.15 MPa
@Strain 1.23 %,
Temperature 150 °C		747 psi
@Strain 1.23 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.35 MPa
@Strain 1.21 %,
Temperature 150 °C		921 psi
@Strain 1.21 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.36 MPa
@Strain 1.23 %,
Temperature 120 °C		922 psi
@Strain 1.23 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.66 MPa
@Strain 1.22 %,
Temperature 90.0 °C		1110 psi
@Strain 1.22 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 7.86 MPa
@Strain 1.21 %,
Temperature 120 °C		1140 psi
@Strain 1.21 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.34 MPa
@Strain 2.43 %,
Temperature 150 °C		1210 psi
@Strain 2.43 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.69 MPa
@Strain 1.21 %,
Temperature 90.0 °C		1410 psi
@Strain 1.21 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 10.37 MPa
@Strain 2.42 %,
Temperature 120 °C		1504 psi
@Strain 2.42 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.46 MPa
@Strain 2.45 %,
Temperature 150 °C		1517 psi
@Strain 2.45 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.54 MPa
@Strain 3.63 %,
Temperature 150 °C		1529 psi
@Strain 3.63 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.86 MPa
@Strain 1.23 %,
Temperature 60.0 °C		1575 psi
@Strain 1.23 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 12.15 MPa
@Strain 4.83 %,
Temperature 150 °C		1762 psi
@Strain 4.83 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.35 MPa
@Strain 2.42 %,
Temperature 90.0 °C		1791 psi
@Strain 2.42 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 12.49 MPa
@Strain 1.23 %,
Temperature 40.0 °C		1812 psi
@Strain 1.23 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 12.88 MPa
@Strain 2.40 %,
Temperature 120 °C		1868 psi
@Strain 2.40 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.11 MPa
@Strain 3.64 %,
Temperature 150 °C		1901 psi
@Strain 3.64 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.19 MPa
@Strain 3.62 %,
Temperature 120 °C		1913 psi
@Strain 3.62 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.32 MPa
@Strain 6.03 %,
Temperature 150 °C		1932 psi
@Strain 6.03 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.29 MPa
@Strain 7.23 %,
Temperature 150 °C		2073 psi
@Strain 7.23 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.06 MPa
@Strain 4.82 %,
Temperature 150 °C		2184 psi
@Strain 4.82 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.07 MPa
@Strain 8.43 %,
Temperature 150 °C		2186 psi
@Strain 8.43 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.3 MPa
@Strain 4.82 %,
Temperature 120 °C		2220 psi
@Strain 4.82 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.7 MPa
@Strain 3.61 %,
Temperature 90.0 °C		2280 psi
@Strain 3.61 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 15.73 MPa
@Strain 9.63 %,
Temperature 150 °C		2281 psi
@Strain 9.63 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 15.79 MPa
@Strain 2.40 %,
Temperature 90.0 °C		2290 psi
@Strain 2.40 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 15.89 MPa
@Strain 1.22 %,
Temperature 60.0 °C		2305 psi
@Strain 1.22 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 16.56 MPa
@Strain 3.64 %,
Temperature 120 °C		2402 psi
@Strain 3.64 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.59 MPa
@Strain 6.01 %,
Temperature 150 °C		2406 psi
@Strain 6.01 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.9 MPa
@Strain 6.02 %,
Temperature 120 °C		2450 psi
@Strain 6.02 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 17.08 MPa
@Strain 2.43 %,
Temperature 60.0 °C		2477 psi
@Strain 2.43 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.24 MPa
@Strain 1.23 %,
Temperature 23.0 °C		2500 psi
@Strain 1.23 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 17.84 MPa
@Strain 7.25 %,
Temperature 150 °C		2587 psi
@Strain 7.25 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.22 MPa
@Strain 7.21 %,
Temperature 120 °C		2643 psi
@Strain 7.21 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.34 MPa
@Strain 4.81 %,
Temperature 90.0 °C		2660 psi
@Strain 4.81 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 18.84 MPa
@Strain 8.43 %,
Temperature 150 °C		2733 psi
@Strain 8.43 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.16 MPa
@Strain 4.83 %,
Temperature 120 °C		2779 psi
@Strain 4.83 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 19.28 MPa
@Strain 8.41 %,
Temperature 120 °C		2796 psi
@Strain 8.41 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 19.6 MPa
@Strain 2.44 %,
Temperature 40.0 °C		2840 psi
@Strain 2.44 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 19.67 MPa
@Strain 9.61 %,
Temperature 150 °C		2853 psi
@Strain 9.61 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 19.91 MPa
@Strain 0.390 %,
Temperature 0.000 °C		2888 psi
@Strain 0.390 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 20.0 MPa
@Strain 0.390 %,
Temperature -20.0 °C		2900 psi
@Strain 0.390 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 20.19 MPa
@Strain 9.61 %,
Temperature 120 °C		2928 psi
@Strain 9.61 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 20.34 MPa
@Strain 3.64 %,
Temperature 90.0 °C		2950 psi
@Strain 3.64 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 20.36 MPa
@Strain 6.00 %,
Temperature 90.0 °C		2953 psi
@Strain 6.00 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 20.94 MPa
@Strain 10.81 %,
Temperature 120 °C		3037 psi
@Strain 10.81 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 21.18 MPa
@Strain 6.02 %,
Temperature 120 °C		3072 psi
@Strain 6.02 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 21.41 MPa
@Strain 3.64 %,
Temperature 60.0 °C		3105 psi
@Strain 3.64 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.6 MPa
@Strain 12.0 %,
Temperature 120 °C		3130 psi
@Strain 12.0 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 22.08 MPa
@Strain 7.26 %,
Temperature 90.0 °C		3202 psi
@Strain 7.26 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 22.74 MPa
@Strain 7.20 %,
Temperature 120 °C		3298 psi
@Strain 7.20 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.41 MPa
@Strain 8.45 %,
Temperature 90.0 °C		3395 psi
@Strain 8.45 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 23.52 MPa
@Strain 2.41 %,
Temperature 60.0 °C		3411 psi
@Strain 2.41 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.61 MPa
@Strain 4.83 %,
Temperature 90.0 °C		3424 psi
@Strain 4.83 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 24.08 MPa
@Strain 8.45 %,
Temperature 120 °C		3493 psi
@Strain 8.45 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 24.51 MPa
@Strain 9.65 %,
Temperature 90.0 °C		3555 psi
@Strain 9.65 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 24.53 MPa
@Strain 3.64 %,
Temperature 40.0 °C		3558 psi
@Strain 3.64 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 24.67 MPa
@Strain 4.84 %,
Temperature 60.0 °C		3578 psi
@Strain 4.84 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.1 MPa
@Strain 9.63 %,
Temperature 120 °C		3640 psi
@Strain 9.63 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 25.65 MPa
@Strain 2.43 %,
Temperature 23.0 °C		3720 psi
@Strain 2.43 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 25.98 MPa
@Strain 10.82 %,
Temperature 120 °C		3768 psi
@Strain 10.82 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 26.15 MPa
@Strain 6.02 %,
Temperature 90.0 °C		3793 psi
@Strain 6.02 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.73 MPa
@Strain 12.01 %,
Temperature 120 °C		3877 psi
@Strain 12.01 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 27.07 MPa
@Strain 6.04 %,
Temperature 60.0 °C		3926 psi
@Strain 6.04 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 28.12 MPa
@Strain 7.20 %,
Temperature 90.0 °C		4078 psi
@Strain 7.20 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 28.29 MPa
@Strain 4.85 %,
Temperature 40.0 °C		4103 psi
@Strain 4.85 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 28.75 MPa
@Strain 3.65 %,
Temperature 60.0 °C		4170 psi
@Strain 3.65 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 28.97 MPa
@Strain 7.24 %,
Temperature 60.0 °C		4202 psi
@Strain 7.24 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 29.8 MPa
@Strain 8.45 %,
Temperature 90.0 °C		4320 psi
@Strain 8.45 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 30.42 MPa
@Strain 8.44 %,
Temperature 60.0 °C		4412 psi
@Strain 8.44 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 30.94 MPa
@Strain 3.63 %,
Temperature 23.0 °C		4487 psi
@Strain 3.63 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 31.08 MPa
@Strain 9.63 %,
Temperature 90.0 °C		4508 psi
@Strain 9.63 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 31.16 MPa
@Strain 6.05 %,
Temperature 40.0 °C		4519 psi
@Strain 6.05 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 31.59 MPa
@Strain 9.65 %,
Temperature 60.0 °C		4582 psi
@Strain 9.65 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 32.14 MPa
@Strain 10.82 %,
Temperature 90.0 °C		4662 psi
@Strain 10.82 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 32.6 MPa
@Strain 4.84 %,
Temperature 60.0 °C		4730 psi
@Strain 4.84 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 33.03 MPa
@Strain 12.0 %,
Temperature 90.0 °C		4791 psi
@Strain 12.0 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 33.46 MPa
@Strain 7.26 %,
Temperature 40.0 °C		4853 psi
@Strain 7.26 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 33.84 MPa
@Strain 13.25 %,
Temperature 90.0 °C		4908 psi
@Strain 13.25 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 34.96 MPa
@Strain 4.83 %,
Temperature 23.0 °C		5071 psi
@Strain 4.83 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 35.15 MPa
@Strain 8.40 %,
Temperature 40.0 °C		5098 psi
@Strain 8.40 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.73 MPa
@Strain 6.03 %,
Temperature 60.0 °C		5182 psi
@Strain 6.03 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.59 MPa
@Strain 9.61 %,
Temperature 40.0 °C		5307 psi
@Strain 9.61 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 36.63 MPa
@Strain 0.770 %,
Temperature 23.0 °C		5313 psi
@Strain 0.770 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 37.44 MPa
@Strain 1.12 %,
Temperature 0.000 °C		5430 psi
@Strain 1.12 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 37.71 MPa
@Strain 10.81 %,
Temperature 40.0 °C		5469 psi
@Strain 10.81 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 38.09 MPa
@Strain 6.03 %,
Temperature 23.0 °C		5524 psi
@Strain 6.03 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 38.16 MPa
@Strain 7.22 %,
Temperature 60.0 °C		5535 psi
@Strain 7.22 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 38.64 MPa
@Strain 12.02 %,
Temperature 40.0 °C		5604 psi
@Strain 12.02 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 39.21 MPa
@Strain 1.21 %,
Temperature 40.0 °C		5687 psi
@Strain 1.21 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 39.47 MPa
@Strain 0.740 %,
Temperature -20.0 °C		5725 psi
@Strain 0.740 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 39.6 MPa
@Strain 0.800 %,
Temperature 0.000 °C		5740 psi
@Strain 0.800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 40.2 MPa
@Strain 8.40 %,
Temperature 60.0 °C		5830 psi
@Strain 8.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 40.61 MPa
@Strain 7.23 %,
Temperature 23.0 °C		5890 psi
@Strain 7.23 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 41.9 MPa
@Strain 9.65 %,
Temperature 60.0 °C		6080 psi
@Strain 9.65 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 42.58 MPa
@Strain 8.43 %,
Temperature 23.0 °C		6176 psi
@Strain 8.43 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 43.24 MPa
@Strain 10.84 %,
Temperature 60.0 °C		6271 psi
@Strain 10.84 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 43.57 MPa
@Strain 0.880 %,
Temperature -20.0 °C		6319 psi
@Strain 0.880 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 44.15 MPa
@Strain 9.62 %,
Temperature 23.0 °C		6403 psi
@Strain 9.62 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 44.34 MPa
@Strain 12.03 %,
Temperature 60.0 °C		6431 psi
@Strain 12.03 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.3 MPa
@Strain 13.21 %,
Temperature 60.0 °C		6570 psi
@Strain 13.21 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.36 MPa
@Strain 10.82 %,
Temperature 23.0 °C		6579 psi
@Strain 10.82 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.11 MPa
@Strain 14.4 %,
Temperature 60.0 °C		6688 psi
@Strain 14.4 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 46.36 MPa
@Strain 12.02 %,
Temperature 23.0 °C		6724 psi
@Strain 12.02 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.82 MPa
@Strain 15.65 %,
Temperature 60.0 °C		6791 psi
@Strain 15.65 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 47.11 MPa
@Strain 13.22 %,
Temperature 23.0 °C		6833 psi
@Strain 13.22 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 47.7 MPa
@Strain 14.42 %,
Temperature 23.0 °C		6920 psi
@Strain 14.42 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 52.45 MPa
@Strain 2.16 %,
Temperature 0.000 °C		7607 psi
@Strain 2.16 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 53.89 MPa
@Strain 1.10 %,
Temperature -20.0 °C		7816 psi
@Strain 1.10 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 53.98 MPa
@Strain 2.43 %,
Temperature 40.0 °C		7829 psi
@Strain 2.43 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 55.97 MPa
@Strain 3.62 %,
Temperature 40.0 °C		8118 psi
@Strain 3.62 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 56.18 MPa
@Strain 1.17 %,
Temperature 0.000 °C		8148 psi
@Strain 1.17 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 58.2 MPa
@Strain 3.25 %,
Temperature 0.000 °C		8440 psi
@Strain 3.25 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 60.98 MPa
@Strain 4.29 %,
Temperature 0.000 °C		8844 psi
@Strain 4.29 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.04 MPa
@Strain 5.38 %,
Temperature 0.000 °C		9143 psi
@Strain 5.38 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 63.77 MPa
@Strain 1.33 %,
Temperature -20.0 °C		9249 psi
@Strain 1.33 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 64.75 MPa
@Strain 6.48 %,
Temperature 0.000 °C		9391 psi
@Strain 6.48 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 65.37 MPa
@Strain 1.53 %,
Temperature 23.0 °C		9481 psi
@Strain 1.53 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.1 MPa
@Strain 7.51 %,
Temperature 0.000 °C		9590 psi
@Strain 7.51 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 67.0 MPa
@Strain 1.49 %,
Temperature -20.0 °C		9720 psi
@Strain 1.49 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 67.28 MPa
@Strain 8.61 %,
Temperature 0.000 °C		9758 psi
@Strain 8.61 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 68.29 MPa
@Strain 9.70 %,
Temperature 0.000 °C		9905 psi
@Strain 9.70 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.07 MPa
@Strain 10.74 %,
Temperature 0.000 °C		10020 psi
@Strain 10.74 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 69.78 MPa
@Strain 11.83 %,
Temperature 0.000 °C		10120 psi
@Strain 11.83 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 70.63 MPa
@Strain 1.54 %,
Temperature 0.000 °C		10240 psi
@Strain 1.54 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 72.83 MPa
@Strain 1.55 %,
Temperature -20.0 °C		10560 psi
@Strain 1.55 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 79.7 MPa
@Strain 2.21 %,
Temperature -20.0 °C		11600 psi
@Strain 2.21 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 80.51 MPa
@Strain 2.27 %,
Temperature 23.0 °C		11680 psi
@Strain 2.27 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 80.91 MPa
@Strain 1.77 %,
Temperature -20.0 °C		11740 psi
@Strain 1.77 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 82.87 MPa
@Strain 1.95 %,
Temperature 0.000 °C		12020 psi
@Strain 1.95 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.89 MPa
@Strain 2.97 %,
Temperature -20.0 °C		12310 psi
@Strain 2.97 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 85.21 MPa
@Strain 3.03 %,
Temperature 23.0 °C		12360 psi
@Strain 3.03 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 86.88 MPa
@Strain 3.69 %,
Temperature -20.0 °C		12600 psi
@Strain 3.69 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 87.74 MPa
@Strain 1.98 %,
Temperature -20.0 °C		12730 psi
@Strain 1.98 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 87.95 MPa
@Strain 4.44 %,
Temperature -20.0 °C		12760 psi
@Strain 4.44 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 88.69 MPa
@Strain 5.16 %,
Temperature -20.0 °C		12860 psi
@Strain 5.16 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 90.88 MPa
@Strain 2.32 %,
Temperature 0.000 °C		13180 psi
@Strain 2.32 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 93.88 MPa
@Strain 2.20 %,
Temperature -20.0 °C		13620 psi
@Strain 2.20 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 96.16 MPa
@Strain 2.69 %,
Temperature 0.000 °C		13950 psi
@Strain 2.69 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 99.04 MPa
@Strain 2.43 %,
Temperature -20.0 °C		14360 psi
@Strain 2.43 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 99.57 MPa
@Strain 3.10 %,
Temperature 0.000 °C		14440 psi
@Strain 3.10 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 100.83 MPa
@Strain 3.47 %,
Temperature 0.000 °C		14624 psi
@Strain 3.47 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 103.22 MPa
@Strain 2.65 %,
Temperature -20.0 °C		14971 psi
@Strain 2.65 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 106.58 MPa
@Strain 2.87 %,
Temperature -20.0 °C		15458 psi
@Strain 2.87 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 109.4 MPa
@Strain 3.09 %,
Temperature -20.0 °C		15870 psi
@Strain 3.09 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 111.23 MPa
@Strain 3.30 %,
Temperature -20.0 °C		16133 psi
@Strain 3.30 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 112.67 MPa
@Strain 3.52 %,
Temperature -20.0 °C		16341 psi
@Strain 3.52 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 113.65 MPa
@Strain 3.75 %,
Temperature -20.0 °C		16484 psi
@Strain 3.75 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
Elongation at Break  15 %
@Temperature 23.0 °C		15 %
@Temperature 73.4 °F		DAM; ISO 527
 40 %
@Temperature 23.0 °C		40 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  1.70 GPa
@Temperature 23.0 °C		247 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 4.80 GPa
@Temperature 23.0 °C		696 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  1.80 GPa
@Temperature 23.0 °C		261 ksi
@Temperature 73.4 °F		50%RH; ISO 178
 4.80 GPa
@Temperature 23.0 °C		696 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 5.50 kJ/m²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 9.00 kJ/m²
@Temperature 23.0 °C		4.28 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  8.50 J/cm²
@Temperature -30.0 °C		40.4 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 8.50 J/cm²
@Temperature -30.0 °C		40.4 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 11.0 J/cm²
@Temperature 23.0 °C		52.3 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
Charpy Impact, Notched  0.350 J/cm²
@Temperature -30.0 °C		1.67 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.350 J/cm²
@Temperature -30.0 °C		1.67 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.550 J/cm²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 1.10 J/cm²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 1180 MPa
@Temperature 23.0 °C		171000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.141 %,
Temperature 90.0 °C		145 psi
@Strain 0.141 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.116 %,
Temperature 90.0 °C		145 psi
@Strain 0.116 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 1.75 MPa
@Strain 0.170 %,
Temperature 60.0 °C		254 psi
@Strain 0.170 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 1.75 MPa
@Strain 0.242 %,
Temperature 60.0 °C		254 psi
@Strain 0.242 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.282 %,
Temperature 90.0 °C		290 psi
@Strain 0.282 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.232 %,
Temperature 90.0 °C		290 psi
@Strain 0.232 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.201 %,
Temperature 23.0 °C		348 psi
@Strain 0.201 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.244 %,
Temperature 23.0 °C		348 psi
@Strain 0.244 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.424 %,
Temperature 90.0 °C		435 psi
@Strain 0.424 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.350 %,
Temperature 90.0 °C		435 psi
@Strain 0.350 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.487 %,
Temperature 60.0 °C		508 psi
@Strain 0.487 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.344 %,
Temperature 60.0 °C		508 psi
@Strain 0.344 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.566 %,
Temperature 90.0 °C		580 psi
@Strain 0.566 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.469 %,
Temperature 90.0 °C		580 psi
@Strain 0.469 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.410 %,
Temperature 23.0 °C		696 psi
@Strain 0.410 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.496 %,
Temperature 23.0 °C		696 psi
@Strain 0.496 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.711 %,
Temperature 90.0 °C		725 psi
@Strain 0.711 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.591 %,
Temperature 90.0 °C		725 psi
@Strain 0.591 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 5.25 MPa
@Strain 0.739 %,
Temperature 60.0 °C		761 psi
@Strain 0.739 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 5.25 MPa
@Strain 0.526 %,
Temperature 60.0 °C		761 psi
@Strain 0.526 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.857 %,
Temperature 90.0 °C		870 psi
@Strain 0.857 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.716 %,
Temperature 90.0 °C		870 psi
@Strain 0.716 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 7.00 MPa
@Strain 1.01 %,
Temperature 90.0 °C		1020 psi
@Strain 1.01 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 7.00 MPa
@Strain 1.00 %,
Temperature 60.0 °C		1020 psi
@Strain 1.00 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 7.00 MPa
@Strain 0.720 %,
Temperature 60.0 °C		1020 psi
@Strain 0.720 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 7.00 MPa
@Strain 0.845 %,
Temperature 90.0 °C		1020 psi
@Strain 0.845 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.763 %,
Temperature 23.0 °C		1040 psi
@Strain 0.763 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.631 %,
Temperature 23.0 °C		1040 psi
@Strain 0.631 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.15 %,
Temperature 90.0 °C		1160 psi
@Strain 1.15 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 8.00 MPa
@Strain 0.978 %,
Temperature 90.0 °C		1160 psi
@Strain 0.978 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 8.75 MPa
@Strain 0.929 %,
Temperature 60.0 °C		1270 psi
@Strain 0.929 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 8.75 MPa
@Strain 1.28 %,
Temperature 60.0 °C		1270 psi
@Strain 1.28 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 9.00 MPa
@Strain 1.31 %,
Temperature 90.0 °C		1310 psi
@Strain 1.31 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 9.00 MPa
@Strain 1.12 %,
Temperature 90.0 °C		1310 psi
@Strain 1.12 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.05 %,
Temperature 23.0 °C		1390 psi
@Strain 1.05 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 9.60 MPa
@Strain 0.874 %,
Temperature 23.0 °C		1390 psi
@Strain 0.874 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 10.0 MPa
@Strain 1.47 %,
Temperature 90.0 °C		1450 psi
@Strain 1.47 %,
Temperature 194 °F		50%RH; 10h; Break; Isochronous; ISO 899
 10.0 MPa
@Strain 1.26 %,
Temperature 90.0 °C		1450 psi
@Strain 1.26 %,
Temperature 194 °F		50%RH; 1h; Break; Isochronous; ISO 899
 10.5 MPa
@Strain 1.58 %,
Temperature 60.0 °C		1520 psi
@Strain 1.58 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 10.5 MPa
@Strain 1.16 %,
Temperature 60.0 °C		1520 psi
@Strain 1.16 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.38 %,
Temperature 23.0 °C		1740 psi
@Strain 1.38 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.15 %,
Temperature 23.0 °C		1740 psi
@Strain 1.15 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 12.2 MPa
@Strain 1.90 %,
Temperature 60.0 °C		1770 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 12.2 MPa
@Strain 1.42 %,
Temperature 60.0 °C		1770 psi
@Strain 1.42 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 14.0 MPa
@Strain 1.71 %,
Temperature 60.0 °C		2030 psi
@Strain 1.71 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 14.0 MPa
@Strain 2.24 %,
Temperature 60.0 °C		2030 psi
@Strain 2.24 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 14.4 MPa
@Strain 1.46 %,
Temperature 23.0 °C		2090 psi
@Strain 1.46 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 14.4 MPa
@Strain 1.74 %,
Temperature 23.0 °C		2090 psi
@Strain 1.74 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 15.8 MPa
@Strain 2.62 %,
Temperature 60.0 °C		2290 psi
@Strain 2.62 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 15.8 MPa
@Strain 2.03 %,
Temperature 60.0 °C		2290 psi
@Strain 2.03 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 16.8 MPa
@Strain 2.15 %,
Temperature 23.0 °C		2440 psi
@Strain 2.15 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 16.8 MPa
@Strain 1.82 %,
Temperature 23.0 °C		2440 psi
@Strain 1.82 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 17.5 MPa
@Strain 3.04 %,
Temperature 60.0 °C		2540 psi
@Strain 3.04 %,
Temperature 140 °F		50%RH; 10h; Break; Isochronous; ISO 899
 17.5 MPa
@Strain 2.40 %,
Temperature 60.0 °C		2540 psi
@Strain 2.40 %,
Temperature 140 °F		50%RH; 1h; Break; Isochronous; ISO 899
 19.2 MPa
@Strain 2.64 %,
Temperature 23.0 °C		2780 psi
@Strain 2.64 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 19.2 MPa
@Strain 2.23 %,
Temperature 23.0 °C		2780 psi
@Strain 2.23 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 21.6 MPa
@Strain 2.73 %,
Temperature 23.0 °C		3130 psi
@Strain 2.73 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 21.6 MPa
@Strain 3.20 %,
Temperature 23.0 °C		3130 psi
@Strain 3.20 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 24.0 MPa
@Strain 3.86 %,
Temperature 23.0 °C		3480 psi
@Strain 3.86 %,
Temperature 73.4 °F		50%RH; 10h; Break; Isochronous; ISO 899
 24.0 MPa
@Strain 3.31 %,
Temperature 23.0 °C		3480 psi
@Strain 3.31 %,
Temperature 73.4 °F		50%RH; 1h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 740 MPa
@Temperature 23.0 °C		107000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.207 %,
Temperature 90.0 °C		145 psi
@Strain 0.207 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.186 %,
Temperature 90.0 °C		145 psi
@Strain 0.186 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 1.00 MPa
@Strain 0.165 %,
Temperature 90.0 °C		145 psi
@Strain 0.165 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 1.75 MPa
@Strain 0.294 %,
Temperature 60.0 °C		254 psi
@Strain 0.294 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 1.75 MPa
@Strain 0.309 %,
Temperature 60.0 °C		254 psi
@Strain 0.309 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 1.75 MPa
@Strain 0.317 %,
Temperature 60.0 °C		254 psi
@Strain 0.317 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.413 %,
Temperature 90.0 °C		290 psi
@Strain 0.413 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.373 %,
Temperature 90.0 °C		290 psi
@Strain 0.373 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 2.00 MPa
@Strain 0.331 %,
Temperature 90.0 °C		290 psi
@Strain 0.331 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.287 %,
Temperature 23.0 °C		348 psi
@Strain 0.287 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.360 %,
Temperature 23.0 °C		348 psi
@Strain 0.360 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 2.40 MPa
@Strain 0.324 %,
Temperature 23.0 °C		348 psi
@Strain 0.324 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.496 %,
Temperature 90.0 °C		435 psi
@Strain 0.496 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.560 %,
Temperature 90.0 °C		435 psi
@Strain 0.560 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 3.00 MPa
@Strain 0.621 %,
Temperature 90.0 °C		435 psi
@Strain 0.621 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.621 %,
Temperature 60.0 °C		508 psi
@Strain 0.621 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.591 %,
Temperature 60.0 °C		508 psi
@Strain 0.591 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 3.50 MPa
@Strain 0.638 %,
Temperature 60.0 °C		508 psi
@Strain 0.638 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.663 %,
Temperature 90.0 °C		580 psi
@Strain 0.663 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.829 %,
Temperature 90.0 °C		580 psi
@Strain 0.829 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 4.00 MPa
@Strain 0.748 %,
Temperature 90.0 °C		580 psi
@Strain 0.748 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.656 %,
Temperature 23.0 °C		696 psi
@Strain 0.656 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.582 %,
Temperature 23.0 °C		696 psi
@Strain 0.582 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 4.80 MPa
@Strain 0.727 %,
Temperature 23.0 °C		696 psi
@Strain 0.727 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.830 %,
Temperature 90.0 °C		725 psi
@Strain 0.830 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 5.00 MPa
@Strain 1.04 %,
Temperature 90.0 °C		725 psi
@Strain 1.04 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.936 %,
Temperature 90.0 °C		725 psi
@Strain 0.936 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 5.25 MPa
@Strain 0.940 %,
Temperature 60.0 °C		761 psi
@Strain 0.940 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 5.25 MPa
@Strain 0.895 %,
Temperature 60.0 °C		761 psi
@Strain 0.895 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 5.25 MPa
@Strain 0.965 %,
Temperature 60.0 °C		761 psi
@Strain 0.965 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 6.00 MPa
@Strain 1.00 %,
Temperature 90.0 °C		870 psi
@Strain 1.00 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 6.00 MPa
@Strain 1.13 %,
Temperature 90.0 °C		870 psi
@Strain 1.13 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 1.25 %,
Temperature 90.0 °C		870 psi
@Strain 1.25 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 7.00 MPa
@Strain 1.32 %,
Temperature 90.0 °C		1020 psi
@Strain 1.32 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 7.00 MPa
@Strain 1.27 %,
Temperature 60.0 °C		1020 psi
@Strain 1.27 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 7.00 MPa
@Strain 1.21 %,
Temperature 60.0 °C		1020 psi
@Strain 1.21 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 7.00 MPa
@Strain 1.17 %,
Temperature 90.0 °C		1020 psi
@Strain 1.17 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 7.00 MPa
@Strain 1.30 %,
Temperature 60.0 °C		1020 psi
@Strain 1.30 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 7.00 MPa
@Strain 1.46 %,
Temperature 90.0 °C		1020 psi
@Strain 1.46 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.892 %,
Temperature 23.0 °C		1040 psi
@Strain 0.892 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 7.20 MPa
@Strain 1.00 %,
Temperature 23.0 °C		1040 psi
@Strain 1.00 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 7.20 MPa
@Strain 1.11 %,
Temperature 23.0 °C		1040 psi
@Strain 1.11 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.51 %,
Temperature 90.0 °C		1160 psi
@Strain 1.51 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.34 %,
Temperature 90.0 °C		1160 psi
@Strain 1.34 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 8.00 MPa
@Strain 1.68 %,
Temperature 90.0 °C		1160 psi
@Strain 1.68 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 8.75 MPa
@Strain 1.66 %,
Temperature 60.0 °C		1270 psi
@Strain 1.66 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 8.75 MPa
@Strain 1.54 %,
Temperature 60.0 °C		1270 psi
@Strain 1.54 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 8.75 MPa
@Strain 1.61 %,
Temperature 60.0 °C		1270 psi
@Strain 1.61 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 9.00 MPa
@Strain 1.71 %,
Temperature 90.0 °C		1310 psi
@Strain 1.71 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 9.00 MPa
@Strain 1.51 %,
Temperature 90.0 °C		1310 psi
@Strain 1.51 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 9.00 MPa
@Strain 1.90 %,
Temperature 90.0 °C		1310 psi
@Strain 1.90 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.23 %,
Temperature 23.0 °C		1390 psi
@Strain 1.23 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.37 %,
Temperature 23.0 °C		1390 psi
@Strain 1.37 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 9.60 MPa
@Strain 1.51 %,
Temperature 23.0 °C		1390 psi
@Strain 1.51 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 10.0 MPa
@Strain 1.68 %,
Temperature 90.0 °C		1450 psi
@Strain 1.68 %,
Temperature 194 °F		50%RH; 100h; Break; Isochronous; ISO 899
 10.0 MPa
@Strain 2.12 %,
Temperature 90.0 °C		1450 psi
@Strain 2.12 %,
Temperature 194 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 10.0 MPa
@Strain 1.90 %,
Temperature 90.0 °C		1450 psi
@Strain 1.90 %,
Temperature 194 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 10.5 MPa
@Strain 1.88 %,
Temperature 60.0 °C		1520 psi
@Strain 1.88 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 10.5 MPa
@Strain 2.03 %,
Temperature 60.0 °C		1520 psi
@Strain 2.03 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 10.5 MPa
@Strain 1.97 %,
Temperature 60.0 °C		1520 psi
@Strain 1.97 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.78 %,
Temperature 23.0 °C		1740 psi
@Strain 1.78 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.59 %,
Temperature 23.0 °C		1740 psi
@Strain 1.59 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 12.0 MPa
@Strain 1.95 %,
Temperature 23.0 °C		1740 psi
@Strain 1.95 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 12.2 MPa
@Strain 2.24 %,
Temperature 60.0 °C		1770 psi
@Strain 2.24 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 12.2 MPa
@Strain 2.42 %,
Temperature 60.0 °C		1770 psi
@Strain 2.42 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 12.2 MPa
@Strain 2.35 %,
Temperature 60.0 °C		1770 psi
@Strain 2.35 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 14.0 MPa
@Strain 2.76 %,
Temperature 60.0 °C		2030 psi
@Strain 2.76 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 14.0 MPa
@Strain 2.84 %,
Temperature 60.0 °C		2030 psi
@Strain 2.84 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 14.0 MPa
@Strain 2.63 %,
Temperature 60.0 °C		2030 psi
@Strain 2.63 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 14.4 MPa
@Strain 2.01 %,
Temperature 23.0 °C		2090 psi
@Strain 2.01 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 14.4 MPa
@Strain 2.22 %,
Temperature 23.0 °C		2090 psi
@Strain 2.22 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 14.4 MPa
@Strain 2.43 %,
Temperature 23.0 °C		2090 psi
@Strain 2.43 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 15.8 MPa
@Strain 3.30 %,
Temperature 60.0 °C		2290 psi
@Strain 3.30 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 15.8 MPa
@Strain 3.19 %,
Temperature 60.0 °C		2290 psi
@Strain 3.19 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 15.8 MPa
@Strain 3.04 %,
Temperature 60.0 °C		2290 psi
@Strain 3.04 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 16.8 MPa
@Strain 2.47 %,
Temperature 23.0 °C		2440 psi
@Strain 2.47 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 16.8 MPa
@Strain 2.72 %,
Temperature 23.0 °C		2440 psi
@Strain 2.72 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 16.8 MPa
@Strain 2.95 %,
Temperature 23.0 °C		2440 psi
@Strain 2.95 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 17.5 MPa
@Strain 3.78 %,
Temperature 60.0 °C		2540 psi
@Strain 3.78 %,
Temperature 140 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 17.5 MPa
@Strain 3.66 %,
Temperature 60.0 °C		2540 psi
@Strain 3.66 %,
Temperature 140 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 17.5 MPa
@Strain 3.49 %,
Temperature 60.0 °C		2540 psi
@Strain 3.49 %,
Temperature 140 °F		50%RH; 100h; Break; Isochronous; ISO 899
 19.2 MPa
@Strain 3.00 %,
Temperature 23.0 °C		2780 psi
@Strain 3.00 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 19.2 MPa
@Strain 3.28 %,
Temperature 23.0 °C		2780 psi
@Strain 3.28 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 19.2 MPa
@Strain 3.54 %,
Temperature 23.0 °C		2780 psi
@Strain 3.54 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 21.6 MPa
@Strain 4.20 %,
Temperature 23.0 °C		3130 psi
@Strain 4.20 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 21.6 MPa
@Strain 3.92 %,
Temperature 23.0 °C		3130 psi
@Strain 3.92 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 21.6 MPa
@Strain 3.61 %,
Temperature 23.0 °C		3130 psi
@Strain 3.61 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 24.0 MPa
@Strain 4.32 %,
Temperature 23.0 °C		3480 psi
@Strain 4.32 %,
Temperature 73.4 °F		50%RH; 100h; Break; Isochronous; ISO 899
 24.0 MPa
@Strain 4.65 %,
Temperature 23.0 °C		3480 psi
@Strain 4.65 %,
Temperature 73.4 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 24.0 MPa
@Strain 4.94 %,
Temperature 23.0 °C		3480 psi
@Strain 4.94 %,
Temperature 73.4 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  102 µm/m-°C
@Temperature 23.0 - 55.0 °C		56.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 102 µm/m-°C
@Temperature 23.0 - 55.0 °C		56.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 196 °C385 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C172 °FDAM; ISO 75-1/-2
UL RTI, Electrical 65.0 °C
@Thickness 0.850 mm		149 °F
@Thickness 0.0335 in		DAM; UL 746B
UL RTI, Mechanical with Impact 65.0 °C
@Thickness 0.850 mm		149 °F
@Thickness 0.0335 in		DAM; UL 746B
UL RTI, Mechanical without Impact 65.0 °C
@Thickness 0.850 mm		149 °F
@Thickness 0.0335 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.850 mm		HB
@Thickness 0.0335 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.850 mm		HB
@Thickness 0.0335 in		DAM; UL94
 
Processing PropertiesMetricEnglishComments
Melt Temperature 221 °C430 °F10°C/min; DAM; ISO 11357-1/-3
 270 °C518 °FDAM; Optimum
 260 - 280 °C500 - 536 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesWarp ResistantDAM
 Warpage, LowDAM
FillerMineral fillerDAM
FormsPelletsDAM
GenericNylon 6DAM
Heat StabilizedYesDAM
Material StatusCurrentDAM
Part Marking Code>PA6-MD30<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA6DAM
Processing MethodInjection MoldingDAM
Product CategoryLow Warp ResinsDAM
 Mineral Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA6-MD30ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-46721.html

免责声明: 本文 DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4