- 密度 [g/cm3]: 1.321
- 缺口冲击强度: 10.0
- 弯曲强度 [MPa]: 22.0
- 弯曲模量 [MPa]: 1.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.321 g/cc | 0.04772 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ISO 868 |
| Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | ISO 527 |
| Elongation at Break | 50 % | 50 % | ISO 527 |
| Modulus of Elasticity | 1.75 GPa | 254 ksi | ISO 527 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | DIN 53453 |
| 0.500 J/cm² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | DIN 53453 | |