- 缺口冲击强度: 0.641
- 弯曲强度 [MPa]: 44.8
- 弯曲模量 [MPa]: 9.65
- 热变形温度 [℃]: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 6.50 g/cc | 6.50 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 44.8 MPa | 6500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1500 ksi | ASTM D638 |
| Flexural Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 246 - 254 °C | 475 - 490 °F | |
| Mold Temperature | 57.2 - 82.2 °C | 135 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 4 hour | 4 hour | |