- 密度 [g/cm3]: 1.02
- 弯曲模量 [MPa]: 0.850
- 热变形温度 [℃]: 58.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 28.0 MPa @Temperature 23.0 °C | 4060 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 130 % @Temperature 23.0 °C | 130 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | |||
| 160 % @Temperature 23.0 °C | 160 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Modulus | 0.900 GPa @Temperature 23.0 °C | 131 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 0.850 GPa @Temperature 23.0 °C | 123 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| Charpy Impact, Notched | 11.0 J/cm² @Temperature 23.0 °C | 52.3 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 58.0 °C | 136 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 230 - 240 °C | 446 - 464 °F | DAM; Extrusion | |||
| 235 °C | 455 °F | DAM; Optimum; Extrusion | |||
| 260 °C | 500 °F | DAM; Optimum; Injection Molding | |||
| 250 - 280 °C | 482 - 536 °F | DAM; Injection Molding | |||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | DAM; Injection Molding | ||
| 60.0 °C | 140 °F | DAM; optimum; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Injection Molding | ||
| 80.0 °C | 176 °F | DAM; Extrusion | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Injection Molding | ||
| <= 0.050 % | <= 0.050 % | DAM; Extrusion | |||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Chemical Resistance, Good | DAM | ||||
| Flexibility, Good | DAM | ||||
| Flexibility, Good | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Impact Modified | DAM | ||||
| Impact Modified | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA6-F< | ISO 11469; DAM | |||
| Processing Method | Extrusion | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA6-F | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Cable Jacketing | DAM | |||
| Cable Jacketing | DAM | ||||
| Hose | DAM | ||||
| Hose | DAM | ||||
| Tubing | DAM | ||||
| Tubing | DAM | ||||