- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.955
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.16
- 拉伸强度 [MPa]: 13.0
- 断裂伸长率 [%]: 5.45
- 弯曲强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 0.0100
- 硬度: 55.0
- 热变形温度 [℃]: 45.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 - 11.0 g/cc | 0.0345 - 0.397 lb/in³ | Average value: 1.31 g/cc Grade Count:446 |
| Filler Content | 10.0 - 50.0 % | 10.0 - 50.0 % | Average value: 27.2 % Grade Count:26 |
| Apparent Bulk Density | 0.215 - 0.425 g/cc | 0.00777 - 0.0154 lb/in³ | Average value: 0.361 g/cc Grade Count:8 |
| Water Absorption | 0.0500 - 3.50 % | 0.0500 - 3.50 % | Average value: 1.00 % Grade Count:219 |
| Moisture Absorption at Equilibrium | 0.000 - 2.00 % | 0.000 - 2.00 % | Average value: 0.590 % Grade Count:194 |
| Water Absorption at Saturation | 0.100 - 1.80 % | 0.100 - 1.80 % | Average value: 1.31 % Grade Count:63 |
| Additive Loading | 10.0 - 30.0 % | 10.0 - 30.0 % | Average value: 22.0 % Grade Count:5 |
| Particle Size | 4.00 - 100 µm | 4.00 - 100 µm | Average value: 34.5 µm Grade Count:9 |
| Filament Diameter | 120 - 400 µm | 120 - 400 µm | Average value: 268 µm Grade Count:3 |
| pH | 4.00 - 6.00 | 4.00 - 6.00 | Average value: 4.25 Grade Count:8 |
| Specific Surface Area | 1.00 - 9.00 m²/g | 1.00 - 9.00 m²/g | Average value: 2.44 m²/g Grade Count:8 |
| Viscosity Test | 190 cm³/g | 190 cm³/g | Average value: 190 cm³/g Grade Count:5 |
| Linear Mold Shrinkage | 0.000200 - 0.0200 cm/cm | 0.000200 - 0.0200 in/in | Average value: 0.00653 cm/cm Grade Count:260 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.0200 cm/cm | 0.00200 - 0.0200 in/in | Average value: 0.00966 cm/cm Grade Count:19 |
| Linear Mold Shrinkage, Transverse | 0.000500 - 0.0400 cm/cm | 0.000500 - 0.0400 in/in | Average value: 0.00948 cm/cm Grade Count:159 |
| Melt Flow | 0.500 - 190 g/10 min | 0.500 - 190 g/10 min | Average value: 25.1 g/10 min Grade Count:115 |
| Fiber Count | 2.20 - 60.0 dtex | 1.98 - 54.0 denier | Average value: 21.8 dtex Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 55.0 - 120 | 55.0 - 120 | Average value: 104 Grade Count:36 |
| Hardness, Shore D | 40.0 - 88.0 | 40.0 - 88.0 | Average value: 71.1 Grade Count:98 |
| Ball Indentation Hardness | 20.0 - 230 MPa | 2900 - 33400 psi | Average value: 122 MPa Grade Count:59 |
| Tensile Strength, Ultimate | 17.0 - 827 MPa | 2470 - 120000 psi | Average value: 81.9 MPa Grade Count:330 |
| 15.0 - 34.0 MPa @Temperature 60.0 - 120 °C | 2180 - 4930 psi @Temperature 140 - 248 °F | Average value: 21.3 MPa Grade Count:2 | |
| Tensile Strength, Yield | 13.0 - 170 MPa | 1890 - 24600 psi | Average value: 46.2 MPa Grade Count:316 |
| Elongation at Break | 0.350 - 400 % | 0.350 - 400 % | Average value: 57.1 % Grade Count:478 |
| Elongation at Yield | 1.50 - 45.0 % | 1.50 - 45.0 % | Average value: 11.2 % Grade Count:200 |
| Modulus of Elasticity | 0.00950 - 64.1 GPa | 1.38 - 9300 ksi | Average value: 5.18 GPa Grade Count:378 |
| Tenacity | 0.297 - 0.545 N/tex | 3.37 - 6.17 g/denier | Average value: 0.413 N/tex Grade Count:3 |
| Flexural Yield Strength | 5.45 - 607 MPa | 790 - 88000 psi | Average value: 111 MPa Grade Count:176 |
| Flexural Modulus | 0.0100 - 51.7 GPa | 1.45 - 7500 ksi | Average value: 5.36 GPa Grade Count:198 |
| 0.275 - 0.685 GPa @Temperature 60.0 - 120 °C | 39.9 - 99.4 ksi @Temperature 140 - 248 °F | Average value: 0.450 GPa Grade Count:1 | |
| Compressive Yield Strength | 38.0 - 110 MPa | 5510 - 16000 psi | Average value: 71.0 MPa Grade Count:7 |
| Izod Impact, Notched | 0.160 - 100 J/cm | 0.300 - 187 ft-lb/in | Average value: 1.44 J/cm Grade Count:157 |
| 0.210 - 1.10 J/cm @Temperature -40.0 - -20.0 °C | 0.393 - 2.06 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.387 J/cm Grade Count:6 | |
| Izod Impact, Unnotched | 0.880 J/cm - NB | 1.65 ft-lb/in - NB | Average value: 8.37 J/cm Grade Count:74 |
| Izod Impact, Notched (ISO) | 1.00 - 100000 kJ/m² | 0.476 - 47600 ft-lb/in² | Average value: 13.2 kJ/m² Grade Count:40 |
| Izod Impact, Unnotched (ISO) | 8.00 kJ/m² - NB | 3.81 ft-lb/in² - NB | Average value: 57.3 kJ/m² Grade Count:30 |
| Charpy Impact Unnotched | 0.900 J/cm² - NB | 4.28 ft-lb/in² - NB | Average value: 7.49 J/cm² Grade Count:251 |
| 0.800 J/cm² - NB @Temperature -40.0 - 30.0 °C | 3.81 ft-lb/in² - NB @Temperature -40.0 - 86.0 °F | Average value: 7.36 J/cm² Grade Count:192 | |
| Charpy Impact, Notched | 0.200 J/cm² - NB | 0.952 ft-lb/in² - NB | Average value: 2.05 J/cm² Grade Count:241 |
| 0.200 J/cm² - NB @Temperature -40.0 - 30.0 °C | 0.952 ft-lb/in² - NB @Temperature -40.0 - 86.0 °F | Average value: 0.937 J/cm² Grade Count:224 | |
| Dart Drop, Total Energy | 2.00 - 16.0 J | 1.48 - 11.8 ft-lb | Average value: 9.54 J Grade Count:13 |
| Falling Dart Impact | 9.73 - 13.0 J | 7.18 - 9.59 ft-lb | Average value: 11.2 J Grade Count:3 |
| Coefficient of Friction | 0.0200 - 0.670 | 0.0200 - 0.670 | Average value: 0.303 Grade Count:16 |
| Coefficient of Friction, Static | 0.0800 - 0.520 | 0.0800 - 0.520 | Average value: 0.281 Grade Count:9 |
| Tensile Creep Modulus, 1 hour | 310 - 1300 MPa | 45000 - 189000 psi | Average value: 833 MPa Grade Count:8 |
| Tensile Creep Modulus, 1000 hours | 60.0 - 800 MPa | 8700 - 116000 psi | Average value: 388 MPa Grade Count:12 |
| Tear Strength Test | 0.200 - 52.0 | 0.200 - 52.0 | Average value: 19.1 Grade Count:3 |
| K (wear) Factor | 14.1 - 898 x 10-8 mm³/N-M | 7.00 - 446 x 10-10 in³-min/ft-lb-hr | Average value: 146 x 10-8 mm³/N-M Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00 - 1.00e+16 ohm-cm | 1.00 - 1.00e+16 ohm-cm | Average value: 2.21e+14 ohm-cm Grade Count:253 |
| Surface Resistance | 0.265 - 3.00e+15 ohm | 0.265 - 3.00e+15 ohm | Average value: 1.04e+14 ohm Grade Count:214 |
| Insulation Resistance | 10.0 - 1.00e+14 ohm | 10.0 - 1.00e+14 ohm | Average value: 4.13e+12 ohm Grade Count:25 |
| Static Decay | 0.00200 - 2.00 sec | 0.00200 - 2.00 sec | Average value: 1.33 sec Grade Count:3 |
| Dielectric Constant | 2.00 - 17.0 | 2.00 - 17.0 | Average value: 4.89 Grade Count:75 |
| Dielectric Strength | 0.200 - 100 kV/mm | 5.08 - 2540 kV/in | Average value: 32.8 kV/mm Grade Count:194 |
| Dissipation Factor | 0.000290 - 0.330 | 0.000290 - 0.330 | Average value: 0.0665 Grade Count:82 |
| Dielectric Loss Index | 0.000200 - 0.0400 | 0.000200 - 0.0400 | Average value: 0.0295 Grade Count:4 |
| Comparative Tracking Index | 60.0 - 600 V | 60.0 - 600 V | Average value: 568 V Grade Count:172 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 9.00 - 414 µm/m-°C | 5.00 - 230 µin/in-°F | Average value: 91.4 µm/m-°C Grade Count:249 |
| 22.7 - 292 µm/m-°C @Temperature 46.0 - 160 °C | 12.6 - 162 µin/in-°F @Temperature 115 - 320 °F | Average value: 127 µm/m-°C Grade Count:3 | |
| CTE, linear, Transverse to Flow | 10.6 - 1350 µm/m-°C | 5.89 - 750 µin/in-°F | Average value: 125 µm/m-°C Grade Count:137 |
| 84.0 - 84.0 µm/m-°C @Temperature 60.0 - 100 °C | 46.7 - 46.7 µin/in-°F @Temperature 140 - 212 °F | Average value: 84.0 µm/m-°C Grade Count:1 | |
| Specific Heat Capacity | 1.70 - 2.50 J/g-°C | 0.406 - 0.598 BTU/lb-°F | Average value: 2.06 J/g-°C Grade Count:5 |
| Thermal Conductivity | 0.140 - 37.0 W/m-K | 0.972 - 257 BTU-in/hr-ft²-°F | Average value: 5.15 W/m-K Grade Count:29 |
| Melting Point | 130 - 193 °C | 266 - 380 °F | Average value: 176 °C Grade Count:258 |
| Maximum Service Temperature, Air | 70.0 - 160 °C | 158 - 320 °F | Average value: 120 °C Grade Count:120 |
| Transformation Temperature, Tg | 110 - 160 °C | 230 - 320 °F | Average value: 140 °C Grade Count:16 |
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 193 °C | 113 - 380 °F | Average value: 135 °C Grade Count:262 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 - 190 °C | 104 - 374 °F | Average value: 103 °C Grade Count:308 |
| Deflection Temperature at 8.0 MPa | 40.0 - 160 °C | 104 - 320 °F | Average value: 111 °C Grade Count:36 |
| Vicat Softening Point | 60.0 - 190 °C | 140 - 374 °F | Average value: 151 °C Grade Count:108 |
| Minimum Service Temperature, Air | -100 - -40.0 °C | -148 - -40.0 °F | Average value: -61.7 °C Grade Count:6 |
| Glass Transition Temp, Tg | 41.0 - 170 °C | 106 - 338 °F | Average value: 122 °C Grade Count:5 |
| UL RTI, Electrical | 110 - 120 °C | 230 - 248 °F | Average value: 115 °C Grade Count:4 |
| UL RTI, Mechanical with Impact | 70.0 - 85.0 °C | 158 - 185 °F | Average value: 77.5 °C Grade Count:4 |
| UL RTI, Mechanical without Impact | 95.0 °C | 203 °F | Average value: 95.0 °C Grade Count:4 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:259 |
| Oxygen Index | 21.0 - 26.0 % | 21.0 - 26.0 % | Average value: 24.0 % Grade Count:7 |
| Shrinkage | 7.00 - 16.0 % | 7.00 - 16.0 % | Average value: 11.7 % Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80.0 - 90.0 % | 80.0 - 90.0 % | Average value: 87.3 % Grade Count:22 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 270 °C | 380 - 518 °F | Average value: 234 °C Grade Count:125 |
| Feed Temperature | 40.0 °C | 104 °F | Average value: 40.0 °C Grade Count:34 |
| Nozzle Temperature | 230 - 280 °C | 446 - 536 °F | Average value: 255 °C Grade Count:16 |
| Die Temperature | 230 °C | 446 °F | Average value: 230 °C Grade Count:83 |
| Melt Temperature | 190 - 288 °C | 374 - 550 °F | Average value: 221 °C Grade Count:133 |
| Mold Temperature | 37.8 - 149 °C | 100 - 300 °F | Average value: 74.4 °C Grade Count:109 |
| Injection Velocity | 100 mm/sec | 3.94 in/sec | Average value: 100 mm/sec Grade Count:34 |
| Die Opening | 0.0400 cm | 0.0157 in | Average value: 0.0400 cm Grade Count:83 |
| Roll Temperature | 50.0 °C | 122 °F | Average value: 50.0 °C Grade Count:83 |
| Drying Temperature | 54.4 - 110 °C | 130 - 230 °F | Average value: 94.3 °C Grade Count:130 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 4.90 hour Grade Count:107 |
| Moisture Content | 0.0200 - 1.00 % | 0.0200 - 1.00 % | Average value: 0.365 % Grade Count:28 |
| Dew Point | -40.0 °C | -40.0 °F | Average value: -40.0 °C Grade Count:16 |
| Injection Pressure | 40.0 - 103 MPa | 5800 - 15000 psi | Average value: 67.8 MPa Grade Count:76 |
| Hold Pressure | 25.0 - 50.0 MPa | 3630 - 7250 psi | Average value: 37.5 MPa Grade Count:34 |
| Back Pressure | 0.172 - 5.00 MPa | 24.9 - 725 psi | Average value: 4.62 MPa Grade Count:37 |
| Screw Speed | 15.0 - 76.0 rpm | 15.0 - 76.0 rpm | Average value: 45.5 rpm Grade Count:83 |